Avaliação das técnicas de soldagem MIG-P CA e MIG-P CC+ aplicadas ao passe de enchimento em liga de alumínio AA5083

For contain beneficial properties, aluminum alloys are gaining more importance in different industrial areas, becoming the subject of study in several academic fields. When related to welding these alloys have some peculiarities that may hinder the union, such as microscopic oxide layer present on the metal surface. The MIG welding process, also known as GMAW, has developed versions that can be effective for welding aluminum. Knowing this, for this paper, two versions of pulsed MIG (CC + and CA) were chosen to evaluate which best suits pass by filling bevel on AA5083 aluminum sheets with 8 and 12 mm thick respectively. Furthermore, two types of wire, ER5087 and ER5183 were evaluated. To evaluate the process and versions of the wires, the high-speed cameras and thermal were used to monitor the metal transfer and the thermal behavior respectively, and the metallographic analysis for macrographic view of the weld beads and non-destructive testing by radiography for observation of possible discontinuities. It was found that the technique of MIG-P CA showed better results ahead of another technique both welding conditions imposed. When connected to the wires, they showed similar results, with uniform cords and seamless

A plasticidade dos amorfos: fazendo pigmentos brancos com fosfato de alumínio

A new white pigment made out of nano-structured non-crystalline aluminum phosphate was recently launched as an industrial product. Pigment opacifying properties are not intrinsic to aluminum phosphate but they arise as the result of a rare hollow particle nano-structure. This is in turn derived from the core-and-shell structure of amorphous aluminum phosphate precipitated under well-defined conditions. The new pigment is a product of the often neglected chemistry of non-crystalline ionic solids that can probably be a rich source of new successful products. The text describes a short account of the R&D activities, from the initial ideas to the present.

Preparação de nanopartículas de prata e ouro: um método simples para a introdução da nanociência em laboratório de ensino

A new practical experiment involving silver and gold nanoparticle syntheses was introduced in an inorganic chemistry laboratory course for undergraduate students at the Institute of Chemistry, UNICAMP. The nanoparticles were synthesized by the reduction of silver nitrate and tetrachloroauric acid with sodium borohydride and sodium citrate in an aqueous medium. Stabilities of the suspensions were tested using several different reactants including sodium chloride, polyvinylpyrrolidone, polyvinyl alcohol and cistamine. Changes in optical properties were observed by electronic spectra and also by transmission electronic microscopy, which also yielded data for estimating particle size.

Effect of casting atmosphere on the shear bond strength of a ceramic to Ni-Cr and Ni-Cr-Be alloys

The success of metal-ceramic restorations depends on an optimal bond between metal and ceramic. This study evaluated the effect of 3 casting atmospheres on the metal-ceramic bond strength (MCBS) of 2 Ni-Cr alloys, with beryllium (Fit Cast V) and without beryllium (Fit Cast SB). Sixty acrylic resin patterns (8 mm long and 5 mm diameter) were obtained using a fluorocarbon resin matrix. Wax was used to refine the surface of acrylic resin patterns that were invested and cast in an induction casting machine under normal, vacuum, and argon atmospheres at a temperature of 1340ºC. The castings were divested manually and airborne-particle abraded with 100-µm aluminum-oxide. Ten castings were obtained for each group. The IPS Classic V ceramic was applied (2 mm high and 5 mm diameter). The shear bond strength was tested in a mechanical testing machine with a crosshead speed of 2.0 mm/min. The MCBS data (MPa) were subjected to 2-way analysis of variance (α=0.05). There was no statistically significant difference (p>0.05) between the alloys or among the casting atmospheres. Within the limitations of this study, it may be concluded that the presence of beryllium and the casting atmosphere did not interfere in the MCBS of the evaluated metal-ceramic combinations

Estudo do comportamento eletroquímico de substâncias complexantes utilizando eletrodo de cobre

Copper electrode can be used for determination of complexing compounds through complexation reactions between Cu(II) and the analites. In this work some studies with three compounds were performed: glycine (precursor of glyphosate synthesis), herbicide glyphosate and aminomethylphosphonic acid (main metabolite of glyphosate). These compounds are complexing agents for Cu electrodes. Through simple experiments (cyclic voltammetry and corrosion studies) the applicability of the copper electrode as electrochemical sensor for complexing compounds in flow systems was presented.

