Combustion synthesis of rare earth cuprates

Rare earth cuprates, La2CuO4 Nd2CuO4, La1.8M0.2CuO4 (M=Ca.Sr) and Nd1.85Ce0.15CuO4 have been prepared by the combustion of redox mixtures containing corresponding metal nitrates and maleic hydrazide, C4H4N2O2, at 350°C. The solid combustion products are submicron size amorphous powders which on heat treatment (700°C, 30 minutes) yield crystalline single phase cuprates. Strontium doped lanthanum cuprate, La1.8Sr0.2CuO4, shows an onset of superconductivity at 36K.

Combustion synthesis and properties of fine-particle rare-earth-metal zirconates, Ln2Zr2O7

Fine-particle rare-earth-metal zirconates, Ln2Zr2O7, where Ln = La, Ce, Pr, Nd, Sm, Gd and Dy having the pyrochlore structure have been prepared using a novel combustion process. The process employs aqueous solutions of the corresponding rare-earth-metal nitrate, zirconium nitrate and carbohydrazide/urea in the required molar ratio. When the solution is rapidly heated to 350–500 °C it boils, foams and burns autocatalytically to yield voluminous oxides. The formation of single-phase Ln2Zr2O7 has been confirmed by powder X-ray diffraction, infrared and fluorescence spectroscopy. The solid combustion products are fine, having surface areas in the range 6–20 m2 g–1. The cold-pressed Pr2Zr2O7 compact when sintered at 1500 °C, 4 h in air, achieved 99% theoretical density.

Cement stabilised rammed earth. Part A: compaction characteristics and physical properties of compacted cement stabilised soils

Rammed earth is used for load bearing walls of buildings and there is growing interest in this low carbon building material. This paper is focused on understanding the compaction characteristics and physical properties of compacted cement stabilised soil mixtures and cement stabilised rammed earth (CSRE). This experimental study addresses (a) influence of soil composition, cement content, time lag on compaction characteristics of stabilised soils and CSRE and (b) effect of moulding water content and density on compressive strength and water absorption of compacted cement stabilised soil mixes. Salient conclusions of the study are (a) compaction characteristics of soils are not affected by the addition of cement, (b) there is 50% fall in strength of CSRE for 10 h time lag, (c) compressive strength of compacted cement stabilised soil increases with increase in density irrespective of moulding moisture content and cement content, and (d) compressive strength increases with the increase in moulding water content and compaction of CSRE on the wet side of OMC is beneficial in terms of strength.

Cement stabilised rammed earth. Part B: compressive strength and stress-strain characteristics

Strength and behaviour of cement stabilised rammed earth (CSRE) is a scantily explored area. The present study is focused on the strength and elastic properties of CSRE. Characteristics of CSRE are influenced by soil composition, density of rammed earth, cement and moisture content. The study is focused on examining (a) role of clay content of the soil on strength of CSRE and arriving at optimum clay fraction of the soil mix, (b) influence of moisture content, cement content and density on strength and (c) stress-strain relationships and elastic properties for CSRE. Major conclusions are (a) there is considerable difference between dry and wet compressive strength of CSRE and the wet to dry strength ratio depends upon the clay fraction of soil mix and cement content, (b) optimum clay fraction yielding maximum compressive strength for CSRE is about 16%, (c) strength of CSRE is highly sensitive to density and for a 20% increase in density the strength increases by 300-500% and (d) in dry state the ultimate strain at failure for CSRE is as high as 1.5%, which is unusual for brittle materials.

Challenges in Earth sciences: the 21st century

The 21st century poses many challenges for global sustainability. Among them, most importantly, the human race will encounter scarcity of raw materials and conventional energy resources. And, India may have to take the brunt of these problems as it is going to be the most populated region of the world with concomitant increase in energy demand and requirement of other resources. India will be the testing ground for introducing newer ways of green technology and innovative principles of resource management and utilization. With the vagaries of potential climate change gathering clouds in the background, Earth sciences will have a special and predominant role in guiding the society in prioritizing our resource discovery, utilization and their consumption and the upkeep of environment. On the fundamental level, Earth sciences are going through a most exciting phase of development as a born-again science. Technological breakthroughs including the satellite-based observations augur well for gaining new insights into Earth processes. A set of exciting fundamental problems that are globally identified will set the stage for an exhilarating period of new discoveries. Improvements in numerical and computer-based techniques will assist in modelling of Earth processes to unprecedented levels. India will have to take special effort in improving the existing experimentation facilities in the Earth science departments of the country, and also the general level of Earth science education to meet the global standards. This article presents an Earth science vision for the 21st century in an Indian context.

