Effect of matrix strength on the mechanical properties of Al-Zn-Mg/SiCp composites

The mechanical properties of Al-Zn-Mg alloy reinforced with SiCP composites prepared by solidification route were studied by altering the matrix strength with different heat treatments. With respect to the control alloy, the composites have shown similar ageing behaviour in terms of microhardness data at 135 degrees C. It was shown that although composites exhibited enhanced modulus values, the strengthening was found to be dependent on the damage that is occurring during straining. Thus the initial matrix strength plays an important role in determining the strengthening. Consequently, compression data had shown a different trend compared to tension. (C) 2000 Elsevier Science Ltd. All rights reserved.

Electron diffraction patterns from the Al-Mn decagonal phase

The variety of electron diffraction patterns arising from the decagonal phase has been explored using a stereographic analysis for generating the important zone axes as intersection points corresponding to important relvectors. An indexing scheme employing a set of five vectors and an orthogonal vector has been followed. A systematic tilting from the decagonal axis to one of the twofold axes has been adopted to generate a set of experimental diffraction patterns corresponding to the expected patterns from the stereographic analysis with excellent agreement.

Ferroelectricity in Bi26-xMxO40-delta (M = Al and Ga) with the gamma-Bi2O3 structure

We report on the dielectric proper-ties of bismuth aluminate and gallate with Bi:AI(Ga) ratio of 1: 1 and 12:1 prepared at high temperature and ambient pressure. These compounds crystallize in a noncentrosymmetric body-centered cubic structure (space group 123) with a similar to 10.18 angstrom rather than in the perovskite structure.This cubic phase is related to the gamma-Bi2O3 structure which has the actual chemical formula Bi-24(3+) (Bi3+Bi5+)O40-delta. In the aluminates and gallates studied by us, the Al and Ga ions are distributed over the 24f and 2a sites. These compounds exibit ferroclectric hysteresis at room temperature with a weak polarization. (c) 2006 Elsevier Ltd. All rights reserved.

Synthesis and structural aspects of quasicrystals in Mg-Al-Ag system: Mg4Al6Ag

The existence of an icosahedral phase in Mg−Al−Ag is better understood on a crystallographic basis rather than on a quantum structural diagram basis. The quasicrystalline structure is delineated in terms of quasiperiodic arrangement of Pauling triacontahedra, which can be identified in the equilibrium structure. Subtle differences in the electron diffraction patterns have been recorded compared to the ideal quasicrystalline pattern. The misalignment of spots and distortions are better attributed to higher order rational approximate structure than anisotropic phason strain. Ares of diffuse intensity have been related to the ordering among the atoms in the clusters.

Experimental and Computational Characterization of Alloy--Spinel--Corundum Equilibrium in the System Fe--Co--Al--O at 1873K

The three-phase equilibrium between alloy, spinel solid solution and alpha -Al sub 2 O sub 3 in the Fe--Co--Al--O system at 1873k was fully characterized as a function of alloy composition using both experimental and computational methods. The equilibrium oxygen content of the liquid alloy was measured by suction sampling and inert gas fusion analysis. The O potential corresponding to the three-phase equilibrium was determined by emf measurements on a solid state galvanic cell incorporating (Y sub 2 O sub 3 )ThO sub 2 as the solid electrolyte and Cr + Cr sub 2 O sub 3 as the reference electrode. The equilibrium composition of the spinel phase formed at the interface between the alloy and alumina crucible was measured by electron probe microanalysis (EPMA). The experimental results were compared with the values computed using a thermodynamic model. The model used values for standard Gibbs energies of formation of pure end-member spinels and Gibbs energies of solution of gaseous O in liquid Fe and cobalt available in the literature. The activity--composition relationship in the spinel solid solution was computed using a cation distribution model. The variation of the activity coefficient of O with alloy composition in the Fe--Co--O system was estimated using both the quasichemical model of Jacob and Alcock and Wagner's model along with the correlations of Chiang and Chang and Kuo and Chang. The computed results of spinel composition and O potential are in excellent agreement with the experimental data. Graphs. 29 ref.--AA

Activities, concentration fluctuations and complexing in liquid Ca-Al alloys

Détermination de l'activité du calcium par la méthode d'effusion de Knudsen. Calcul, à partir de la distribution mesurée pour l'aluminium entre l'alliage et du fer pur, de l'activité de l'aluminium dans des alliages riches en calcium. Détermination en combinant les deux méthodes, des activités des deux composants et de l'énergie de Gibbs de mélange pour tout le domaine de composition. Calcul et analyse du facteur de structure concentration-concentration

Al/SiC carriers for microwave integrated circuits by a new technique of pressureless infiltration

Materials with high thermal conductivity and thermal expansion coefficient matching with that of Si or GaAs are being used for packaging high density microcircuits due to their ability of faster heat dissipation. Al/SiC is gaining wide acceptance as electronic packaging material due to the fact that its thermal expansion coefficient can be tailored to match with that of Si or GaAs by varying the Al:SiC ratio while maintaining the thermal conductivity more or less the same. In the present work, Al/SiC microwave integrated circuit (MIC) carriers have been fabricated by pressureless infiltration of Al-alloy into porous SiC preforms in air. This new technique provides a cheaper alternative to pressure infiltration or pressureless infiltration in nitrogen in producing Al/SiC composites for electronic packaging applications. Al-alloy/65vol% SiC composite exhibited a coefficient of thermal expansion of 7 x 10(-6) K-1 (25 degrees C-100 degrees C) and a thermal conductivity of 147 Wm(-1) K-1 at 30 degrees C. The hysteresis observed in thermal expansion coefficient of the composite in the temperature range 100 degrees C-400 degrees C has been attributed to the presence of thermal residual stresses in the composite. Thermal diffusivity of the composite measured over the temperature range from 30 degrees C to 400 degrees C showed a 55% decrease in thermal diffusivity with temperature. Such a large decrease in thermal diffusivity with temperature could be due to the presence of micropores, microcracks, and decohesion of the Al/SiC interfaces in the microstructure (all formed during cooling from the processing temperature). The carrier showed satisfactory performance after integrating it into a MIC.

