The effect of microwave annealing on the electrical characteristics of lanthanum doped bismuth titanate films obtained by the polymeric precursor method

Lanthanum doped bismuth titanate thin films (Bi3.25La0.75Ti3O12-BLT) were produced by the polymeric precursor method and crystallized in a domestic microwave oven and in conventional furnace. Using platinum coated silicon substrates configuration, ferroelectric properties of the films were determined with remanent polarization P-r and a coercive field E-c of 3.9 mu C/cm(2) and 70 kV/cm for the film annealed in the microwave oven and 20 mu C/cm(2) and 52 kV/cm for the film annealed in conventional furnace, respectively. The films annealed in conventional furnace exhibited excellent retention-free characteristics at low infant periods indicating that BLT thin films can be a promise material for use in nonvolatile memories. on the other hand, the pinning of domains wall causes a strong decay at low infant periods for the films annealed in the microwave furnace which makes undesireable the application for future FeRAMS memories. (c) 2005 Elsevier B.V. All rights reserved.

Physical properties of silicate glasses doped with SnO2

The presence of tin in the network of silicate glasses produces changes in several of their physico-chemical properties. Glasses with the composition (mol%) 22Na(2)O (.) 8CaO (.) 70SiO(2) containing up to 5 wt% of SnO2 were analyzed under several experimental techniques. Dilatometric measurements showed an increase of the glass transition temperature with increasing tin content, while the average thermal expansion coefficient is reduced. Vickers microhardness, density, and refractive index also increase with the tin content. Diffuse reflectance spectra in the infrared (DRIFT) showed that the presence of tin, even at low concentrations, is responsible for some structural changes since there is an increase of the bridging oxygen concentration. The doped glasses present a brown color and optical absorption spectra measurements are interpreted as being due to precipitation of tin in the form of colloidal particles during cooling of the melted glass. In the Na+ <-> K+ ion exchange process the presence of tin in the glass network hinders the diffusion of these ions. The diffusion coefficients of those ions were calculated by the Boltzmann-Matano technique, after concentration profiles obtained by EDS measurements. All results obtained present evidences that Sn4+ cation acts as a glass network former. (c) 2005 Elsevier B.V. All rights reserved.

Temperature dependence of electron properties of Sn doped In2O3 nanobelts

This paper reports on the measurements of transport properties of high crystalline quality Sn doped In2O3 nanobelts. The samples presented metallic conduction in a large range of temperatures; however, at low temperatures, the resistivity showed a slight increase and the current-voltage curves showed a tendency to saturate even in the low-voltage range. From these observations, we discuss some arguments on the possibility of low dimensional conducting channels as the main responsible for the conduction at low temperatures. Additionally, we present an alternative technique for production of low resistance ohmic contacts, which can be further used in devices' construction. (C) 2007 Elsevier B.V. All rights reserved.

Application of standard and modified Judd-Ofelt theories to thulium doped fluoroindate glass

Fluoroindate glasses of the following compositions: (40-x)InF3-20ZnF(2)-16BaF(2)-20SrF(2)-2GdF(3)-2NaF-xTmF(3) with x = 1,3 mol% were prepared in a dry box under an argon atmosphere. The absorption spectra at room temperature in the spectral range 350-2200 nm were obtained. The spectra obtained for each sample had similar absorption and only the amplitude of the different bands changed as the concentration of Tm3+. The experimental oscillator strengths were determined from the areas under the absorption bands. Using the standard and modified Judd-Ofelt theory, intensity parameters Ohm(lambda) (lambda = 2,4,6) and (lambda = 2,3,4,5,6), respectively for f-f transitions of Tm3+ ions as well as transition probabilities, branching ratios and radiative lifetimes for each band were determined. The results are compared with those of other glasses described in the literature. (C) 1999 Elsevier B.V. B.V. All rights reserved.

Local and nanoscopic structure of potassium triflate-doped siloxane-polyoxyethylene ormolytes

Siloxane-poly(oxyethylene) hybrids obtained by the sol-gel process and containing short polymer chain have been doped with potassium triflate (KCF3SO3). The local structure of these hybrids was investigated by X-ray absorption spectroscopy near the potassium K-edge. Small angle X-ray scattering was used to determine the structure at the nanometer scale. Results revealed that at low and medium potassium concentration (n = [O][K] >= 8, where n represents the molar ratio of ether-type oxygen atoms per alkaline cation) the cations interact mainly with the polymer chains, while at larger doping level (n < 8) the formation of a polyehter:KCF3SO3 Complex is observed. The nanoscopic structure of the hybrids is also affected by doping. By increasing the doping level, decreasing trends in the electronic density contrast between siloxane nanoparticles and polyether matrix and in the siloxane interparticle distance are observed. At high doping level the small angle X-ray scattering patterns are strongly modified, showing the disappearance of the correlation peak and the formation of a potassium-containing nanophase. (c) 2006 Elsevier B.V. All rights reserved.

