V(2)O(5) nanoparticles obtained from a synthetic bariandite-like vanadium oxide: Synthesis, characterization and electrochemical behavior in an ionic liquid

Highly stable and crystalline V(2)O(5) nanoparticles with an average diameter of 15 nm have been easily prepared by thermal treatment of a bariandite-like vanadium oxide, V(10)O(24)center dot 9H(2)O. Their characterization was carried out by powder X-ray diffractometry (XRD). Fourier transform infrared (FT-IR) and Raman spectroscopies, and transmission electron microscopy (TEM). The fibrous and nanostructured film obtained by electrophoretic deposition of the V(2)O(5) nanoparticles showed good electroactivity when submitted to cyclic voltammetry in an ionic liquid-based electrolyte. The use of this film for the preparation of a nanostructured electrode led to an improvement of about 50% in discharge capacity values when compared with similar electrodes obtained by casting of a V(2)O(5) xerogel. (C) 2009 Elsevier Inc. All rights reserved.

Spectroscopic characterization of the structural changes of polyaniline nanofibers after heating

The thermal behavior of PANI nanofibers doped with beta-naphthalenesulfonic acid (beta-NSA) was investigated and their morphological and structural changes after heating were monitored by SEM, XRD and Raman techniques, respectively. By using electron-scanning microscopy it is possible to verify that the nanofiber morphology is stable and no polymer degradation is observed in thermogravimetric (TG) data up to 200 degrees C. Nevertheless, the heating promotes the formation of cross-linking structures (phenazine and/or oxazine-like rings), that is clearly demonstrated by the presence of bands at ca. 578, 1398, and 1644 cm(-1) in resonance Raman spectra of heated PANI-NSA samples. The most important consequence of the formation of cross-linking structures in PANI-NSA samples is that these samples retain their nanofiber morphology upon HCl doping in contrast to PANI-NSA nanofibers without heating. (c) 2007 Elsevier Ltd. All rights reserved.

Photocatalyst TiO(2)-Co: the effect of doping depth profile on methylene blue degradation

In this work, we study the effect of doping depth profile on the photocatalytic and surface properties of TiO(2) films. Two thin film layers of TiO(2) (200 nm) and Co (5 nm), respectively, were deposited by physical evaporation on glass substrate. These films were annealed for 1 s at 100 and 400 A degrees C and the Co layer was removed by chemical etching. Atomic force microscopy (AFM) phase images showed changes in the surface in function of thermal treatment. The grazing-incidence X-ray fluorescence (GIXRF) measurements indicated that the thermal treatment caused migration of Co atoms to below the surface, the depths found were between 19 and 29 nm. The contact angle showed distinct values in function of the doped profile or Co surface concentration. The UV-vis spectra presented a red shift with the increasing of thermal treatment. Photocatalytical assays were performed by methylene blue discoloration and the higher activity was found for TiO(2)-Co treated at 400 A degrees C, the ESI-MS showed the fragments formed during the methylene blue decomposition.

Photocatalytic decomposition of methylene blue via Fenton mechanisms by silicon wafer doped with Au and Cu: a theoretical and experimental study

In this work, we studied the photocatalytic and the structural aspects of silicon wafers doped with Au and Cu submitted to thermal treatment. The materials were obtained by deposition of metals on Si using the sputtering method followed by fast heating method. The photocatalyst materials were characterized by synchrotron-grazing incidence X-ray fluorescence, ultraviolet-visible spectroscopy, X-ray diffraction, and assays of H(2)O(2) degradation. The doping process decreases the optical band gap of materials and the doping with Au causes structural changes. The best photocatalytic activity was found for thermally treated material doped with Au. Theoretical calculations at density functional theory level are in agreement with the experimental data.

The role of cross-linking structures to the formation of one-dimensional nano-organized polyaniline and their Raman fingerprint

In the present work. the resonance Raman. UV-vis-NIR and scanning electron microscopic (SEM) data of nanorods (about similar to 300 rim in diameter) and nanofibers (about similar to 93 nm in diameter) of PANI are presented and compared. The PANI samples were synthesized in aqueous media with dodecybenzenesulfonic acid (DBSA) and beta-naphtalenesulfonic acid (beta-NSA) as dopants, respectively. The presence of hands at 578, 1400 and 1632cm(-1) in the Raman spectra of PANI-NSA and PANI-DBSA shows that the formation of cross-linking structures is a general feature of the PANI chains prepared in micellar media. It is proposed that these structures are responsible for the one-dimensional PANI morphology formation. In addition, the Raman band at 609cm(-1) of PANI fibers is correlated with the extended PANI chain coil formation. (C) 2008 Elsevier B.V. All rights reserved.

