Estudo Comparativo de Juntas Soldadas a TIG e Laser Empregando-se Ti com Pureza Comercial Utilizado em Prótese sobre Implantes

Welding in the dentistry has been used for great part of the specialized dentist-surgeons in the implants area to solve prosthesis supported by implant adaptation problems. The development of new equipments Laser and TIG allowed a larger use of these processes in the prosthesis production. In this work, it was studied welded joints made by Laser and TIG, using commercial purity titanium, cpTi, applied in prosthesis supported by implants. The weld characterizations were carried out by light microscopy, EDS_elementary mapping, microhardness and tensile test. Through metallographic characterization, the weld bead presented a martensitic microstructure in the Laser welding process, originated from shear provoked by deformations in the lattice. This caused structural changes of the transformed area, which determines a fine plate-like morphology. In the weld bead from TIG, besides presenting higher hardness, was observed formation of Widmansttaten structure, which is characteristic of a geometric model, resulted of new phase formation along of the crystallographic plans. The martensitic structure is more refined than Widmansttaten structure, due to the high-speed cooling (10(3)degrees C/s) imposed by the Laser process.

Luminescence in semi-crystalline zirconium titanate doped with lanthanum

This paper aims to describe the synthesis of the semi-crystalline and crystalline powder of lanthanum doped with zirconium titanate (65/35), LZT through Pechini method. The analysis done by Raman demonstrated that semi-crystalline phase at 550 degrees C and crystalline phase after 600 degrees C were formed. The XRD pattern shows the ZrTiO4 phase formation demonstrating that La substitutions into the lattice take place. The calcined powder at different temperatures shows a semi-crystalline phase presenting photoluminescence effect when processed at low temperatures. From 300 to 400 degrees C a broadband is observed at 563 nm and 568 nm, respectively. Defects creation such as: Zr3+ center dot Vo(center dot center dot) and Ti3+ - V-O(center dot center dot), Zr and Ti replaced by La with vacancy formation, impurities and imperfections contributed to the photoluminescence effect. However, the main emission is due to a reverse Ti4+ -> O2- or/and Zr4+ -> O2- transition that occur within a regular titanate or zirconate eight-fold coordination [BO8-delta], B = Zr4+, Ti4+. (c) 2006 Elsevier B.V. All rights reserved.

Characterization of bismuth titanate ceramics derived by mechanochemical synthesis

Bismuth titanate, Bi(4)Ti(3)O(12) (BIT) nanosized powders have been successfully synthesized via high energy mechanochemical activation. The phase formation of BIT, crystal structure, microstructure, crystallite size and specific surface area were followed by XRD, scanning electron microscopy (SEM) and the BET specific surface area measurements. The BIT milled 2 h shows the orthorhombic crystalline structure with small amount of amorphous phase. The microstructure of Bi(4)Ti(3)O(12) ceramics sintered at 1000 degrees C for 12h exhibit plate-like grain structure.

Sintering and characterization of PLZT (9/65/35)

PLZT(9/65/35) obtained by association between the Pechini method (ZT) and partial oxalate (PLZT) was prepared. The stoichiometric phase and monophasic (cubic) PLZT obtained by calcination did not occur after sintering. The sintering process, by using two stages, caused a liquid phase formation due to a PbO excess (5 and 10 wt%). Samples with high density (similar to 8 g/cm(3)) and optical transparency(similar to 12%) were obtained. However, an equilibrium between the excess of PbO of sample/atmosphere PbO leads to a segregated PbO phase on the boundaries of the microstructure. A diffusion of Zr, Ti and La ions from PLZT to PbO phase promoted a stoichiometric deviation of the matrix and modified the optical and dielectric characteristics. (C) 2000 Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.

Aging behaviour of 25Cr-17Mn high nitrogen duplex stainless steel

The precipitation behaviour of a nickel free stainless steel containing 25% chromium, 17% manganese and 0.54% nitrogen, with duplex ferritic-austenitic microstructure, was studied using several complementary techniques of microstructural analysis after aging heat treatments between 600 and 1 000 degrees C for periods of lime between 15 and 6 000 min. During aging heat treatments, ferrite was decomposed into sigma phase and austenite by a eutectoid reaction, like in the Fe-Cr-Ni duplex stainless steel. Chromium nitride precipitation occurred in austenite, which had a high nitrogen supersaturation. Some peculiar aspects were observed in this austenite during its phase transformations. Chromium nitride precipitation occurred discontinuously in a lamellar morphology, such as pearlite in carbon steels. This kind of precipitation is not an ordinary observation in duplex stainless steels and the high levels of nitrogen in austenite can induce this type of precipitation, which has not been previously reported in duplex stainless steels. After chromium nitride precipitation in austenite, it was also observed sigma phase formation near the cells or colonies of discontinuously precipitated chromium nitride. Sigma phase formation was made possible by the depletion of nitrogen in those regions. Time-temperature-transformation (precipitation) diagrams were determined.

