Quantification of Peroxide Ion Passage in Dentin, Enamel, and Cementum After Internal Bleaching With Hydrogen Peroxide

The aim of this study was to evaluate the amount of peroxide passage from the pulp chamber to the external enamel surface during the internal bleaching technique. Fifty bovine teeth were sectioned transversally 5 mm below the cemento-enamel junction (CEJ), and the remaining part of the root was sealed with a 2-mm layer of glass ionomer cement. The external surface of the samples was coated with nail varnish, with the exception of standardized circular areas (6-mm diameter) located on the enamel, exposed dentin, or cementum surface of the tooth. The teeth were divided into three experimental groups according to exposed areas close to the CEJ and into two control groups (n=10/group), as follows: GE, enamel exposure area; GC, cementum exposed area; GD, dentin exposed area; Negative control, no presence of internal bleaching agent and uncoated surface; and Positive control, pulp chamber filled with bleaching agent and external surface totally coated with nail varnish. The pulp chamber was filled with 35% hydrogen peroxide (Opalescence Endo, Ultradent). Each sample was placed inside of individual flasks with 1000 mu L of acetate buffer solution, 2 M (pH 4.5). After seven days, the buffer solution was transferred to a glass tube, in which 100 mu L of leuco-crystal violet and 50 mu L of horseradish peroxidase were added, producing a blue solution. The optical density of the blue solution was determined by spectrophotometer and converted into microgram equivalents of hydrogen peroxide. Data were submitted to Kruskal-Wallis and Dunn-Bonferroni tests (alpha=0.05). All experimental groups presented passage of peroxide to the external surface that was statistically different from that observed in the control groups. It was verified that the passage of peroxide was higher in GD than in GE (p<0.01). The GC group presented a significantly lower peroxide passage than did GD and GE (p<0.01). It can be concluded that the hydrogen peroxide placed into the pulp chamber passed through the dental hard tissues, reaching the external surface and the periodontal tissue. The cementum surface was less permeable than were the dentin and enamel surfaces.

Sensibilidade do colo dental. Uma nova alternativa terapêutica.

The cervical hypersensitivity tooth was analysed and treated by application of a varnish with high fluoride ions content (Duraphat) and of a glass ionomer cement usually indicated to cavity lining (XR-ionomer-Kerr). This technique was applied in sixty-seven teeth of Clinic Graduation patients (Faculdade de Odontologia de Araçatuba) and demonstrated a high index of satisfactory results. The clinical findings of this study relate that, this technique is more one method of choose by clinicians.

Influência de diferentes agentes de fixação na resistência de união, por tração, de ligas metálicas fixadas à dentina.

They were casted pieces using three kinds of alloy (Ni-Cr, Ag-Sn and Cu-Al) with circular and smooth surface. They were cemented to human teeth, on occlusal surface, grounded at dentin level, through three different materials kind (zinc polycarboxylate cement, glassionomer cement and composite). After 24 hours storing, the samples were subjected to the tensile test. The results showed that the samples cemented with composite and the casts made with Ag-Sn alloy had higher bond strength.

Inhibition of demineralization in vitro around amalgam restorations

Objective: The purpose of this in vitro study was to evaluate some forms of preventing or avoiding demineralization within enamel cavity walls adjacent to amalgam restorations. Method and materials: Third molar teeth were sectioned to obtain 72 specimens, divided into one control and five experimental groups: amalgam only; varnish plus amalgam; acidulated phosphate fluoride plus amalgam; adhesive amalgam; glass-ionomer cement plus amalgam; control (amalgam only, not subjected to a demineralization challenge). The experimental groups were subjected to pH and thermal cycling and then submitted to enamel hardness determinations. Results: Significant differences between the treatment groups revealed that the bonded amalgam technique offered the best resistance to demineralization. The use of cavity varnish resulted in greater mineral loss than amalgam placed alone. Conclusion: The use of an adhesive system, glass-ionomer cement, or acidulated phosphate fluoride under amalgam restorations may interfere with development of secondary caries.

Microleakage evaluation of pit and fissure sealants done with different procedures, materials, and laser after invasive technique

This study evaluated the microleakage of pit and fissure sealants after different surface preparation (invasive technique and laser irradiation) and the use of different materials (fluoride resin-filled sealant, resin-modified glass ionomer cement and adhesive system). Eighty-four pre molars were used in this study, which were divided into seven groups. After the accomplishment of the different treatments, these were submitted to thermocycling process and assess for microleakage by examination under an epifluorescent microscope and scored zero to seven. Two specimens of each group were observed under scanning electron microscope (SEM). The results showed that laser irradiation did not lessen microleakage in pit and fissures when using a filled-resin sealant with fluoride or a resin-modified glass ionomer cement. The use of laser irradiation and adhesive system, followed by a resin-filled sealant with fluoride, showed the lowest microleakage scores in pit and fissures. Comparing this group to the resin-modified glass ionomer cement group, there was statistical significance. The use of a adhesive system decreased microleakage when using a fluoride resin-filled sealant with or without previous laser irradiation; although it was not statistically significant.

