Changes in pH at the dentin surface in roots obturated with calcium hydroxide pastes

The purpose of this study was to determine the pH, after defined periods of time, in cavities prepared in the facial surface of the cervical, middle, and apical regions of roots obturated with calcium hydroxide pastes. Root canal instrumentation was performed on 40 recently extracted, single-rooted human teeth. Cavities 1.5 mm in diameter and 0.75 mm in depth were prepared in the cervical, middle, and apical regions of the facial surface of each root. Teeth were randomly divided into four groups. One group was left unobturated and served as a control. The three remaining groups were obturated with either aqueous calcium hydroxide, calcium hydroxide mixed with camphorated monochlorophenol, or Pulpdent pastes. Access cavities and apical foramina were closed with Cavit. Each tooth was stored individually in a vial containing unbuffered isotonic saline. pH at the surface was measured in the cervical, middle, and apical cavities at 0 and 3, 7, 14, 21, 28, 45, 60, 90, and 120 days. Results indicate that hydroxyl ions derived from calcium hydroxide pastes diffused through root dentin at all regions over the experimental period of 120 days. The pattern of pH change at the tooth surface was similar in all regions of the root, regardless of the type of calcium hydroxide paste used. This was a rapid rise in pH from a control value of pH 7.6, to greater than pH 9.5 by 3 days, followed by a small decline to pH 9.0 over the next 18 days, before finally rising and remaining at, or above pH 10.0 for the remainder of the experimental period. Pulpdent paste in the apical region was the only exception in this pattern, producing a pH rise nearly one full unit below the other pastes, pH 9.3. These results indicate that, for all pastes tested, a high pH is maintained at the root surface for at least 120 days. Copyright © 1996 by The American Association of Endodontists.

Reaction of rat connective tissue to implanted dentin tubes filled with mineral trioxide aggregate or calcium hydroxide

This study was conducted to observe the rat subcutaneous connective tissue reaction to the implanted dentin tubes filled with calcium hydroxide or mineral trioxide aggregate. The animals were sacrificed after 7 and 30 days, and the specimens were prepared for morphological study. Some undecalcified specimens were prepared for histological analysis with polarized light and Von Kossa technique for calcium. The results were similar for both studied materials. At the tube openings, there were Von Kossa-positive granules that were birefringent to polarized light. Next to these granulations, there was an irregular tissue like a bridge that was Von Kossa-positive. The dentin walls of the tubes exhibited in the tubules a structure highly birefringent to polarized light, usually like a layer and at different depths. It is possible that the mechanism of action of both materials has some similarity. Copyright © 1999 by The American Association of Endodontists.

Effect of whitening agents on dentin bonding

Background: Several studies have shown a reduction in enamel bond strengths when the bonding procedure is carried out immediately after vital bleaching with peroxides. This reduction in bond strengths has become a concern in cosmetic dentistry with the introduction of new in-office and waiting-room bleaching techniques. The aim of this in vitro study was to evaluate the effect of three bleaching regimens: 35% hydrogen peroxide (HP), 35% carbamide peroxide (CP), and 10% CP, on dentin bond strengths. Materials and Methods: One hundred and twenty fresh bovine incisors were used in this study. The labial surface of each tooth was ground flat to expose dentin and was subsequently polished with 600-grit wet silicon carbide paper. The remaining dentin thickness was monitored and kept at an average of 2 mm. The teeth were randomly assigned to four bleaching regimens (n = 30): (A) control, no bleaching treatment; (B) 35% HP for 30 minutes; (C) 35% CP for 30 minutes; and (D) 10% CP for 6 hours. For each group, half of the specimens (n = 15) were bonded with Single Bond/Z100 immediately after the bleaching treatment, whereas the other half was bonded after the specimens were stored for 1 week in artificial saliva at 37°C. The specimens were fractured in shear using an Instron machine. Results: For the groups bonded immediately after bleaching, one-way analysis of variance (ANOVA) followed by the Duncan's post hoc test revealed a statistically significant reduction in bond strengths in a range from 71% to 76%. For the groups bonded at 1 week, one-way ANOVA showed that group B (35% HP for 30 min) resulted in the highest bond strengths, whereas 10% CP resulted in the lowest bond strengths. Student's t-test showed that delayed bonding resulted in a significant increase in bond strengths for groups B (35% HP) and C (35% CP); whereas the group bleached with 10% CP (group D) remained in the same range obtained for immediate bonding. Storage in artificial saliva also affected the control group, reducing its bond strengths to 53% of the original. ©2000 BC Decker Inc.

