The thermodynamics and phase behaviour of Tb2Pd2O5 and Er2Pd2O5

Isothermal sections of the phase diagrams for the systems Ln-Pd-O (with Ln = Tb or Er) have been established by equilibration of samples at T = 1223 K, and phase identification after quenching by optical and scanning electron microscopy (OM, SEM), energy dispersive spectroscopy (EDS), and X-ray powder diffraction (XRPD). Two oxide phases were stable along the binary Tb-O: Tb2O3+x, a phase of variable composition, and Tb7O12 at T = 1223K. The oxide PdO was not stable at this temperature. Only one ternary oxide Tb2Pd2O5 was identified in the Tb-Pd-O system. No ternary compound was found in the system Er-Pd-O at T = 1223K. However, the compound Er2Pd2O5 could be synthesized at T = 1075 K by the hydrothermal route. In both systems, the alloys and inter-metallic compounds were all found to be in equilibrium with the lanthanide sesquioxide Ln(2)O(3) (where Ln is either Tb or Er). Two solid-state cells, each incorporating a buffer electrode, were designed to measure the Gibbs energy of formation of the ternary oxides, using yttria-stabilized zirconia as the solid electrolyte and pure oxygen gas as the reference electrode. Electromotive force measurements were conducted in the temperature range (900-1275) K for Th-Pd-O system, and at temperatures from (900-1075) K for the system Er-Pd-O. The standard Gibbs energy of formation Delta(f)G(m)degrees,, of the inter-oxide compounds from their component binary oxides Ln(2)O(3) and PdO are represented by equations linear in temperature. Isothermal chemical potential diagrams for the systems Ln-Pd-O (with Ln = Tb or Er) are developed based on the thermodynamic information. (C) 2002 Elsevier Science Ltd. All rights reserved.

Calcium ruthenates: Determination of Gibbs energies of formation using electrochemical cells

Metallic Ru has been found to coexist separately with CaO, RuO2, and the interoxide phases, Ca2RuO4, Ca3Ru2O7, and CaRuO3, present along the pseudobinary system CaO-RuO2. The standard Gibbs energies of formation (Df((ox))G(o)) of the three calcium ruthenates from their component oxides have been measured in the temperature range 925-1350 K using solid-state cells with yttria-stabilized zirconia as the electrolyte and Ru+RuO2 as the reference electrode. The standard Gibbs energies of formation (Deltaf((ox))G(o)) of the compounds can be represented by Ca2RuO4:Deltaf((ox))G(o)/J mol(-1)=-38,340-6.611 T (+/-120), Ca3Ru2O7 : Df((ox))G(o)/J mol(-1)=-75,910-11.26 T (+/-180), and CaRuO3 : Deltaf((ox))G(o)/J mol(-1)=-35,480-3.844 T(+/-70). The data for Ca2RuO4 corresponds to the stoichiometric composition, which has an orthorhombic structure, space group Pbca, with short c axis ("S'' form). The structural features of the ternary oxides responsible for their mild entropy stabilization are discussed. A three-dimensional oxygen potential diagram for the system Ca-Ru-O is developed as a function of composition and temperature from the results obtained. Using the Neumann-Kopp rule to estimate the heat capacity of the ternary oxides relative to their constituent binary oxides, the standard enthalpies of formation of the three calcium ruthenates from the elements and their standard entropies at 298.15 K are evaluated. (C) 2003 The Electrochemical Society.

Standard Gibbs energy of formation of Pb2Ru2O6.5

Lead ruthenate is used as a bifunctional electrocatalyst for both oxygen evolution and reduction and as a conducting component in thick-film resistors. It also has potential applications in supercapacitors and solid oxide fuel cells. However, thermodynamic properties of the compound have not been reported in the literature. The standard Gibbs energy of formation has now been determined in the temperature range from 873 to 1123 K using a solid-state cell incorporating yttria-stabilized zirconia (YSZ) as the electrolyte, a mixture of PbO + Pb2Ru2O6.5 + Ru as the measuring electrode, and Ru + RuO2 as the reference. The design of the measuring electrode is based on a study of phase relations in the ternary system Pb–Ru–O at 1123 K. For the reaction,S0884291400095625_eqnU1 the standard enthalpy of formation and standard entropy at 298.15 K are estimated from the high-temperature measurements. An oxygen potential diagram for the system Pb–Ru–O is composed based on data obtained in this study and auxiliary information from the literature

