Adsorption of frog foam nest proteins at the air-water interface

The surfactant properties of aqueous protein mixtures ( ranaspumins) from the foam nests of the tropical frog Physalaemus pustulosus have been investigated by surface tension, two-photon excitation. uorescence microscopy, specular neutron reflection, and related biophysical techniques. Ranaspumins lower the surface tension of water more rapidly and more effectively than standard globular proteins under similar conditions. Two- photon excitation. uorescence microscopy of nest foams treated with fluorescent marker ( anilinonaphthalene sulfonic acid) shows partitioning of hydrophobic proteins into the air-water interface and allows imaging of the foam structure. The surface excess of the adsorbed protein layers, determined from measurements of neutron reflection from the surface of water utilizing H2O/D2O mixtures, shows a persistent increase of surface excess and layer thickness with bulk concentration. At the highest concentration studied ( 0.5 mg ml(-1)), the adsorbed layer is characterized by three distinct regions: a protruding top layer of similar to20 Angstrom, a middle layer of similar to30 Angstrom, and a more diffuse submerged layer projecting some 25 Angstrom into bulk solution. This suggests a model involving self-assembly of protein aggregates at the air-water interface in which initial foam formation is facilitated by specific surfactant proteins in the mixture, further stabilized by subsequent aggregation and cross-linking into a multilayer surface complex.

A thermoreversible supramolecular polyurethane with excellent healing ability at 45 °C

We report the synthesis and characterization of a healable, elastomeric shape recovery supramolecular polyurethane whose properties result from self-complementary π−π stacking and hydrogen bonding interactions plus phase separation. ESEM analysis and photographic images have revealed that this material can heal at 45 °C in 15 min to recover the mechanical properties of the pristine material with healing efficiencies >99%. This supramolecular polyurethane is also able to recover an applied strain of 25% within 5 min of release of the load.

An adhesive elastomeric supramolecular polyurethane healable at body temperature

In this paper, we report the synthesis and healing ability of a non-cytotoxic supramolecular polyurethane network whose mechanical properties can be recovered efficiently (> 99%) at the temperature of the human body (37 ºC). Rheological analysis revealed an acceleration in the drop of the storage modulus above 37 ºC, on account of the dissociation of the supramolecular polyurethane network, and this decrease in viscosity enables the efficient recovery of the mechanical properties. Microscopic and mechanical characterisation has shown that this material is able to recover mechanical properties across a damage site with minimal contact required between the interfaces and also demonstrated that the mechanical properties improved when compared to other low temperature healing elastomers or gel-like materials. The supramolecular polyurethane was found to be non-toxic in a cytotoxicity assay carried out in human skin fibroblasts (cell viability > 94% and non-significantly different compared to the untreated control). This supramolecular network material also exhibited excellent adhesion to pig skin and could be healed completely in situ post damage indicating that biomedical applications could be targeted, such as artificial skin or wound dressings with supramolecular materials of this type.

Effect of temperature and strain rate on the compressive behaviour of supramolecular polyurethane

Supramolecular polyurethanes (SPUs) possess thermoresponsive and thermoreversible properties, and those characteristics are highly desirable in both bulk commodity and value-added applications such as adhesives, shape-memory materials, healable coatings and lightweight, impact-resistant structures (e.g. protection for mobile electronics). A better understanding of the mechanical properties, especially the rate and temperature sensitivity, of these materials are required to assess their suitability for different applications. In this paper, a newly developed SPU with tuneable thermal properties was studied, and the response of this SPU to compressive loading over strain rates from 10−3 to 104 s−1 was presented. Furthermore, the effect of temperature on the mechanical response was also demonstrated. The sample was tested using an Instron mechanical testing machine for quasi-static loading, a home-made hydraulic system for moderate rates and a traditional split Hopkinson pressure bars (SHPBs) for high strain rates. Results showed that the compression stress-strain behaviour was affected significantly by the thermoresponsive nature of SPU, but that, as expected for polymeric materials, the general trends of the temperature and the rate dependence mirror each other. However, this behaviour is more complicated than observed for many other polymeric materials, as a result of the richer range of transitions that influence the behaviour over the range of temperatures and strain rates tested.

