THE EFFECT of DIFFERENT SURFACE TREATMENTS on THE SHEAR BOND STRENGTH of LUTING CEMENTS TO TITANIUM

Statement of problem. Although titanium presents attractive physical and mechanical properties, there is a need for improving the bond at the titanium/luting cement interface for the longevity of metal ceramic restorations.Purpose. The purpose of this study was to evaluate the effect of surface treatments on the shear bond strength (SBS) of resin-modified glass ionomer and resin cements to commercially pure titanium (CP Ti).Material and methods. Two hundred and forty CP Ti cast disks (9.0 x 3.0 mm) were divided into 8 surface treatment groups (n=30): 1) 50 mu m Al2O3 particles; 2) 120 mu m Al2O3 particles; 3) 250 mu m Al2O3 particles; 4) 50 mu m Al2O3 particles + silane (RelyX Ceramic Primer); 5) 120 mu m Al2O3 particles + silane; 6) 250 mu m Al2O3 particles + silane; 7) 30 mu m silica-modified Al2O3 particles (Cojet Sand) + silane; and 8) 120 mu m Al2O3 particles, followed by 110 mu m silica-modified Al2O3 particles (Rocatec). The luting cements 1) RelyX Luting 2; 2) RelyX ARC; or 3) RelyX U100 were applied to the treated CP Ti surfaces (n=10). Shear bond strength (SBS) was tested after thermal cycling (5000 cycles, 5 degrees C to 55 degrees C). Data were analyzed by 2-way analysis of variance (ANOVA) and the Tukey HSD post hoc test (alpha=.05). Failure mode was determined with a stereomicroscope (x20).Results. The surface treatments, cements, and their interaction significantly affected the SBS (P<.001). RelyX Luting 2 and RelyX U100 exhibited similar behavior for all surface treatments. For both cements, only the group abraded with 50 mu m Al2O3 particles had lower SBS than the other groups (P<.05). For RelyX ARC, regardless of silane application, abrasion with 50 mu m Al2O3 particles resulted in significantly lower SBS than abrasion with 120 mu m and 250 mu m particles, which exhibited statistically similar SBS values to each other. Rocatec + silane promoted the highest SBS for RelyX ARC. RelyX U100 presented the highest SBS mean values (P<.001). All groups showed a predominance of adhesive failure mode.Conclusions. The adhesive capability of RelyX Luting 2 and RelyX U100 on the SBS was decisive, while for RelyX ARC, mechanical and chemical factors were more influential. (J Prosthet Dent 2012;108:370-376)

Influence of Er,Cr: YSGG laser on bond strength of self-adhesive resin cement

The purpose of this study was to investigate the bond strength of fiber post previously laser treated root canals. Forty single-rooted bovine teeth were endodontically treated, randomly and equally divided into two main groups according to the type of pretreatment: G1: 2.5% NaOCl (control group); and G2: Er,Cr:YSGG laser. Each group was further subdivided into 2 groups based on the category of adhesive systems/ luting materials used: a: an etch-and-rinse resin cement (Single Bond/RelyX ARC; 3M ESPE), and b: a self-adhesive resin cement (Rely X Unicem; 3M ESPE). Three 1.5 mm thick slabs were obtained per root and the push-out test was performed at a crosshead speed of 0.5 mm/min until post dislodgement occurred. Data were analyzed by ANOVA and post-hoc Tukey's test at a pre-set alpha of 0.05. Analysis of variance showed no statistically significant difference (p > 0.05) among the groups G1a (25.44 ± 2.35) and G1b (23.62 ± 3.48), G2a (11.77 ± 2.67) and G2b (9.93 ± 3.37). Fractures were observed at the interface between the dentin and the resin in all groups. The Er,Cr:YSGG laser irradiation did not influence on the bond strength of the resin cements and the etch-and-rinse resin cement had better results on bond strength than self-adhesive resin cement.

Bond strength of different endodontic sealers to dentin: push-out test

Objective: The aim of this in vitro study was to evaluate the bond strength of different root canal sealers to dentin. Material and Methods: Forty extracted single-rooted human teeth were examined and the coronal and middle thirds of the canals were prepared with a 1.50 mm post drill (FibreKor Post System, Pentron). The teeth were allocated in two experimental groups, irrigated with 2.5% NaOCl+17% EDTA or saline solution (control group) and instrumented using Race rotary files (FKG) to a size #40 at the working length. Then, the groups were divided into four subgroups and filled with Epiphany sealer (Group 1), EndoREZ (Group 2), AH26 (Group 3) and Grossman's Sealer (Group 4). After 2 weeks of storage in 100% humidity at 37 degrees C, all teeth were sectioned transversally into 2-mm-thick discs. Push-out tests were performed at a cross-head speed of 1 mm/min using a universal testing machine. The maximum load at failure was recorded and expressed in MPa. Results: Means (+/- SD) in root canals irrigated with 2.5% NaOCl and 17% EDTA were: G1 (21.6 +/- 6.0), G2 (15.2 +/- 3.7), G3 (14.6 +/- 4.5) and G4 (11.7 +/- 4.1). Two-way ANOVA and Tukey's test showed the highest bond strength for the Epiphany's group (p < 0.01) when compared to the other tested sealers. Saline solution decreased the values of bond-strength (p < 0.05) for all sealers. Conclusion: Epiphany sealer presented higher bond strength values to dentin in both irrigating protocols, and the use of 2.5% NaOCl and 17% EDTA increased the bond strength values for all sealers.

