Gellan gum-hyaluronate spongy-like hydrogels promote angiogenesis in hindlimb ischemia

"Tissue engineering: part A", vol. 21, suppl. 1 (2015)

Highly robust hydrogels via a fast, simple and cytocompatible dual crosslinking-based process

A highly robust hydrogel device made from a single biopolymer formulation is reported. Owing to the presence of covalent and non-covalent crosslinks, these engineered systems were able to (i) sustain a compressive strength of ca. 20 MPa, (ii) quickly recover upon unloading, and (iii) encapsulate cells with high viability rates.

Highly robust chitosan hydrogels via a fast, simple and biocompatible dual crosslinking-based process

Load-bearing soft tissues such as cartilage, blood vessels and muscles are able to withstand a remarkable compressive stress of several MPa without fracturing. Interestingly, most of these structural tissues are mainly composed of water and in this regard, hydrogels, as highly hydrated 3D-crosslinked polymeric networks, constitute a promising class of materials to repair lesions on these tissues. Although several approaches can be employed to shape the mechanical properties of artificial hydrogels to mimic the ones found on biotissues, critical issues regarding, for instance, their biocompatibility and recoverability after loading are often neglected. Therefore, an innovative hydrogel device made only of chitosan (CHI) was developed for the repair of robust biological tissues. These systems were fabricated through a dual-crosslinking process, comprising a photo- and an ionic-crosslinking step. The obtained CHIbased hydrogels exhibited an outstanding compressive strength of ca. 20 MPa at 95% of strain, which is several orders of magnitude higher than those of the individual components and close to the ones found in native soft tissues. Additionally, both crosslinking processes occur rapidly and under physiological conditions, enabling cellsâ encapsulation as confirmed by high cell survival rates (ca. 80%). Furthermore, in contrast with conventional hydrogels, these networks quickly recover upon unloading and are able to keep their mechanical properties under physiological conditions as result of their non-swell nature.

Lentes de contacto e líquidos de manutenção: alterações na humectabilidade

Dissertação de mestrado em Optometria Avançada

Desenvolupament d'hidrogels superficials que contenen motius d'adhesió cel·lular

Projecte de recerca elaborat a partir d’una estada al Departament d’Enginyeria Química del Massachusetts Institute of Technology entre abril i octubre del 2006. S’ha dissenyat i sintetitzat uns nous films polimèrics, amb aplicacions en l’àmbit de l’enginyeria de teixits, utilitzant la tècnica anomenada iCVD (initiated Chemical Vapor Deposition), prèviament desenvolupada pel grup receptor. Es tracta d’uns hidrogels superficials de gruix controlable, que incorporen un monòmer fluorat, el qual s’havia estudiat extensament en el grup d’origen. Aquest monòmer es caracteritza per reaccionar molt fàcilment amb pèptids, de manera que aquests queden units covalentment a la superfície. Diferents estratègies pel desenvolupament d’aquests copolímers han estat avaluades, tant des del punt de vista purament sintètic com de la pròpia aplicació. Les condicions de polimerització han estat optimitzades i els hidrogels s’han caracteritzat químicament per tècniques espectroscòpiques (FTIR, XPS), i físicament per angle de contacte i el·lipsometria. D’aquesta manera, s’ha estudiat la capacitat dels hidrogels d’absorbir aigua i alhora augmentar el seu gruix, depenent de la quantitat d’agent reticulant introduït i de la incorporació del nou monòmer. A continuació, s’han optimitzat les condicions de reacció d’aquestes superfícies amb pèptids que incorporen una molècula fluorescent, la qual permet detectar fàcilment per microscòpia de fluorescència si la reacció ha tingut lloc. Una vegada la plataforma ha estat posada a punt, s’han iniciat assajos cel·lulars tant amb fibroblasts embriònics de ratolí com amb cèl·lules humanes umbilicals. Els resultats preliminars suggereixen una morfologia diferent de les cèl·lules segons si es cultiven sobre films modificats amb pèptids que promouen l’adhesió cel·lular o sobre les seves seqüències permutades no actives. Però, el més interessant és que també s’han observat certes diferències depenent si els films contenen el component hidrogel o no, fet que suggeriria un paper actiu d’aquests noves superfícies en el comportament cel·lular.

Altérations anatomopathologiques liées au traitement par cerclage des globes oculaires atteints de décollement de rétine [Histological changes related to scleral buckling for treatment of retinal detachment].

