Cr^3＋，Yb^3＋，Er^3＋共掺磷酸盐铒玻璃转镜调Q激光性质研究

研究了Cr^3＋，Yb^3＋，Er^3＋共掺磷酸盐铒玻璃转镜调Q激光性质．三种Er2O3掺杂浓度的激光实验结果表明，在Er2O3名义掺杂浓度为0．5wt％时，玻璃的综合激光性质最好，重复频率为0．1Hz时，它的激光阈值功率为14．5mJ，最大输出能量为9．6mJ，斜率效率为0．55％．在同种实验条件下，比较了Cr14和Kigre公司生产的QE-7S激光性质参数，实验表明，前者激光阈值功率稍低，而后者的斜率效率和最大输出功率略高．

977nm抽运下掺铒碲酸盐基氧卤玻璃的光谱特性

研究了掺铒TeO2-ZnO-PbCl2碲酸盐基氧卤玻璃在977nm激光二极管抽运下的发光和上转换发光特性，结果发现除红外1．53μm^4I13.2→^4I15/2发光外(荧光半高宽高达69nm)，该玻璃还存在很强的^2H11/2→^4I15/2(527nm)，^4S3/2→^4I15/2(549nm)和^4R9/2→^4I15/2(666nm)可见上转换发光．应用Judd-Ofelt理论计算得到玻璃强度参数Ω1(t=2，4，6)分别为Ω2=5．87×10^20cm^2,Ω4=2．08×10^2-cm^2，

Near infrared broadband emission from bismuth-dysprosium codoped chalcohalide glasses

We investigate the broadband infrared emission of bismuth doped and bismuth/dysprosium codoped chalcohalide glasses. It is found that the bismuth/dysprosium codoping can drastically enhance the fluorescence as compared with either bismuth or dysprosium doped glasses. Meanwhile, the full width at half maximum of bismuth/dysprosium codoped glasses is over 170 nm, which is the largest value among all the reported rare-earth doped chalcohalide glasses. An ideal way for energy consumption between bismuth and dysprosium ions is supposed. Such improved gain spectra of both bismuth and dysprosium ions may have potential applications in developing broadband fibre amplifiers.

Structural role of fluoride in aluminophosphate sol-gel glasses: High-resolution double-resonance NMR studies

The local structure of Na-Al-P-O-F glasses, prepared by a novel sol-gel route, was extensively investigated by advanced solid-state NMR techniques. Al-21{F-19} rotational echo double resonance (REDOR) results indicate that the F incorporated into aluminophosphate glass is preferentially bonded to octahedral Al units and results in a significant increase in the concentration of six-coordinated aluminum. The extent of Al-F and Al-O-P connectivities are quantified consistently by analyzing Al-27{P-31} and Al-21{F-19} REDOR NMR data. Two distinct types of fluorine species were identified and characterized by various F-19{Al-27}, F-19{Na-23}, and F-19{P-31} double resonance experiments, which were able to support peak assignments to bridging (Al-F-Al, -140 ppm) and terminal (Al-F, -170 ppm) units. On the basis of the detailed quantitative dipole-dipole coupling information obtained, a comprehensive structural model for these glasses is presented, detailing the structural speciation as a function of composition.

X 射线转换屏用Tb3+激活磷酸盐发光玻璃

Phosphate glasses 60P2O5-15CS2O- 15Al2O3-10BaO were made by high temperature melt-annealing method. The absorption spectra, excitation spectra and emission spectra of Gd³⁺-Tb³⁺ and Ce3+-Gd³⁺-Tb³⁺ co-doped phosphate glass 60P2O5-15CS2O- 15Al2O3-10BaO were studied. The experimental results indicate that, the doping of Ce3+ and Gd³⁺ in Tb³⁺ phosphate glass has a good effect on the 545 nm emission of Tb³⁺ at UV excitation. The Ce3+-Gd³⁺-Tb³⁺ co-doped phosphate glass have a good x-ray luminescence at the radiation of x-ray with energy in 50-120 kev, and a high space resolution. The Ce3+-Gd³⁺-Tb³⁺ co-doped phosphate luminescence glass is a promising material for using in the digital radiography system in medical devices.