Shear bond strength of repairs in porcelain conditioned with laser

The aim of this study was to evaluate the shear bond strength of repairs in porcelain conditioned with laser. Sixty porcelain discs were made and six groups were formed (n = 10): G1: conditioning with laser with potency 760 mW; G2: conditioning with laser with potency 760 mW and application of 37% phosphoric acid for 15 s; G3: conditioning with laser with potency 900 mW; G4: conditioning with laser with potency 900 mW and application of 37% phosphoric acid for 15 s; G5: application of 37% phosphoric acid for 15 s (group control) and G6: application of 10% hydrofluoric acid for 2 min. The composite resin was insert of incremental layers at the porcelain surface aided with a metal matrix, and photoactivation for 20 s each increment. The specimens were submitted to a thermal cycling by 1000 cycles of 30 s in each bath with temperature between 5 and 55 degrees C. After the thermal cycling, specimens were submitted to the shear bond strength. The results were evaluated statistically through analysis of variance and Tukey's tests with 5% significance. The averages and standard deviation founded were: G1, 11.25 (+/- 3.10); G2, 12.32 (+/- 2.65); G3, 14.02 (+/- 2.38); G4, 13.44 (+/- 2,07); G5, 9.91 (-/+ 2,18); G6, 12.74 (+/- 2.67). The results showed that the femtosecond laser produced a shear bond strength of repairs in porcelain equal to the hydrofluoric acid and significantly superior to the use of phosphoric acid. Microsc. Res. Tech., 2012. (C) 2012 Wiley Periodicals, Inc.

Factors affecting on bond strength of glass fiber post cemented with different resin cements to root canal

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

THE EFFECT of IMMEDIATE DENTIN SEALING on THE MARGINAL ADAPTATION and BOND STRENGTHS of TOTAL-ETCH and SELF-ETCH ADHESIVES

Statement of problem. Sealing ability and bond strengths of total-etch and self-etch dentin adhesives used for immediate dentin sealing have not been assessed and established.Purpose. The purpose of this study was to determine the effectiveness of immediate dentin sealing (IDS) using total-etch or self-etch dentin adhesives on microleakage and microtensile bond strength.Material and methods. Twenty recently extracted molars were selected, and standard MOD inlay preparations were made with the gingival margins located below the cemento-enamel unction. The teeth were assigned to 4 experimental groups (n=5) according to the indirect composite restoration cementation technique used: (1) immediate dentin sealing with Adper Single Bond (TEBI); (2) conventional adhesive cementation technique using Adper Single Bond (TEAI); (3) immediate dentin sealing using Adper Prompt L-Pop (SEBI); or (4) conventional adhesive cementation technique using Adper Prompt L-Pop (SEAI). The restored teeth were thermal cycled 1,000 times between 5 degrees and 55 degrees C and then immersed in 50% ammoniacal silver nitrate. Three specimens per restoration were evaluated for microleakage, according to predefined scores, and submitted to Friedman's test (alpha-.05). The specimens were then sectioned to obtain 0.8 +/- 0.2-mm-thick sticks (with n ranging from 32 to 57 specimens) and submitted to microtensile bond strength (mu TBS) testing. The obtained data were submitted to 2-way ANOVA test (alpha=.05).Results. None of the experimental groups demonstrated complete elimination of marginal microleakage. There were significant differences in microleakage of the tested adhesives (P>.001). IDS microleakage scores were similar to those obtained using the conventional cementation technique (CCT) for both adhesives. The highest mean bond strengths were obtained with TEBI (51.1 MPa), whereas SEAI showed the lowest mean bond strengths (1.7 MPa). IDS resulted in significantly higher bond strengths than CCT (P<.001).Conclusions. Total-etch and self-etch adhesives have a significant effect on IDS. IDS resulted in high bond strengths for both adhesives; however, the microleakage was similar to that obtained with CCT (J Prosthet Dent 2009;102:1-9)