Speech segmentation using extrema based signal track length measure

We introduce a novel temporal feature of a signal, namely extrema-based signal track length (ESTL) for the problem of speech segmentation. We show that ESTL measure is sensitive to both amplitude and frequency of the signal. The short-time ESTL (ST_ESTL) shows a promising way to capture the significant segments of speech signal, where the segments correspond to acoustic units of speech having distinct temporal waveforms. We compare ESTL based segmentation with ML and STM methods and find that it is as good as spectral feature based segmentation, but with lesser computational complexity.

Gibbs free energies of formation of ZnAl2O4 and ZnCr2O4

The standard free energies of formation of zinc aluminate and chromite were determined by measuring the oxygen potential over a solid CuZn alloy, containing 10 at.−% Zn, in equilibrium with ZnO, ZnAl2O4+Al2O3(χ) and ZnCr2O4+Cr2O3, in the temperature range 700–900°C. The oxygen potential was monitored by means of a solid oxide galvanic cell in which a Y2O3 ThO2 pellet was sandwiched between a CaOZrO2 crucible and tube. The temperature dependence of the free energies of formation of the interoxidic compounds can be represented by the equations, The heat of formation of the spinels calculated from the measurements by the “Second Law method” is found to be in good agreement with calorimetrically determined values. Using an empirical correlation for the entropy of formation of cubic spinel phases from oxides with rock-salt and corundum structures and the measured high temperature cation distribution in ZnAl2O4, the entropy of transformation of ZnO from wurtzite to rock-salt structure is evaluated.

Potentiometric determination of the Gibbs free energy of formation of cadmium and magnesium chromites

The standard Gibbs free energy of formation of magnesium and cadmiumchromites have been determined by potentiometric measurements on reversiblesolid-state electrochemical cells [dformula (Au-5%Cd, , Au-5%Cd; Pt, + , CaO-ZrO[sub 2], + ,Pt; CdO, , CdCr[sub 2]O[sub 4] + Cr[sub 2]O[sub 3])] in the temperature range 500°–730°C, and [dformula Pt, Cr + Cr[sub 2]O[sub 3]/Y[sub 2]O[sub 3]-ThO[sub 2]/Cr + MgCr[sub 2]O[sub 4] + MgO, Pt] in the temperature range 800°–1200°C. The temperature dependence of the freeenergies of formation of the ternary compounds can be represented by theequations [dformula CdO(r.s.) + Cr[sub 2]O[sub 3](cor) --> CdCr[sub 2]O[sub 4](sp)] [dformula Delta G[sup 0] = - 42,260 + 7.53T ([plus-minus]400) J] and [dformula MgO(r.s.) + Cr[sub 2]O[sub 3](cor) --> MgCr[sub 2]O[sub 4](sp)] [dformula Delta G[sup 0] = - 45,200 + 5.36T ([plus-minus]400) J] The entropies of formation of these spinels are discussed in terms of cationdisorder and extent of reduction of Cr3+ ions to Cr2+ ions. Thermodynamicdata on the chromates of cadmium and magnesium are derived by combiningthe results obtained in this study with information available in the literatureon high temperature, high pressure phase equilibria in the systems CdO-Cr2O3-O2 and MgO-Cr2O3-O2.

Gibbs free energy of formation of magnesium stannate

he thermodynamic properties of the spinel Mg2SnO4 have been determined by emf measurements on the solid oxide galvanic cell,View the MathML source in the temperature range 600 to 1000°C. The Gibbs' free energy of formation of Mg2SnO4 from the component oxides can be expressed as View the MathML source,View the MathML source These values are in good agreement with the information obtained by Jackson et al. [Earth Planet. Sci. Lett.24, 203 (1974)] on the high pressure decomposition of magnesium stannate into component oxides at different temperatures. The thermodynamic data suggest that the spinel phase is entropy stabilized, and would be unstable below 207 (±25)°C at atmospheric pressure. Based on the information obtained in this study and trends in the stability of aluminate and chromite spinels, it can be deduced that the stannates of nickel and copper(II) are unstable.

