Anomalous magnetic behavior of La0.6Sr0.4MnO3 nano-tubes constituted with 3-12 nm particles

Uniform La0.6Sr0.4MnO3 (LSMO) nanotubes of an average diameter 180 nm were synthesized by a modified sol-gel method employing nanochannel porous anodic alumina templates. The nanotubes were characterized chemically and structurally by XRD, SEM, EDX, and TEM. Postannealed (700 degrees C for 1 h hour) nanotubes were found to be polycrystalline from XRD and SAED studies. To get further insight into the nanotube structure, HRTEM studies were done, which revealed that obtained LSMO nanotubes were structurally constituted with nanoparticles of 3-12 nm size. These constituent nanoparticles were randomly aligned and self-knitted to build the nanotube wall. Investigation of magnetic properties at this structured nanoscale revealed remarkable irreversibility between the zero field cooling (ZFC) and field cooling (FC) magnetization curves accompanied with a peak in the ZFC curve indicating spin-glass-like behavior. Structural defects and compositional variations at surfaces and grain-boundaries of constituent nanoparticles might be responsible for this anomalous magnetic behavior.

Does aluminium bind to histidine? an NMR investigation of Amyloid beta 12 and Amyloid beta 16 fragments

Aluminium and zinc are known to be the major triggering agents for aggregation of amyloid peptides leading to plaque formation in Alzheimer's disease. While zinc binding to histidine in A (amyloid ) fragments has been implicated as responsible for aggregation, not much information is available on the interaction of aluminium with histidine. In the NMR study of the N-terminal A fragments, DAEFRHDSGYEV (A12) and DAEFRHDSGYEVHHQK (A16) presented here, the interactions of the fragments with aluminium have been investigated. Significant chemical shifts were observed for few residues near the C-terminus when aluminium chloride was titrated with A12 and A16 peptides. Surprisingly, it is nonhistidine residues which seem to be involved in aluminium binding. Based on NMR constrained structure obtained by molecular modelling, aluminium-binding pockets in A12 were around charged residues such as Asp, Glu. The results are discussed in terms of native structure propagation, and the relevance of histidine residues in the sequences for metal-binding interactions. We expect that the study of such short amyloid peptide fragments will not only provide clues for plaque formation in aggregated conditions but also facilitate design of potential drugs for these targets.

A nearly constant switching frequency current hysteresis controller with generalized parabolic boundaries using 12-sided polygonal voltage space vectors for IM drives

In this paper, a current hysteresis controller with parabolic boundaries for a 12-sided polygonal voltage space vector inverter fed induction motor (IM) drive is proposed. Parabolic boundaries with generalized vector selection logic, valid for all sectors and rotational direction, is used in the proposed controller. The current error space phasor boundary is obtained by first studying the drive scheme with space vector based PWM (SVPWM) controller. Four parabolas are used to approximate this current error space phasor boundary. The system is then run with space phasor based hysteresis PWM controller by limiting the current error space vector (CESV) within the parabolic boundary. The proposed controller has simple controller implementation, nearly constant switching frequency, extended modulation range and fast dynamic response with smooth transition to the over modulation region.

A Medium-Voltage Inverter-Fed IM Drive Using Multilevel 12-Sided Polygonal Vectors, With Nearly Constant Switching Frequency Current Hysteresis Controller

In this paper, a current error space vector (CESV)-based hysteresis current controller for a multilevel 12-sided voltage space vector-based inverter-fed induction motor (IM) drive is proposed. The proposed controller gives a nearly constant switching frequency operation throughout different speeds in the linear modulation region. It achieves the elimination of 6n +/- 1, n = odd harmonics from the phase voltages and currents in the entire modulation range, with an increase in the linear modulation range. It also exhibits fast dynamic behavior under different transient conditions and has a simple controller implementation. Nearly constant switching frequency is obtained by matching the steady-state CESV boundaries of the proposed controller with that of a constant switching frequency SVPWM-based drive. In the proposed controller, the CESV reference boundaries are computed online, using the switching dwell time and voltage error vector of each applied vector. These quantities are calculated from estimated sampled reference phase voltages. Vector change is decided by projecting the actual current error along the computed hysteresis space vector boundary of the presently applied vector. The estimated reference phase voltages are found from the stator current error ripple and the parameters of the IM.