Broadband amplification and upconversion luminescence properties of Er3+/Yb3+ co-doped fluorophosphate glass

Broadband and upconversion properties were studied in Er3+/Yb3+ co-doped fluorophosphate glasses. Large Omega(6) and S-ed/(S-ed + S-md) values and the flat gain profile over 1530-1585 nm indicate the good broadband properties of the glass system. And a premise of using Omega(6) as a parameter to estimate the broadband properties of the glasses is proposed for the first time to our knowledge. Results showed that fluorescence intensity, upconversion luminescence intensity, the intensity ratio of red/green light (656 nm/545 nm) are closely related to the Yb3+:Er3+ ratio and Er3+ concentration, and the corresponding calculated lifetime of F-4(9/2) and S-4(3/2) states for red and green upconversion samples proves this conclusion. The upconversion mechanism is also discussed. (c) 2005 Elsevier Ltd. All rights reserved.

Investigation on nonradiative decay of the (Er3+I13/2)-I-4 -> I-4(15/2) transition in different tellurite glass matrix

Three kinds of Er3+-doped tellurite glasses with different hydroxyl groups are prepared by the conventional melt-quenching method. Infrared spectra are measured to estimate the exact content of OH- groups in samples. The maximum phonon energy in glasses are obtained by measuring the Raman scattering spectra. The strength parameters Omega(t) (t = 2, 4, 6) for all the samples are calculated and compared. The nonradiative decay rate of the Er3+ I-4(13/2) -> I-4(15/2) transition are calculated for the glass samples with different phonon energy and OH- group contents. Finally, the effect of OH- groups on fluorescence decay rate of Er3+ is analysed, the constant KOH-Er Of TWN, TZPL and TZL glasses are calculated to be 9.2 x 10(-19) cm(4)s(-1), 5.9 x 10(-19) cm(4)s(-1), and 3.5 x 10(-19) cm(4)s(-1), respectively.

Space-selective co-precipitation of silver and gold nanoparticles in femtosecond laser pulses irradiated Ag+, Au3+ co-doped silicate glass

We report on space-selective co-precipitation of silver and gold nanoparticles in Ag+, Au3+ co-doped silicate glasses by irradiation of femtosecond laser pulses and subsequent annealing at high temperatures. The color of the irradiated area in the glass sample changed from yellow to red with the increase of the annealing temperature. The effects of average laser power and annealing temperature on precipitation of the nanoparticles were investigated. A reasonable mechanism was proposed to explain the observed phenomena. (c) 2006 Elsevier Ltd. All rights reserved.

荧光俘获效应对掺铒氧化物玻璃光谱性质的影响

测试了不同掺杂浓度和样品厚度下掺铒磷酸盐和碲酸盐玻璃的吸收光谱、荧光光谱和荧光寿命，计算了Er^3＋离子在1．53μm处的吸收截面（σa）、发射截面（σe）、自发辐射跃迁概率（Arad）、辐射跃迁寿命（τrad）、以及辐射跃迁量子效率（η）等光谱参数．讨论了荧光俘获效应对掺铒磷酸盐和碲酸盐玻璃光谱性质及光谱参数的影响．结果表明即使在铒离子低掺杂浓度（0．1mol％Er2O3）下，荧光俘获效应也普遍存在于掺铒玻璃材料中，使得荧光寿命（τt）和荧光半高宽（FWHM）随样品的厚度和铒离子掺杂浓度增加而增大，导致

Effects of Yb ion concentration on the spectral properties of lead silica glasses

The spectral properties in different concentration of Yb ions (0.5-5 mol%)-doped silica glasses are explored in this paper. The glasses are prepared by traditional melting method. The absorption spectra and the fluorescent lifetime (tau(f)) are measured at room temperature and low temperature (18 K). The stimulated cross-section (sigma(emi)) and potential laser properties (beta(min), I-sat, I-min) are calculated based on the absorption spectra. The absorption cross-section (sigma(abs)) are in the range 1.08 x 10(-20) - 1.18 x 10(-20) cm(2) in different glasses, the fluorescence lifetime (tau(f)) change from 1.9 to 1.2 ms with the increase of Yb3+ concentration. The potential laser properties indicate that lead silica glass is a good host for highly Yb ion doping glass. (c) 2005 Elsevier B.V. All rights reserved.