Co-eletrodeposição oscilatória de cobre e estanho

It is investigated in the present contribution the oscillatory co-electrodeposition of CuSn on a polycrystalline gold surface in the presence of Triton X-100 surfactant and citric acid as additive, in acidic media. The experiments were conducted under potentiostatic control and the system dynamics characterized in terms of the morphology and stability of the current oscillations. Besides modulations in the frequency and amplitude of the current oscillations, several patterned states were observed, including relaxation-like and mixed mode oscillations. The oscillations were found to be very robust and some time series presented regular motions up to about two hours.

Fontes orgânicas e inorgânicas de zinco e cobre como melhoradores de desempenho em leitões desmamados

Foram conduzidos dois experimentos para avaliar fontes orgânicas e inorgânicas de zinco e cobre nas dietas e seus efeitos no desempenho de leitões desmamados aos 21 dias de idade. Em cada experimento, foram utilizados 90 leitões em delineamento experimental de blocos ao acaso, com cinco dietas, seis repetições e três animais por parcela. As dietas utilizadas nos experimentos 1 e 2 continham 120 ppm de zinco e 10 ppm de cobre na forma de sulfato. No experimento 1, foram suplementadas com 0, 300, 600 e 900 ppm de zinco na forma orgânica ou 2.400 ppm na forma de óxido (ZnO) e, no experimento 2, com 0, 50, 100 e 150 ppm de cobre na forma orgânica ou 240 ppm de cobre na forma de sulfato (CuSO4 H2O). No experimento 1, os níveis de zinco de fonte orgânica tiveram efeito linear no consumo de ração e no ganho de peso nos períodos de 0 a 15 dias e de 0 a 21 dias pós-desmame. O ganho de peso nas fases de 0 a 35 dias e de 0 a 42 dias pós-desmame e o consumo de ração dos leitões que receberam a dieta com 900 ppm de zinco de fonte orgânica não diferiram dos valores observados naqueles que receberam a dieta com 2.400 ppm de zinco na forma inorgânica. A suplementação da dieta com zinco na forma orgânica (900 ppm) ou inorgânica (2.400 ppm) aumentou o consumo de ração e o ganho de peso de leitões nas primeiras três semanas após o desmame. A suplementação da dieta com 2.400 ppm de zinco na forma inorgânica reduziu a incidência de diarreia nas primeiras três semanas pós-desmame. No experimento 2, os níveis de cobre de fonte orgânica tiveram efeito quadrático no consumo de ração dos leitões nos períodos de 0 a 31 e de 0 a 40 dias pós-desmame. A suplementação da dieta com cobre, tanto de fonte orgânica (90 ppm) como inorgânica (240 ppm), aumenta o consumo de ração e o ganho de peso de leitões nos primeiros 40 dias pós-desmame.

Pernambuco, Rio da Prata e a crise do antigo regime na América ibérica: o “caso” de Félix José Tavares Lira

The aim of this article is to discuss conexions between Pernambuco and Rio de la Plata around the year 1817. In a more general sense, it offers a large pattern of comprehension of the indepdendences of Luso and Spanish America in terms of its mutual relationships.

