Electrolytic Deposition and Diffusion of Lithium onto Magnesium-9 Wt Pct Yttrium Bulk Alloy in Low-Temperature Molten Salt of Lithium Chloride and Potassium Chloride

The electrolytic deposition and diffusion of lithium onto bulk magnesium-9 wt pct yttrium alloy cathode in molten salt of 47 wt pct lithium chloride and 53 wt pct potassium chloride at 693 K were investigated. Results show that magnesium-yttrium-lithium ternary alloys are formed on the surface of the cathodes, and a penetration depth of 642 mu m is acquired after 2 hours of electrolysis at the cathodic current density of 0.06 A center dot cm(-2). The diffusion of lithium results in a great amount of precipitates in the lithium containing layer. These precipitates are the compound of Mg41Y5, which arrange along the grain boundaries and hinder the diffusion of lithium, and solid solution of yttrium in magnesium. The grain boundaries and the twins of the magnesium-9 wt pct yttrium substrate also have negative effects on the diffusion of lithium.

Determination of Cd2+ and Pb2+ on glassy carbon electrode modified by electrochemical reduction of aromatic diazonium salts

Carbon modified by the reduction of aromatic diazonium derivatives was first used as electrode for the electrochemical stripping analysis of heavy metals. As a model, the glassy carbon electrode was modified with benzoic acid by electrochemical reduction of diazobenzoic acid, and the resulting modified electrodes were used for determination of Cd2+ and Pb2+. The anodic peak currents of cadmium and lead at the benzoic acid-modified glassy carbon electrode are 7.2 and 6 times of that at the bare glassy carbon electrode. A linear response was observed for Pb2+ and Cd2+ in the range of 0.5-50 mu g/l.

Influence of laser-glazing on hot corrosion resistance of yttria-stabilized zirconia TBC in molten salt mixture of V2O5 and Na2SO4

Plasma-sprayed 8YSZ (zirconia stabilized with 8 wt% yttria)/NiCoCrAlYTa thermal barrier coatings (TBCs) were laser-glazed using a continuous-wave CO2 laser. Open pores within the coating surface were eliminated and an external densified layer was generated by laser-glazing. The hot corrosion resistances of the plasma-sprayed and laser-glazed coatings were investigated. The two specimens were exposed for the same period of 100 h at 900 degrees C to a salt mixture of vanadium pentoxide (V2O5) and sodium sulfate (Na2SO4). Serious crack and spallation occurred in the as-sprayed coating, while the as-glazed coating exhibited good hot corrosion behavior and consequently achieved a prolonged lifetime. The results showed that the as-sprayed 8YSZ coating achieved remarkably improved hot corrosion resistance by laser-glazing.

Carbon deposition behavior over copper salts of molybdovanadophosphoric acid catalyst supported by magnesia

MgO supported copper salt of molybdovanadophosphoric acid H4PMo11VO40 catalysts were prepared in alcohol by impregnation and the carbon deposition over these catalysts during the n-hexanol oxidation reaction was studied. The coke predominantly deposited on the catalyst surface in the form of CH., and it was not found that it caused the deactivation of the catalyst. The XRD, IR, XPS characterizations reveal that the Keggin structure of the CPMV was unaffected by carbon deposition. Moreover, it was shown that the supported CPMVs over the MgO surface can be beneficial to eliminate the coke. The temperature programmed oxidation (TPO) study showed that coke was formed over the catalyst on two different sites: (1) deposited on the CPMVs which can be burn off at a low temperature; (2) deposited on the MgO which could only be removed at higher temperature. The coke content reached constant with the reaction time increasing.

Enantioselective iodolactonization catalyzed by chiral quaternary ammonium salts derived from cinchonidine

Chiral quaternary ammonium salts derived from cinchonidine have been applied to catalyze the stereoselective iodolactonizations of trans-5-aryl-4-pentenoic acids leading to a mixture of two regioselectively iodolactonized products with fair to excellent yield (37-98%) and moderate enantioselectivity (exo = 42.0% ee, endo = 31.0% ee) under mild conditions. This work is the first example of asymmetric iodolactonization reaction in the presence of less than a stoichiometric amount of chiral reagent.