Effect of temporary cements on the shear bond strength of luting cements

Objective: The purpose of this study was to evaluate, by shear bond strength (SBS) testing, the influence of different types of temporary cements on the final cementation using conventional and self-etching resin-based luting cements. Material and Methods: Forty human teeth divided in two halves were assigned to 8 groups (n=10): I and V (no temporary cementation); II and VI: Ca(OH)(2)-based cement; III and VII: zinc oxide (ZO)based cement; IV and VIII: ZO-eugenol (ZOE)-based cement. Final cementation was done with RelyX ARC cement (groups I to IV) and RelyX Unicem cement (groups V to VIII). Data were analyzed statistically by ANOVA and Tukey's test at 5% significance level. Results: Means were (MPa): I - 3.80 (+/- 1.481); II - 5.24 (+/- 2.297); III - 6.98 (+/- 1.885); IV - 6.54 (+/- 1.459); V - 5.22 (+/- 2.465); VI - 4.48 (+/- 1.705); VII - 6.29 (+/- 2.280); VIII - 2.47 (+/- 2.076). Comparison of the groups that had the same temporary cementation (Groups II and VI; III and VII; IV and VIII) showed statistically significant difference (p<0.001) only between Groups IV and VIII, in which ZOE-based cements were used. The use of either Ca(OH) 2 based (Groups II and VI) or ZO-based (Groups III and VII) cements showed no statistically significant difference (p>0.05) for the different luting cements (RelyX (TM) ARC and RelyX (TM) Unicem). The groups that had no temporary cementation (Groups I and V) did not differ significantly from each other either (p>0.05). Conclusion: When temporary cementation was done with ZO- or ZOE-based cements and final cementation was done with RelyX ARC, there was an increase in the SBS compared to the control. In the groups cemented with RelyX Unicem, however, the use of a ZOE-based temporary cement affected negatively the SBS of the luting agent used for final cementation.

Bond strength of Epiphany (TM) Sealer combined with different adhesive systems photo-activated with LED and QTH

The Epiphany (TM) Sealer is a new dual-curing resin-based sealer and has been introduced as an alternative to gutta-percha and traditional root canal sealers. The canal filling is claimed to create a seal with the dentinal tubules within the root canal system producing a 'monoblock' effect between the sealer and dentinal tubules. Therefore, considering the possibility to incorporate the others adhesive systems, it is important to study the bond strength of the resulting cement. Forty-eight root mandibular canines were sectioned 8-mm below CEJ. The dentine discs were prepared using a tapered diamond bur and irrigated with 1% NaOCl and 17% EDTA. Previous the application Epiphany (TM) Sealer, the Epiphany (TM) Primer, AdheSE, and One Up Bond F were applied to the root canal walls. The LED and QTH (Quartz Tungsten Halogen) were used to photo-activation during 45 s with power density of 400 and 720 mW/cm(2), respectively. The specimens were performed on a universal testing machine at a cross-head speed of 1 mm/min until bond failure occurred. The force was recorded and the debonding values were used to calculate Push-out bond strength. The analysis of variance (ANOVA) and Tukey's post-hoc tests showed significant statistical differences (P < 0.05) to Epiphany (TM) Sealer/Epiphany (TM) Primer/QTH and EpiphanyTM Sealer/AdheSE/QTH, which had the highest mean values of bond strength. The efficiency of resin-based filling materials are dependent the type of light curing unit used including the power density, the polymerization characteristics of these resin-based filling materials, depending on the primer/adhesive used.

Effect of Resin Cement System and Root Region on the Push-out Bond Strength of a Translucent Fiber Post

Objectives: This study evaluated the bond strength of luting systems for bonding glass fiber posts to root canal dentin. The hypothesis tested was that there are no differences in bond strength of glass fiber posts luted with different cement systems.Methods: Forty bovine incisors were randomly assigned to five different resin cement groups (n=8). After endodontic treatment and crown removal, translucent glass fiber posts were bonded into the root canal using five different luting protocols (self-cured cement and etch-and-rinse adhesive system; dual-cured cement and etch-and-rinse adhesive system; self-cured cement and self-etch adhesive system; dual-cured cement and self-etch adhesive system; and dual-cured self-adhesive cement). Push-out bond strength was evaluated at three different radicular levels: cervical, middle, and apical. The interface between resinous cement and the post was observed using a stereoscopic microscope.Results: Analysis of variance showed a statistically significant difference among the cements (p<0.05) and the root canal thirds (p<0.05). The self-adhesive resinous cement had lower values of retention.Conclusions: The resin cements used with etch-and-rinse and self-etch adhesive systems seem to be adequate for glass fiber post cementation.

