Synthesis of an indium oxide nanoparticle embedded graphene three-dimensional architecture for enhanced lithium-ion storage

Indium oxide nanoparticles were synthesised by using a facile and scalable strategy. The as-prepared nanoparticles (20-40 nm) were in situ and homogeneously distributed in a three-dimensional (3D) graphene architecture subsequently during the fabrication process. The obtained nanocomposite acts as a high capacity anode material for lithium-ion batteries and demonstrates good cycle stability. A drastically enhanced capacity of 750 mA h g^-1 in comparison with that of bare In2O3 nanoparticles can be maintained after 100 cycles, along with an improved high rate performance (210 mA h g^-1 at 1 A g^-1 and 120 mA h g^-1 at 2 A g^-1). The excellent performance is linked with the indium oxide nanoparticles and the unique 3D interconnected porous graphene structure. The highly conductive and porous 3D graphene structure greatly enhances the performance of lithium-ion batteries by protecting the nanoparticles from the electrolyte, stabilizing the nanoparticles during cycles and buffering the volume expansion upon lithium insertion.

GaN and Gax In1-x N nanoparticles with tunable indium content: synthesis and characterization

Semiconducting GaN and Gax In1-x N nanoparticles (4-10 nm in diameter, depending on the metal ratio) with tunable indium content are prepared through a chemical synthesis (the urea-glass route). The bandgap of the ternary system depends on its composition, and therefore, the color of the final material can be turned from bright yellow (the color of pure GaN) to blue (the color of pure InN). Transmission electron microscopy (TEM and HRTEM) and scanning electron microscopy (SEM) images confirm the nanoparticle character and homogeneity of the as-prepared samples. X-ray diffraction (XRD), electron diffraction (EDX), elemental mapping, and UV/Vis, IR, and Raman spectroscopy investigations are used to confirm the incorporation of indium into the crystal structure of GaN. These nanoparticles, possessing adjusted optical properties, are expected to have potential applications in the fabrication of novel optoelectronic devices.

Synthesis and thermal studies of solid state 2-chloro-benzylidenepyruvic acid and its compounds with sodium, aluminium (III), gallium (III) and indium (III) cations

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Synthesis, characterization and thermal behaviour of solid state compounds of 2-chlorobenzylidenepyruvate with trivalent aluminium, gallium, indium and scandium metals

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Spectroscopic studies on glassy Ni(II) and Co(II) polyphosphate coacervates

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Spectroscopic investigation of a new hybrid glass formed by the interaction between croconate ion and calcium polyphosphate

In this work, a new organic-inorganic hybrid material has been synthesized by the incorporation of croconate ion into a calcium polyphosphate coacervate. The hybrid so obtained was characterized by means of electronic and vibrational spectroscopies. The material is a homogeneous mixture described by a structural model, which includes helical chains of polyphosphate ions, where the calcium ion occupies the internal vacancies of the structure. The croconate ion appears to be occupying the regions outside the polymeric structure, surrounded by several water molecules. The electronic spectrum of the incorporated material shows a broad band peaking at the same wavelength region (363 nm) observed for the aqueous solution of croconate ion, and manifesting the Jahn-Teller effect as evidenced by the doublet structure of the band. The infrared spectrum is widely dominated by the absorption bands of the polyphosphate ion and the appearance of the carbonyl stretching band at ca. 1550 cm(-1) indicates the presence of croconate ion incorporated in the structure. The Raman spectrum of the material shows several vibrational bands related to the oxocarbon moiety; most of them are shifted in comparison with the free ion. These shifts can be understood in terms of strong hydrogen bonding interactions between water molecules and the oxocarbon moiety. The low temperature methodology proposed here can be well used in the preparation of new phosphate glasses containing organic moieties opening the route to an entirely new class of hybrid glasses. (c) 2004 Elsevier B.V All rights reserved.

Ultrafast nonlinearity of antimony polyphosphate glasses

We report on the ultrafast nonlinearity of antimony polyphosphate glasses measured using the Kerr shutter technique. The nonlinear refractive index, n(2), was (1.1+/-0.2)x10(-14) cm(2)/W at 800 nm, and enhancement of n(2) by approximate to80% was observed by adding 10% of lead oxide in the glass composition. The full width at half-maximum of the third-order correlation signal was 150 fs, which implies a fast response of the samples (less than or equal to100 fs). Nonlinear absorption was negligible in the range of intensities used. (C) 2003 American Institute of Physics.

