Behaviour and design of crest-fixed profiled steel roof claddings under wind uplift

Profiled steel roof claddings in Australia are commonly made of very thin high tensile steel and are crest-fixed with screw fasteners. At present the design of these claddings is entirely based on testing. In order to improve the understanding of the behaviour of these claddings under wind uplift, and thus the design methods, a detailed investigation consisting of a finite element analysis and laboratory experiments was carried out on two-span roofing assemblies of three common roofing profiles. It was found that the failure of the roof cladding system was due to a local failure (dimpling of crests/pull-through) at the fasteners. This paper presents the details of the investigation, the results and then proposes a design method based on the strength of the screwed connections, for which testing of small-scale roofing models and/or using a simple design formula is recommended.

Effect of overload cycles on thin steel roof claddings during cyclonic winds

During an investigation on thin steel roof claddings under simulated cyclonic wind loading, it was found that trapezoidal roof claddings behaved quite differently to corrugated (arc and tangent type) roof claddings due to the presence of overload cycles. The overload cycles caused a reduction in fatigue life for corrugated roofing whereas the reverse occurred for trapezoidal roofing. This contrasting behavior of the two crest-fixed roof claddings was investigated using small scale roofing models instead of the commonly used large scale two-span roof claddings. It was found that overload cycles formed a weaker locally dimpled mechanism around the fastener holes of corrugated roofing and thus accelerated the fatigue-caused pull-through failure. In contrast, a stronger deformed shape was formed in trapezoidal roofing which delayed the pull-through failure. Both laboratory testing and finite element analysis of small scale models were used to study the contrasting behavior of roof claddings.

The modulus of elasticity of steel - is it 200 GPa?

In cold-formed steel construction, the use of a range of thin, high strength steels (0.35 mm thickness and 550 MPa yield stress) has increased significantly in recent times. A good knowledge of the basic mechanical properties of these steels is needed for a satisfactory use of them. In relation to the modulus of elasticity, the current practice is to assume it to be about 200 GPa for all steel grades. However, tensile tests of these steels have consistently shown that the modulus of elasticity varies with grade of steel and thickness. It was found that it increases to values as high as 240 GPa for smaller thicknesses and higher grades of steel. This paper discusses this topic, presents the tensile test results for a number of steel grades and thicknesses, and attempts to develop a relationship between modulus of elasticity, yield stress and thickness for the steel grades considered in this investigation.

Local plastic mechanisms in thin steel plates under in-plane compression

Thin-walled steel plates subjected to in-plane compression develop two types of local plastic mechanism, namely the roof-shaped mechanism and the so-called flip-disc mechanism, but the intriguing question of why two mechanisms should develop was not answered until recently. It was considered that the location of first yield point shifted from the centre of the plate to the midpoint of the longitudinal edge depending on the b/t ratio, imperfection level, and yield stress of steel, which then decided the type of mechanism. This paper has verified this hypothesis using analysis and laboratory experiments. An elastic analysis using Galerkin's method to solve Marguerre's equations was first used to determine the first yield point, based on which the local plastic mechanism/imperfection tolerance tables have been developed which give the type of mechanism as a function of b/t ratio, imperfection level and yield stress of steel. Laboratory experiments of thin-walled columns verified the imperfection tolerance tables and thus indirectly the hypothesis. Elastic and rigid-plastic curves were them used to predict the effect on the ultimate load due to the change of mechanism. A finite element analysis of selected cases also confirmed the results from simple analyses and experiments.

Pull-out strength of steel roof and wall cladding systems

When steel roof and wall cladding systems are subjected to wind uplift/suction forces, local pull-through/dimpling failures or pull-out failures occur prematurely at their screwed connections. During extreme wind events such as storms and hurricanes, these localized failures then lead to severe damage to buildings and their contents. An investigation was therefore carried out to study the failure that occurs when the screw fastener pulls out of the steel battens, purlins, or girts. Both two-span cladding tests and small-scale tests were conducted using a range of commonly used screw fasteners and steel battens, purlins, and girts. Experimental results showed that the current design formula may not be suitable unless a reduced capacity factor of 0.4 is used. Therefore, an improved design formula has been developed for pull-out failures in steel cladding systems. The formula takes into account thickness and ultimate tensile strength of steel, along with thread diameter and the pitch of screw fasteners, in order to model the pull-out behavior more accurately. This paper presents the details of this experimental investigation and its results.