The role of coke in the deactivation of Mo/MCM-22 catalyst for methane dehydroaromatization with CO2

The effect of space velocity on reaction performance and coke deposition over 6Mo/MCM-22 catalyst in methane dehydro-aromatization (MDA) with CO2 were studied. The characterization of catalysts reacted at different space velocity after the same amount of methane feed by TG, TPO and Benzene/NH3-TPD techniques suggested that the inert coke maybe responsible for the deactivation of catalyst because of its blockage effect for pore system.

A facile and effective method for the distribution of Mo/HZSM-5 catalyst active centers

Post-steaming treatment of Mo/HZSM-5 catalysts results in more molybdenum species migrating into and residing in the HZSM-5 zeolite channels. This is confirmed by XRF and XPS measurements. H-1 MAS NMR and Si-29 MAS NMR also demonstrate that the number of free Bronsted acid sites decreases in the Mo/HZSM-5 catalysts that underwent post-steaming treatment, compared to untreated Mo/HZSM-5 catalysts. As a result, the deactivation rate constant (kd) on the Mo/HZSM-5 catalyst after post-steaming treatment for 0.5 h is much smaller, and the catalyst therefore shows remarkable stability in the probe reaction of methane dehydro-aromatization. The results suggest that a more beneficial bi-functional balance between active Mo species for methane activation and acid sites for the following aromatization is developed over those Mo/HZSM-5 catalysts that have experienced post-steaming treatment for 0.5 h, in comparison with the untreated Mo/HZSM-5 catalysts.

Post-steam-treatment of Mo/HZSM-5 catalysts: An alternative and effective approach for enhancing their catalytic performances of methane dehydroaromatization

Post-steam-treatment is a facile and effective method for improving the catalytic performances of Mo/HZSM-5 catalysts in methane dehydroaromatization under nonoxidative conditions. The treatment can enhance the stability of the catalyst and also give a higher methane conversion and a higher yield of light aromatics, as well as a decrease in the formation rate of carbonaceous deposits. (27)Al, (29)Si, and (1)H multinuclear magic angle spinning nuclear magnetic resonance, X-ray photoelectron spectroscopy, X-ray diffraction, X-ray fluorescence spectroscopy, and thermogravimetric analysis measurements as well as catalytic reaction evaluations were employed to conduct comparative studies on the properties of the catalysts before and after the post-steam-treatment. The results revealed that the number of free Bronsted acid sites per unit cell decreased, while more Mo species migrated into the HZSM-5 channels for the 6Mo/HZSM-5 catalysts after the post-steam-treatment. In addition, the average pore diameter was also larger for the post-steam-treated catalysts, and this was advantageous for mass transport of the reaction products. However, a severe post-steam-treatment, i.e., with longer treating time, of the 6Mo/HZSM-5 catalyst will lead to the formation of the Al(2)(MoO(4))(3) phases, which is detrimental to the reaction.

Shape selectivity in methane dehydroaromatization over Mo/MCM-22 catalysts during a lifetime experiment

Dehydroaromatization of CH4 with 2% CO2 on 6Mo/MCM-22 in a 100-h lifetime test was carried out at 993 K, atmospheric pressure and 1500 mL/gh. The duration of the lifetime test can be divided into an induction stage, stable stage and deactivation stage on the basis of the selectivities of hydrocarbons and coke. The characteristics of deposited coke with different time onstream were studied using TPO and TG techniques. There were two peaks corresponding to two kinds of coke recorded in TPO profiles, and the oxidation temperature of coke shifted to higher values with less hydrogen content with the increase of coke deposits. BET and Benzene-TPD techniques were employed to study the variation of specific surface area of the external and micropore surface versus time onstream. With the accumulation of coke deposits, although the pores became partially blocked and the internal surface decreased, methane could still enter the channel and was converted to benzene with shape selectivity until a critical value of coke deposition was reached.