High-temperature reactions of alkali and plagioclase feldspars with alkali and alkaline-earth chlorides-formation of celsian

High-temperature reactions (Ca 900-degrees-C) involving albite, K-feldspar or plagioclase and K, Ba-or K, Sr chlorides were experimentally studied. These experiments reveal that the reaction between K-exchanged albite, potash feldspar, or plagioclase and Ba-chloride/Ba-K chloride results in the formation of celsian by the breakdown of the starting feldspar structure above 800-degrees-C. Sr-feldspar does not form under similar conditions. A size-effect of the large M-site cation appears to be responsible for the formation of celsian. The reaction between K-feldspar and barium chloride may be used as a method for synthesizing celsian.

Structural Behavior of Story-High Cement-Stabilized Rammed-Earth Walls under Compression

A rammed-earth wall is a monolithic construction made by compacting processed soil in progressive layers in a rigid formwork. There is a growing interest in using this low-embodied-carbon building material in buildings. The paper investigates the strength and structural behavior of story-high cement-stabilized rammed-earth (CSRE) walls, reviews literature on the strength of CSRE, and discusses results of the compressive strength of CSRE prisms, wallettes, and story-high walls. The strength of the story-high wall was compared with the strength of wallettes and prisms. There is a nearly 30% reduction in strength as the height-to-thickness ratio increases from about 5 to 20. The ultimate compressive strength of CSRE walls predicted using the tangent modulus theory is in close agreement with the experimental values. The shear failures noticed in the story-high walls resemble the shear failures of short-height prism and wallette specimens. The paper ends with a discussion of structural design and characteristic compressive strength of CSRE walls. DOI: 10.1061/(ASCE)MT.1943-5533.0000155. (C) 2011 American Society of Civil Engineers.

Magnetic properties of rare earth nickelates of the Ln(2)BaNiO(5) family

Rare-earth nickelates Ln(2)BaNi(1-x)Cu(2)O(5), Ln = Nd and Dy, and Dy2-xYxBaNiO5 have been synthesized in order to investigate the effect of substitution of Ni by Cu and Dy by nonmagnetic Y on the magnetic properties of the nickelates. In Ln(2)BaNi(1-x)Cu(x)O(5), the nickelate structure (x=0.0) changes to the cuprate structure (x=1.0) at a specific composition (x=0.3). The Neel temperature of Nd2BaNi1-xCuxO5 decreases continuously with increase in x upto x=0.3 (T-N = 18K); when x > 0.3, the materials are paramagnetic down to 20K. The mu(eff) in Nd2BaNi1-xCxO5 essentially corresponds to the contribution of the Nd ions. In Dy2-xYxBaNiO5, the Neel temperature decreases from 40K when x=0.0 to 24K when x=1.5. The compositions with 1.5 less than or equal to x less than or equal to 2 (including the x=1.95 composition) are paramagnetic down to 20K, unlike Y2BaNiO5 (x=2.0) which exhibits a T-N of 370K. Even the smallest concentration of paramagnetic Dy seems to destroy the antiferromagnetic Ni-O-Ni chains in Y2BaNiO5.

New uniform solid catalyst for the low-temperature oxidation of carbon monoxide: A triple-layered rare earth perovskite containing Co and Cu ions

Oxygen reactivity and catalytic activity of the cobalt-containing layered defect perovskites, YBa2Cu2CoO7+delta and LaBa2Cu2CoO7+delta, in comparison with LaBa2Cu3O7-delta have been investigated employing temperature-programmed desorption (TPD) and temperature-programmed surface reactions (TPSR) in the stoichiometric and catalytic mode using carbon monoxide as a probe molecule. TPD studies showed evidence for the presence of two distinct labile oxygen species, one at (0 0 1/2) sites and the other at (0 1/2 0) sites in LaBa2Cu2CoO7+delta against a single labile species at (0 1/2 0) in the case of two other oxides. The activation energies for the catalytic oxidation of carbon monoxide by oxygen over LaBa2Cu3O7-delta, YBa2Cu2CoO7+delta, and LaBa2Cu2CoO7+delta have been estimated to be 24.2, 15.9, and 13.6 kcal/mol, respectively. The reactivity and catalytic activity of the oxide systems have been interpreted in terms of the structural changes brought about by substituents, guided by a directing effect of the larger rare earth cation. TPSR profiles, structural analysis, and infrared spectroscopic investigations suggest that the oxygen present at (0 0 1/2) sites in the case of LaBa2Cu2CoO7+delta is accessible to catalytic oxidation of CO through a Mars-Van Krevelen pathway. Catalytic conversion of CO to CO2 over LaBa2Cu2CoO7+delta occurs at 200 degrees C. The enhanced reactivity is explained in terms of changes brought about in the coordination polyhedra around transition metals, enhanced basal plane oxygen diffusivity, and redox potentials of the different transition metal cations.