Indium tin oxide films prepared via wet chemical route

In this work, indium tin oxide (ITO) films were prepared using a wet chemical route, the Pechini method. This consists of a polyesterification reaction between an alpha-hydroxicarboxylate complex (indium citrate and tin citrate) with a polyalcohol (ethylene glycol) followed by a post annealing at 500 degrees C. A 10 at.% of doping of Sn4+ ions into an In2O3 matrix was successfully achieved through this method. In order to characterize the structure, the morphology as well as the optical and electrical properties of the produced ITO films, they were analyzed using different experimental techniques. The obtained films are highly transparent, exhibiting transmittance of about 85% at 550 nm. They are crystalline with a preferred orientation of [222]. Microscopy discloses that the films are composed of grains of 30 nm average size and 0.63 nm RMS roughness. The films' measured resistivity, mobility and charge carrier concentration were 5.8 x 10(-3) Omega cm, 2.9 cm(2)/V s and -3.5 x 10(20)/cm(3), respectively. While the low mobility value can be related to the small grain size, the charge carrier concentration value can be explained in terms of the high oxygen concentration level resulting from the thermal treatment process performed in air. The experimental conditions are being refined to improve the electrical characteristics of the films while good optical, chemical, structural and morphological qualities already achieved are maintained. (C) 2007 Elsevier B.V. All rights reserved.

Structural electrical and optical properties of undoped and indium doped ZnO thin films prepared by the pyrosol process at different temperatures

The influence of the substrate temperature on the structural features and opto-electrical properties of undoped and indium-doped ZnO thin films deposited by pyrosol process was investigated. The addition of indium induces a drastic decrease (by a factor approximate to 10(10) for samples deposited at 300 degreesC) in the electrical resistivity of films, the lowest electrical resistivity (6 mOmega-cm) being observed for the film deposited at 450 degreesC. Films are highly transparent (>80%) in the Vis-NIR ranges, and the optical band gap exhibits a blue shift (from 3.29 to 3.33 eV) for the In-doped films deposited at increasing temperature. Preferential orientation of the ZnO crystallites with the c-axis perpendicular to the substrate surface and an anisotropic morphology of the nanoporous structure was observed for films growth at 300 and 350 degreesC. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Influence of ambient gas on the growth and properties of porous tin-doped indium oxide thin films made by pulsed laser deposition

The laser ablation method was used for depositing porous nanocrystalline indium-tin oxide thin films for gas sensing applications. Samples were prepared at different pressures using three gases (O-2, 0.8N(2):0.2O(2), N-2) and heat-treated in the same atmosphere used for the ablation process. X-ray diffraction results show that the films are not oriented and the grain sizes are in the range between 15 and 40 nm. The grains are round shaped for all samples and the porosity of the films increases with the deposition pressure. The degree of sintering after heat treatment increases for lower oxygen concentrations, generating fractures on the surface of the samples. Film thicknesses are in the range of I pm for all gases as determined from scanning electron microscopy cross-sections. Electrical resistance varies between 36.3 ohm for the film made at 10 Pa pressure in N-2 until 9.35 x 10(7) ohm for the film made at 100 Pa in O-2. (C) 2007 Elsevier B.V. All rights reserved.

Spectroscopic study and local coordination of polyphosphate colloidal systems

The interaction between metaphosphate chains and the metal ions Ca2+ and Eu3+ has been studied in water by Eu3+ luminescence, infrared absorption, and P-31 NMR spectroscopy. Two main families of sites could be identified for the metal ions in the aqueous polyphosphate colloidal systems: (1) cagelike sites provided by the polyphosphate chain and (2) a family which arises following saturation of cagelike sites. Occupation of this second family leads to supramolecular interactions between polyphosphate chains and the consequent destabilization of the colloidal system. In the polyphosphate-Ca2+ system, this destabilization appears as a coacervation process. Equilibrium existing between colloidal species as a function of the compositions could be reasoned based on the spectroscopic measurements. The determination of coordination numbers and the correlation of the results with the observation of coacervates show that Eu3+ luminescence properties can be used to probe in a unique way the coacervation process.

Photoinduced structural changes in antimony polyphosphate based glasses

A photocontraction effect in amorphous films of the binary glass system 0.20 [Sb(PO3)(3)](n)-0.80 Sb2O3 has been observed after UV irradiation using the 350.7 nm Kr+ ion laser line with 5.0 W/cm(2). Good optical quality films up to 4.0 mum were deposited on silica substrates at room temperature in vacuum by electron beam physical vapor deposition (EB-PVD) and characterized using WDX, XRD, optical absorption, infrared reflectance, profilometry and atomic force microscopy (AFM) techniques. Very stable glasses were prepared by the melt quenching technique and used as evaporation source for the production of films. The photoinduced structural change (PSC) was observed as a variation of about 6% in the film thickness and this effect is accompanied by a photobleaching of the irradiated area with a blue shift of the optical absorption edge. Otherwise this photoinduced change in the film thickness is very sensitive to the variations in the shape and intensity of the laser beam; therefore several possibilities in optical recording arise from these results. (C) 2003 Published by Elsevier B.V.