Reaction of rat connective tissue to implanted dentin tube filled with mineral trioxide aggregate, Portland cement or calcium hydroxide.

The subject of this study was to observe the rat subcutaneous connective tissue reaction to implanted dentin tubes filled with mineral trioxide aggregate, Portland cement or calcium hydroxide. The animals were sacrificed after 7 or 30 days and the undecalcified specimens were prepared for histological analysis with polarized light and Von Kossa technique for mineralized tissues. The results were similar for the studied materials. At the tube openings, there were Von Kossa-positive granules that were birefringent to polarized light. Next to these granulations, there was an irregular tissue like a bridge that was Von Kossa-positive. The dentin walls of the tubes exhibited in the tubules a structure highly birefringent to polarized light, usually like a layer and at different depths. The mechanism of action of the studied materials has some similarity.

Histologic Evaluation of the Osteoinductive Property of Autogenous Demineralized Dentin Matrix on Surgical Bone Defects in Rabbit Skulls Using Human Amniotic Membrane for Guided Bone Regeneration

The aim of this investigation was to evaluate the osteoinductive property of autogenous demineralized dentin matrix (ADDM) on experimental surgical bone defects in the parietal bone of rabbits using the guided bone regeneration (GBR) technique incorporating human amniotic membrane (HAM). Thirty-six rabbits were divided into 2 groups, HAM and ADDM+HAM. It was possible to conclude that HAM did not interfere with bone repair and was resorbed. Slices of ADDM induced direct bone formation and were incorporated by the newly formed bone tissue and remodeled. The bone defects healed faster in the ADDM+HAM group than in the group with HAM only.

Reaction of rat connective tissue to implanted dentin tubes filled with a white mineral trioxide aggregate.

The purpose of this paper was to study the reaction of rat subcutaneous connective tissue to the implantation of dentin tubes filled with white mineral trioxide aggregate (MTA), a material that will be marketed. The tubes were implanted into rat subcutaneous tissue and the animals were sacrificed after 7 and 30 days. The undecalcified pieces were prepared for histological analysis with polarized light and von Kossa technique for mineralized tissues. Granulations birefringent to polarized light and an irregular structure like a bridge were observed next to the material; both were von Kossa positive. Also, in the dentin wall tubules a layer of birefringent granulations was observed. The results were similar to those reported for gray MTA, indicating that the mechanisms of action of the white and gray MTA are similar.

Cariostatic effect of fluoride-containing restorative systems associated with dentifrices on root dentin

Objective. The aim of this in vitro study was to evaluate the interaction between two sources of fluoride (restorative systems and dentifrices) in inhibiting artificial root caries development. Methods. One hundred and eighty tooth segments were embedded in polyester resin, and sanded flat. Cylindrical cavities 1.0 mm-deep and 1.5 mm-diameter were prepared in root dentin and randomly restored by fluoride-containing restorative systems: Ketac-fil/Espe (Ke), Fuji II LC/GC Corp (Fj), F2000/3M (F2), Surefil/Dentsply (Su) or a control: Filtek Z250/3M (Z2). Ten experimental groups were made to test the association among the five restorative systems and two dentifrices: with F - (Sensodyne Baking Soda) or without F- (Sensodyne Original) (n = 18). After surface polishing, a 1 mm-wide margin around the restorations was demarcated and initial dentin surface Knoop microhardness values (KHNi) were obtained. The specimens were submitted to a pH-cycling model, and to applications of slurries of dentifrice. Afterwards the final dentin surface Knoop microhardness values (KHNf) were measured. Results. The differences between KHNi and KHNf, and the covariate KHNi were considered by the ANCOVA and Tukey's test (α = 0.05). The interaction between restorative system and dentifrice was statistically significant (p = 0.0026). All restorative systems provided some protection against artificial caries challenge when associated with the fluoride-containing dentifrice treatment. The means (standard deviation) of reductions in Knoop hardness values for systems associated with the fluoride-containing dentifrice were: Ke: 40.0(1.02)a, Fj: 41.9(1.02)b, F2: 43.3(1.04)c, Su: 43.5(1.00)c, Z2: 44.0(1.02)c; and with the non-fluoride-containing dentifrice were: Ke: 42.9(1.02)a, Fj: 44.7(1.01)b, F2: 45.2(1.09)bc, Su: 46.0(0.99)c, Z2: 46.6(0.99)c (statistical differences were expressed by different letters). Conclusion. The cariostatic effect shown by the fluoride-containing dentifrice could enhance that shown by Ketac-fil and Fuji II LC, and could mask that shown by F2000. © 2002 Elsevier Science Ltd. All rights reserved.

