Effect of thermal cycling on microleakage between hard chairside relines and denture base acrylic resins

Objectives:Microleakage is a pre-stage of debonding between hard chairside relines and denture base acrylic resins. Therefore, it is important to assess them with regard to the longevity of the relined denture. This study investigated the effect of thermal cycling on the microleakage at the interface of three hard chairside reline resins and three denture base resins.Material and methods:Rectangular bars (12 mm x 3 mm x 3 mm) of Lucitone 550, Acron MC and QC 20 were made and relined with Kooliner, Tokuyama Rebase Fast II and Ufi Gel Hard, Lucitone 550, Acron MC and QC 20 resins. Specimens were divided into one control and two test groups (n = 10). In specimens of the control group, the microleakage was performed after the reline procedure. In Test Group 1, the specimens were stored for 24 h in distilled water at room temperature and in Test Group 2; the specimens were thermal cycled from 5 to 55 degrees C for 5000 cycles with a 30-s dwell time. Subsequently, all specimens were immersed in 50% silver nitrate solutions for 24 h. All specimens were sectioned longitudinally into three fractions and the lateral sections were examined (n = 20). Silver nitrate stain penetration was examined under a stereoscopic lens with x30 magnification, and the images were captured. Leica Qwin image analysis software was used to determine microleakage at the interface of the materials. Data were analysed using the Kruskal-Wallis test at a 95% level of significance.Results:For all cycles, there were no statistically significant differences between thermal cycled and non-thermal cycled groups (p > 0.05).Conclusion:It can be concluded that thermal cycling had no effect on the microleakage.

Effects of thickness coating on the electrochemical behaviour of thermal spray Cr3C2-NiCr coatings

Thermally sprayed HVOF coatings are increasingly being used in industrial applications where high wear and corrosion resistance are needed [1,2]. In this paper, electrochemical ac and de experiments were used in order to obtain the corrosion resistance of coated steel with different numbers of Cr3C2-NiCr layers. This work has been performed in order to determine the role of coating thickness in the corrosion behaviour of a steel protected with cermet thermally sprayed coatings. It is known that a thicker layer protects better against corrosion when a metallic coating is evaluated. But cermet coatings, such as Cr3C2-NiCr, contain higher levels of porosity and residual stresses than metallic coatings, which really could influence the corrosion resistance of the deposited layer. Electrochemical measurements, such as Open-Circuit Potential (E-Osubset of), Polarisation Resistance (RP) and Cyclic Voltammetry (CV), were performed in an aerated 3.4 NaCI media (%wt.). Electrochemical Impedance Measurements (EIS) were also done in order to obtain a mechanism that explains the corrosion process. Structural Characterisation was carried out by means of Optical and Scanning Electron Microscopes (OM, SEM) with an Energy Dispersive Spectrometry analyser (EDS). Results show that the corrosion resistance of the complete system is mainly influenced by the substrate behaviour. The application of a higher number of deposited layers did not substantially increase their anticorrosive properties. Stress generation during the spraying deposition process plays an important role in the behaviour of the coated steel against corrosion phenomena. (C) 2002 Elsevier B.V. B.V All rights reserved.

Simultaneous Determination of Cadmium and Lead in Medicinal Plants Using Graphite Furnace Atomic Absorption Spectrometry and Direct Slurry Sampling

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Simultaneous and Direct Determination of As, Bi, Pb, Sb, and Se and Co, Cr, Cu, Fe, and Mn in Milk by Electrothermal Atomic Absorption Spectrometry

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Synthesis and thermal study of the barium complexes with 8-hydroxyquinolinate derivatives

In this present work, barium ion was reacted with different ligands which are 5,7-dibromo, 5,7-dichloro, 7-iodo and 5-chloro-7-iodo-8-hydroxyquinoline, in acetone/ammonium hydroxide medium under constant stirring and the obtained compounds were as follows: (I) Ba[(C9H4ONBr2)(2)].1.5H(2)O; (II) Ba[(C9H4ONCl2)(OH)]. 1H(2)O; (III) Ba[(C9H5ONI)(2)]. 1H(2)O and (IV) Ba[(C9H4ONICl)(2)]. 5H(2)O, respectively. The compounds were characterized by elemental analysis, infrared absorption spectrum (IR), inductively coupled plasma spectrometry (ICP), simultaneous thermogravimetry-differential thermal analysis (TG-DTA) and differential scanning calorimeter (DSC).The final residue of the thermal decomposition was characterized as orthorhombic BaBr2 from (I); the intermediate residue, as a mixture of orthorhombic BaCO3 and BaCl2 and cubic BaO and the final residue, as a mixture of cubic and tetragonal BaO and orthorhombic BaCl2 (II); the intermediate residue, as orthorhombic BaCO3 and as a final residue, a mixture of cubic and tetragonal BaO from (III); and the intermediate residue, as a mixture of orthorhombic BaCO3 and BaCl2 and as a final residue, a mixture of cubic and tetragonal BaO and orthorhombic BaCl2 from (IV).

