Numerical modelling of solder joint formation

Solder materials are used to provide a connection between electronic components and printed circuit boards (PCBs) using either the reflow or wave soldering process. As a board assembly passes through a reflow furnace the solder (initially in the form of solder paste) melts, reflows, then solidifies, and finally deforms between the chip and board. A number of defects may occur during this process such as flux entrapment, void formation, and cracking of the joint, chip or board. These defects are a serious concern to industry, especially with trends towards increasing component miniaturisation and smaller pitch sizes. This paper presents a modelling methodology for predicting solder joint shape, solidification, and deformation (stress) during the assembly process.

A computational modelling framework to predict macroscopic phenomena in solder joint formation

A computational model of solder joint formation and the subsequent cooling behaviour is described. Given the rapid changes in the technology of printed circuit boards, there is a requirement for comprehensive models of solder joint formation which permit detailed analysis of design and optimization options. Solder joint formation is complex, involving a range of interacting phenomena. This paper describes a model implementation (as part of a more comprehensive framework) to describe the shape formation (conditioned by surface tension), heat transfer, phase change and the development of elastoviscoplastic stress. The computational modelling framework is based upon mixed finite element and finite volume procedures, and has unstructured meshes enabling arbitrarily complex geometries to be analysed. Initial results for both through-hole and surface-mount geometries are presented.

An integrated modeling approach to solder joint formation

The attachment of electronic components to printed circuit boards using solder material is a complex process. This paper presents a novel modeling methodology, which integrates the governing physics taking place. Multiphysics modeling technology, imbedded into the simulation tool—PHYSICA is used to simulate fluid flow, heat transfer, solidification, and stress evolution in an integrated manner. Results using this code are presented, detailing the mechanical response of two solder materials as they cool, solidify and then deform. The shape that a solder joint takes upon melting is predicted using the SURFACE EVOLVER code. Details are given on how these predictions can be used in the PHYSICA code to provide a modeling route by which the shape, solidification history, and resulting stress profiles can be predicted.

Mechanism of motion of an optical fiber aligned by a solder droplet

Solder is often used as an adhesive to attach optical fibers to a circuit board. In this proceeding we will discuss efforts to model the motion of an optical fiber during the wetting and solidification of the adhesive solder droplet. The extent of motion is determined by several competing forces, during three “stages” of solder joint formation. First, capillary forces of the liquid phase control the fiber position. Second, during solidification, the presence of the liquid-solid-vapor triple line as well as a reduced liquid solder volume leads to a change in the net capillary force on the optical fiber. Finally, the solidification front itself impinges on the fiber. Publicly-available finite element models are used to calculate the time-dependent position of the solidification front and shape of the free surface.

Experimental and modeling analysis of the reliability of the anisotropic conductive films

Experiments as well as computer modeling methods have been used to investigate the effect of the solder reflow process on the electrical characteristics and reliability of anisotropic conductive film (ACF) interconnections. In the experiments, the contact resistance of the ACF interconnections was found to increase after a subsequent reflow and the magnitude of this increase was strongly correlated to the peak temperature of the reflow profile. In fact, nearly 40 percent of the joints were opened (i.e. lifted away from the pad) after the reflow with a peak temperature of 260 OC while no openings was observed when the peak temperature was 210 "C. It is believed that the CTE mismatch between the polymer particle and the adhesive matrix is the main cause of this contact degradation. To understand this phenomenon better, a 3-D model of an ACF joint structure was built and Finite Element Analysis was used to predict the stress distrihution in the conductive particles, adhesive matrix and metal pads during the reflow process. The effects of the peak temperature, the CTE of the adhesive matrix and the bump height on the reliability of the ACF interconnections were discussed.

Correlation of solder paste rheology with computational simulations of the stencil printing process

Soldering technologies continue to evolve to meet the demands of the continuous miniaturisation of electronic products, particularly in the area of solder paste formulations used in the reflow soldering of surface mount devices. Stencil printing continues to be a leading process used for the deposition of solder paste onto printed circuit boards (PCBs) in the volume production of electronic assemblies, despite problems in achieving a consistent print quality at an ultra-fine pitch. In order to eliminate these defects a good understanding of the processes involved in printing is important. Computational simulations may complement experimental print trials and paste characterisation studies, and provide an extra dimension to the understanding of the process. The characteristics and flow properties of solder pastes depend primarily on their chemical and physical composition and good material property data is essential for meaningful results to be obtained by computational simulation.This paper describes paste characterisation and computational simulation studies that have been undertaken through the collaboration of the School of Aeronautical, Mechanical and Manufacturing Engineering at Salford University and the Centre for Numerical Modelling and Process Analysis at the University of Greenwich. The rheological profile of two different paste formulations (lead and lead-free) for sub 100 micron flip-chip devices are tested and applied to computational simulations of their flow behaviour during the printing process.