Effect of 2% chlorhexidine on microtensile bond strength of composite to dentin

Purpose: To evaluate the effect of 2% chlorhexidine on the microtensile bond strength of composite resin to dentin treated with three dentin bonding systems. Materials and Methods: Flat dentinal surfaces were prepared in 24 extracted human third molars. Teeth were randomly divided into 8 distinct experimental groups according to the adhesive applied (Prime & Bond NT, Single Bond and Clearfil SE Bond), the application (yes/no) of chlorhexidine, and the time point at which it was applied (before or after acid etching the dentin). Composite resin blocks were built up over treated surfaces, and teeth were then stored in water at 37°C for 24 h. Samples were thermocycled, stored under the same conditions, and then vertically sectioned, thus obtaining specimens with 1.0 ± 0.1 mm2 cross-sectional area. Specimens were stressed in tension at 0.5 mm/min crosshead speed. Bond strength results were evaluated using a one-way ANOVA (p < 0.05). The modes of failures were verified using optical microscopy. Dentin disks were obtained from 3 additional teeth treated in the same manner for observation under SEM. The most representative samples of fractured specimens were also observed under SEM. Results: No statistically significant differences of bond strength values were found between any groups. Failures occurred mainly within the bond; exclusively adhesive fractures (adhesive-dentin) were not observed. Conclusion: The 2% chlorhexidine solution, applied before or after acid etching of the dentin, did not interfere with the microtensile bond strength of composite resin to the dentin treated with Prime & Bond NT, Single Bond, or Clearfil SE Bond bonding systems.

Effects of dentin collagen removal on microleakage of bonded restorations

Purpose: To evaluate the effects of removing dentin collagen exposed by acid etching on the microleakage of bonded restorations with and without flowable composite application and submitted to thermocycling and long-term water storage. Materials and Methods: Standardized Class V cavities were prepared in 180 bovine incisors. They were randomly assigned to three groups according to the adhesive technique used. Conventional group (C): Single Bond was applied according to the manufacturer's instructions and Z250 composite was placed. Hypochlorite group (H): After acid etching a 10% NaOCl aqueous solution was applied for 1 min, then Single Bond and Z250 were applied. Hypochlorite and Flowable group (HF): Similar to group H, but following adhesive application, a thin layer of Natural Flow flowable composite was applied before the Z250. Each group was divided into three subgroups (0, 6, 12), which remained immersed in distilled water for 24 h or 6 or 12 months and underwent 500, 1500 or 2500 thermal cycles, respectively. At the end of each storage time, the specimes were stained with silver nitrate, decalcified, immersed in methyl salicylate for clearing and observed under a stereomicroscope to determine microleakage (scores 0 to 4). The data were analyzed using the Kruskal-Wallis and the Multiple Comparison Tests (α = 0.05). Results: After 12 months, every group showed significant increases in microleakage. There was no significant difference between Groups H and HF for the three different periods of time, but they showed statistically less microleakage than Group C. Conclusion: The removal of dentinal collagen reduced the marginal microleakage when compared to the conventional technique. The use of the flowable composite did not produce significant effects. No technique was completely effective in preventing microleakage.