Evaluation of Ir, Ru, and W as permanent modifiers for the simultaneous determination of As, Bi, Pb, Sb, and Se in natural water by electrothermal atomic absorption spectrometry

Iridium-, Ru-, and W-coated platforms were prepared by thermal treatment of the transversely heated graphite atomizer and investigated for the simultaneous determination of As, Bi, Pb, Sb, and Se in tap water by electrothermal atomic absorption spectrometry. The maximum pyrolysis temperature for As and Bi increased in a modifier sequence W < Ru < Ir. For Pb, Sb, and Se, this sequence was W < Ru, It. Calculated characteristic masses in the presence of It, Ru, and W were 35, 33, and 35 pg for As; 63, 51, and 52 pg for Bi; 50, 32, and 34 pg for Pb; 40, 35, and 31 pg for Sb; and 39, 39, and 93 pg for Se, respectively. Ruthenium was elected as the optimum modifier.Repeatability of the measurements was typically < 6%. Recoveries of As, Bi, Pb, Sb, and Se added to tap water samples varied from 79 to 109%. Accuracy was also checked by analysis of five certified reference materials (CRMs) from the National Institute of Standards and Technology (NIST1640 - Trace Elements in Natural Water; NIST 1643d Trace Elements in Water) and High Purity Standards (Trace Metals in Drinking Water Standards, lots #812708, #591107, and #710710). A paired t-test showed that the results for the CRMs were in agreement at the 95% confidence level with the certified values. The graphite tube lifetime was about 650 firings. multi-element determination is particularly challenging due to the necessity of carefully optimizing compromise conditions.Based on the considerations listed above, the aim of this paper was to evaluate the behavior of Ir, Ru, and W as permanent modifiers for the simultaneous determination of As, Bi, Pb, Sb, and Se. The performance of the proposed procedure was also verified after the ETAAS analysis of tap waters and reference materials.

Simultaneous determination of cadmium and lead in wine by electrothermal atomic absorption spectrometry

A method has been developed for the direct simultaneous determination of Cd and Pb in white and red wine by electrothermal atomic absorption spectrometry (ET-AAS) using a transversely heated graphite tube atomizer (THGA) with longitudinal Zeeman-effect background correction. The thermal behavior of both analytes during pyrolysis and atomization stages were investigated in 0.028 mol l(-1) HNO3 and in 1 + 1 v/v diluted wine using mixtures of Pd(NO3)(2) + Mg(NO3)(2) and NH4H2PO4 + Mg(NO3)(2) as chemical modifiers. With 5 mug Pd + 3 mug Mg as the modifiers and a two-step pyrolysis (10 s at 400 degreesC and 10 s at 600 degreesC), the formation of carbonaceous residues inside the atomizer was avoided. For 20 mul of sample (wine + 0.056 mol l(-1) HNO3, 1 + 1, v/v) dispensed into the graphite tube, analytical curves in the 0.10-1.0 mug l(-1) Cd and 5.0-50 mug l(-1) Pb ranges were established. The characteristic mass was approximately 0.6 pg for Cd and 33 pg for Pb, and the lifetime of the tube was approximately 400 firings. The limits of detection (LOD) based on integrated absorbance (0.03 mug l(-1) for Cd, 0.8 mug l(-1) for Pb) exceeded the requirements of Brazilian Food Regulations (decree #55871 from Health Department), which establish the maximum permissible level for Cd at 200 mug l(-1) and for Pb at 500 mug l(-1). The relative standard deviations (n = 12) were typically < 8% for Cd and < 6% for Pb. The recoveries of Cd and Pb added to wine samples varied from 88 to 107% and 93 to 103%, respectively. The accuracy of the direct determination of Cd and Ph was checked for 10 table wines by comparing the results with those obtained for digested wine using single-element ET-AAS, which were in agreement at the 95% confidence level. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Thermal behavior of the Ti(IV), Zr(IV) and Pb(II) complexes with 5-nitro-8-hydroxyquinoline

