Antioxidant activity and cytotoxicity of solubilized C60 and its conjugates with butylated hydroxytoluene

It has been described that fullerenes (C60) present interesting properties with potential application in clinical conditions related to oxidative stress. One of the most prominent features of fullerenes is the ability to quench free radicals. However, because of its poor solubility, this has been studied mostly in organic solutions, while the antioxidant activity and cytotoxicity of fullerenes and their derivates in aqueous medium is not well characterized. The antioxidant capacity of synthesised C60-conjugates has been investigated and its was higher comparing to C60 isolated. The aim of this study was to assess the viability of C60-conjugates by determining its antioxidant activity and cytotoxicity in bio-relevant media.

Teor crítico de cloretos para iniciação da corrosão do aço no betão

Este trabalho tem como objectivo a determinação do teor crítico de cloretos no betão, ou seja, o teor de cloretos à profundidade da armadura que é necessário para sustentar uma quebra localizada do filme de passivação e, por isso, iniciar a corrosão activa. Uma vez que não existe consenso quanto ao seu valor, este trabalho pretendia dar um contributo no estudo deste parâmetro, utilizando um procedimento que modele realisticamente a corrosão das armaduras em estruturas de betão armado expostas directamente a água do mar. Realizaram-se três séries de testes com cimentos de fontes diferentes. Utilizaram-se varões nervurados e incorporados no betão. Os iões cloreto foram introduzidos por absorção capilar e difusão e a despassivação foi detectada por medição do potencial de corrosão do aço. O teor crítico de cloretos foi determinado em relação à massa de cimento por titulação potenciométrica obtendo-se para a amassadura 1 um intervalo entre 1.0% e 1.6%, para a amassadura 2, um teor entre 0.5% e 0.9% e para a amassadura 3 obtiveram-se teores críticos entre 0.6% e 1.0%. Comparando com o teor máximo de cloretos definido pela norma NP EN 206-1, 0.4%, conclui-se que este valor não é conservador e é um valor para o qual efectivamente ainda não se iniciou a corrosão por cloretos podendo ser utilizado em modelos de previsão do início da corrosão das armaduras. Verificou-se que a não protecção dos varões nas amassaduras, principalmente na amassadura 1, levam a uma maior acessibilidade de oxigénio, provocando “crevice” e corrosão na armadura exposta ao ar, levando a teores críticos de cloretos erróneos. Efectuaram-se registos fotográficos e observações à lupa das armaduras bem como micrografias em MEV e microanálises por dispersão de Raios-X no betão adjacente à armadura. Verificou-se a existência de produtos de corrosão na armadura os quais continham iões cloreto.

Microscopia eletrônica de varredura de ovos de Haemagogus leucocelaenus (Diptera: Culicidae)

OBJETIVO: Observar detalhes morfológicos de ovos de Haemagogus leucocelaenus visualizados pela primeira vez por microscopia eletrônica de varredura (MEV) e realizar morfometria das principais estruturas. MÉTODOS: Foram utilizados ovos de Hg. leucocelaenus provenientes de fêmeas capturadas na Reserva Biológica do Tinguá, RJ, sendo parte destinada à eclosão e outra ao processamento de MEV, dos quais três foram submetidos à análise morfométrica. O material foi fixado em glutaraldeído 2,5% e pós-fixado em tetróxido de ósmio 1%, ambos em tampão cacodilato de sódio 0.1M, pH 7.2, processado e observado ao MEV Jeol 5310. Medições foram realizadas com o auxílio do software de análise Semafore. RESULTADOS: Os ovos apresentaram contorno elíptico com aproximadamente 574 µm de comprimento e 169 µm de largura, sendo o índice do ovo (l/wratio) 3,39 µm. O exocório é extremamente regular, possuindo ornamentação hexagonal e algumas vezes pentagonal. Nas células coriônicas, observaram-se tubérculos simetricamente dispostos com relação ao eixo longitudinal, e, no interior delas, tubérculos menores, individualizados, dispostos na periferia, e poucos agrupados no centro. A superfície do retículo coriônico não apresentou rugosidades. O aparelho micropilar apresenta colar proeminente, contínuo, com disco micropilar bem evidente. CONCLUSÕES: A ornamentação do exocório apresenta diferenças em relação aos tubérculos das células coriônicas e ao retículo coriônico externo entre os ovos de Hg. leucocelaenus comparados aos ovos de Hg. janthinomys e Hg. equinus, bem como com relação aos de Aedes aegypti, Ae. albopictus e Ae bahamensis.