Characterization of Alloy-Spinel-Corundum Equilibrium in the System Fe-Ni-Al-O

The three phase equilibrium between alloy, spinel solid solution and α-alumina in the Fe-Ni-Al-O system has been fully characterized at 1823K as a function of alloy composition using both experimental and computational methods. The oxygen potential was measured using a solid state cell incorporating yttria-doped thoria as the electrolyte and Cr+ Cr2O3 as the reference electrode. Oxygen concentration of the alloy was determined by an inert gas fusion technique. The composition of the spinel solid solution, formed at the interface between the alloy and an alumina crucible, was determined by EPMA. The variation of the oxygen concentration and potential and composition of the spinel solid solution with mole fraction of nickel in the alloy have been computed using activities in binary Fe-Ni system, free energies of formation of end member spinels FeO•(1+x)Al2O3 and NiO•(1+x)Al2O3 and free energies of solution of oxygen in liquid iron and nickel, available in the literature. Activities in the spinel solid solution were computed using a cation distribution model. The variation of the activity coefficient of oxygen with alloy composition in Fe-Ni-O system was calculated using both the quasichemical model of Jacob and Alcock and the Wagner's model, with the correlation of Chiang and Chang. The computed results for the oxygen potential and the composition of the spinel solid solution are in good agreement with the measurements. The measured oxygen concentration lies between the values computed using models of Wagner and Jacob and Alcock. The results of the study indicate that the deoxidation hyper-surface in multicomponent systems can be computed with useful accuracy using data for end member systems and thermodynamic models.

Laser Surface Alloying of a Creep Resistant Magnesium Alloy MRI 230D with Al and Al2O3

A creep resistant permanent mould cast Mg alloy MRI 230D was laser surface alloyed with Al and a mixture of Al and Al2O3 using pulsed Nd:YAG laser irradiation at four different scan speeds in order to improve the corrosion and wear resistance. The microstructure, corrosion and wear behavior of the laser surface alloyed material is reported in this manuscript. The coating comprised of a featureless microstructure with cellular-dendritic microstructure near the interface and exhibited good interfacial bonding. A few solidification cracks reaching down to substrate were also observed. The two step coating with Al followed by a mixture of Al and Al2O3 exhibited a slightly better corrosion resistance than the single step coating with Al. In the long run, however, corrosion resistance of both the coatings became comparable to the as-cast alloy. The corroded surface of the laser surface alloyed specimens revealed a highly localized corrosion. The laser surface alloyed specimens exhibited an improvement in wear resistance. The laser scan speed did not exhibit a monotonic trend either in corrosion or wear resistance.

Microstructure and Properties of the Spray-Formed and Extruded 7075 Al Alloy

In the present investigation, a very good combination of strength and ductility, 630MPa 0.2% proof stress and 14.8% elongation to fracture in tensile test, has been obtained for the 7075 Al alloy after optimizing the processing parameters for spray forming, hot extruding the spray deposit, and peak aging the samples taken from the extruded rod. The spray deposits contained some porosity but it was almost eliminated on hot extrusion. Electron probe microanalysis revealed that even though spray forming was carried out in an open atmosphere, it did not affect the oxygen content and its distribution in the material on spray forming, because the atomizing argon gas provided a protective cover to molten droplets and prevented their oxidation. The chemical composition of the spray-formed material was found to be almost the same as the raw material, and the major alloying elements were found to be uniformly distributed in the extruded rod.

Synthesis and characterization of Ti5Te4-type molybdenum cluster compounds, AxMo5As4(A = Cu, Al, or Ga)

A new series of molybdenum cluster compounds of the general formula AxMo5As4(A = Cu, Al, or Ga) has been synthesized. They are isostructural with the host Mo5As4(Ti5Te4-type) consisting of trans-vertex shared Mo6 octahedral chains. Investigations by X-ray photoelectron and Auger electron spectroscopies revealed a charge transfer from A to Mo5As4 in AxMo5As4. The occurrence of metallic (CuxMo5As4) and non-metallic (Al2Mo5As4 and Ga2Mo5As4) properties in this isostructural series of solids is consistent with the electronic structure of Ti5Te4-type solids involving M–M bonding in the cluster chains.

Strain-rate sensitivity and microstructural evolution in a Mg-Al-Zn alloy

Strain rate sensitivity measurements are used to identify twinning and changes in deformation mechanisms in a Mg AZ31 alloy over a wide range of temperatures and grain sizes. At low temperatures, there is significant twinning at low strains with strain-rate insensitivity; at large strains, strain rate sensitivity is noted, corresponding to deformation by multiple slip. At high temperatures, there is very little twinning and this leads to a significant strain rate sensitivity from the early stages of deformation. (C) 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.