Glucose reactivity with filling materials as a limitation for using the glucose leakage model

Aim To evaluate the reactivity of different endodontic materials and sealers with glucose and to asses the reliability of the glucose leakage model in measuring penetration of glucose through these materials.Methodology Ten uniform discs (radius 5 mm, thickness 2 mm) were made of each of the following materials: Portland cement, MTA (grey and white), sealer 26, calcium sulphate, calcium hydroxide [Ca(OH)(2)], AH26,Epiphany, Resilon, gutta-percha and dentine. After storing the discs for 1 week at 37 degrees C and humid conditions, they were immersed in 0.2 mg mL(-1) glucose solution in a test tube. The concentration of glucose was evaluated using an enzymatic reaction after 1 week. Statistical analysis was performed with the ANOVA and Dunnett tests at a significant level of P < 0.05.Results Portland cement, MTA, Ca(OH)(2) and sealer 26 reduced the concentration in the test tube of glucose significantly after 1 week (P < 0.05). Calcium sulphate reduced the concentration of glucose, but the difference in concentrations was not significant (P = 0.054).Conclusions Portland cement, MTA, Ca(OH)(2) and sealer 26 react with a 0.2 mg mL(-1) glucose solution. Therefore, these materials should not be evaluated for sealing ability with the glucose leakage model.

Leakage current, ferroelectric and structural properties in Pb(1-x)Ba(x)TiO(3) thin films prepared by chemical route

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Microbial leakage of MTA, Portland cement, Sealapex and zinc oxide-eugenol as root-end filling materials

Objective: The aim of this study was to compare the microbial leakage of mineral trioxide aggregate (MTA), Portland cement (PC), Sealapex and zinc oxide-eugenol (ZOE) as root-end filling materials.Study design: An in vitro microbial leakage test (MLT) with a split chamber was used in this study. A mixture of facultative bacteria and one yeast (S. aureus + E. faecalis + P. aeruginosa + B. subtilis + C. albicans) was placed in the upper chamber and it could only reach the lower chamber containing Brain Heart Infusion broth by way of leakage through the root-end filling. Microbial leakage was observed daily for 60 days. Sixty maxillary anterior human teeth were randomly assigned to different groups - MTA and PC (gray and white), Sealapex + zinc oxide and ZOE, control groups and subgroups to evaluate the influence of EDTA for smear layer removal. These materials were further evaluated by an agar diffusion test (ADT) to verify their antimicrobial efficacy. Data were analyzed statistically by Kruskal-Wallis and Mann-Whitney test.Results: In the MLT, Sealapex + zinc oxide and ZOE did not show evidence of microbial leakage over the 60-day experimental period. The other materials showed leakage from the 15th day. The presence of smear layer influenced microbial leakage. Microbial inhibition zones were not observed in all samples tested by ADT.Conclusion: Sealapex + zinc oxide and ZOE did not show microbial leakage over the experimental period, whereas it was verified within 15 to 45 days in MTA and Portland cement.

Structure, ferroelectric/magnetoelectric properties and leakage current density of (Bi0.85Nd0.15)FeO3 thin films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of dentine surface treatment on leakage of root fillings with a glass ionomer sealer.

The purpose of this study was to observe the quality of seal of the glass ionomer cement, Ketac-Endo, after treatment of the root canal wall. The root canals of 140 extracted human teeth were prepared biomechanically. The root canals were treated with either EDTA or received an intracanal dressing of calcium hydroxide or camphorated paramonochlorphenol. The root canals were filled by the lateral condensation technique with gutta-percha points and the sealer Ketac-Endo, or zinc oxide-eugenol cement or Sealapex. The teeth were placed into a 2% methylene blue dye solution inside a flask, which was attached to a vacuum pump. Leakage was measured linearly. Sealapex exhibited significantly less leakage than Ketac-Endo or zinc oxide-eugenol cement (P<0.01). The use of EDTA and intermediary dressings reduced significantly (P<0.01) the leakage observed with the zinc oxide-eugenol sealer and Ketac-Endo.

Apical leakage following root canal dressing with calcium hydroxide.

The purpose of this study was to analyse the apical leakage in teeth filled by the lateral condensation technique following medication with calcium hydroxide. One hundred and twenty extracted human teeth were biomechanically prepared by using exclusively reaming motion with files up to #40. Half of the teeth received a calcium hydroxide dressing for 3 days. The medication was removed by irrigation and reaming motion with files #40 up to #70. The teeth were divided in 6 experimental groups, according to the dimension of the utilized instrument. The root canals were filled and posteriorly the teeth were placed into a 2% methylene blue dye solution inside a flask, which was attached to a vacuum pump. Leakage was measured linearly, and the results showed significantly (p<0.01) less leakage in the experimental groups that received calcium hydroxide dressings than in the control groups. The results persisted even after the removal of 300 micrometers of dentin from the root canal dentinal walls.