Dissolução redutiva de minério de ferro por Acidithiobacillus ferrooxidans para a recuperação de metais de interesse econômico

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Dosimetric effect by shallow air cavities in high energy electron beams

This study evaluates the dosimetric impact caused by an air cavity located at 2 mm depth from the top surface in a PMMA phantom irradiated by electron beams produced by a Siemens Primus linear accelerator. A systematic evaluation of the effect related to the cavity area and thickness as well as to the electron beam energy was performed by using Monte Carlo simulations (EGSnrc code), Pencil Beam algorithm and Gafchromic EBT2 films. A home-PMMA phantom with the same geometry as the simulated one was specifically constructed for the measurements. Our results indicate that the presence of the cavity causes an increase (up to 70%) of the dose maximum value as well as a shift forward of the position of the depthedose curve, compared to the homogeneous one. Pronounced dose discontinuities in the regions close to the lateral cavity edges are observed. The shape and magnitude of these discontinuities change with the dimension of the cavity. It is also found that the cavity effect is more pronounced (6%) for the 12 MeV electron beam and the presence of cavities with large thickness and small area introduces more significant variations (up to 70%) on the depthedose curves. Overall, the Gafchromic EBT2 film measurements were found in agreement within 3% with Monte Carlo calculations and predict well the fine details of the dosimetric change near the cavity interface. The Pencil Beam calculations underestimate the dose up to 40% compared to Monte Carlo simulations; in particular for the largest cavity thickness (2.8 cm).

Controlo da qualidade dosimétrico no serviço de radioterapia do Hospital CUF Descobertas (HCD): importância do controlo da qualidade do sector da física e resultados da auditoria ESTRO-EQUAL

A calibração e o controlo da qualidade de um acelerador linear são passos muito importantes num serviço de Radioterapia, para garantir a qualidade dos tratamentos prestados. O sector da Física da Unidade de Radioterapia do Hospital Cuf Descobertas implementou um rigoroso Programa de controlo de qualidade ao equipamento produtor de radiação e aos equipamentos medidores de radiação, de acordo com o Dec-Lei 180/2002 e com os protocolos internacionais. Para tal, foram implementados procedimentos, criadas folhas de cálculo, instruções de trabalho e impressos. Foram ainda implementados testes aos equipamentos com periodicidade definida: controlo de qualidade diário e controlo de qualidade após intervenções (manutenções preventivas e correctivas). No decorrer do ano de 2005, o sector da Física colaborou activamente com toda a equipa da Radioterapia na implementação da Norma ISO 9001:2000 no serviço, contribuindo com o seu know how na implementação desta, numa área tão importante como a da garantia da qualidade dos feixes de radiação e das respectivas calibrações em dose. Numa procura de melhoria contínua da qualidade dos serviços prestados aos pacientes, decorre ainda uma auditoria externa da EQUAL-ESTRO*, intercomparação postal com dosímetros termoluminescentes. A qualidade dos feixes de energias utilizados diariamente é analisada, tanto ao nível das calibrações absolutas de cada um dos feixes de fotões e de electrões, como ao nível dos cálculos de dose obtidos com o sistema de planimetria XiO da CMS. Os resultados das duas primeiras fases da intercomparação, relativa aos dois feixes de fotões de 6 MV e 15 MV e feixes de electrões de 4 MeV, 8 MeV e 12 MeV, foram considerados pela EQUAL-ESTRO num nível óptimo (desvio máximo na dose medida em relação à dose de referência |d| ≤ 3%).

Effects of sulphurization time on Cu2ZnSnS4 absorbers and thin films solar cells obtained from metallic precursors

We report the results of a study of the sulphurization time effects on Cu2ZnSnS4 absorbers and thin film solar cells prepared from dc-sputtered tackedmetallic precursors. Three different time intervals, 10 min, 30min and 60 min, at maximum sulphurization temperature were considered. The effects of this parameter' change were studied both on the absorber layer properties and on the final solar cell performance. The composition, structure, morphology and thicknesses of the CZTS layers were analyzed. The electrical characterization of the absorber layer was carried out by measuring the transversal electrical resistance of the samples as a function of temperature. This study shows an increase of the conductivity activation energy from 10 meV to 54meV for increasing sulphurization time from 10min to 60min. The solar cells were built with the following structure: SLG/Mo/CZTS/CdS/i-ZnO/ZnO:Al/Ni:Al grid. Several ac response equivalent circuit models were tested to fit impedance measurements. The best results were used to extract the device series and shunt resistances and capacitances. Absorber layer's electronic properties were also determined using the Mott–Schottky method. The results show a decrease of the average acceptor doping density and built-in voltage, from 2.0 1017 cm−3 to 6.5 1015 cm−3 and from 0.71 V to 0.51 V, respectively, with increasing sulphurization time. These results also show an increase of the depletion region width from approximately 90 nm–250 nm.