Effect of Sodium Ascorbate and the Time Lapse before Cementation after Internal Bleaching on Bond Strength between Dentin and Ceramic

Purpose: To evaluate the effects of the elapsed time (ET) after nonvital bleaching (NVB) and sodium ascorbate application (10%) (SAA) on the shear bond strength of dentin to ceramic.Materials and Methods: Bovine incisors were selected, internally bleached (35% carbamide peroxide) for 9 days and submitted to the following treatments (n = 10): G1, G2, G3-luting after 1, 7, and 14 days; G4, G5, and G6-luting after SAA, 1, 7, and 14 days, respectively. G7 and G8 were not bleached: G7-luting 24 hours after access cavity sealing; G8-luting 24 hours after access cavity sealing after SAA. After NVB, the vestibular dentin was exposed and flattened. The SAA was applied to the dentin (G4, G5, G6, G8) for 10 minutes, and it was then washed and dried. The dentin was etched (37% phosphoric acid), and an adhesive system (Single Bond 2) was applied. Feldspathic ceramic discs (VM7; 4-mm diameter, 3-mm thick) were luted with a dual-resin agent (RelyX ARC, 3M ESPE Dental Products, St. Paul, MN). After 24 hours, specimens were submitted to shear test on a universal testing machine. The data (MPa) were submitted to ANOVA and Dunnet's test (5%).Results: The means (+/- SD) obtained were (MPa): G1 (14 +/- 4.5), G2 (14.6 +/- 3.1), G3 (14 +/- 3.7), G4 (15.5 +/- 4.6), G5 (19.87 +/- 4.5), G6 (16.5 +/- 3.7), G7 (22.8 +/- 6.2), and G8 (18.9 +/- 5.4). SAA had a significant effect on bond strength (p = 0.0054). The effect of ET was not significant (p = 0.1519). G5 and G6 presented higher values than the other bleached groups (p < 0.05) and similar to G7 and G8 (p > 0.05).Conclusions: After NVB, adhesive luting to dentin is recommended after 7 days if sodium ascorbate has been applied prior to dentin hybridization.

Shear bond strength of a ceramic to Co-Cr alloys

Statement of problem. Different combinations of Co-Cr alloys bonded to ceramic have been used in dentistry; however, the bond strength of ceramic to metal can vary because of different compositions of these alloys.Purpose. The purpose of this study was to evaluate the shear bond strength of a dental ceramic to 5 commercially available Co-Cr alloys.Material and methods. Five Co-Cr alloys (IPS d.SIGN 20, IPS d.SIGN 30, Remanium 2000, Heranium P, and Wirobond C) were tested and compared to a control group of an Au-Pd alloy (Olympia). Specimen disks, 5 mm high and 4 mm in diameter, were fabricated with the lost-wax technique. Sixty specimens were prepared using opaque and dentin ceramics (VITA Omega 900), veneered, 4 mm high and 4 mm in diameter, over the metal specimens (n = 10). The shear bond strength test was performed in a universal testing machine with a crosshead speed of 0.5 mm/min. After shear bond testing, fracture surfaces were evaluated in a stereomicroscope under x25 magnification. Ultimate shear bond strength (MPa) data were analyzed with 1-way ANOVA and the Tukey HSD test (alpha = .05).Results. The mean (SID) bond strengths (MPa) were: 61.4 (7.8) for Olympia; 94.0 (18.9) for IPS 20; 96.8 (10.2) for I PS 30; 75.1 (12.4) for Remanium; 71.2 (14.3) for Heranium P; and 63.2 (10.9) for Wirobond C. Mean bond strengths for IPS 20 and IPS 30 were not significantly different, but were significantly (P<.001) higher than mean bond strengths for the other 4 alloys, which were not significantly different from each other.Conclusions. Bond strength of a dental ceramic to a Co-Cr alloy is dependent on the alloy composition.

Effect of Cement Type, Relining Procedure, and Length of Cementation on Pull-out Bond Strength of Fiber Posts

Introduction: As opposed to the cementation metal posts, the cementation of fiber posts has several details that can significantly influence the success of post retention. This study evaluated the effect of the relining procedure, the cement type, and the luted length of the post on fiber posts retention. Methods: One hundred eighty bovine incisors were selected to assess post retention; after endodontic treatment, the canals were flared with diamonds burs. Post holes were prepared in lengths of 5, 7.5, and 10 mm; the fiber posts were relined with composite resin and luted with RelyX ARC, RelyX Unicem, or RelyX Luting 2. All cements are manufactured by 3M ESPE (St. Paul, MN). Samples were subjected to a pull-out bond strength test in a universal testing machine; the results (N) were submitted to a three-way analysis of variance and the Tukey post hoc test (alpha = 0.05). Results: The improvement of post retention occurred with the increase of the post length luted into the root canal; the relining procedure improved the pull-out bond strength. RelyX Unicem and RelyX ARC showed similar values of retention, both showing higher values than RelyX Luting 2. Conclusion: Post length, the reining procedure, and the cement type are all important factors for improving the retention of fiber posts. (J Endod 2010;36:1543-1546)

Does Adhesive Resin Application Contribute to Resin Bond Durability on Etched and Silanized Feldspathic Ceramic?