Thermoelectric properties of Fe(0.2)Co(3.8)Sbi(12-x)Te(x) skutterudites

Skutterudites Fe(0.)2Co(3.8)Sb(12),Te-x (x = 0, 0.1, 0.2, 0.3, 0.4, 0.5, 0.6) were synthesized by induction melting at 1273 K, followed by annealing at 923 K for 144 h. X-ray powder diffraction and electron microprobe analysis confirmed the presence of the skutterudite phase as the main phase. The temperature-dependent transport properties were measured for all the samples from 300 to 818 K. A positive Seebeck coefficient (holes are majority carriers) was obtained in Fe0.2Co3.8Sb 12 in the whole temperature range. Thermally excited carriers changed from n-type to p-type in Fe(0.)2Co(3.8)Sb(12),Te-x 19Te0.1 at 570 K, while in all the other samples, Fe(0.)2Co(3.8)Sb(12),Te-x (x = 0.2, 0.3, 0.4, 0.5, 0.6) exhibited negative Seebeck coefficients in the entire temperature range measured. Whereas for the alloys up to x = 0.2 (Fe(0.)2Co(3.8)Sb(12),Te-x ) the electrical resistivity decreased by charge compensation, it increased for x> 0.2 with an increase in Te content as a result of an increase in the electron concentration. The thermal conductivity decreased with Te substitution owing to carrier phonon scattering and point defect scattering. The maximum dimensionless thermoelectric figure of merit, ZT = 1.04 at 818 K, was obtained with an optimized Te content for Fe0.2Co3.8Sb1 1.5Te0.5 and a carrier concentration of,,J1/ =- 3.0 x 1020 CM-3 at room temperature. Thermal expansion (a = 8.8 x 10-6 K-1), as measured for Fe(0.)2Co(3.8)Sb(12),Te-x , compared well with that of undoped Co4Sb12. A further increase in the thermoelectric figure of merit up to ZT = 1.3 at 820 K was achieved for Fe(0.)2Co(3.8)Sb(12),Te-x , applying severe plastic deformation in terms of a high-pressure torsion process. (C) 2013 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

C-12 Helices in Long Hybrid (alpha gamma)(n) Peptides Composed Entirely of Unconstrained Residues with Proteinogenic Side Chains

Unconstrained gamma(4) amino acid residues derived by homologation of proteinogenic amino acids facilitate helical folding in hybrid (alpha gamma)(n) sequences. The C-12 helical conformation for the decapeptide, Boc-Leu-gamma(4)(R)Val](5)-OMe, is established in crystals by X-ray diffraction. A regular C-12 helix is demonstrated by NMR studies of the 18 residue peptide, Boc-Leu-gamma(4)(AR)Val](9)-OMe, and a designed 16 residue (alpha gamma)(n) peptide, incorporating variable side chains. Unconstrained (alpha gamma)(n) peptides show an unexpectedly high propensity for helical folding in long polypeptide sequences.

A Nearly Constant Switching Frequency Current Error Space Vector Based Hysteresis Controller for an IM Drive with 12-sided Polygonal Voltage Space Vectors

In this paper, a current error space vector (CESV) based hysteresis controller for a 12-sided polygonal voltage space vector inverter fed induction motor (IM) drive is proposed, for the first time. An open-end winding configuration is used for the induction motor. The proposed controller uses parabolic boundary with generalized vector selection logic for all sectors. The drive scheme is first studied with a space vector based PWM (SVPWM) control and from this the current error space phasor boundary is obtained. This current error space phasor boundary is approximated with four parabolas and then the system is run with space phasor based hysteresis PWM controller by limiting the CESV within the parabolic boundary. The proposed controller has increased modulation range, absence of 5th and 7th order harmonics for the entire modulation range, nearly constant switching frequency, fast dynamic response with smooth transition to the over modulation region and a simple controller implementation.

12 V / kilo-Farad Range Lead-Carbon Hybrid Ultracapacitors and Their Envisaged Applications

12 V / kilo-Farad (kF) range substrate-integrated lead-carbon hybrid ultracapacitors (HUCs) wherein the conventional positive plates of lead-acid batteries are replaced with substrate-integrated PbO2 positive plates and the negative plates are replaced with carbon-coated graphitic electrodes, providing totally non-faradaic and corrosion-free electrodes, are developed and performance tested. Constant-current discharge data at varying load-currents, constant-power discharge data at varying power values, and the capacitance data at different temperature for a 12 V / kF range substrate-integrated lead-carbon HUC are described along with its resistance, leakage current, self-discharge and cycle-life characteristics.