Evaluation of apical sealing of three endodontic sealers

Aim: The apical sealing ability of three different endodontic sealers was evaluated in extracted teeth using dye penetration. Methodology: The root canals of 99 extracted human maxillary central incisors were prepared sequentially 2 mm beyond the apical foramen with a size 55 Nitiflex file. The teeth were divided into three experimental groups and obturated by lateral condensation of cold gutta-percha and one of the following sealers: group 1, zinc oxide and eugenol sealer (Fill Canal); group 2, glass ionomer sealer (Ketac-Endo) and group 3, epoxy resin sealer (AH Plus). The teeth were covered with nail varnish to within 1 mm of the apical foramen and immersed in 2% methylene blue in a reduced pressure environment for 24h. After this period, the teeth were washed and cut longitudinally for apical leakage analysis. The values were obtained from the maximum depth of leakage as well as the average between the maximum and minimum values observed for each group. Results: Statistical evaluation of the results showed no significant difference in the leakage between Fill Canal and Ketac-Endo (P > 0.05). Leakage with AH Plus was significantly less (P < 0.01) than with the other sealers. Conclusions: All three sealers allowed some leakage to occur. Leakage with AH Plus was significantly different than with Fill Canal or Ketac-Endo.

The influence of ultrasound on the retention of cast posts cemented with different agents

Aim: The aim of this study was to evaluate the influence of ultrasound during the removal of posts cemented with either zinc phosphate cement, glass ionomer cement or resin cement. Methodology: Eighty-four single-rooted teeth were prepared and after cementation of cast posts, they were randomly divided into six groups of 14. Groups 1, 2 and 3 did not receive ultrasonic vibration, whilst groups 4, 5 and 6 received ultrasonic vibration for 10 min. The force necessary for post removal was determined using a universal testing machine. Results were statistically analysed using ANOVA and Tukey tests (5%). Results: The application of ultrasonic vibration reduced the retention provided by zinc phosphate and glass ionomer cements by 39% and 33%, respectively. Conclusions: A statistically significant reduction in the force necessary to remove posts cemented with zinc phosphate and glass ionomer cements occurred following application of ultrasound. The application of ultrasonic vibration did not influence the retention of cast posts cemented with resin cement.

Cariostatic effect of fluoride-containing restorative systems associated with dentifrices on root dentin

Objective. The aim of this in vitro study was to evaluate the interaction between two sources of fluoride (restorative systems and dentifrices) in inhibiting artificial root caries development. Methods. One hundred and eighty tooth segments were embedded in polyester resin, and sanded flat. Cylindrical cavities 1.0 mm-deep and 1.5 mm-diameter were prepared in root dentin and randomly restored by fluoride-containing restorative systems: Ketac-fil/Espe (Ke), Fuji II LC/GC Corp (Fj), F2000/3M (F2), Surefil/Dentsply (Su) or a control: Filtek Z250/3M (Z2). Ten experimental groups were made to test the association among the five restorative systems and two dentifrices: with F - (Sensodyne Baking Soda) or without F- (Sensodyne Original) (n = 18). After surface polishing, a 1 mm-wide margin around the restorations was demarcated and initial dentin surface Knoop microhardness values (KHNi) were obtained. The specimens were submitted to a pH-cycling model, and to applications of slurries of dentifrice. Afterwards the final dentin surface Knoop microhardness values (KHNf) were measured. Results. The differences between KHNi and KHNf, and the covariate KHNi were considered by the ANCOVA and Tukey's test (α = 0.05). The interaction between restorative system and dentifrice was statistically significant (p = 0.0026). All restorative systems provided some protection against artificial caries challenge when associated with the fluoride-containing dentifrice treatment. The means (standard deviation) of reductions in Knoop hardness values for systems associated with the fluoride-containing dentifrice were: Ke: 40.0(1.02)a, Fj: 41.9(1.02)b, F2: 43.3(1.04)c, Su: 43.5(1.00)c, Z2: 44.0(1.02)c; and with the non-fluoride-containing dentifrice were: Ke: 42.9(1.02)a, Fj: 44.7(1.01)b, F2: 45.2(1.09)bc, Su: 46.0(0.99)c, Z2: 46.6(0.99)c (statistical differences were expressed by different letters). Conclusion. The cariostatic effect shown by the fluoride-containing dentifrice could enhance that shown by Ketac-fil and Fuji II LC, and could mask that shown by F2000. © 2002 Elsevier Science Ltd. All rights reserved.