Histomorphometric analysis of homogenous demineralized dentin matrix as osteopromotive material in rabbit mandibles

Purpose: The aim of this work was to evaluate the effectiveness of homogenous demineralized dentin matrix (HDDM) slices in surgical bone defects created in the mandibles of rabbits and occluded with a polytetrafluoroethylene (PTFE) membrane in the promotion of bone growth. Materials and Methods: Surgical bone defects were created in 36 adult rabbits and divided into 4 groups: bone defect (control), bone defect with PTFE membrane, bone defect with HDDM, and bone defect with both HDDM and a PTFE membrane (HDDM + PTFE). The rabbits were sacrificed after 30, 60, and 90 days, and the bone defects were examined histologically and by histomorphometric analysis (analysis of variance and the Tukey test). Results: The volume of newly formed bone matrix was significantly greater in the HDDM and HDDM + PTFE groups than in the control and PTFE groups. The discrete inflammatory reaction found in the HDDM and HDDM + PTFE groups did not prevent the osteopromotive activity of the dentin matrix. Discussion: HDDM slices were biocompatible and were resorbed during the bone remodeling process. They stimulated the newly formed bone until 30 days after implantation. Conclusion: Bone repair was accelerated in the bone defects treated with HDDM in comparison to the control group.

Effect of cyclic compressive loading on the bond strength of an adhesive system to dentin after collagen removal

Purpose: The objective of this study was to verify the effect of cyclic compressive loading on the shear bond strength of an adhesive system following collagen removal. Materials and Methods: Sixty bovine teeth were divided into 4 groups based on the adhesive procedure used: groups 1 and 2 - etching with 35% phosphoric acid and application of the Single Bond adhesive system; groups 3 and 4 - after etching, a 10% sodium hypochlorite solution was applied for 1 min before the application of the adhesive. In all the specimens, a Z100 resin cylinder was built up over the bond area. Groups 2 and 4 were submitted to 500,000 cycles with a load of 100 N. Results: The mean values for the shear bond test (MPa) were: group 1: 7.37 ± 1.15; group 2: 5.72 ± 1.66; group 3: 5.95 ± 1.21; group 4: 3.66 ± 1.12. There was no difference between groups 1 and 2 (p > 0.01). Between groups 1 and 3, 2 and 4, and 3 and 4 there was a significant difference (p < 0.01). The majority of the specimens demonstrated an adhesive failure. Conclusion: The application of sodium hypochlorite on dentin decreased the values of shear bond strength, as did the load cycling in the group treated with sodium hypochlorite.

Shear bond strength of adhesive systems to enamel and dentin. Thermocycling influence

Objectives: The purpose of the this study was to evaluate the influence of thermocycling on shear bond strength on bovine enamel and dentin surfaces of different adhesive systems. Methods: Thirty sound bovine incisors were sectioned in mesiodistal and inciso-cervical direction obtaining 60 incisal surfaces (enamel) and 60 cervical surfaces (dentin). Specimens were randomly assigned to 3 groups of equal size (n = 40), according to the adhesive system used: I-Single Bond; II-Prime & Bond NT/NRC; III-One Coat Bond. After 24-h storage in distilled water at 37 o C, each main group was divided into two subgroups: A- specimens tested after 24 h storage in distilled water at 37°C; B - specimens submitted to thermocycling (500 cycles). Shear bond strength tests were performed. Data were submitted to ANOVA and Tukey test. Results: Means (MPa) of different groups were: I-AE-16.96, AD-17.46; BE-21.60, BD-12.79; II-AE-17.20, AD-11.93; BE-20.67, BD-13.94; III-AE-25.66, AD-17.53; BE-24.20, BD-19.38. Significance: Thermocycling did not influence significantly the shear bond strength of the tested adhesive systems; enamel was the dental substrate that showed larger adhesive strength; One Coat Bond system showed the best adhesive strength averages regardless of substrate or thermocycling. © 2005 Springer Science + Business Media, Inc.