Effects of reflow process on the reliability of flip chip on flex interconnections using anisotropic conductive adhesives

In this paper, the effects of the solder reflow process on the reliability of anisotropic conductive film (ACF) interconnections for flip chip on flex (FCOF) applications are investigated. Experiments as well as computer modeling methods have been used. In the experiments, it was found that the contact resistance of ACF joints increased after the subsequent reflow process, and the magnitude of this increase was strongly correlated to the peak temperature of the reflow profile. Nearly 40% of the joints were opened (i.e. lifted away from the pad) after the reflow process with 260 °C peak temperature while no opening was observed when the peak temperature was 210 °C. It is believed that the CTE mismatch between the polymer particle and the adhesive matrix is the main cause of this contact degradation. It was also found that the ACF joints after the reflow process with 210 °C peak temperature showed a high ability to resist water absorption under steady state 85 °C/85%RH conditions, probably because the curing degree of the ACF was improved during the reflow process. To give a good understanding, a 3D model of an ACF joint structure was built and finite element analysis was used to predict the stress distribution in the conductive particles, adhesive matrix and metal pads during the reflow process.

The effect of thermal cycle profiles on solder joint damage

The relationship between the damage caused at different thermal cycles is very important. The whole of accelerated thermal cycle testing is based on the premise that damage at one cycle is representative of damage at a different cycle. In this paper, the relative damage caused by six thermal cycle profiles are predicted using Finite Element (FE) modelling and the results validated against experiments. Both creep strain and strain energy density were used as damage indicators and creep strain was found to correlate better with experiment. The validated FE model is then used to investigate the effect of altering each of the thermal profile parameters (ramp and swell times, hot and cold temperatures). The components used for testing are surface mount resistors - 1206, 0805 and 0603. The solders investigated are eutectic SnAgCu and eutectic SnAg.

Solder life prediction in a thermal analysis software environment

This paper describes recent developments made to the stress analysis module within FLOTHERM, extending its capability to handle viscoplastic behavior. It also presents the validation of this approach and results obtained for an SMT resistor as an illustrative example. Lifetime predictions are made using the creep strain energy based models of Darveaux. Comment is made about the applicability of the damage model to the geometry of the joint under study.

Wetting and Reaction of Sn-2.8Ag-0.5Cu-1.0Bi Solder with Cu and Ni Substrates

The wettability of newly developed Sn-2.8Ag-0.5Cu-1.0Bi lead-free solder on Cu and Ni substrates was assessed through the wetting balance tests. The wettability assessment parameters such as contact angle (ϑc) and maximum wetting force (Fw) were documented for three solder bath temperatures with three commercial fluxes, namely, no-clean (NC), nonactivated (R), and water-soluble organic acid flux (WS). It was found that the lead-free Sn-2.8Ag-0.5Cu-1.0Bi solder exhibited less wetting force, i.e., poorer wettability, than the conventional Sn-37Pb solder for all flux types and solder bath temperatures. The wettability of Sn-2.8Ag-0.5Cu-1.0Bi lead-free solder on Cu substrate was much higher than that on Ni substrate. Nonwetting for Sn-2.8Ag-0.5Cu-1.0Bi and Sn-Pb solders on Ni substrate occurred when R-type flux was used. A model was built and simulations were performed for the wetting balance test. The simulation results were found very close to the experimental results. It was also observed that larger values of immersion depth resulted in a decrease of the wetting force and corresponding meniscus height, whereas the increase in substrate perimeter enhanced the wettability. The wetting reactions between the solder and Cu/Ni substrates were also investigated, and it was found that Cu atoms diffused into the solder through the intermetallic compounds (IMCs) much faster than did the Ni atoms. Rapid formation of IMCs inhibited the wettability of Sn-2.8Ag-0.5Cu-1.0Bi solder compared to the Sn-Pb solder.