Apical leakage after root canal filling with an experimental calcium hydroxide gutta-percha point

This study was an in vitro analysis of the apical seal of root canals filled with an experimental calcium hydroxide gutta-percha point. One hundred and ten recently extracted human permanent teeth with a single root were used. The root canals were biomechanically prepared, and some received a dressing of calcium hydroxide for 7 days. Root canals not dressed were filled by the lateral condensation technique with either regular gutta-percha or calcium hydroxide gutta-percha points. The dressed root canals were filled with the same sealers and regular gutta-percha points. The specimens were placed into a 2% methylene blue dye solution under vacuum, and the apical leakage was linearly evaluated. The experimental groups with calcium hydroxide dressing and the one with calcium hydroxide gutta-percha points exhibited significantly (p < 0.05) less leakage than the groups filled with regular gutta-percha points. The results obtained indicated that calcium hydroxide guttapercha points produced an improvement in the apical sealing quality of the root canal filling. Copyright © 1996 by The American Association of Endodontists.

An active leakage-injection scheme applied to low-voltage SRAMs

An active leakage-injection scheme (ALIS) for low-voltage (LV) high-density (HD) SRAMs is presented. By means of a feedback loop comprising a servo-amplifier and a common-drain MOSFET, a current matching the respective bit-line leakage is injected onto the line during precharge and sensing, preventing the respective capacitances from erroneous discharges. The technique is able to handle leakages up to hundreds of μA at high operating temperatures. Since no additional timing is required, read-out operations are performed at no speed penalty. A simplified 256×1bit array was designed in accordance with a 0.35 CMOS process and 1.2V-supply. A range of PSPICE simulation attests the efficacy of ALIS. With an extra power consumption of 242 μW, a 200 μA-leakage @125°C, corresponding to 13.6 times the cell current, is compensated.

In vitro evaluation of marginal leakage in bonded restorations, with mechanical or chemical-mechanical (Carisolv) removal of carious tissue

This study carried out an in vitro evaluation and comparison of the occurrence of marginal leakage in bonded restorations using mechanical or chemical-mechanical (Carisolv) removal of carious tissue. For that purpose, 40 extracted decayed human molars were divided into 4 groups: GI (burs + Prime & Bond NT + TPH), GII (Carisolv + Prime & Bond NT + TPH), GIII (burs + SBMP + Z100) and GIV (Carisolv + SBMP + Z100). After accomplishment of the restorations and thermal cycling, the teeth were exposed to dye, sectioned and qualitatively evaluated. The results demonstrated that the system of removal of carious tissue did not influence the results of microleakage at any of the cavity margins. At dentinal margins, use of the Prime & Bond NT + TPH restorative system allowed the occurrence of less microleakage than the SBMP + Z100 system.

The effect of endodontic materials on the optical density of dyes used in marginal leakage studies

The aim of this study was to determine the effect of the exposure of different endodontic materials to different dye solutions by evaluating the optical density of the dye solutions. Seventy-five plastic tubes were filled with one of the following materials: AH Plus, Sealapex, Portland cement, MTA (Angelus and Pro Root) and fifteen control plastic tubes were not. Each specimen of material and control was immersed in a container with 1 ml of each dye solution. A 0.1 ml-dye solution aliquote was removed before immersion and after 12, 24, 48 and 72 hours of each specimen immersion to record its optical density (OD) in a spectrophotometer. Statistical analysis was performed with ANOVA and Tukey tests (5%). No significant difference was found among any of the solution OD values for AH Plus cement. Portland cement promoted different OD values after 12 hours of immersion. MTA-Angelus cement presented different OD values only for 2% rhodamine B and the MTA-Pro Root cement presented different OD values in all 2% rhodamine B samples. Sealapex cement promoted a reduction in the India Ink OD values. Dye evaluation through OD seems to be an interesting method to select the best dye solution to use in a given marginal leakage study.

Leakage detection in water pipe networks using electromechanical impedance (EMI) based technique

The electromechanical impedance (EMI) technique has been successfully used in structural health monitoring (SHM) systems on a wide variety of structures. The basic concept of this technique is to monitor the structural integrity by exciting and sensing a piezoelectric transducer, usually a lead zirconate titanate (PZT) wafer bonded to the structure to be monitored and excited in a suitable frequency range. Because of the piezoelectric effect, there is a relationship between the mechanical impedance of the host structure, which is directly related to its integrity, and the electrical impedance of the PZT transducer, obtained by a ratio between the excitation and the sensing signals.This work presents a study on damage (leaks) detection using EMI based method. Tests were carried out in a rig water system built in a Hydraulic Laboratory for different leaks conditions in a metallic pipeline. Also, it was evaluated the influence of the PZT position bonded to the pipeline. The results show that leaks can effectively be detected using common metrics for damage detection such as RMSD and CCDM. Further, it was observed that the position of the PZT bonded to the pipes is an important variable and has to be controlled.