Influence of TeO2, PbF2, ZnF2 on the spectroscopic and lasing properties of Yb3+ doped fluorophosphate glass

The influence of TeO2 on the crystallization stability, thermal stability, spectroscopic and lasing properties of Yb3+ doped fluorophosphate (FP) glass was studied. It is shown that 2 mol% TeO2 is the optimum doping amount which results in better spectroscopic and lasing properties as well as improve the crystallization and thermal stabilities of the glass. In order to enhance the physical and optical properties further, the effect of PbF2 and ZnF2 to the TeO2 contained FP glasses is also investigated, which shows that PbF2 has advantages in improving the crystallization properties while ZnF2 is preferable in enhancing spectroscopic and lasing properties. Results indicate that the co-existence of TeO2, PbF2 or ZnF2 is an effective way to enhance the spectroscopic, lasing and physical properties of Yb3+ doped FP glasses. (c) 2004 Published by Elsevier B.V.

Effect of PbO on precipitation of laser-induced gold nanoparticles inside silicate glasses

We report on three-dimensional precipitation of Au nanoparticles in gold ions-doped silicate glasses by a femtosecond laser irradiation and further annealing. Experimental results show that PbO addition plays the double roles of inhibiting hole-trapped centers generation and promoting formation and growth of gold nanoparticles. Additionally, glass containing PbO shows an increased non-linear absorption after femtosecond laser irradiation and annealing. The observed phenomena are significant for applications such as fabrications of three-dimensional multi-colored images inside transparent materials and three-dimensional optical memory, and integrated micro-optical switches. (c) 2007 Elsevier B.V. All rights reserved.

Spectroscopic properties of Nd3+-doped high silica glass prepared by sintering porous glass

A new kind of Nd3+, -doped high silica glass (SiO2 > 96% (mass fraction)) was obtained by sintering porous glass impregnated with Nd3+, ions. The absorption and luminescence properties of high silica glass doped with different Nd3+, concentrations were studied. The intensity parameters Omega(t) (t = 2, 4, 6), spontaneous emission probability, fluorescence lifetime, radiative quantum efficiency, fluorescence branching ratio, and stimulated emission cross section were calculated using the Judd-Ofelt theory. The optimal Nd3+ concentration in high silica glass was 0.27% (mole fraction) because of its high quantum efficiency and emission intensity. By comparing the spectroscopic parameters with other Nd3+ doped oxide glasses and commercial silicate glasses, the Nd3+-doped high silica glasses are likely to be a promising material used for high power and high repetition rate lasers.

Rare-earth-doped silica microchip laser fabricated by sintering nanoporous glass

We report a new method for fabricating rare-earth-doped silica glasses for laser materials obtained by sintering nanoporous silica glasses impregnated with rare-earth-doped ions. The fabricated materials have no residual pores and show good optical and mechanical properties. Good performance from a Nd3+-doped silica microchip laser operating at 1.064 mum is successfully demonstrated, suggesting that the fabricated silica glasses have potential for use as active materials for high-power solid-state lasers. (C) 2005 Optical Society of America.

Er3+-doped glass-polymer composite thin films fabricated using combinatorial pulsed laser deposition

Siloxane Polymer exhibits low loss in the 800-1500 nm range which varies between 0.01 and 0.66 dB cm1. It is for such low loss the material is one of the most promising candidates in the application of engineering passive and active optical devices [1, 2]. However, current polymer fabrication techniques do not provide a methodology which allows high structurally solubility of Er3+ ions in siloxane matrix. To address this problem, Yang et al.[3] demonstrated a channel waveguide amplifier with Nd 3+-complex doped polymer, whilst Wong and co-workers[4] employed Yb3+ and Er3+ co-doped polymer hosts for increasing the gain. In some recent research we demonstrated pulsed laser deposition of Er-doped tellurite glass thin films on siloxane polymer coated silica substrates[5]. Here an alternative methodology for multilayer polymer-glass composite thin films using Er3+ - Yb3+ co-doped phosphate modified tellurite (PT) glass and siloxane polymer is proposed by adopting combinatorial pulsed laser deposition (PLD). © 2011 IEEE.