Fatigue resistance of the bond of a glass-infiltrated alumina ceramic to human dentin

Purpose: To evaluate the fatigue resistance of the bond between dentin and glass-infiltrated alumina ceramic, using different luting protocols. Materials and Methods: The null hypothesis is that the fatigue resistance varies with the luting strategy. Forty blocks of In-Ceram Alumina were prepared, and one surface of each block was abraded with 110-μm aluminum oxide particles. Then, the blocks were luted to flat dentin surfaces of 40 human third molars, using 4 different luting strategies (luting system [LS]/ceramic surface conditioning [CSC]) (n=10): (G1) [LS] RelyX-Unicem/[CSC] airborne abrasion with 110-μm Al2O3 particles; (G2) [LS] One-Step + Duo-Link (bis-GMA-based resin)/[CSC] etching with 4% hydrofluoric acid + silane agent; (G3) [LS] ED-Primer + Panavia F (MDP-based resin)/[CSC] Al2O 3; (G4) [LS] Scotchbond1+RelyX-ARC (bis-GMA-based resin)/[CSC] chairside tribochemical silica coating (air abrasion with 30-μm SiO x particles + silane). After 24 h of water storage at 37°C, the specimens were subjected to 106 fatigue cycles in shear with a sinusoidal load (0 to 21 N, 8 Hz frequency, 37°C water). A fatigue survivor score was given, considering the number of the fatigue cycles until fracture. The failure modes of failed specimens were observed in a SEM. Results: G3 (score = 5.9, 1 failure) and G4 (score = 6, no failures) were statistically similar (p = 0.33) and had significantly higher fatigue resistance than G1 (score = 3.9, 5 failures) and G2 (score = 3.7, 6 failures) (p < 0.03). SEM analysis of fractured specimens of G1 and G2 showed that almost all the failures were between ceramic and cement. Conclusion: The MDP-based resin cement + sandblasting with Al2O3 particles (G3) and bis-GMA-based resin cement + tribochemical silica coating (G4), both using the respective dentin bonding systems, were the best luting protocols for the alumina ceramic. The null hypothesis was confirmed.

Densitometric analysis of the autogenous demineralized dentin matrix on the dental socket wound healing process in humans

The aim of this study was to evaluate the effects of the autogenous demineralized dentin matrix (ADDM) on the third molar socket wound healing process in humans, using the guided bone regeneration technique and a polytetrafluoroethylene barrier (PTFE). Twenty-seven dental sockets were divided into three groups: dental socket (Control), dental socket with PTFE barrier (PTFE), and dental socket with ADDM slices associated to PTFE banier (ADDM + PTFE). The dental sockets were submitted to radiographic bone densitometry analysis and statistical analysis on the 15th, 30th, 60th and 90th days using analysis of variance (ANOVA) and Tukey's test (p ≤ 0.05). The radiographic analysis of the ADDM + PTFE group showed greater homogeneity of bone radiopacity than the Control group and the PTFE group, during all the observation times. The dentin matrix gradually disappeared from the dental socket during the course of the repair process, suggesting its resorption during the bone remodeling process. It was concluded that the radiographic bone density of the dental sockets treated with ADDM was similar to that of the surrounding normal bone on the 90th day. The ADDM was biocompatible with the bone tissue of the surgical wounds of human dental sockets. The radiographic analysis revealed that the repair process was discreetly faster in the ADDM + PTFE group than in the Control and PTFE groups, although the difference was not statistically significant. In addition, the radiographic image of the ADDM + PTFE group suggested that its bone architecture was better than that of the Control and PFTE groups.

Does the thickness of the resin cement affect the bond strength of a fiber post to the root dentin?

This study aimed to evaluate the influence of cement thickness on the bond strength of a fiber-reinforced composite (FRC) post system to the root dentin. Eighteen single-rooted human teeth were decoronated (length: 16 mm), the canals were prepared, and the specimens were randomly allocated to 2 groups (n = 9): group 1 (low cement thickness), in which size 3 FRC posts were cemented using adhesive plus resin cement; and group 2 (high cement thickness), in which size 1 FRC posts were cemented as in group 1. Specimens were sectioned, producing 5 samples (thickness: 1.5 mm). For cement thickness evaluation, photographs of the samples were taken using an optical microscope, and the images were analyzed. Each sample was tested in push-out, and data were statistically analyzed. Bond strengths of groups 1 and 2 did not show significant differences (P = .558), but the cement thicknesses for these groups were significantly different (P < .0001). The increase in cement thickness did not significantly affect the bond strength (r2 = 0.1389, P = .936). Increased cement thickness surrounding the FRC post did not impair the bond strength.