Structure and catalytic properties of magnesia-supported copper salts of molybdovanadophosphoric acid

The structure and stability of magnesia-supported copper salts of molybdovanadophosphoric acid (Cu2PMo11VO40) were characterized by different techniques. The catalyst was prepared in ethanol by impregnation because this solvent does not hurt texture of the water-sensitive MgO and Cu2PMo11VO40. The Keggin-type structure compound may be degraded partially to form oligomerized polyoxometalate when supported on MgO. However, the oligomers can rebuild as the Keggin structure again after thermal treatment in air or during the reaction. Meanwhile, the V atoms migrate out of the Keggin structure to form a lacunary structure, as observed by Fourier transform IR spectroscopy. Moreover, the presence of Cu2+ as a countercation showed an affirmative influence on the migration of V atoms, and the active sites derived from the lacunary species generated after release of V from the Keggin anion. The electron paramagnetic resonance data imply that V5+ autoreduces to V4+ in the fresh catalyst, and during the catalytic reaction a large number of V4+ ions are produced, which enhance the formation of O2- vacancies around the metal atoms. These oxygen vacancies may also improve the reoxidation function of the catalyst. This behavior is correlated to higher catalytic properties of this catalyst. The oxidative dehydrogenation of hexanol to hexanal was studied over this catalyst.

Dispersion copolymerization of acrylamide with quaternary ammonium cationic monomer in aqueous salts solution

Dispersion copolymerization of acrylamide (AM) with 2-methylacryloylxyethyl trimethyl ammonium chloride (DMC) has been carried out in aqueous salts solution containing ammonium sulfate and sodium chloride with poly(acryloylxyethyl trimethyl ammonium chloride) (PDAC) as the stabilizer and 2,2'-azobis[2-(2-inidazolin-2-yl)propane]-dihydro chloride (VA-044) as the initiator. A new particle formation mechanism of the dispersion polymerization for the present system has been proposed. The effects of inorganic salts and stabilizer concentration on dispersion polymerization have been investigated. The results show that varying the salt concentration could affect the morphology and molecular weight of the resultant copolymer particles significantly. With increasing the stabilizer concentration, the particle size decreased at first and then increased, meanwhile the effect on the copolymer molecular weight was the contrary. These results had been rationalized based on the proposed mechanism.

Facile preparation of ZnTiO3 ceramic powders in sodium/potassium chloride melts

A facile molten salt synthesis route was developed to prepare ZnTiO3 ceramic powders with simple oxides ZnO and TiO2 using sodium and potassium chloride eutectic salts as flux. The role of calcination temperature and time and the amount of salt addition to ZnTiO3 formation was investigated by thermogravimetry-differential thermal analysis, X-ray diffraction and Fourier transformation-infrared spectroscopy measurements. Pure hexagonal phase of ZnTiO3 could be obtained from the mixture of the simple oxides and the chlorides (50 mol% KCl, 20 times to oxides in molar ratio) heating at 800 degrees C for 6 h. The scanning electron microscopy images revealed the products were hexagonal sheets of about 1-3 mu m size. Increasing the amount of salt aids in reducing the crystal sizes of final ceramic powders because of diluting the solution.

Metal ion and anion coordination in the thiamine-[Pt-II(NO2)(4)](2-) system. Structures of a metal complex, Pt(thiamine)(NO2)(3), and two salts, (H-thiamine)[Pt(NO2)(4)]center dot 2H(2)O and (thiamine monophosphate)(2)[Pt(NO2)(4)]center dot 2H(2)O

Reaction of thiamine or thiamine monophosphate (TMP) with K2Pt(NO2)(4) afforded a metal complex, Pt(thiamine)(NO2)(3) (1), and two salt-type compounds, (H-thiamine)[Pt(NO2)(4)]. 2H(2)O (2) and (TMP)(2)[Pt(NO2)(4)]. 2H(2)O (3), which were structurally characterized by X-ray diffraction. In 1, the square-planar Pt2+ ion is coordinated to the pyrimidine N(1'), a usual metal-binding site, and three NO2- groups. The thiamine molecule exists as a monovalent cation in 1 and a divalent cation in 2 while the TMP molecule is a monovalent cation in 3. In each compound, thiamine or TMP adopts the usual F conformation and forms two types of host-guest-like interactions with anions, which are of the bridging forms, C(2)-H . . . anion . . . pyrimidine-ring and N(4'1)-H(...)anion(...)thiazolium-ring. In 3, there is an additional anion-bridging interaction between the pyrimidine and thiazolium rings of TMP, being of the form C(6')-H . . . anion . . . thiazolium-ring. The salts 2 and 3 show similar hydrogen-bonded cyclic dimers of thiamine or TMP between which the anions are held. Results are compared with those of the other thiamine-platinum complexes. (C) 2001 Elsevier Science B.V. All rights reserved.