Treatment of retinal detachment frequently uses biocompatible materials to obtain scleral buckling. These materials are not devoid of consequences on surrounding tissues. In 3 eyes enucleated for failure of surgical treatment using scleral buckling materials, the changes prompted by episcleral implants could be observed. The sclera underwent both an inversion of its curvature and a reduction of its thickness under the material, as well as an encapsulation of the material was observed. While a silicone sponge was used in part to encircle one of these eyes, its capsular inner surface was regular and smooth. In contrast, hydrogel implants used in the three eyes showed a peripheral fragmentation prompting in two of them a typical foreign body giant cell granulomatous reaction. Changes in scleral curvature and scleral thinning were observed reflecting the consequences of the buckling procedure. The capsule formation occurred as it does for any nonabsorbable matérial implanted in tissues. Degradation and fragmentation of the hydrogel material suscitated a granuloma in response to fragments. These hydrogel specific changes should be recognized on microscopic examination of slides of either capsule or eyes previously in contact with this implanted material. They attested of the instability of hydrogel after implantation.

The in vivo performance of magnetic particle-loaded injectable, in situ gelling, carriers for the delivery of local hyperthermia.

We investigated the use of in situ implant formation that incorporates superparamagnetic iron oxide nanoparticles (SPIONs) as a form of minimally invasive treatment of cancer lesions by magnetically induced local hyperthermia. We developed injectable formulations that form gels entrapping magnetic particles into a tumor. We used SPIONs embedded in silica microparticles to favor syringeability and incorporated the highest proportion possible to allow large heating capacities. Hydrogel, single-solvent organogel and cosolvent (low-toxicity hydrophilic solvent) organogel formulations were injected into human cancer tumors xenografted in mice. The thermoreversible hydrogels (poloxamer, chitosan), which accommodated 20% w/v of the magnetic microparticles, proved to be inadequate. Alginate hydrogels, however, incorporated 10% w/v of the magnetic microparticles, and the external gelation led to strong implants localizing to the tumor periphery, whereas internal gelation failed in situ. The organogel formulations, which consisted of precipitating polymers dissolved in single organic solvents, displayed various microstructures. A 8% poly(ethylene-vinyl alcohol) in DMSO containing 40% w/v of magnetic microparticles formed the most suitable implants in terms of tumor casting and heat delivery. Importantly, it is of great clinical interest to develop cosolvent formulations with up to 20% w/v of magnetic microparticles that show reduced toxicity and centered tumor implantation.

Does locally delivered Zoledronate influence peri-implant bone formation? - Spatio-temporal monitoring of bone remodeling in vivo.

Bisphosphonates are known for their strong inhibitory effect on bone resorption. Their influence on bone formation however is less clear. In this study we investigated the spatio-temporal effect of locally delivered Zoledronate on peri-implant bone formation and resorption in an ovariectomized rat femoral model. A cross-linked hyaluronic acid hydrogel was loaded with the drug and applied bilaterally in predrilled holes before inserting polymer screws. Static and dynamic bone parameters were analyzed based on in vivo microCT scans performed first weekly and then biweekly. The results showed that the locally released Zoledronate boosted bone formation rate up to 100% during the first 17 days after implantation and reduced the bone resorption rate up to 1000% later on. This shift in bone remodeling resulted in an increase in bone volume fraction (BV/TV) by 300% close to the screw and 100% further away. The double effect on bone formation and resorption indicates a great potential of Zoledronate-loaded hydrogel for enhancement of peri-implant bone volume which is directly linked to improved implant fixation.

Combined Electrostatic and Covalent Polymer Networks for Cell Microencapsulation

Two types of hydrogel microspheres have been developed. Fast ionotropic gelation of sodium alginate (Na-alg) in the presence of calcium ions was combined with slow covalent cross-linking of poly(ethylene glycol) (PEG) derivatives. For the first type, the fast obtainable Ca-alg hydrogel served as spherical matrix for the simultaneously occurring covalent cross-linking of multi-arm PEG derivative. A two-component interpenetrating network was formed in one step upon extruding the mixture of the two polymers into the gelation bath. For the second type, heterobifunctional PEG was grafted onto Na-alg prior to gelation. Upon extrusion of the polymer solution into the gelation bath, fast Ca-alg formation ensured the spherical shape and was accompanied by cross-linker-free covalent cross-linking of the PEG side chains. Thus, one-component hydrogel microspheres resulted. We present the physical properties of the hydrogel microspheres and demonstrate the feasibility of cell microencapsulation for both types of polymer networks.

Photopolymerizable hydrogels for implants: Monte-Carlo modeling and experimental in vitro validation.