Fluoride release by restorative materials before and after a topical application of fluoride gel

The release of fluoride from restorative materials (Vitremer, Ketac-Fil, Fuji II LC and Freedom) was evaluated during two 15-day periods, before and after a topical application of acidulated phosphate fluoride gel (APF). For each material, 6 specimens were made, which were immersed in 2 ml of deionized water. The fluoride concentration dosages in the solutions were read at intervals of 24 hours for 15 days. After this period, the specimens of each material received treatment with APF gel for 4 minutes and the fluoride released was analyzed at 24-hour intervals during the following 15 days. The analysis of variance and the Tukey test (p < 0.05) showed that the total mean fluoride released during the initial 15 days was greater for Vitremer and Ketac-Fil and lower for Fuji II LC and Freedom; and in the final 15 days there was a difference in release readings, with the greatest value for Vitremer, followed by Fuji II LC, Ketac-Fil and Freedom. The comparison of the results between the 1st day and the 16th day (after gel application) showed a greater fluoride release on the 16th day for Vitremer, Fuji II LC and Freedom and was equal for Ketac-Fil. Although all the materials evaluated gained fluoride with the application of APF, the data suggest that the resin-modified ionomers are more efficient in releasing fluoride to the medium than the other materials.

Effects of bleaching with carbamide peroxide gels on microhardness of restoration materials

The objective of this in vitro study was to quantitatively assess the effects of bleaching with 10 and 15% carbamide peroxide (CP) on restoration materials by performing superficial microhardness analysis. Acrylic cylindrical containers (4 x 2 mm) were filled with the following restoration products: Charisma (Heraues Kulzer, Vila Santa Catarina, São Paulo, Brazil), Durafill VS (Heraeus Kulzer), Vitremer (3M, Sumaré, São Paulo, Brazil), Dyract (Dentsply, Petrópolis, Rio de Janeiro, Brazil), and Permite C (SDI, São Pauio, São Paulo, Brazil). Sixty samples were prepared of each restoration material. Twenty samples received bleaching treatment with 10% CP, 20 samples received bleaching treatment with 15% CP, and 20 samples were kept submerged in artificial saliva, which was replaced daily. The treatment consisted of immersion of the specimens in 1 cm3 of CP at 10 and 15% for 6 hours per day during 3 weeks, whereupon the test specimens were washed, dried, and kept immersed in artificial saliva for 18 hours. Then the test and control specimens were analyzed using a microhardness gauge. The Knoop Hardness Number (KHN) was taken for each test and control specimen at five different locations by applying a 25 g force for 20 seconds. The values obtained were transformed into KHNs and the mean was calculated. The data were submitted to statistical analysis by analysis of variance and Tukey test, p < .05. The means/standard deviations were as follows: Charisma: CP 10% 38.52/4.08, CP 15% 34.31/6.13, saliva 37.36/4.48; Durafill VS: CP 10% 18.65/1.65, CP 15% 19.38/2.23, saliva 18.27/1.43; Dyract AP: CP 10% 30.26/2.81, CP 15% 28.64/5.44, saliva 33.88/3.46; Vitremer: CP 10% 28.15/3.04, CP 15% 17.40/3.11, saliva 40.93/4.18; and Permite C: CP 10% 183.50/27.09, CP 15% 159.45/5.78, saliva 215.80/26.15. A decrease in microhardness was observed for the materials Dyract AP, Vitremer, and Permite C after treatment with CP at 10 and 15%, whereas no effect on either of the two composites (Charisma and Durafill) was verified. CLINICAL SIGNIFICANCE: The application of the carbamide peroxide gels at 10 and 15% did not alter the microhardness of the composite resins Charisma and Durafill. In situ and clinical studies are necessary to enable one to conclude that the reduction in microhardness of the materials effectively results in clinical harm to the restorations.

Scanning electron microscope analysis of internal adaptation of materials used for pulp protection under composite resin restorations