NMR and UV-Vis study on phenyl-capped oligoaniline salts

Phenyl-capped oligoanilines in the oxidized state and their salts (by camphor sulfonic acid, CSA) were comparatively studied by UV-Vis and NMR spectroscopy. The UV-Vis spectra revealed a similar electron transfer behaviour and similar structure in the tetraaniline to those in polyaniline. Upon formation of the salt, H-1 NMR CH peaks of the oligomers showed large shifts to lower fields. The longer the molecule of a oligomer is, the more the shift, indicating that the charge brought into the N atoms by the proton was redistributed over the whole molecule. The CH and quaternary carbon peak-shifts support the electron cloud motion route H -->C -->C -->N -->H. This is in agreement with the four ring BQ derivatives model.

LB multilayers and superlattice films of erbium fatty acid salts

Multilayers of Y-type bilayers of pure and mixed erbium palmitate(EP), nonadecanate(Er) and behenate(EB) on CaF2 substrates were prepared by conventional Langmuir-Blodgett (LB) method. II is demonstrated that two systems composed of alternating bilayer of different fatty acid salts are unidimensional superlattices. These LB films were characterized by means of x-ray photoelectronic Spectrometry (XPS), FTIR and x-ray diffraction (XRD) measurements.

Preparation of Pb-Ca-Na master alloy using molten chloride salt electrolysis

An electrolysis technique for co-deposition of Ca2+ and Na+ at the liquid lead cathode was put forward. The experiment was carried out at an electrolysis temperature below 650 degrees C and had a current efficiency of 98%, which are respectively 100 similar to 300 degrees C lower and 15% similar to 30% higher than those reported both at home and abroad.

THE CATALYTIC ACTIVITY OF HETEROPOLY ACIDS (SALTS) AND MONO-LACUNARY HETEROPOLY TUNGSTOPHOSPHORIC COMPOUND IN THE OXIDATION OF ALCOHOLS

The catalytic activity of heteropoly compounds in the oxidation of benzyl alcohol and cyclohexa nol under phase transfer conditions has been studied. The catalytic activity of six kinds of heteropoly acids with Keggin structure will drop by the order of GeMo12 (H4GeMo12O40). PW12, PMo12, SiMo12, GeW12 and SiW12. When the three protons of H3PW12O40 Were replaced by Na+ step by step, the catalytic activity will raise gradually with the drop of acidity. The addition of base and trace amount of sulfuric acid to the reaction system resulted in an increase of catalytic activity. It was found that catalytic activity of mono-lacunary heteropoly compounds is higher than that of the primary heteropoly acids (or salts). The catalytic oxidation system of HPA-H2O2-PTC is very active in the oxidation of benzyl alcohol ana cyclohexanol, but it has little activity in the oxidation of inactive compounds such as n(or iso)-proplalcohol. n-butyl alcohol and n-hexanol. Solvent has great effect on reaction, when polar compounds such as water were used as solvent, the catalytic activity is better than that when non-polar compounds were used as solvent.

ELECTROCHEMICAL FORMATION OF NI-Y INTERMETALLIC COMPOUND LAYER IN MOLTEN CHLORIDE

The reduction of Y(III) ions in molten chloride is known to be a one-step three electron reaction [1, 2, 3], but a voltammogram of YCl3 in molten LiCl-KCl-NaCl at a nickel electrode shows at least two reduction peaks of Y(III) ions, indicating the possibility of formation of Ni-Y intermetallic compounds. Using a galvanostatic electrolysis method, samples were prepared at several current densities at 450, 500, 600 and 700-degrees-C, respectively, and were identified with X-ray diffraction (XRD) and electron probe microanalysis (EPMA) methods. The results show that Ni2Y, Ni2Y3 and NiY can be produced by electrolysis and Ni2Y is found to be the predominant Ni-Y intermetallic compound under the experimental conditions. Nickel appears to diffuse in Ni2Y faster than yttrium, and the diffusion process is the rate determining step during Ni2Y formation.