Synthesis of Fructooligosaccharides in Banana `Prata` and Its Relation to Invertase Activity and Sucrose Accumulation

Levels of sucrose and total fructool igosaccha rides (FOS) were quantified in different phases of banana `Prata` ripening during storage at ambient (similar to 19 degrees C) and low (similar to 10 degrees C) temperature. Total FOS levels were detected in the first days after harvest, whereas 1-kestose remained undetectable until the sucrose levels reached approximately 200 mg/g (dry weight) in both groups. Sucrose levels increased slowly but constantly at low temperature, but they elevated rapidly when the temperature was raised to 19 degrees C. Total FOS and sucrose levels were higher in bananas stored at low temperature than in the control group. In both samples, total FOS levels were higher than those of 1-kestose. The carbohydrate profiles obtained by HPLC and TLC suggest the presence of neokestose, 6-kestose, and bifurcose. The enzymes putatively involved in banana fructosyltransferase activity were also evaluated. Results obtained indicate that the banana enzyme responsible for the synthesis of FOS by transfructosylation is an invertase rather than a sucrose-sucrosyl transferase-like enzyme.

Eficiência de absorção e utilização de boro, zinco, cobre e manganês em mudas enxertadas de cafeeiro

O estudo da eficiência nutricional de plantas enxertadas de cafeeiro é importante para a seleção de combinações enxerto/porta-enxerto, visando atingir melhor desenvolvimento e produção. Este trabalho teve como objetivo avaliar as diferenças na eficiência de absorção e utilização de B, Zn, Cu e Mn em mudas enxertadas de cafeeiro. O experimento foi conduzido em vasos de 20 litros contendo como substrato terra, areia e esterco na proporção de 3:1:1, onde as plantas permaneceram por um período de 18 meses. Utilizaram-se como enxerto quatro genótipos de Coffea arabica L.: os cultivares Catuaí-Vermelho IAC 15 ('Catuaí 15') e Oeiras MG 6851 ('Oeiras') e os híbridos H419-10-3-4-4 ('H419') e H514-5-5-3 ('H514') do programa de melhoramento da EPAMIG/UFV. Como porta-enxerto foram empregados cinco progênies de famílias de meio-irmãos de clones de Coffea canephora Pierre ex Froenher cv. Conilon: ES 21, ES 36, ES 26, ES 23 e ES 38 do programa de melhoramento de café robusta do Incaper. O delineamento experimental foi inteiramente casualizado, com 24 tratamentos e três repetições, sendo quatro pés-francos e 20 combinações de enxertia. A eficiência nutricional das plantas variou conforme a combinação enxerto/porta-enxerto. O cultivar Oeiras não foi beneficiado por nenhuma enxertia, apresentando redução da produção total de matéria seca em todas as combinações comparativamente ao respectivo pé-franco. O cultivar Catuaí 15 foi mais eficiente na produção de matéria seca e utilização de B e Zn quando combinado com os materiais genéticos de conilon ES 26 e ES 23.

Adubação fosfatada em mudas de bananeira 'Prata anã'(AAB), cultivadas em dois Latossolos

As informações relacionadas com os efeitos do fósforo sobre o desenvolvimento de bananeiras ainda são poucas. Os objetivos deste trabalho foram avaliar os efeitos da aplicação de fósforo sobre o desenvolvimento de mudas de bananeira "Prata Anã", cultivadas em Latossolo Vermelho (LV) e Latossolo Vermelho- Amarelo (LVA, e determinar o nível crítico de fósforo. Os tratamentos foram distribuídos em um delineamento inteiramente casualizado, em esquema fatorial 8 x 2, com três repetições. Os fatores corresponderam a oito doses de fósforo (0; 50; 100; 150; 300; 450; 600; 750 mg.dm-3) e dois tipos de solos, respectivamente. A produção de matéria seca das mudas de bananeira aumentou com as aplicações de fósforo nos solos. Os níveis críticos de fósforo nos solos LV e LVA foram 18,9 e 40,2 mg dm-3, respectivamente e, nas folhas das mudas cultivadas no LV e LVA os níveis críticos de fósforo foram 0,20 e 0,31 dag kg-1, respectivamente. O fósforo foi utilizado com maior eficiência pelas mudas de bananeira cultivadas no LV.