Photopolymerization is commonly used in a broad range of bioapplications, such as drug delivery, tissue engineering, and surgical implants, where liquid materials are injected and then hardened by means of illumination to create a solid polymer network. However, photopolymerization using a probe, e.g., needle guiding both the liquid and the curing illumination, has not been thoroughly investigated. We present a Monte Carlo model that takes into account the dynamic absorption and scattering parameters as well as solid-liquid boundaries of the photopolymer to yield the shape and volume of minimally invasively injected, photopolymerized hydrogels. In the first part of the article, our model is validated using a set of well-known poly(ethylene glycol) dimethacrylate hydrogels showing an excellent agreement between simulated and experimental volume-growth-rates. In the second part, in situ experimental results and simulations for photopolymerization in tissue cavities are presented. It was found that a cavity with a volume of 152  mm3 can be photopolymerized from the output of a 0.28-mm2 fiber by adding scattering lipid particles while only a volume of 38  mm3 (25%) was achieved without particles. The proposed model provides a simple and robust method to solve complex photopolymerization problems, where the dimension of the light source is much smaller than the volume of the photopolymerizable hydrogel.

Resistência mecânica de hidrogéis termo-sensíveis constituídos de Alginato-Ca2+ / PNIPAAm, tipo Semi-IPN

Thermosensitive hydrogels were synthesized using alginate-Ca2+ in association with a thermosensitive polymer, such as PNIPAAm. The mechanical properties of the hydrogels were determined measuring the maximum tension of deformation. With the increase of the temperature by 25 to 40 ºC above the LCST the chains of PNIPAAm collapsed, dragging the alginate net and diminishing the size of the pores. The decrease in the size of the pores of the hydrogel was followed by an increase in the mechanicals resistance of the material.

Application of ftir in the determination of acrylate content in poly(sodium acrylate-co-acrylamide) superabsorbent hydrogels

Hydrogels have been prepared by free-radical solution copolymerization of acrylamide and sodium acrylate (NaAc), with molar ratio ranging from 25/75 to 80/20, respectively, using methylene bisacrylamide as the crosslinking agent. A FTIR spectroscopy procedure to determine the acrylate/acrylamide ratio in these hydrogels was proposed based on absorbance at 1410 cm-1 (nCOO-) and 2940 cm-1 (nCH and nCH2). A straight line with a good linear correlation coefficient (0.998) was obtained by plotting the acrylate content (Ac%) versus relative absorbance (Arel = A1410/A2940). Results were confirmed by the amount of sodium cation released in acid medium determined by atomic absorption spectrometry.

Síntese e caracterização de hidrogéis compósitos a partir de copolímeros acrilamida-acrilato e caulim: efeito da constituição de diferentes caulins do nordeste brasileiro

Superabsorbent hydrogels based on poly (acrylamide-co-acrylate) and different kaolins, were prepared by free-radical aqueous copolymerization. FTIR and WAXS techniques were employed for characterization of a series of hydrogels, obtained by varying the percentage of clay, crosslinking and constitution of kaolin. The water absorbency at equilibrium (Weq) decreased with increasing clay content and the amount of crosslinking agent. Superabsorbent hydrogel (Weq > 1084 g H2O/g gel) was obtained as 10 wt% of white kaolin and 0.05 mol% of crosslinking agent were used. The hydrogel proved sensitive to pH variation and the presence of salts.

Hydrogels of cellulose acetate crosslinked with pyromellitic dianhydride: part I: synthesis and swelling kinetics

This work describes the synthesis of hydrogels of cellulose acetate (AC) crosslinked with 1,2,4,5-benzenotetracarboxylic dianhydride (PMDA). The crosslinking reaction was monitored by FTIR. Analysis of aromatic fragments from the alkaline hydrolysis of the gels by UV spectroscopy indicated that an increase in the stoichiometric ratio of dianhydride resulted in higher degrees of crosslinking. The non-porous nature of the gels was confirmed by analysis of nitrogen adsorption. Water absorption isotherms showed that as the temperature and degree of crosslinking increased, the percentage of water absorbed at equilibrium (%Seq) also increased. The hydrogels presented second order swelling kinetics.

Influência do pH nas propriedades físico-químicas, térmicas e mecânicas de filmes de poli(vinil álcool)/poli(ácido acrílico)/aciclovir

Drug-loaded films represent an alternative method for the treatment of skin lesions caused by Herpes simplex, since they facilitate delivery of the drug directly at the site of lesion. The objective of this work was to prepare PVA/PAA films containing AC at pH 2.0 and 4.0. The results show that the pH of the film preparations influences the polymer¾drug interaction kinetic order and the degree of swelling. The mechanism of release of AC from the films obtained at pH 4.0 was anomalous, whereas for the films prepared at pH 2.0 the release followed zero-order kinetics.