Influence of the growth temperature of the high-temperature AlN buffer on the properties of GaN grown on Si(111) substrate

We have studied the influence of the growth temperature of the high-temperature (HT) AIN buffer layer on the properties of the GaN epilayer which was grown on Si(111) substrate by metalorganic chemical vapor deposition (MOCVD). It was found that the crystal quality of the GaN epilayer strongly depends on the growth temperature of the HT-AIN buffer. The growth temperature of the AIN buffer to obtain high-quality GaN epilayers lies in a narrow window of several tens of degrees. When the temperature is lower than a certain temperature range, the appearance of AIN polycrystals results in the deterioration of the crystal quality of the AIN buffer layer, which is greatly disadvantageous to the coalescence of the GaN epilayer. Although the AIN buffer's crystal quality is improved as the growth temperature increases, the Si outdiffusion from the substrate is also enhanced when the temperature is higher than a certain temperature range, which will demolish the subsequent growth of the GaN epilayer. Therefore, there exists an optimum growth temperature range of the AIN buffer around 1080degreesC for the growth of high-quality GaN epilayers. (C) 2003 Elsevier B.V. All rights reserved.

Effect of the N/Al ratio of AlN buffer on the crystal properties and stress state of GaN film grown on Si(111) substrate

The effect of the N/Al ratio of AlN buffers on the optical and crystal quality of GaN films, grown by metalorganic chemical vapor deposition on Si(111) substrates, has been investigated. By optimizing the N/Al ratio during the AlN buffer, the threading dislocation density and the tensile stress have been decreased. High-resolution X-ray diffraction exhibited a (0002) full-width at half-maximum as low as 396 acrsec. The variations of the tensile stress existing in the GaN films were approved by the redshifts of the donor bound exiton peaks in the low-temperature photoluminescence measurement at 77 K. (C) 2003 Elsevier B.V. All rights reserved.

Optical properties of GaN grown on Si(111) substrates by MOCVD

GaN epilayers were grown on Si (111) substrates by MOCVD. The optical properties of the samples under different growth conditions were characterized The abnormal peaks of excitonic emissions related to cubic-GaN were observed on the samples under improper growth conditions based on the LT PL measurements. Also the peak intensity is much higher than that of hexagonal-GaN. The higher intensity of exciton peaks is attributed to the local quantum well formed between the hexagonal- and cubic-GaN. No exciton peaks of cubic-GaN were found on the sample using the optimal growth conditions.

Growth and properties of GaN on Si (111) substrates with AlGaN/AlN buffer layer by NH3-GSMBE

We describe the growth of GaN on Si (111) substrates with a AlGaN/AlN buffer layer by NH3-GSMBE. The influence of the AlN and AlGaN buffer layer thickness on the crack density of GaN has been investigated. It is found that the optimum thickness is 120 nm and 250 nm for AlN and AlGaN layers, respectively. The full width at half maximum of the GaN (0002) peak in the triple-crystal x-ray rocking curve measurement is about 15 arcmin.

The effect of the AlxGa1-xN/AIN buffer layer on the properties of GaN/Si(111) film grown by NH3-MBE

We describe the growth of GaN on Si(111) substrates with AlxGa1-xN/AlN buffer layer by ammonia gas source molecular beam epitaxy (NH3-GSMBE). The influence of the AlN and AlxGa1-xN buffer layer thickness and the Al composition on the crack density of GaN has been investigated. It is found that the optimum thickness is 120 and 250 nm for AlN and AlxGa1-xN layers, respectively. The optimum Al composition is between 0.3 < x < 0.6. (c) 2005 Elsevier B.V. All rights reserved.

Crack-free GaN/Si(111) epitaxial layers grown with InAlGaN alloy as compliant interlayer by metalorganic chemical vapor deposition

A new method is demonstrated to be effective in reducing mismatch-induced tensile stress and suppressing the formation of cracks by inserting InAlGaN interlayers during the growth of GaN upon Si (1 1 1) substrate. Compared with GaN film without quaternary interlayer, GaN layer grown on InAlGaN compliant layers shows a five times brighter integrated PL intensity and a (0 0 0 2) High-resolution X-ray diffraction (HRXRD) curve width of 18 arcmin. Its chi(min), derived from Rutherford backscattering spectrometry (RBS), is about 2.0%, which means that the crystalline quality of this layer is very good. Quaternary InAlGaN layers, which are used as buffer layers firstly, can play a compliant role to endure the large mismatch-induced stress and reduce cracks during the growth of GaN epitaxy. The mechanisms leading to crack density reduction are investigated and results show that the phase immiscibility and the weak In-N bond make interlayer to offer tenability in the lattice parameters and release the thermal stress. (c) 2005 Elsevier B.V. All rights reserved.