Gibbs free energies of formation of indium (III) oxide and sulphate

Emf measurements on the galvanic cell Pt, Ta, In + In,O, / Tho,-Y,03 / Cu + C+O, Pt were used to obtain the standard free energy of formation of 1%03fr om 600 to 900°C. Differential thermal analysis was used to detect the decomposition of In2(S0,), under controlled SO2 + O2 + Ar mixtures in thqtemperature range 640-8wC. X-ray diffraction analysis indicated that the decomposition product was 1%03 without an oxywlphate intermediate. The following equations were obtained for the variation of the standard free-energy change(Jlmole) with temperature:

Gibbs energy of formation of lead zirconate

The Gibbs energy of formation of zirconia-saturated lead zirconate was determined by emf measurements on the solid state cells and at 800 to 1400 K. The results obtained differ significantly from those reported in the literature based on vapor-pressure measurements, using Knudsen effusion and transportation techniques and assuming that the vapor phase consisted entirely of monomeric PbO molecules. A reanalysis of the data obtained in the earlier vapor-pressure studies, using mass-spectrometric measurements on polymeric PbO species in the gas phase, gives Gibbs energies of formation of lead zirconate which are in better agreement with those obtained in this study. Recent electrochemical measurements using CaO-ZrO2 and PbF2 solid electrolytes are in good agreement with the present study. The results obtained in this study are also consistent with the phase diagram which shows decomposition of the zirconate to tetragonal zirconia and a liquid phase rich in PbO at 1843 K.

Gibbs energy formation of lead titanate

The Gibbs energy of formation of titania-saturated lead titanate has been determined by e.m.f. measurements on the solid state cell;Pt,Ir,Pb + Pb1−xTiO3−x + TiO2(rutile)/CaO-ZrO2/Ni + NiO,Pt in the temperature range 1075–1350 K. The results obtained are significantly different from those reported in the literature based upon vapour pressure measurements, employing Knudsen effusion and transportation techniques, and assuming that the vapor phase consisted entirely of monomeric PbO molecules. A reanalysis of the data obtained in the earlier vapor pressure studies using mass spectrometric measurements on polymeric PbO species in the gas phase, gives Gibbs energies of formation of lead titanate which are in better agreement with those obtained in this study. Earlier electrochemical measurements by Mehrotra et al. and more recent electrochemical measurements by Schmahl et al. both employing CaO-ZrO2 solid electrolytes are in good agreement with the present study. The electro-chemical measurements by Schmahl et al. using PbF 2 solid electrolyte give a slightly more positive Gibbs energy of formation. There was no evidence supporting the formation of compounds other than Pb1−xTiO3−x from yellow PbO and rutile form of TiO2 in the temperature range covered in this study.Résumé L'enthalpie libre de formation du titanate de plomb saturé en oxyde de titane a été déterminée par des mesures de FEM de la pile: Pt,Ir,Pb + Pb1−xTiO3−x + TiO2(rutile)/CaO-ZrO2/Ni + NiO,Pt dans le domaine de températures 1075–1350 K. Les résultats obtenus, different appréciablement de ceux publiés, déterminés par mesures de tensions de vapeur (techniques de transport et d'effusion de Knudsen) en supposant que la phase gazeuse etait uniquement constituée de molécules monomériques de PbO. Une réanalyse des résultats de la littérature, à partir de mesures par spectrométrie de masse sur les polymères de PbO gazeux, donne des enthalpies libres de formation du titanate de plomb se rapprochant de celles obtenues dans cette étude. Les mesures de Mehrotra et al. et plus récemment de Schmahl et al. utilisant toutes deux l'électrolyte CaO-ZrO2 concordent bien avec celles de la présente étude. Les mesures de Schmahl et al., à l'aide de l' électrolyte solide PbF2, donnent une enthalpie de formation légèrement plus positive. Pour la gammede températures étudiée, rien ne permet de supposer que des composés autres que Pb1−x TiO3−x puissent se former à partir du PbO Gaune) et du rutile (TiO2).