Purpose: The aim of this study was to evaluate the interfacial microgap with different materials used for pulp protection. The null hypothesis tested was that the combination of calcium hydroxide, resin-modified glass ionomer, and dentin adhesive used as pulp protection in composite restorations would not result in a greater axial gap than that obtained with hybridization only. Materials and Methods: Standardized Class V preparations were performed in buccal and lingual surfaces of 60 caries-free, extracted human third molars. The prepared teeth were randomly assessed in six groups: (1) Single Bond (SB) (3M ESPE, St. Paul, MN, USA); (2) Life (LF) (Kerr Co., Romulus, MI, USA) + SB; (3) LF + Vitrebond (VT) (3M ESPE) + SB; (4) VT + SB; (5) SB + VT; (6) SB + VT + SB. They were restored with microhybrid composite resin Filtek Z250 (3M ESPE), according to the manufacturer's instructions. However, to groups 5 and 6, the dentin bonding adhesive was applied prior to the resin-modified glass ionomer. The specimens were then thermocycled, cross-sectioned through the center of the restoration, fixed, and processed for scanning electron microscopy. The specimens were mounted on stubs and sputter coated. The internal adaptation of the materials to the axial wall was analyzed under SEM with × 1,000 magnification. Results: The data obtained were analyzed with nonparametric tests (Kruskal-Wallis, p ≤ .05). The null hypothesis was rejected. Calcium hydroxide and resin-modified glass ionomer applied alone or in conjunction with each other (p < .001) resulted in statistically wider microgaps than occurred when the dentin was only hybridized prior to the restoration. ©2005 BC Decker Inc.

Restorative treatment on class I and II restorations in primary molars: A survey of Brazilian dental schools

A survey was sent to 70 Brazilian dental schools evaluating techniques and restorative materials being taught for Class I and II preparation in posterior primary teeth by Pediatric Dentistry courses. After a 54% response rate, marked teaching diversity was found among Brazilian dental schools. Amalgam continues to be taught, but a tendency of preference towards more esthetic-like materials was observed.

Biological response of pulps submitted to different capping materials

Pulp capping is a procedure that comprises adequate protection of the pulp tissue exposed to the oral environment, aiming at the preservation of its vitality and functions. This study evaluated the response of the dental pulps of dog teeth to capping with mineral trioxide aggregate (MTA) or calcium hydroxide P.A. For that purpose, 37 teeth were divided into two groups, according to the capping material employed. Two dogs were anesthetized and, after placement of a rubber dam, their pulps were exposed in a standardized manner and protected with the experimental capping materials. The cavities were then sealed with resin-modified glass ionomer cement and restored with composite resin. After sixty days, the animals were killed and the specimens were processed in order to be analyzed with optic microscopy. It was observed that MTA presented a higher success rate compared to calcium hydroxide, presenting a lower occurrence of infection and pulp necrosis.

Clinical and radiographic evaluation of pulpotomies employing calcium hydroxide and trioxide mineral aggregate

This study utilized clinical and radiographic examinations to compare the effectiveness of calcium hydroxide paste and mineral trioxide aggregate (MTA) for pulpotomies of primary molars in children. Ninety primary molars that showed clinical and radiographic indications for pulpotomy treatment were selected. The pulpotomies were performed in two sessions, using a corticosteroid/ antibiotic solution as therapeutic dressing. The sample was divided into two groups of 45 teeth, in which the pulpal remains were protected with either calcium hydroxide paste (Group 1) or MTA (Group 2). Radiographs were taken immediately and at 3-, 6-, and 12-month follow-up appointments. Three teeth in Group 1 failed after three months, while two cases failed after six months and one more failed at one year. Two failures were found in Group 2 at the 12-month follow-up. These results indicate that both materials may be utilized for pulpotomies in primary teeth.

Shear bond strength fatigue limit of rest seats made with dental restoratives

Purpose: This study compared the shear bond strength (SBS) to enamel of rest seats made with a glass-ionomer cement (Fuji IX GP Fast), a resin-modified glass-ionomer cement (Fuji II LC), and a composite resin (Z100 MP) under monotonic and cyclic loading. Materials and Methods: Rest seats were built up onto the lingual surfaces of 80 intact human mandibular incisors. Specimens (n=10) were stored in distilled water at 37°C for 30 days and subjected to shear forces in a universal testing machine (0.5 mm/min) until fracture. The SBS values were calculated (MPa) using the bonding area (9.62 mm2) delimited by adhesive tags. A staircase approach was used to determine the SBS fatigue limit of each material. Specimens were submitted to either 10,000 cycles (5 Hz) or until specimen fracture. A minimum of 15 specimens was tested for each material. Scanning electron microscopy was used to examine the mode of failure. Data were statistically analyzed with one-way ANOVA and Tukey HSD tests (α = 0.05). Results: Z100 MP yielded higher (p < 0.05) SBS (12.25 MPa) than Fuji IX GP Fast (7.21 MPa). No differences were found between Fuji II LC (10.29 MPa) and the other two materials (p > 0.05). Fuji II LC (6.54 MPa) and Z100 MP (6.26 MPa) had a similar SBS limit. Fuji IX GP Fast promoted the lowest (p < 0.05) SBS fatigue limit (2.33 MPa). All samples showed cohesive failure patterns. Conclusion: Fatigue testing can provide a better means of estimating the performance of rest seats made with dental restoratives.