Photoluminescence and electrical study of fluctuating potentials in Cu2ZnSnS4-based thin films

In this work, we investigated structural, morphological, electrical, and optical properties from a set of Cu2ZnSnS4 thin films grown by sulfurization of metallic precursors deposited on soda lime glass substrates coated with or without molybdenum. X-ray diffraction and Raman spectroscopy measurements revealed the formation of single-phase Cu2ZnSnS4 thin films. A good crystallinity and grain compactness of the film was found by scanning electron microscopy. The grown films are poor in copper and rich in zinc, which is a composition close to that of the Cu2ZnSnS4 solar cells with best reported efficiency. Electrical conductivity and Hall effect measurements showed a high doping level and a strong compensation. The temperature dependence of the free hole concentration showed that the films are nondegenerate. Photoluminescence spectroscopy showed an asymmetric broadband emission. The experimental behavior with increasing excitation power or temperature cannot be explained by donor-acceptor pair transitions. A model of radiative recombination of an electron with a hole bound to an acceptor level, broadened by potential fluctuations of the valence-band edge, was proposed. An ionization energy for the acceptor level in the range 29–40 meV was estimated, and a value of 172 ±2 meV was obtained for the potential fluctuation in the valence-band edge.

Admittance spectroscopy of Cu2ZnSnS4 based thin film solar cells

In this report, we propose an AC response equivalent circuit model to describe the admittance measurements of Cu2ZnSnS4 thin film solar cell grown by sulphurization of stacked metallic precursors. This circuit describes the contact resistances, the back contact, and the heterojunction with two trap levels. The study of the back contact resistance allowed the estimation of a back contact barrier of 246 meV. The analysis of the trap series with varying temperature revealed defect activation energies of 45 meV and 113 meV. The solar cell’s electrical parameters were obtained from the J-V curve: conversion efficiency, 1.21%; fill factor, 50%; open circuit voltage, 360 mV; and short circuit current density, 6.8 mA/cm2.

Teor crítico de cloretos para iniciação da corrosão do aço no betão: influência do estado de superfície da armadura

Trabalho Final de Mestrado para obtenção do grau de Mestre em Engenharia Química e Biológica - Processos Químicos

Permeabilidade e microestrutura de BAC com incorporação de fíler calcário

A durabilidade do betão está diretamente relacionada com o transporte de fluídos no seu interior que, por sua vez, está condicionado pela microestrutura do mesmo. Dadas as diferenças da estrutura porosa do betão auto-compactável (BAC) quando comparada com a de um betão convencional (BC), serão expectáveis algumas diferenças na durabilidade do primeiro. Um dos principais elementos diferenciadores entre ambos é a necessidade de quantidades significativas de material ultra fino (cimento e adições) por parte do BAC, essencialmente de modo a garantir os seus requisitos de comportamento no estado fresco. A utilização de adições, como o fíler calcário (FC), pode melhorar não só o comportamento do BAC no estado fresco como também influenciar a resistência mecânica e a durabilidade, através de uma microestrutura mais densa. Nesse sentido, o objetivo do presente trabalho é avaliar o efeito da utilização de FC na permeabilidade e na microestrutura do BAC. De modo a comprovar as referidas relações, foram efetuados estudos sobre a correlação entre as propriedades da microestrutura e os mecanismos de transporte, através da produção de misturas de BAC com 0%, 30%, 45% e 60% de substituição de cimento por FC. A caracterização físico-química das amostras de BAC foi realizada por difracção de raios-x e por microscopia eletrónica de varrimento (MEV), sendo esta última técnica também um método de caracterização morfológica. Para analisar as propriedades de transporte do BAC foram executados ensaios de absorção por imersão e absorção capilar. A análise dos resultados obtidos permitiu concluir que os betões em estudo apresentam características satisfatórias ao nível da microestrutura e propriedades de transporte. Salienta-se que em todas as amostras foi encontrada uma microestrutura densa, não tendo sido encontrada uma zona de transição entre o agregado e a pasta com características que a diferenciem da restante da pasta. Estas observações complementam os valores encontrados no estudo das propriedades de transporte, fazendo prever que as amostras apresentam uma baixa porosidade.