Heteroepitaxial gold (111) rings on mica substrates

Two-dimensionally arranged gold rings were prepared by depositing a polymeric membrane bearing a dense array of uniform pores onto a mica substrate, filling the pores with a solution of a gold precursor, evaporation of the solvent and calcinations. The epitaxy of gold rings is confirmed by x-ray diffraction measurements, and the epitaxial relationship between gold rings and the mica was found to be Au(111)[1-10]parallel to mica(001)[010]. The polar and azimuthal angular spreads are 0.3 degrees and 1 degrees, respectively, which is at least equal to or better than the quality of the corresponding epitaxial gold-film on mica. (c) 2005 American Institute of Physics.

Design of the low-temperature AlN interlayer for GaN grown on Si(111) substrate

We have investigated the effect of the thickness and layer number of the low-temperature A1N interlayer (LT-A1N IL) on the stress relaxation and the crystal quality of GaN epilayers grown on Si (111) substrate by metalorganic chemical vapor deposition. It is found that the stress decreases with the increase of the LT-AIN IL thickness, but the crystal quality of the GaN epilayer goes worse quickly when the LT-AIN IL thickness is larger than 16 nm. This is because the increase of the LT-AIN IL thickness will increase the coalescence thickness of its upper GaN layer, which sensitively affects the crystal quality of the epilayer. Using multiple LT-AIN ILs is an effective method not only to reduce the stress, but also to improve the crystal quality of the GaN epilayer. With the increase of the interlayer number, the probability that dislocations are blocked increases and the probability that dislocations are produced at interfaces decreases. Thus, dislocations in the most upper part of GaN are reduced, resulting in the improvement of the crystal quality. Finally, it is suggested that when the total thickness of the epilayer is fixed, both the thickness and the number of the LT-AIN IL should be carefully designed to reduce the stress and improve the crystal quality of the epilayer simultaneously. (c) 2004 Elsevier B.V.. All rights reserved.

Effect of the variation of temperature on the structural and optical properties of ZnO thin films prepared on Si (111) substrates using PLD

ZnO thin films were prepared on Si (1 11) substrates at various temperatures from 250 to 700 degrees C using pulsed laser deposition (PLD) technique in order to investigate the structural and optical properties of the films. The structural and morphological properties of the films were investigated by XRD and SEM measurements, respectively. The quality of the films was improved with the increase of the temperature. By XRD patterns the FWHMs of the (0 0 2) peaks of the ZnO films became narrower when the temperatures were above 500 degrees C. The FWHMs of the peaks of (0 0 2) of the films were as narrow as about 0. 19 degrees when films were grown at 650 and 700 degrees C. This indicates the superior crystallinity of the films. The optical properties of the films were studied by photoluminescence spectra using a 325 nm He-Cd laser. The two strongest UV peaks were found at 377.9 nm from ZnO films grown at 650 and 700 degrees C. This result is consistent with that of the XRD investigation. Broad bands in visible region from 450 to 550 nm were also observed. Our works suggest that UV emissions have close relations with not only the crystallinity but also the stoichiometry of the ZnO films. (c) 2005 Elsevier Ltd. All rights reserved.

Crack-free InAlGaN quaternary alloy films grown on Si(111) substrate by metalorganic chemical vapor deposition

Crack-free In0.08Al0.25Ga0.67N quaternary films, with and without thick (> 1.5 mum) high-temperature-GaN (HTGaN) interlayer, have been grown on Si(1 1 1) substrates by a low-pressure metalorganic chemical vapor deposition (MOCVD) system. Mole fractions of In and Al in quaternary alloy layers are determined by Energy dispersive spectroscopy (EDS) and Rutherford backscattering spectrometry (RBS), which are recorded as similar to8% and similar to25-27%, respectively. High-resolution X-ray diffraction (HRXRD) and room temperature photoluminescence (RT-PL) results evidence the film's single crystal structure and the existence of local In- and/or Al-rich regions. Compared with GaN film grwon on Si(1 1 1) substrate, no crack is observed in the quaternary ones. Two explanations are proposed. First, mismatch-induced strain is relaxed significantly due to gradual changes of In concentration. Second, the weak In-N bond is likely to break when the sample is cooled down to the room temperature, which is expected to favor the releasing of thermal stress. (C) 2004 Elsevier B.V. All rights reserved.