Subtle leakage of a Majorana mode into a quantum dot

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effects of coronal leakage on concentration of hydrogen ions and calcium hydroxide release of several calcium hydroxide pastes over different periods of time

Purpose: To evaluate the effects of coronal leakage on concentration of hydrogen ions (pH) and calcium release of several calcium hydroxide pastes, over different periods of time. Material and Methods: Fifty extracted human mandibular central incisors (n=10) were instrumented up to the F2 instrument and assigned to the following intracanal dressing: G1- Calen, G2- Calen with 0.4% chlorhexidine (CHX), G3- Calcium hydroxide with camphorated paramonochlorophenol (CPMC) and glycerin, G4- Calen, but temporary filling material maintained during all test (positive control) and G5- Root canal without intracanal dressing (negative control). All groups were immersed in distilled water for 7 days. In sequence, the temporary filling materials were removed, except in controls groups. All specimens were individually mounted on a specific device and only its root again immersed in distilled water. Concentration of hydrogen ions and calcium release by calcium hydroxide pastes in distilled water were evaluated in 24h, 7, 14 and 28 days. The results were submitted to ANOVA test (p = 0.05). After 28 days, root canals from experimental groups were examined in SEM. Results: G1, G2, G3 and G4 presented similar pH values and calcium release and did not differ from each other (p>0.05), up to 7 days. After this time G1, G2 and G3 presented values lower values than G4 (p<0.05). In SEM analysis, calcium hydroxide residues were observed in all experimental groups. Conclusions: After 7 days, coronal leakage decreased the concentration of hydrogen ions and calcium ion release provided by all calcium hydroxide pastes.

CLSM assessment of tubule penetration and bacterial leakage evaluation of two resin-based sealer

Aim: The aims of this study were to assess the penetration of two endodontic sealers (salicylate and epoxy resin-based sealers) into dentinal tubules using CLSM; and to evaluate the bacterial leakage of roots filled with the same sealers associated with gutta-percha. Material and Methods: For sealer penetrability assessment, thirty bovine roots were instrumented and divided into three groups: AHP: EDTA + filling with AH Plus and gutta-percha (n=10), MTAF: EDTA + filling with MTA Fillapex and gutta-percha (n=10), control group: canals were not irrigated with EDTA and were filled with gutta-percha and AH Plus (n=5) or MTA Fillapex (n=5). Rhodamine B was added to the sealers in order to provide adequate fluorescence. The roots were transversely sectioned 3mm from the apex to enable CLSM analysis. Leakage was evaluated for turbidity of the broth in a split chamber model system for 30 days, using Enterococcus faecalis as a microbial marker. Thirty roots were instrumented and divided in four grupos: AHP: filling with AH Plus and gutta-percha (n=10); MTAF: filling with MTA Fillapex and gutta-percha (n=10); positive control: filling with gutta-percha without sealer (n = 5); negative control: sealing with cyanoacrylate to test the seal of the system (n = 5). Results: The medians for dentinal tubule penetration were 6.8% (AHP) and 6.6% (MTAF) (P = 0.82). The average time for bacterial leakage was 8 days in both experimental groups (P = 0.79). Conclusion: MTA Fillapex and AH Plus presented similar behavior regarding dentinal tubule penetration and bacterial leakage.

Abutment coating with diamond-like-carbon films to reduce implant-abutment bacterial leakage

Backgroud: The influence of diamond-like-carbon (DLC) films on bacterial leakage through the interface between abutments and dental implants of external hexagon (EH) and internal hexagon (IH) was evaluated. Film deposition was performed by PECVD (Plasma Enhanced Chemical Vapor Deposition). Sets of implants and abutments (N=180, n=30) were divided according to the connection design and the treatment of the abutment base: (1) no treatment (control); (2) DLC film deposition, and (3) Ag-DLC film deposition. Under sterile conditions, 1 µL of Enterococcus faecalis was inoculated inside the implants, and abutments were tightened. The sets were tested for immediate external contamination, suspended in test tubes containing sterile culture broth, and followed-up for five days. Turbidity of the broth indicated bacterial leakage. At the end of the period, the abutments were removed and the internal content of the implants was collected with paper points and plated in Petri dishes. They were incubated for 24 h for bacterial viability assessment and colony-forming unit (CFU) counting. Bacterial leakage was analyzed by Chi-square and Fisher exact tests (α=5%). The percentage of bacterial leakage was 16.09% for EH implants and 80.71% for IH implants (P<0.0001). The bacterial load was higher inside these implants (P=0.000). The type of implant significantly influenced the results (P=0.000), whereas the films did not (P=0.487). We concluded that: (1) IH implants showed a higher frequency of bacterial leakage and (2) the DLC and Ag-DLC films did not significantly reduce the frequency of bacterial leakage and bacteria load inside the implants.