Study of ethanol electro-oxidation in acid environment on Pt(3)Sn/C anode catalysts prepared by a modified polymeric precursor method under controlled synthesis conditions

A carbon-supported binary Pt(3)Sn catalyst has been prepared using a modified polymeric precursor method under controlled synthesis conditions This material was characterized using X-ray diffraction (XRD). and the results indicate that 23% (of a possible 25%) of Sn is alloyed with Pt, forming a dominant Pt(3)Sn phase. Transmission election microscopy (TEM) shows good dispersion of the electrocatalyst and small particle sizes (3 6 nm +/- 1 nm) The polarization curves for a direct ethanol fuel cell using Pt(3)Sn/C as the anode demonstrated Improved performance compared to that of a PtSn/C E-TEK. especially in the intrinsic resistance-controlled and mass transfer regions. This behavior is probably associated with the Pt(3)Sn phase. The maximum power density for the Pt(3)Sn/C electrocatalyst (58 mW cm(-2)) is nearly twice that of a PtSn/C E-TEK electrocatalyst (33 mW cm(-2)) This behavior is attributed to the presence of a mixed Pt(9)Sn and Pt(3)Sn alloy phase in the commercial catalysts (C) 2009 Elsevier B V All rights reserved

Projeto, construção e analise de células de carga de placa e de anel

Iniciamos o presente trabalho fazendo um estudo comparativo entre duas células de carga de compressão, ambas em formato cilíndrico, possuindo internamente, à meia altura do corpo, uma placa engastada. Estas duas células de carga são de aço SAE 1045; para uma delas adaptamos um modelo matemático teórico, através do qual foram pré-determinadas as suas dimensões, objetivando em comportamento ótimo no que se refere às distribuições de tensões e deformações, esta denominamos de Célula de Carga I. Na outra, denominada de Célula de Carga II, alteramos algumas dimensões, com a finalidade de comparar seu comportamento em relação à primeira. Também, no transcorrer do trabalho analisamos e comparamos os resultados matemáticos com os valores práticos encontrados. Frente aos resultados obtidos neste estudo prévio, projetamos, construímos e analisamos cinco outras células de carga (Células de Carga III, IV, V, VI e VII), em termos de geometria, material e tratamento térmico, visando o aperfeiçoamento de tais transdutores de força no que concerne a usinagem, resposta de sinal elétrico, limitações e aplicações industriais.

Efeito do consumo de farinha de linhaça (Linum usitatissimum) no crescimento de ratos Wistar e relação com a digestibilidade de globulinas e fatores antinutricionais protéicos

Linseed is an important oilseed consumed raw as nutritional supplement, that although represents a rich source of nutrients, its nutritional value could be impaired due to the presence of antinutritional factors. In this study, protein fractions from raw linseed flour were extracted and isolated being obtained 12% of albumins, 82% of globulins, 5% of glutelins and 1% of prolamins. These proteins were visualized by SDS-PAGE and albumins showed low molecular mass protein bands around 21 kDa and minor bands, similar to that of trypsin inhibitor; Globulins presented protein bands with high molecular masses, which possibly are constituents of multimeric proteins, such as legumins. After determination of the centesimal composition of raw linseed, it was used as exclusive protein source for young rats to evaluate its effect on animal growth. The results showed negative effects on rat growth (weight gain 73% less than the control group) and reduction of intestinal villus (35%), that could be related with in vitro and in vivo globulin digestibility and proteinaceous antinutritional factors (mammalian digestive enzymes inhibitors and lectins) in albumin fraction. Native globulins showed, by SDS-PAGE, low susceptibility in vitro to trypsin and chymotrypsin, however presented high degradation by pancreatin. Thermal treatment of globulins for 5 and 15 minutes at 100ºC improved considerably its digestibility by trypsin and pancreatin. Globulins presented 93.2% in vivo digestibility, similar to the control protein. Albumin fraction had high trypsin inhibition activity (100%) and chymotrypsin inhibition of 28.3%; haemagglutinating activity was not detected. The results of this study indicate the negative action of trypsin inhibitors on animal growth, but can not be discarded its combined action with other antinutritional factors, which could compromise the raw linseed utilization as an alternative food