Produção de fibras de hidroxiapatite por electrofiação

Dissertação apresentada na Faculdade de Ciências e Tecnologia da Universidade Nova de Lisboa para obtenção do grau de Mestre em Biotecnologia

New textures for the lepton mass matrices

We study predictive textures for the lepton mass matrices in which the charged-lepton mass matrix has either four or five zero matrix elements while the neutrino Majorana mass matrix has, respectively, either four or three zero matrix elements. We find that all the viable textures of these two kinds share many predictions: the neutrino mass spectrum is inverted, the sum of the light-neutrino masses is close to 0.1 eV, the Dirac phase delta in the lepton mixing matrix is close to either 0 or pi, and the mass term responsible for neutrinoless double-beta decay lies in between 12 and 22 meV. (C) 2014 The Authors. Published by Elsevier B.V. This is an open access article under the CC BY license.

Optimização e Validação da Produção de [13n]-Nh3 para Estudos Clínicos de Tomografia por Emissão de Positrões na Avaliação da Perfusão Miocárdica

A par das patologias oncológicas, as doenças do foro cardíaco, em particular a doença arterial coronária, são uma das principais causas de morte nos países industrializados, devido sobretudo, à grande incidência de enfartes do miocárdio. Uma das formas de diagnóstico e avaliação desta condição passa pela obtenção de imagens de perfusão miocárdica com radionuclídeos, realizada por Tomografia por Emissão de Positrões (PET). As soluções injectáveis de [15O]-H2O, [82Rb] e [13N]-NH3 são as mais utilizadas neste tipo de exame clínico. No Instituto de Ciências Nucleares Aplicadas à Saúde (ICNAS), a existência de um ciclotrão tem permitido a produção de uma variedade de radiofármacos, com aplicações em neurologia, oncologia e cardiologia. Recentemente, surgiu a oportunidade de iniciar exames clínicos com [13N]-NH3 para avaliação da perfusão miocárdica. É neste âmbito que surge a oportunidade do presente trabalho, pois antes da sua utilização clínica é necessário realizar a optimização da produção e a validação de todo o processo segundo as normas de Boas Práticas Radiofarmacêuticas. Após uma fase de optimização do processo, procedeu-se à avaliação dos parâmetros físico-químicos e biológicos da preparação de [13N]-NH3, de acordo com as indicações da Farmacopeia Europeia (Ph. Eur.) 8.2. De acordo com as normas farmacêuticas, foram realizados 3 lotes de produção consecutivos para validação da produção de [13N]-NH3. Os resultados mostraram um produto final límpido e ausente de cor, com valores de pH dentro do limite especificado, isto é, entre 4,5 e 8,5. A pureza química das amostras foi verificada, uma vez que relativamente ao teste colorimétrico, a tonalidade da cor da solução de [13N]-NH3 não era mais intensa que a solução de referência. As preparações foram identificadas como sendo [13N]-NH3, através dos resultados obtidos por cromatografia iónica, espectrometria de radiação gama e tempo de semi-vida. Por examinação do cromatograma obtido com a solução a ser testada, observou-se que o pico principal possuia um tempo de retenção aproximadamente igual ao pico do cromatograma obtido para a solução de referência. Além disso, o espectro de radiação gama mostrou um pico de energia 0,511 MeV e um outro adicional de 1,022 MeV para os fotões gama, característico de radionuclídeos emissores de positrões. O tempo de semi-vida manteve-se dentro do intervalo indicado, entre 9 e 11 minutos. Verificou-se, igualmente, a pureza radioquímica das amostras, correspondendo um mínimo de 99% da radioactividade total ao [13N], bem como a pureza radionuclídica, observando-se uma percentagem de impurezas inferiores a 1%, 2h após o fim da síntese. Os testes realizados para verificação da esterilidade e determinação da presença de endotoxinas bacterianas nas preparações de [13N]-NH3 apresentaram-se negativos.Os resultados obtidos contribuem, assim, para a validação do método para a produção de [13N]-NH3, uma vez que cumprem os requisitos especificados nas normas europeias, indicando a obtenção de um produto seguro e com a qualidade necessária para ser administrado em pacientes para avaliação da perfusão cardíaca por PET.

Avaliação da evolução das características de argamassas de cal aérea com diferentes teores de metacaulino em exposição natural

Dissertação para obtenção do grau de Mestre em Engenharia Civil – Perfil de Construção