Synthesis, structure and IR absorption studies of LnBaCuCoO(5) (Ln equal earth) oxides

A series of oxides LnBaCuCoO(5) (Ln = Pr, Nd, Sm, Dy, Gd, Ho and Er) have been synthesized by ceramic method. The oxides crystallize in a tetragonal structure, isostructural to YBaCuCoO5. All the oxides in the series are semiconducting. IR spectra of these oxides show distinct absorption bands at 630 cm(-1), 550 cm(-1) and 330 cm(-1) which are assigned to E, A(2) and A(1) modes respectively. Doping of holes in these oxides, by calcium substitution in Er1-xCaxBaCuCoO5-x (up to x similar or equal to 0.3) was done but, these oxides did not show metallic behaviour.

Synthesis and properties of rare earth doped lamp phosphors

Red, blue and green emitting lamp phosphors such as EU(3+) doped Y2O3 (red phosphor), EU(2+) doped Ba0.64Al12O18.64, BaMgAl10O17 and BaMg2Al16O27 (blue phosphors) and Ce0.67Tb0.33MgAl11O19 and Eu2+, Mn2+ doped BaMgAl10O17 (green phosphors) have been prepared by the combustion of the corresponding metal nitrates (oxidizer) and oxalyl dihydrazide/urea/carbohydrazide (fuel) mixtures at 400 degrees-500 degrees C within 5 min. The formation of these phosphors has been confirmed by their characteristic powder X-ray diffraction patterns and fluorescence spectra. The phosphors showed characteristic emission bands at 611 nm (red emission), 430-450 nm (blue emission) and 515-540 nm (green emission). The fine-particle nature of the combustion derived phosphors has been investigated using powder density, particle size and BET surface area measurements.

The nature of charge ordering in rare earth manganates and its strong dependence on the size of the A-site cations

Charge ordering in rare earth manganates of the type Ln(0.5)A(0.5)MnO(3) (Ln = rare earth, A = alkaline earth) is highly sensitive to the average radius of the A-site cations, [r(A)]. Tn the small [r(A)] regime (e.g., Y0.5Ca0.5MnO3), charge ordering occurs in the paramagnetic state, the transformation to an antiferromagnetic state occurring at still lower temperatures. At moderate [r(A)] values (e.g., Nd0.5Sr0.5MnO3), a ferromagnetic metallic state transforms to a charge-ordered antiferromagnetic state with cooling. These two distinct types of charge ordering and associated properties are explained in terms of the variation of the exchange couplings J(FM) and J(AFM) with [r(A)] and the invariance of the single-ion Jahn-Teller energy with [r(A)]. A qualitative temperature-[r(A)] phase diagram, consistent with the experimental observations, has been constructed to describe the properties of the manganates in the different [r(A)] regimes. (C) 1997 Academic Press.

Nonlinear electrical conduction and broad band noise in the charge-ordered rare earth manganate Nd0.5Ca0.5MnO3

Measurements of the dc transport properties and the low-frequency conductivity noise in films of charge-ordered Nd0.5Ca0.5MnO3 grown on Si substrate reveal the existence of a threshold field in the charge-ordered regime beyond which strong nonlinear conduction sets in along with a large broad band conductivity noise. Threshold-dependent conduction disappears as T --> T-CO, the charge-ordering temperature. This observation suggests that the charge-ordered state gets depinned at the onset of the nonlinear conduction. (C) 1999 American Institute of Physics. [S0003-6951(99)05247-X].

Studies on strontium substituted rare earth manganites

Sintering, electrical conductivity and thermal expansion behaviour of combustion synthesised strontium substituted rare earth manganites with the general formula Ln(1-x)Sr(x)MnO(3) (Ln = Pr, Nd and Sm; x = 0, 0.16 and 0.25) have been investigated as solid oxide fuel cell cathode materials. The combustion derived rare earth manganites have surface area in the range of 13-40 m(2)/g. Strontium substitution increases the electrical conductivity values in all the rare earth manganites. With the decreasing ionic radii of rare earth ions, the conductivity value decreases. Among the rare earth manganites studied, (Pr/Nd)(0.75)Sr0.25MnO3 show high electrical conductivity ( > 100 S/cm). The thermal expansion coefficients of Pr0.75Sr0.25MnO3 and Nd0.75Sr0.25MnO3 were found to be 10.2 x 10(-6) and 10.7 x 10(-6) K-1 respectively, which is very close to that of the electrolyte (YSZ) used in solid oxide fuel cells. (C) 1999 Elsevier Science B.V. All rights reserved.