Obtenção e caracterização de nanopartículas de argilominerais

Natural nanoclays are of great interest particularly for the production of polymer-based nanocomposites. In this work, kaolinite clays from two natural deposits in the State of the Rio Grande do Norte and Paraiba were purified with thermal treatment and chemical treatments, and characterized. Front to the gotten data, had been proposals methodologies for elimination or reduction of coarse particle texts, oxide of iron and organic substance. These methodologies had consisted of the combination of operations with thermal treatments, carried through in electric oven, and acid chemical attacks with and hydrogen peroxide. The Analyzers Thermogravimetric was used to examine the thermal stability of the nanoclays. The analysis indicated weight losses at temperatures under 110 ºC and over the temperature range of 350 to 550 ºC. Based on the thermal analysis data, the samples were submitted to a thermal treatment at 500 °C, for 8 h, to remove organic components. The X-ray diffraction patterns indicated that thermal treatment under 500 °C affect the basic structure of kaolinite. The BET surface area measurements ranged from 32 to 38 m2/g for clay samples with thermal treatment and from 36 to 53 m2/g for chemically treated samples. Thus, although the thermal treatment increased the surface area, through the removal of organic components, the effect was not significant and chemical treatment is more efficient, not affect the basic structure of kaolinite, to improve particle dispersion. SEM analysis confirms that the clay is agglomerated forming micron-size particles

Síntese e caracterização de ferrita ni-zn pelo método dos precursores poliméricos calcinada por energia de microondas

Magnetic ceramics have been widely investigated, especially with respect to intrinsic and extrinsic characteristics of these materials. Among the magnetic ceramic materials of technological interest, there are the ferrites. On the other hand, the thermal treatment of ceramic materials by microwave energy has offered various advantages such as: optimization of production processes, high heat control, low consumption of time and energy among others. In this work were synthesized powders of Ni-Zn ferrite with compositions Ni1- xZnxFe2O4 (0.25 ≤ x ≤ 0.75 mols) by the polymeric precursor route in two heat treatment conditions, conventional oven and microwave energy at 500, 650, 800 and 950°C and its structural, and morphological imaging. The materials were characterized by thermal analysis (TG/ DSC), X-ray diffraction (XRD), absorption spectroscopy in the infrared (FTIR), scanning electron microscopy (SEM), X-ray spectroscopy and energy dispersive (EDS) and vibrating sample magnetometry (VSM). The results of X-ray diffraction confirmed the formation of ferrite with spinel-type cubic structure. The extrinsic characteristics of the powders obtained by microwave calcination and influence significantly the magnetic behavior of ferrites, showing particles ferrimagnéticas characterized as soft magnetic materials (soft), is of great technological interest. The results obtained led the potential application of microwave energy for calcining powders of Ni-Zn ferrite

Síntese e caracterização de catalisadores de LaNiO3 não suportados e suportados em Al2O3 e ZrO2 para a reforma a vapor do metano

Ionic oxides with ABO3 structure, where A represents a rare earth element or an alkaline metal and B is a transition metal from group VIII of the periodic table are potential catalysts for oxidation and good candidates for steam reforming reaction. Different methods have been considered for the synthesis of the oxide materials with perovskite structure to produce a high homogeneous material with low amount of impurities and low calcination temperatures. In the current work, oxides with the LaNiO3 formula had been synthesized using the method of the polymeric precursors. The thermal treatment of the materials took place at 300 ºC for 2h. The material supported in alumina and/or zirconia was calcined at 800 ºC temperature for 4h. The samples had been characterized by the following techniques: thermogravimetry; infrared spectroscopy; X-ray diffraction; specific surface area; distribution of particle size; scanning electron microscopy and thermo-programmed reduction. The steam reforming reaction was carried out in a pilot plant using reducing atmosphere in the reactor with a mixture of 10% H2-Argon, a mass about 5g of catalyst, flowing at 50 mL.min-1. The temperature range used was 50 - 1000 oC with a heating rate of 10 oC.min-1. A thermal conductivity detector was used to analyze the gas after the water trapping, in order to permit to quantify the consumption of hydrogen for the lanthanum nickelates (LaNiO3). The results showed that lanthanum nickelate were more efficient when supported in alumina than when supported in zirconia. It was observed that the methane conversion was approximately 100% and the selectivity to hydrogen was about 70%. In all cases were verified low selectivity to CO and CO2