Depth distribution of the strain in the GaN layer with low-temperature AlN interlayer on Si(111) substrate studied by Rutherford backscattering/channeling

The depth distribution of the strain-related tetragonal distortion e(T) in the GaN epilayer with low-temperature AlN interlayer (LT-AlN IL) on Si(111) substrate is investigated by Rutherford backscattering and channeling. The samples with the LT-AlN IL of 8 and 16 nm thickness are studied, which are also compared with the sample without the LT-AlN IL. For the sample with 16-nm-thick LT-AlN IL, it is found that there exists a step-down of e(T) of about 0.1% in the strain distribution. Meanwhile, the angular scan around the normal GaN <0001> axis shows a tilt difference about 0.01degrees between the two parts of GaN separated by the LT-AlN IL, which means that these two GaN layers are partially decoupled by the AlN interlayer. However, for the sample with 8-nm-thick LT-AlN IL, neither step-down of e(T) nor the decoupling phenomenon is found. The 0.01degrees decoupled angle in the sample with 16-nm-thick LT-AlN IL confirms the relaxation of the LT-AlN IL. Thus the step-down of e(T) should result from the compressive strain compensation brought by the relaxed AlN interlayer. It is concluded that the strain compensation effect will occur only when the thickness of the LT-AlN IL is beyond a critical thickness. (C) 2004 American Institute of Physics.

Stress reduction in GaN films on (111) silicon-on-insulator substrate grown by metal-organic chemical vapor deposition

The GaN film was grown on the (111) silicon-on-insulator (SOI) substrate by metal-organic chemical vapor deposition and then annealed in the deposition chamber. A multiple beam optical stress sensor was used for the in-situ stress measurement, and X-ray diffraction (XRD) and Raman spectroscopy were used for the characterization of GaN film. Comparing the characterization results of the GaN films on the bulk silicon and SOI substrates, we can see that the Raman spectra show the 3.0 cm(-1) frequency shift of E-2(TO), and the full width at half maximum of XRD rocking curves for GaN (0002) decrease from 954 arc see to 472 are sec. The results show that the SOI substrates can reduce the tensile stress in the GaN film and improve the crystalline quality. The annealing process is helpful for the stress reduction of the GaN film. The SOI substrate with the thin top silicon film is more effective than the thick top silicon film SOI substrate for the stress reduction. (C) 2007 Elsevier B.V. All rights reserved.

The influence of AlN/GaN superlattice intermediate layer on the properties of GaN grown on Si(111) substrates

AlN/GaN superlattice buffer is inserted between GaN epitaxial layer and Si substrate before epitaxial growth of GaN layer. High-quality and crack-free GaN epitaxial layers can be obtained by inserting AlN/GaN superlattice buffer layer. The influence of AlN/GaN superlattice buffer layer on the properties of GaN films are investigated in this paper. One of the important roles of the superlattice is to release tensile strain between Si substrate and epilayer. Raman spectra show a substantial decrease of in-plane tensile strain in GaN layers by using AlN/GaN superlattice buffer layer. Moreover, TEM cross-sectional images show that the densities of both screw and edge dislocations are significantly reduced. The GaN films grown on Si with the superlattice buffer also have better surface morphology and optical properties.

Effect of an indium-doped barrier on enhanced near-ultraviolet emission from InGaN/AlGaN: In multiple quantum wells grown on Si(111)

Low indium content InGaN/AlGaN multiple quantum wells (MQWs) have been grown on Si(111) substrate by metal-organic chemical vapour deposition (MOCVD). A new method of using an isoelectronic indium-doped AlGaN barrier has been found to be very effective in improving the crystalline quality and interfacial abruptness of InGaN quantum well layers. We grew five periods of In0.06Ga0.94N/Al0.20Ga0.80N:In MQWs with In-doped barrier layers and obtained strong near-ultraviolet (UV) emission (similar to 400 nm) at room temperature. An In-doped AlGaN barrier improves the room-temperature PL intensity of InGaN/AlGaN MQWs, making it a candidate barrier for a near-UV source on Si substrate.

Influence of the AlN interlayer crystal quality on the strain evolution of GaN layer grown on Si (111)

The strain evolution in metal organic chemical vapor deposition growth of GaN on Si (111) substrate with an AlN interlayer is studied. During the growth of GaN film on AlN interlayer, the growth stress changes from compression to tension. The study shows that the density of V trenches in the AlN interlayer surface and the threading dislocations generated in the AlN interlayer have a significant influence on this strain evolution process. The dislocations generated in AlN interlayer may thread across the interface and play a key role in the strain evolution process of the GaN layer grown on AlN interlayer.