A Graphite-Polyurethane Composite Electrode for the Analysis of Furosemide

A graphite-polyurethane composite electrode has been used for the determination of furosemide, a antihypertensive drug, in pharmaceutical samples by anodic oxidation. Cyclic voltammetry and electrochemical impedance spectroscopy were used to characterize the electrooxidation process at +1.0 V vs. SCE over a wide pH range, with the result that no adsorption of analyte or products occurs, unlike at other carbon-based electrode materials. Quantification was carried out using cyclic voltammetry, differential pulse voltammetry, and square-wave voltammetry. Linear ranges were determined (up to 21 mu mol L-1 with cyclic voltammetry) as well as limits of detection (0.15 mu mol L-1 by differential pulse voltammetry). Four different types of commercial samples were successfully analyzed. Recovery tests were performed which agreed with those obtained by spectrophotometric evaluation. The advantages of this electrode material for repetitive analyzes, due to the fact that no electrode surface renewal is needed owing to the lack of adsorption, are highlighted.

Effect of polyol excess on the electrical property of vegetable-polyurethane film

Freestanding castor oil-based polyurethane (PU) film was obtained using spin-coating method. The effect of polyol content was analysed by means of thermally stimulated depolarisation current and AC dielectric measurements techniques. Two relaxation peaks were observed in the temperature range of -40 to 60 degrees C for PU with different polyol contents. The presence of polyol excess provides a shift to lower temperature of the a relaxation and the decrease in the activation energy of the transition in this region might be attributed to the plasticising effect of the polyol. The peak at higher temperature is due to the Maxwell-Wagner-Sillars relaxation, which also shifts in the low temperature direction as the polyol content is increased.

Characterization of Polyurethane Resins by FTIR, TGA, and XRD

Fourier Transformed Infrared Spectroscopy, Thermogravimetric Analysis, and X-ray Diffractometry have been used to investigate the rigid, semi rigid, and soft polyurethane (PU) forms, which were developed by the Group of Analytic Chemistry and Technology of Polymers - USF - Sao Carlos. The -NCO/-OH ratios were 0.6, 0.5, and 0.3% for rigid, semi rigid, and soft PUs, respectively, showing that different ratios cause differences in thermal behaviors and crystalline structures of the synthesized PU resins. (C) 2009 Wiley Periodicals, Inc. J Appl Polym Sci 115: 263-268, 2010

Electrochemical Behavior of Verapamil at Graphite-Polyurethane Composite Electrodes: Determination of Release Profiles in Pharmaceutical Samples

A solid graphite-polyurethane composite electrode has been used to determine release profiles of verapamil, a calcium-channel blocker. The electro-oxidation process was characterized by cyclic voltammetry and electrochemical impedance spectroscopy and showed no adsorption of analyte or oxidation products, unlike at other carbon-based electrodes. Quantification gave linear ranges up to 40molL-1 with cyclic voltammetry and detection limits of 0.7molL-1 by differential pulse and square-wave voltammetry. Commercial product samples were successfully analyzed with results equal to those from spectrophotometry. Because no electrode surface renewal is needed, this electrode material has many advantages.

Compósito de poliuretano de mamona e vermiculita para isolação térmica

They are in this study the experimental results of the analysis of thermal performance of composite material made from a plant matrix of polyurethane derived from castor oil of kernel of mamona (COF) and loading of clay-mineral called vermiculite expanded. Bodies of evidence in the proportions in weight of 10%, 15% and 20% were made to determine the thermal properties: conductivity (k), diffusivity (ά) and heat capacity (C), for purposes of comparison, the measurements were also performed the properties of polyurethane of castor without charge and also the oil polyurethane (PU), both already used in thermal insulation. Plates of 0.25 meters of material analyzed were manufactured for use as insulation material in a chamber performance thermal coverage. Thermocouples were distributed on the surface of the cover, and inside the material inside the test chamber and this in turn was subjected to artificial heating, consisting of a bank of incandescent lamps of 3000 w. The results obtained with the composite materials were compared with data from similar tests conducted with the camera alone with: (a) of oil PU, (b) of COF (c) glass wool, (d ) of rock wool. The heat resistance tests were performed with these composites, obtaining temperature limits for use in the range of 100 º C to 130 º C. Based on the analysis of the results of performance and thermal properties, it was possible to conclude that the COF composites with load of expanded vermiculite present behavior very close to those exhibited by commercial insulation material

Composito de poliuretano de mamona e residuo industrial para isolacao termica e absorcao sonora