Structural effects of Li and K additives on the columbite precursor and 0.9PMN-0.1PT powders

Single-phase perovskite 0.9Pb(Mg1/3Nb2/3)O-3-0.1PbTiO(3) (PMN-PT) powders were prepared by using a Ti-modified columbite precursor (MNT) obtained by the polymeric precursor method. The innovation consists in the preparation of Ti-modified columbite in order to react directly with a stoichiometric amount of PbO to obtain pyrochlore-free PMN-PT powders. It has been shown that titanium oxide forms a solid solution with columbite (MN) and does not affect the obtaining of a single-phase columbite precursor. Thus, a high amount of perovskite phase can be obtained by reaction with PbO at 800 degreesC for 2 h. Effects of K and Li additives on the structure of MNT and PMN-PT were studied. X-ray diffraction studies were carried out to verify the phase formation at each processing step and these data were used for structural refinement by the Rietveld method. Both K and Li additives increase the crystallinity of MNT powders, being this effect more intense for the Li-doped samples. For PMN-PT samples the additives cause an insignificant decrease in the amount of perovskite phase. The morphology of the PMN-PT powder depends on the type of the additive. (C) 2003 Elsevier B.V All rights reserved.

Synthesis and electrical characterization of tungsten doped Pb(Zr0.53Ti0.47)O-3 ceramics obtained from a hybrid process

Pure and W-doped PZT ceramics (PZT and PZTW) were prepared by a hybrid process consisting in the association of polymeric precursor and partial oxalate methods. The phase formation was investigated by simultaneous thermal analysis (TG/DSC) and X-ray diffraction (XRD). The effect of W doping PZT and their electrical properties was evaluated. Substitution of W by Ti leads to an increase of Curie temperature and broadening of dielectric constant. A typical hysteresis loop was observed at room temperature and the remnant polarization was increased with the content of W. (c) 2007 Elsevier B.V. All rights reserved.

Effect of niobia on the crystal structure and dielectric characteristics of Pb(Zr0.45Ti0.55)O-3 prepared from polymeric precursor

The influence of niobia addition on the phase formation and dielectric properties of Pb(Zr0.45Ti0.55)O-3 powder prepared from polymeric precursor was analyzed. The weight fraction and unit-cell volume of the tetragonal phase decreased, and the mass fraction of the rhombohedral phase increased, with increasing niobia concentration. The rhombohedral unit-cell volume increased up to 5 mol% of added Nb and then decreased. Small amounts of pyrochlore and tetragonal zirconia phases were observed in PZT powder with more than 10 mol% Nb. These results were interpreted as an indication that the Nb ion was substituted for the zirconium ion in the tetragonal phase. For sintered PZT samples at 1100 degrees C, no free-zirconia phase was observed. The dielectric constant increased with the niobia addition up to 5 mol% and decreased for higher concentrations. The Curie temperature decreased with niobia addition up to 10 mol% before the formation of pyrochlore phase. (C) 2000 Elsevier B.V. Ltd. All rights reserved.

Design, manufacturing, and testing of a Nb3Sn coil employing Ti alloy as structural material

We describe the design, manufacturing, and testing results of a Nb3Sn superconducting coil in which TiAIV alloys were used instead of stainless steel to reduce the magnetization contribution caused by the heat treatment for the A-15 Nb-3 Sn phase formation that affects the magnetic field homogeneity. Prior to the coil manufacturing several structural materials were studied and evaluated in terms of their mechanical and magnetic properties in as-worked, welded, and heat-treated conditions. The manufacturing process employed the wind-and-react technique followed by vacuum-pressure impregnation(VPI) at 1 MPa atm. The critical steps of the manufacturing process, besides the heat treatment and impregnation, are the wire splicing and joint manufacturing in which copper posts supported by Si3N4 ceramic were used. The coil was tested with and without a background NbTi coil and the results have shown performance exceeding the design quench current confirming the successful coil construction.