Termoterapia e quimioterapia de banana 'Prata-Anã' associadas à temperatura de armazenamento no controle de podridões em pós-colheita

O objetivo deste estudo foi avaliar o efeito da termoterapia (56 ºC por 6 min) e quimioterapia (propiconazole 250 ml.l-1) associado com temperatura de armazenamento (temperatura ambiente, 18 ºC e 13 ºC) no controle de podridões de bananas (Musa spp.) 'Prata-Anã' (AAB) em pós-colheita. Os tratamentos apresentaram diferenças significativas na percentagem de área lesionada por fruto, perda de peso e coloração externa da casca em todas as temperaturas de armazenamento. A quimioterapia e a combinação termoterapia e quimioterapia evitaram a manifestação de podridões nas três condições de armazenamento, enquanto a termoterapia reduziu a percentagem de área lesionada por fruto de 98% para 11% em temperatura ambiente, de 8% para 7% em 18 ºC e de 10% para 0% em 13 ºC, sendo mais eficiente sob a temperatura de 13 ºC. Frutos não tratados perderam 25%, 10% e 3% de peso e atingiram a cor 7, 5 e 1 em temperatura ambiente, 18 ºC e 13 ºC, respectivamente. Frutos tratados com termoterapia e quimioterapia perderam 24, 11 e 5% e 20, 10 e 3%, e atingiram índice médio de cor 4 e 3,5, respectivamente. O período de conservação foi estendido para 18, 24 e 45 dias em temperatura ambiente, 18 ºC e 13 ºC, respectivamente. A combinação dos métodos evitou a manifestação de podridões, reduziu a perda de peso e manteve a cor da casca e a qualidade dos frutos.

THE EFFECT of ANIONIC SORPTION on THE METAKAOLINITE

This paper reports an investigation on the effect of thermal activation of kaolinite. It is well known that during calcinations (400-650 degrees C), kaolinite loses the OH lattice water and is transformed into metakaolinite or amorphous material. Arsenic is trace element that is toxic to animals including humans. The adsorption of arsenic on kaolinite was investigated at varying pH and thermal pretreatment. Calcination of sample is carried out at 650 degrees C for 3 h. The decomposition of kaolinite is recorded using methods of thermal analysis. The resultant product is identified by XRD. Laboratory experiments were conducted examining the effect of arsenic by thermally modified kaolinite. The Langmuir isotherm was used to describe arsenite and arsenate sorption by the calcined kaolinite. The equilibrium parameters used were based on experimental data obtained for the dynamic adsorption process of arsenic. Removal of arsenate using natural kaolinite was satisfactory, whereas arsenic was not removed by adsorption with thermally modified kaolinite. Moreover, the adsorption of arsenic by kaolinite and metakaolinite decreases with increasing pH.

CERAMIC MATERIAL FROM SEWAGE SLUDGE AS SUPPORT MATERIAL SUPPLY WATER FILTRATION

This study shows a possibility of using municipal sewage sludge after thermal treatment in the production of a filtering material to water treatment. Due to the fast urbanization and implementation of high standards for effluent in many countries in recent years, the sewage sludge is being produced in an ever increasing amount. Therefore, the use of sludge is a suitable solution for the expected large quantity of sludge. Dehydration of sludge was performed by controlled heating at temperatures of 1100 degrees C, 850 degrees C, 650 degrees C, 350 degrees C for 3 hours. After thermal treatment the sludge was characterized by X-ray fluorescence, TG/DTG/DTA, residue solubilization and residue lixiviation tests. The aim of the present work was to observe, thought the characterization techniques, if the treated sewage sludge is or not adequate to be used as filter material to water treatment. It will be verified which treatment temperature of the sludge offer possibility to its use in water treatment without carrying pollutants in concentrations out of the standards.

Sintered Sewage Sludge As Support Material Used In Drinking Water Filtration

The processing of industry and domestic effluents in wastewater treatment plants reduces the amount of polluted material and forms reusable water and dehydrated sludge. the generation of hazardous municipal sludge can be decreased, as well as the impact on surface and underground water and the risk to human health. The aim this study is to verify the possibility to use sintered sewage sludge as support material after thermal treatment in the production of a filtering material to water supply systems. After thermal treatment the sewage sludge ash was characterized by X-ray fluorescence (XRF), leaching test and water solubilization. Dehydration of sludge was performed by controlled heating at temperatures of 180 degrees C, 350 degrees C, 600 degrees C, 850 degrees C and 1000 degrees C for 3 hours.