This work proposes the development of an innovative material made from a vegetable polyurethane matrix and load of industrial waste, from retread tires, for thermal insulation and environmental comfort. Experimental procedures are presented, as well as the results of the thermal and acoustic performance of this composite material, made from an expansive foam derived from the castor seed oil and fiber of scrap tires. The residue was treated superficially with sodium hydroxide, to eliminate contaminants, and characterized macroscopically and microscopically. Samples were produced with addition of residues at levels of 5%, 10%, 15% and 20% by weight, for determination of thermal properties: conductivity, heat capacity and thermal diffusivity, sound absortion index and density. The results were compared to commercially available thermal insulation and sound absorbing products. According to the analysis of results, it was concluded that the developed composite presents characteristics that qualify it as a thermal insulation with superior performance, compared to commercial available insulation, and sound absorption capacity greater than the castor oil polyurethane s, without addition of the residue

Desidratação de polpas de frutas pelo método foam-mat

This study aimed to investigate the foam mat drying process of pineapple and mango pulp, as well as to evaluate the final product quality. Initially, the selection of fruit and additives was conducted based on density and stability determinations of mango, seriguela, umbu and pineapple foams. After selecting pineapple and mango for further studies, the fruit pulps and fruit foams were characterized in regard to their physicochemical composition. The temperature (60oC or 70oC) and the foam thickness (4 and 11 mm) were evaluated in accordance to the obtained drying curves and after model adjustment. Mango and pineapple powders obtained at the best process conditions were characterized in regard to their physicochemical composition, solubility, reconstitution time. Yoghurts were prepared with the addition of pineapple and mango powders and they were evaluated for their sensory acceptance. Results show that the best drying rates were achieved by using 70o C and layers 4mm thick for both fruits. The Page model successfully fitted the drying experimental data and it can be used as a predictive model. Pineapple and mango powders showed acid pH, high soluble solids content, low water activity (approx. 0.25), lipids between 1.46% and 2.03%, protein around 2.00%, and ascorbic acid content of 17,73 mg/100g and 14.32 mg/100g, for mango and pineapple, respectively. It was observed higher ascorbic acid retention for pineapple and mango powders processed at 70o C, which would be explained by the lower drying time applied. The fruit powders exhibited high solubility and fast reconstitution in water. The sensory acceptance indexes for yoghurts with the addition of both fruit powders were higher than 70%, which reflect the satisfactory product acceptance

Surface modification of siloxane containing polyurethane polymer by dielectric barrier discharge at atmospheric pressure

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Polyurethane coating with thin polymer films produced by plasma polymerization of diglyme

Aqueous-based polyurethane dispersions have been widely utilized as lubricants in textile, shoes, automotive, biomaterial and many other industries because they are less aggressive to surrounding environment. In this work thin films with different thickness were deposited on biocompatible polyurethane by plasma polymerization process using diethylene glycol dimethyl ether (Diglyme) as monomer. Molecular structure of the films was analyzed by Fourier Transform Infrared spectroscopy. The spectra exhibited absorption bands of O-H (3500-3200cm(-1)), C-H (3000-2900cm(-1)), C=O (1730-1650cm(-1)), C-O and C-O-C bonds at 1200-1600cm(-1). The samples wettability was evaluated by measurements of contact angle using different liquids such as water, glycerol, poly-ethane and CMC. The polyurethane surface showed hydrophilic behavior after diglyme plasma-deposition with contact angle dropping from 85(0) to 22(0). Scanning Electron Microscopy revealed that diglyme films covered uniformly the polyurethane surfaces ensuring to it a biocompatible characteristic.

Cure Kinetic of Castor Oil-Based Polyurethane

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Dynamic mechanical properties for polyurethane elastomers applied in elastomeric mortar

Dynamic mechanical properties of a polyurethane (PU) elastomer and a mortar processed with the same elastomer (modified polytetramethylene ether glycol (PTMEG)) were studied. The results obtained showed that the liquid aromatic amine ETHACURE (R) 300, used as cure agent, can be used to substitute the aromatic amine MOCA (R), which is usually used as cure agent in high performance elastomers. The resulting mortar produced with ETHACURE (R) 300 presents similar dynamic-mechanical thermal properties when compared with MOCA (R). However, dynamic-mechanical thermal analysis studies showed that the mortar developed with ETHACURE (R) 300 presents some advantages such as the low values of tan d, indicating a good capacity of recovery of the strain after retreating an applied force. (c) 2012 Wiley Periodicals, Inc. J Appl Polym Sci, 2012