Influence of heat treatment on the optical properties of SnO2 : Sb thin films deposited by dip coating using aqueous solution

Antimony doped tin oxide thin films were deposited on glass by a chemical route derived from Pechini method. Particular emphasis was given to the microstructure of crystallized films. Crystalline phase formation was studied by grazing incident X-ray diffraction and by thermal analyses. Scanning electron microscopy was carried out for microstructure characterization, surface roughness was observed using scanning tunneling microscope and the optical transmittance measurements were performed in the wavelength range of 200-800 nm. (C) 2002 Kluwer Academic Publishers.

Effect of magnesium on the properties of LiNbO3 thin films prepared from polymeric precursors

The effect of magnesium addition on the phase formation, microstructure and electric and ferroelectric properties of LiNbO3 thin films prepared through polymeric precursors was analyzed. By X ray diffraction no secondary phase was observed with the increase of magnesium concentration. Comparing to pure LiNbO3, the addition of 0.5 and 1.0 mol% of Mg+2 increased of the dielectric constant, while 2.0 mol% decreased it. It was noticed that the increase in additive concentration decreases the ferroelectric remanent polarization and increases the coercive field.

Hot-pressed 9.5/65/35 PLZT prepared by the polymeric precursor method

A 9.5/65/35 PLZT ceramic with a Pb-0.905 La-0.095 (Zr-0.65 Ti-0.35)(0.976) O-3 + 35 w% PbO formula was prepared using the Pechini method for powder preparation and two-step sintering in an oxygen atmosphere. Thr first step consisted of sintering at 1200 degrees C for 4 h with slow heating and cooling rates. The second step consisted of hot pressing at 1200 degrees C for 3 h, with slow heating and cooling rates and pressing pressures of 20 MPa (initial pressure) and 40 MPa (at sintering temperature). Investigations were made of the powder phase formation and powder morphology, i.e. The structure of sintered and hot-pressed PLZT ceramics. SEM microstructural analyses were carried out on the sintering and hot-pressing processes. (C) 2000 Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.

Synthesis of nanocrystalline tetragonal zirconia by a polymeric organometallic method

A polymeric precursor method based on the Pechini process was successfully used to synthesize zirconia-12 mol% ceria ceramic powders, the influence of the main process variables (citric acid-ethylene glycol ratio, citric acid-total oxides ratio and calcination temperature) on phase formation and powder morphology (surface area and crystallite size) were investigated. The thermal decomposition behavior of the precursor is presented. X-ray diffraction (XRD) patterns of powders revealed a crystalline tetragonal zirconia single-phase, with crystallite diameter ranging from 6 to 15 nm. The BET surface areas were relatively high, reaching 95 m(2) g(-1) Nitrogen adsorption/desorption on the powders suggested that nonaggregated powders could be attained, depending on the synthesis conditions. Copyright (C) 1999 John Wiley & Sons, Ltd.

Seeding of PMN powders made by the Pechini method

The partial oxalate method, with the columbite route, associated with the Pechini method, was used to obtain a very fine ceramic powder at low temperature. Using this route it was possible to obtain a very reactive powder and to synthesize a lead magnesium niobate (PMN) powder with up to 100% of perovskite phase at a lower temperatures than the PbO melting point. The influence of the BaTiO3 and PbTiO3 seeds in the phase formation, along with time and temperature during the PMN calcination, was also investigated. The amount of 2% of BaTiO3 seeds promoted PMN powder formation with 100% of perovskite phase and a very narrow particle size distribution. (C) 2001 Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.

Effect of Ag concentration on the thermal behavior of the Cu-10 mass% Al and Cu-11 mass% Al alloys

In this work the effect of Ag concentration on the thermal behavior of the Cu-10 mass% Al and Cu-11 mass% Al alloys with additions of 4, 6, 8 and 10 mass% Ag was studied using differential scanning calorimetry (DSC), in situ X-ray diffractometry (XRD) and scanning electron microscopy (SEM). The results showed that for the Cu-10 mass% Al alloy Ag addition induce the beta'(1) phase formation and for the Cu-11 mass% Al alloy these additions increase the amount of martensite formed on quenching and decrease the stability range of this phase on heating.