Sol-gel Eu3+/Tm3+ doped transparent glass-ceramic waveguides

Eu3+ and Tm3+ doped lanthanum fluoride and lanthanum oxyfluoride are obtained from Eu3+, Tm3+ containing lanthanum fluoracetate solutions. The nature of the crystal phase obtained could be controlled by the temperature of heat treatment. Spectral characteristics of Eu3+ doped crystal phases were sufficiently different to allow utilization of Eu3+ as structural probes. Tm3+ emission at the technologically important spectral region of 1450nm could be observed for the fluoride and oxyfluoride crystal phases. The large bandwidth obtained (around 120nm) suggests potential applications in optical amplification. SiO2-LaF3-LaOF composite materials were also prepared. It is observed that for heat treatments above 800degreesC, fluorine loss, probably in the form of SiF4 hinder the observation of Tm3+ emission. Eu3+ spectroscopic characteristics clearly show the evolution of a fluoride like environment to an amorphous oxide one as the temperature of heat treatment increased. Thin films obtained by dip-coating on V-SiO2 substrates and treated at 300degreesC, 500degreesC and 800degreesC display guided modes in the visible and infrared regions. Optical characteristics (refractive index and films thickness) were obtained at 543.5, 632.8 and 1550nm. Attenuation as low as 1.8dB/cm was measured at 632.8nm. (C) 2004 Published by Elsevier B.V.

Effect of presence of an acid catalyst on structure and properties of iron-doped siloxane-polyoxyethylene nanocomposites prepared by sol-gel

In this work we investigate the effect of hydrochloric acid (HC) addition on the structure and thermal and magnetic properties of iron-doped siloxane-polyoxyethylene (POE) hybrids prepared by the sol-gel route. X-ray powder diffraction (XRD) and X-ray absorption near edge structure (XANES) results reveal the dominance of ferrihydrite nanoparticles and a mixture of this phase with FeCl4- species in the hybrid prepared without and with HCl, respectively. Thermal analysis reveals the existence of two crystalline polymeric phases in the hybrid prepared with HCl whereas hybrids prepared without HCl are amorphous. The 105 and 60 Angstrom sized ferrihydrite nanoparticles were detected by SAXS analysis of the composite prepared without and with HCl, respectively. The magnetic results suggest that in both samples antiferromagnetic nanoparticles coexist with small clusters/isolated ions. In the sample without HCl addition, larger particles dominate the magnetic behavior, while the opposite occurs for the sample prepared using HCl catalyst. (C) 2004 Elsevier B.V. All rights reserved.

Tin-doped indium oxide nanobelts grown by carbothermal reduction method

This communication discusses the formation of doped nanobelts produced by a simple route. Tin-doped indium oxide (ITO) nanobelts were obtained by a carbothermal reduction method. The nanostructures were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDX) and wavelength-dispersive X-ray spectroscopy (WDX). The results show that the nanobelts have a cubic structure, are single crystalline and doped with tin and grow in the [400] direction.

Er3+-doped germanate glasses for active waveguides prepared by Ag+/K+ <-> Na+ ion-exchange

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Active planar waveguides based on sol-gel Er3+-doped SiO2-ZrO2 for photonic applications: Morphological, structural and optical properties

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of the ytterbium concentration on the upconversion luminescence of Yb3+/Er3+ co-doped PbO-GeO2-Ga2O3 glasses

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Infrared-to-visible upconversion in Yb3+/Er3+ co-doped PbO-GeO2 glass with silver nanoparticles

Enhanced frequency upconversion (UC) emission was studied in Yb3+/Er3+ co-doped PbO-GeO2 glass containing silver nanoparticles (NPs). Optical excitation was achieved with a laser operating at 980 nm in resonance with the Yb3+ transition F-4(5/2)-> F-4(7/2). The intensity of the whole UC spectrum from 400 to 700 nm was intensified due to the influence of silver NPs. The green and red emissions were enhanced by more than 300%. Emission bands centered at 408 nm and 480 nm were also detected corresponding to the H-2(9/2)-> I-4(15/2) and F-4(7/2)-> I-4(15/2) transitions of Er3+ ion. An intensity enhancement of approximate to 150% due to the NPs was measured. For the first time the influence of silver NPs on the blue emission of Yb3+/Er3+ co-doped PbO-GeO2 glass is reported. The large enhancement in the whole UC spectrum is due to the increased local field in the Er3+ ions locations and the proximity between the luminescence wavelengths and the NPs surface plasmon resonance. (C) 2010 Elsevier B.V. All rights reserved.

Structural evolution of Eu-doped hydroxyapatite nanorods monitored by photoluminescence emission

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structural and Spectroscopic Properties of Luminescent Er3+-Doped SiO2-Ta2O5 Nanocomposites

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structural and dielectric relaxor properties of yttrium-doped Ba(Zr0.25Ti0.75)O-3 ceramics

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)