Produção da bananeira 'Prata anã'(AAB) em função de diferentes doses e fontes de potássio

Dentre os nutrientes exigidos pela bananeira, o K é o que mais influencia na produção desta cultura. Este trabalho teve por objetivos comparar os efeitos de duas fontes de K (cloreto de potássio e sulfato de potássio) sobre a produção, bem como estimar as doses de K para obter a máxima eficiência física (MEF) e econômica (MEE) e determinar o nível crítico de K na folha da bananeira 'Prata anã' (AAB) irrigada, cultivada na região semiárida do norte de Minas Gerais, Brasil. O experimento foi realizado em Latossolo Vermelho-Amarelo (LVA), textura média. Os tratamentos foram originados do fatorial (4 x 2), sendo quatro doses de K (0, 400, 800 e 1200 kg /ha ano de K2O) e duas fontes de K (KCl e K2SO4), gerando oito tratamentos, que foram distribuídos em blocos ao acaso, com quatro repetições. Não houve diferenças entre os efeitos do KCl e K2SO4 sobre a produção da bananeira. A análise econômica demonstrou que o KCl apresentou maior viabilidade para ser utilizado como fonte de K. As doses estimadas para a MEF nos 2º e 3º ciclos de produção, utilizando-se o KCl, foram de 827 e 835 kg ha-1 ano-1 de K2O, respectivamente. Já para a MEE, as doses foram de 157 e 670 kg/ha ano de K2O, respectivamente. Os níveis críticos foliares de K, obtidos nos 2º e 3º ciclos de produção, foram de 2,85 dag kg-1 para a MEF e, para a MEE, de 2,41 e 2,80 dag kg-1, respectivamente.

Produção e caracterização da bananeira 'Prata Anã' (AAB) em dois ciclos de produção (Juazeiro, Bahia)

A avaliação do comportamento de genótipos de bananeira em diferentes ecossistemas é essencial ao programa de melhoramento genético, tornando-se de fundamental importância para o sistema produtivo. O objetivo deste trabalho foi avaliar o crescimento da bananeira 'Prata Anã' (AAB), nos 1° e 2° ciclos de produção, e os atributos físico-químicos dos frutos, no Submédio São Francisco. As mudas foram produzidas pelo processo de cultura de tecidos, na Biofábrica de Cruz das Almas, BA, e transplantadas para o campo com seis meses de idade, cultivadas no espaçamento 3 x 3 m. Foram avaliados os ciclos de produção (em dias) e, em cada ciclo, a altura das plantas, o perímetro do pseudocaule e o número de folhas adultas. Quanto à produção, foram avaliadas as seguintes características: massa da matéria fresca do cacho; número de pencas e de frutos por cacho; massa da matéria fresca da 2ª penca; número, comprimento e diâmetro de frutos da 2ª penca; relação polpa/casca; firmeza; pH; sólidos solúveis (SS); acidez titulável (AT) e a relação SS/AT. Verificou-se diferença significativa para a maioria das variáveis analisadas: o segundo ciclo de produção da bananeira 'Prata Anã' foi menor do que o primeiro, sendo que, no segundo ciclo, ocorreram tendências de maior crescimento e de melhor desempenho dos caracteres que expressam a produção e a qualidade física dos frutos.

A competitividade da indústria brasileira de alumínio: avaliação e perspectivas

A indústria do alumínio é um dos setores mais competitivos do país, sendo responsável por quase 10% do saldo da balança comercial brasileira. Apenas cinco empresas disputam o mercado doméstico e aproximadamente 90% das exportações brasileiras são constituídas de metal primário. A expansão desta indústria no mercado internacional deu-se num contexto de escassez energética nos países industrializados que coincide com um período de grande retração da economia brasileira. Através da análise dos determinantes das vantagens comparativas nacionais, explicam-se as razões do elevado grau de competitividade internacional alcan.çado por este setor industrial. São também indicados alguns Importantes fatores que poderão comprometer, no futuro, a competitividade das empresas brasileiras de alumínio.