RADIATION-INDUCED CROSS-LINKING OF POLY(METHYL METHACRYLATE)-POLY(ETHYLENE OXIDE) BLEND

Radiation-induced crosslinking of poly(methyl methacrylate) (PMMA)-poly(methylene oxide) (PEO) blends was studied. It was found that PMMA in PMMA-PEO blend can be crosslinked in the range of certain doses (1 approximately 20 x 10(4) Gy) and composition (PMMA% = 30 approximately 70) under the absence of oxygen. Moreover, it was also found that the crosslinking degree of PMMA in the blend in which the content of PMMA is 70% is the largest. The crosslinking degree of PMMA in the blend is closely related with the polymer miscibility. The crosslinking degree of the blend prepared at 60-degrees-C is far higher than one at ambient temperature.

INVESTIGATION OF PHASE SEPARATION BEHAVIOR IN POLY (METHYL METHACRYLATE)/POLY (STYRENE-CO-ACRYLONITRILE) MIXTURES WITH PULSED NUCLEAR MAGNETIC RESONANCE

Thermally induced phase separation in the mixture of poly (methyl methacrylate) (PMMA) with poly(styrene-co-acrylonitite (SAN) has intern studied with pulsed nuclear magnetic resonance(NMR) in single spin-lattice retaxation time T-1 of the eornpatibl. mixture two T-1 corresponding to those of PM MA-rich and SAN-rich comairis. Meanwhile, both T-1 gradually changing with annealing time provides the direct evidence that the phase separation takes place with a decomposition mechanism. Diffusion coeffieient was to lac negative, indicating an uphal diffusion characteristics, The basic parameters governing its kinetics were estimated using NMR date which were in good agreement with those evaluated from time-resolved light scattering experiments for a 60/40(PMMA/SAN) mixture annealed at 180.0 degrees C.