Potentiometric determination of the Gibbs energies of formation of lead aluminates

The Gibbs energies of formation of three compounds in the PbO-Al2O3 system—2PbO · Al2O3, PbO · Al2O3, andPbO· 6Al2O3—have been determined from potentiometric measurements on reversible solid-state galvanic cells [dformula Pt, Ir | Pb, alpha-Al[sub 2]O[sub 3], PbO [center-dot] 6Al[sub 2]O[sub 3] | ZrO[sub 2]-CaO | NiO, Ni | Pt] [dformula Pt | NiO, Ni | ZrO[sub 2]-CaO | Pb, PbO [center-dot] 6Al[sub 2]O[sub 3], PbO [center-dot] Al[sub 2]O[sub 3] | Ir, Pt] and [dformula Pt | NiO, Ni | ZrO[sub 2]-CaO | Pb, PbO [center-dot] Al[sub 2]O[sub 3], 2PbO [center-dot] Al[sub 2]O[sub 3] | Ir, Pt] in the temperature range 850–1375 K. The results are discussed in the light of reported phase diagrams for the PbO-Al2O3system. The partial pressures of different lead oxide species, PbnOn, n = 1–6, in the gas phase in equilibrium withthe aluminates are calculated by combining the results of this study with the mass-spectrometric data of Drowart et al.(1) for polymerization equilibria in the gas phase. The concentration of oxygen in lead in equilibrium with the aluminatesare also derived from the results and the literature data on the Gibbs energy of solution of oxygen in liquid lead.

Gibbs energy of formation of nickel orthosilicate (Ni2SiO4)

Two solid state galvanic cells:Pt, Ni + Ni2Si04 + Si02/(Y203)Zr02/Ni + + NiO, Pt (1) and Pt, Ni + NizSiOj + Si02/CaF2/Ni + + NiO, Pt (11) have been employed for the determination of the Gibbs' energy of formation of nickel orthosilicate(Ni2Si04) from nickel oxide and quartz. The emf of cell (I) was reversible and reproducible in the temperature range 925 to 1375K whereas emf of cell (11) drifted with time and changed polarity. From the results of cell (I), the Gibbs' energy of formation of nickel silicate is obtained as,2Ni0 (r.s.) + Si02 (quartz) + Ni2Si04 (olivine)Gibbs' energy of formation of the spinel form of Ni2Si04 is obtained by combining the data for olivine obtained in this study with high pressure data on olivine to spinel transition reported in the literature. The complex time dependence of the emf of cell (11) can be rationalised on the basis of formation of calcium silicates from calcium oxide, generally present as an impurity in the calcium fluoride electrolyte, and silica. The emf of cell (11) is shown to be the function of the activity of calcium oxide at the electrolyte/ electrode interface. The results provide strong evidence against the recent suggestion of mixed anionic conduction in calcium fluoride.

Measurement of Gibbs energies of formation of CoF2 and MnF2 using a new composite dispersed solid electrolyte

Gibbs energies of formation of CoF2 and MnF2 have been measured in the temperature range from 700 to 1100 K using Al2O3-dispersed CaF2 solid electrolyte and Ni+NiF2 as the reference electrode. The dispersed solid electrolyte has higher conductivity than pure CaF2 thus permitting accurate measurements at lower temperatures. However, to prevent reaction between Al2O3 in the solid electrolyte and NiF2 (or CoF2) at the electrode, the dispersed solid electrolyte was coated with pure CaF2, thus creating a composite structure. The free energies of formation of CoF2 and MnF2 are (± 1700) J mol−1; {fx37-1} The third law analysis gives the enthalpy of formation of solid CoF2 as ΔH° (298·15 K) = −672·69 (± 0·1) kJ mol−1, which compares with a value of −671·5 (± 4) kJ mol−1 given in Janaf tables. For solid MnF2, ΔH°(298·15 K) = − 854·97 (± 0·13) kJ mol−1, which is significantly different from a value of −803·3 kJ mol−1 given in the compilation by Barinet al.