A Reactive Intermediate, Ni-5(C6H4N3)(6)(CO)(4)], in the Formation of Nonameric Clusters of Nickel, Ni-9(C6H4N3)(12)(CO)(6)] and Ni-9(C6H4N3)(12)(CO)(6)].2(C3H7NO)

Three new molecular compounds, Ni-5(bta)(6)(CO)(4)], I, Ni-9(bta)(12)(CO)(6)], II, Ni-9(bta)(12)(CO)(6)]. 2(C3H7NO), III, (bta = benzotriazole) were prepared employing solvothermal reactions. Of these, I have pentanuclear nickel, whereas II and III have nonanuclear nickel species. The structures are formed by the connectivity between the nickel and benzotriazole giving rise to the 5- and 9-membered nickel clusters. The structures are stabilised by extensive pi aEuro broken vertical bar pi and C-H... pi interactions. Compound II and III are solvotamorphs as they have the same 9-membered nickel clusters and have different solvent molecules. To the best of our knowledge, the compounds I-III represent the first examples of the same transition element existing in two distinct coordination environment in this class of compounds. The studies reveal that compound I is reactive and could be an intermediate in the preparation of II and III. Thermal studies indicate that the compounds are stable upto 350(a similar to)C and at higher temperatures (similar to 800(a similar to)C) the compounds decompose into NiO. Magnetic studies reveal that II is anti-ferromagnetic.

Performance comparison for 12 V lead-carbon hybrid ultracapacitors with substrate-integrated and conventional pasted positive plates

Lead-carbon hybrid ultracapacitors comprise positive lead dioxide plates of the lead-acid battery and negative plates of carbon-based electrical double-layer capacitors (EDLCs). Accordingly, a lead-carbon hybrid ultracapacitor has the features of both the battery and that of an EDLC. In this study, the development and performance comparison between the two types of lead-carbon hybrid ultracapacitors, namely those with substrate-integrated and conventional pasted positive plates, is presented as such a study is lacking in the literature. The study suggests that the faradaic efficiencies for both types of lead-carbon hybrid ultracapacitors are comparable. However, their capacitance values as well as energy and power densities differ significantly. For substrate-integrated positive plate hybrid ultracapacitor, capacitance and energy density values are lower, but power density values are higher than pasted positive plate lead-carbon hybrid ultracapacitors due to their shorter response time. Accordingly, internal resistance values are also lower for substrate-integrated lead-carbon hybrid ultracapacitors. Both types of lead-carbon hybrid ultracapacitors exhibit good cycle life of 100,000 pulse charge-discharge cycles with only a nominal loss in their capacitance values.

Directing peptide conformation with centrally positioned pre-organized dipeptide segments: studies of a 12-residue helix and beta-hairpin

Secondary structure formation in oligopeptides can be induced by short nucleating segments with a high propensity to form hydrogen bonded turn conformations. Type I/III turns facilitate helical folding while type II'/I' turns favour hairpin formation. This principle is experimentally verified by studies of two designed dodecapeptides, Boc-Val-Phe-Leu-Phe-Val-Aib-Aib-Val-Phe-Leu-Phe-Val-OMe 1 and Boc-Val-Phe-Leu-Phe-Val- (D) Pro- (L) Pro-Val-Phe-Leu-Phe-Val-OMe 2. The N- and C-terminal flanking pentapeptide sequences in both cases are identical. Peptide 1 adopts a largely alpha-helical conformation in crystals, with a small 3(10) helical segment at the N-terminus. The overall helical fold is maintained in methanol solution as evidenced by NMR studies. Peptide 2 adopts an antiparallel beta-hairpin conformation stabilized by 6 interstrand hydrogen bonds. Key nuclear Overhauser effects (NOEs) provide evidence for the antiparallel beta-hairpin structure. Aromatic proton chemical shifts provide a clear distinction between the conformation of peptides 1 (helical) and 2 (beta-hairpin). The proximity of facing aromatic residues positioned at non-hydrogen bonding positions in the hairpin results in extensively ring current shifted proton resonances in peptide 2.