Modelling the Performance of Flexible Substrates for Lead-Free Applications

In this paper, the performance of flexible substrates for lead-free applications was studied using finite element method (FEM). Firstly, the thermal induced stress in the flex substrate during the lead free solder reflow process was predicted. The shear stress at the interface between the copper track and flex was plotted. This shear stress increases with the thickness of the copper track. Secondly, an ACF flip chip was taken as a typical lead-free application of the flex substrate. The reflow effect on the reliability of ACF interconnections was analyzed. Higher stress was identified along the interface between the conductive particle and the metallization, and the interfacial stress increases with the reflow peak temperature and the coefficient of thermal expansion (CTE) of the adhesive. The moisture effect on the reliability of ACF joints were studied using a macro-micro modeling technique, the predominantly tensile stress found at the interface between the conductive particle and metallization could reduce the contact area and even cause the electrical failure. Modeling results are consistent with the findings in the experimental work

Computational modelling for reliable flip-chip packaging at sub-100 micron pitch using isotropic conductive adhesives

This paper presents the assembly process using next generation electroformed stencils and Isotropic Conductive Adhesives (ICAs) as interconnection material. The utilisation of ICAs in flip-chip assembly process is investigated as an alternative to the lead and lead-free solder alloys and aims to ensure a low temperature (T < 100 °C) assembly process. The paper emphasizes and discusses in details the assembly of a flip-chip package based on copper columns bumped die and substrate with stencil printed ICA deposits at sub-100 μm pitch. A computational modelling approach is undertaken to provide comprehensive results on reliability trends of ICA joints subject to thermal cycling of the flip-chip assembly based on easy to use damage criteria and damage evaluation. Important design parameters in the package are selected and investigated using numerical modelling techniques to provide knowledge and understanding of their impact on the thermo-mechanical behaviour of the flip-chip ICA joints. Sensitivity analysis of the damage in the adhesive material is also carried out. Optimal design rules for enhanced performance and improved thermo-mechanical reliability of ICA assembled flip-chip packages are finally formulated.

Analyzing the performance of flexible substrates for lead-free applications

The performance of flexible substrates for lead-free applications was studied using finite element method (FEM). Firstly, the thermal induced stress in the flex substrate during the lead free solder reflow process was predicted. The shear stress at the interface between the copper track and flex was plotted. This shear stress increases with the thickness of the copper track and the thickness of the flex. Secondly, an anisotropic conductive film (ACF) flip chip was taken as a typical lead-free application of the flex substrate and the moisture effect on the reliability of ACF joints were studied using a 3D macro-micro modeling technique. It is found that the time to be saturated of an ACF flip chip is much dependent on the moisture diffusion rate in the polyimide substrate. The majority moisture diffuses into the ACF layer from the substrate side rather than the periphery of the ACF. The moisture induced stress was predicted and the predominant tensile stress was found at the interface between the conductive particle and metallization which could reduce the contact area and even cause the electrical failure

Thermal-mechanical analysis of flexible substrates during lead-free solder reflow

This paper presents modeling results about the performance of flexible substrates when subjected to higher lead-free reflow temperatures. Both adhesiveless and adhesive types of polyimide substrates were studied. Finite element (FE) models of flex substrates were built, two copper tracks located in the centre of the substrate was considered. The thermal induced shear stress in the flex substrate during the lead-free reflow process was studied and the effect of the design changes including the track thickness, flex thickness, and copper width were studied. For both types of flexes, the one of most important variables for minimizing damage to the substrate is the height of the copper tracks. The height of flex and the width of copper track show less impact. Beside of the geometry effects, the increase in reflow peak temperature can also result in a significant increase in the interfacial stress between the copper track and flex. Higher stresses were identified within the adhesive flex due to the big CTE mismatch between the copper and adhesive/dielectric

Effect of 0.5 wt % Cu addition in Sn–3.5% Ag solder on the dissolution rate of Cu metallization

The dissolution of thin film under-bump-metallization (UBM) by molten solder has been one of the most serious processing problems in electronic packaging technology. Due to a higher melting temperature and a greater Sn content, a molten lead-free solder such as eutectic SnAg has a faster dissolution rate of thin film UBM than the eutectic SnPb. The work presented in this paper focuses on the role of 0.5 wt % Cu in the base Sn–3.5%Ag solder to reduce the dissolution of the Cu bond pad in ball grid array applications. We found that after 0.5 wt % Cu addition, the rate of dissolution of Cu in the molten Sn–3.5%Ag solder slows down dramatically. Systematic experimental work was carried out to understand the dissolution behavior of Cu by the molten Sn–3.5%Ag and Sn–3.5%Ag–0.5%Cu solders at 230–250 °C, for different time periods ranging from 1 to 10 min. From the curves of consumed Cu thickness, it was concluded that 0.5 wt % Cu addition actually reduces the concentration gradient at the Cu metallization/molten solder interface which reduces the driving force of dissolution. During the dissolution, excess Cu was found to precipitate out due to heterogeneous nucleation and growth of Cu6Sn5 at the solder melt/oxide interface. In turn, more Cu can be dissolved again. This process continues with time and leads to more dissolution of Cu from the bond pad than the amount expected from the solubility limit, but it occurs at a slower rate for the molten Sn–3.5%Ag–0.5%Cu solder. © 2003 American Institute of Physics.