Ti(IV), Zr(IV) and Pb(II) complexes with 5-nitro-8-hydroxyquinoline (5-NQ) were obtained by precipitation in acetone/ammonium solution medium. The compounds TiO(C9H5N2O3)(2).0.5H(2)O, ZrO(C9H5N2O3)(2)2H(2)O and Pb(C9H5N2O3)(2) were characterized by Elemental Analysis, X-ray Diffratometry and Infrared Absorption Spectrometry and their thermal behavior followed by TG/DTA. This present study intends to show the variations in the thermal behavior of the compounds and in the composition and/or structure of final oxide residues, in different atmospheres and heating rates.

Synthesis, characterization and thermal behaviour of solid-state compounds of folates with some bivalent transition metals ions

Solid-state M-L compounds, where M stands for bivalent Mn, Co, Ni, Cu and Zn and L is folate (C19H17N7O6), have been synthesized. Simultaneous thermogravimetry and differential scanning calorimetry (TG-DSC), X-ray powder diffractometry, infrared spectroscopy (FTIR), TG-DSC coupled to FTIR, elemental analysis and high-resolution continuum source flame atomic absorption spectrometry technique (HR-CS FAAS) were used to characterize and to study the thermal behaviour of these compounds. The results provided information concerning the composition, dehydration, thermal stability and thermal decomposition. © 2013 Akadémiai Kiadó, Budapest, Hungary.

Study of the thermal resistance of alpha-phase aluminum oxide (alpha-Al2O3) films deposited on the paper substrate

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Home Cooking and Phenolics: Effect of Thermal Treatment and Addition of Extra Virgin Olive Oil on the Phenolic Profile of Tomato Sauces

Tomato products are a key component of the Mediterranean diet, which is strongly related to a reduced risk of cardiovascular events. The effect of cooking time (15, 30, 45, and 60 min) and the addition of extra virgin olive oil (5 and 10%) on the phenolic content of tomato sauces was monitored using liquid chromatography coupled to tandem mass spectrometry. Concentration of phenolics in the tomato sauces decreased during the cooking process, with the exception of caffeic acid and tyrosol. The main degradation observed was the oxidation of quercetin, since the hydroxy-function at the C-ring of this flavonoid is not blocked by a sugar moiety, unlike rutin. Higher levels of virgin olive oil in tomato sauce seemed to enhance the extraction of phenolic compounds from the tomato, leading to higher phenolic contents in the sauces. Thus, the food matrix containing the phenolic compounds plays a crucial role in determining their accessibility.

Direct determination of chromium in empty medicine capsules by tungsten coil atomic emission spectrometry

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

K-41(n, gamma)K-42 thermal and resonance integral cross section measurements

We measured the K-41 thermal neutron absorption and resonance integral cross sections after the irradiation of KNO3 samples near the core of the IEA-R1 IPEN pool-type research reactor. Bare and cadmium-covered targets were irradiated in pairs with Au-Al alloy flux-monitors. The residual activities were measured by gamma-ray spectroscopy with a HPGe detector, with special care to avoid the K-42 decay beta(-) emission effects on the spectra. The gamma-ray self-absorption was corrected with the help of MCNP simulations. We applied the Westcott formalism in the average neutron flux determination and calculated the depression coefficients for thermal and epithermal neutrons due to the sample thickness with analytical approximations. We obtained 1.57(4) and 1.02(4) b, for thermal and resonance integral cross sections, respectively, with correlation coefficient equal to 0.39.

Vapor phase composition as an indicator of thermal stability of the Sm, Eu, and Yb chlorides

The Sm, Eu, and Yb tri- and dichlorides were investigated by Knudsen effusion mass spectrometry. It was found out by the analysis of mass spectra and ionization efficiency curves that the vapor composition is complex due to the partial high temperature decomposition/disproportionation of the samples. Up to five vapor species were identified for both LnCl3 (LnCl3, LnCl2, Ln2Cl4, Ln2Cl5, and Ln2Cl6) and LnCl2 (LnCl3, LnCl2, LnCl, Ln, and Ln2Cl4). The quantitative evaluation of vapor composition was made. It indicates that the disproportionation of SmCl2 and EuCl2 is negligible in the temperature range studied whereas that of YbCl2 and the decomposition of SmCl3 and YbCl3 cannot be neglected.