Studies on 12 V substrate-integrated lead-carbon hybrid ultracapacitors

A cost-effective 12 V substrate-integrated lead-carbon hybrid ultracapacitor is developed and performance tested. These hybrid ultracapacitors employ flexible-graphite sheets as negative plate current-collectors that are coated amperometrically with a thin layer of conducting polymer, namely poly-aniline to provide good adhesivity to activated-carbon layer. The positive plate of the hybrid ultracapacitors comprise conventional lead-sheet that is converted electrochemically into a substrate-integrated lead-dioxide electrode. 12 V substrate-integrated lead-carbon hybrid ultracapacitors both in absorbent-glass-mat and polymeric silica-gel electrolyte configurations are fabricated and characterized. It is possible to realize 12 V configurations with capacitance values of similar to 200 F and similar to 300 F, energy densities of similar to 1.9 Wh kg(-1) and similar to 2.5 Wh kg(-1) and power densities of similar to 2 kW kg(-1) and similar to 0.8 kW kg(-1), respectively, having faradaic-efficiency values of similar to 90 % with cycle-life in excess of 100,000 cycles. The effective cost of the mentioned hybrid ultracapacitors is estimated to be about similar to 4 US$/Wh as compared to similar to 20 US$/Wh for commercially available ultracapacitors.

An Open-End winding IM drive with Multilevel 12-sided Polygonal Vectors with Symmetric Triangles

Multilevel inverters with hexagonal voltage space vector structures have improved performance of induction motor drives compared to that of the two level inverters. Further reduction in the torque ripple on the motor shaft is possible by using multilevel dodecagonal (12-sided polygon) voltage space vector structures. The advantages of dodecagonal voltage space vector based PWM techniques are the complete elimination of fifth and seventh harmonics in phase voltages for the full modulation range and the extension of linear modulation range. This paper proposes an inverter circuit topology capable of generating multilevel dodecagonal voltage space vectors with symmetric triangles, by cascading two asymmetric three level inverters with isolated H-Bridges. This is made possible by proper selection of DC link voltages and the selection of resultant switching states for the inverters. In this paper, a simple PWM timing calculation method is proposed. Experimental results have also been presented in this paper to validate the proposed concept.

Interlaboratory comparison of magnesium isotopic compositions of 12 felsic to ultramafic igneous rock standards analyzed by MC-ICPMS

To evaluate the interlaboratory mass bias for high-precision stable Mg isotopic analysis of natural materials, a suite of silicate standards ranging in composition from felsic to ultramafic were analyzed in five laboratories by using three types of multicollector inductively coupled plasma mass spectrometer (MC-ICPMS). Magnesium isotopic compositions from all labs are in agreement for most rocks within quoted uncertainties but are significantly (up to 0.3 parts per thousand in Mg-26/Mg-24, > 4 times of uncertainties) different for some mafic samples. The interlaboratory mass bias does not correlate with matrix element/Mg ratios, and the mechanism for producing it is uncertain but very likely arises from column chemistry. Our results suggest that standards with different matrices are needed to calibrate the efficiency of column chemistry and caution should be taken when dealing with samples with complicated matrices. Well-calibrated standards with matrix elements matching samples should be used to reduce the interlaboratory mass bias.

Comments on ``Influence of chemical reaction and viscous dissipation on MHD mixed convection flow'' by K. Das JMST 28 (5) (2014) 1881 similar to 1885] and ``Cu-water nanofluid flow and heat transfer over a shrinking sheet'' by K. Das JMST 28 (12) 5089 similar to 5094]

In this letter, we submit our comment on the following recently published papers by Kalidas Das: (1) ``Influence of chemical reaction and viscous dissipation on MHD mixed convection flow,'' Journal of Mechanical Science and Technology 28 (5) (2014) 1881-1885; and (2) ``Cu-water nanofluid flow and heat transfer over a shrinking sheet,'' Journal of Mechanical Science and Technology 28 (12) (2014) 5089-5094. The authors attempt to present the similarity solutions in both papers. We comment that the similarity transformations considered in Refs. 1, 2] are incorrect. Thus, the results presented by Kalidas Das lead to invalid conclusions.