Preparation of glasses and glass ceramics of heavy metal oxides containing silver: optical, structural and electrochemical properties

Silver containing heavy metal oxide glasses and glass ceramics of the system WO3-SbPO4-PbO-AgCl with different AgCl contents have been prepared and their thermal, structural and optical properties characterized. Glass ceramics containing metallic silver nanoparticles have been prepared by annealing glass samples at temperatures above the glass transition and analyzed by transmission electron microscopy and energy dispersive X-ray microanalysis. The presence of the metallic clusters has been also confirmed by the observation of a surface plasmon resonance band in the visible range. Cyclic voltammetric measurements indicated the presence of metallic silver into the glasses, even before to perform the thermal treatment.

Synthesis and Structural Studies of Er3+ Containing Lead Cadmium Fluoroborate Glasses and Glass-Ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Lead-cadmium oxyfluoride glasses and glass-ceramics

Glasses and glass-ceramics have been obtained in oxyfluoride systems involving lead and cadmium fluorides and one of the well-known glass former oxides SiO2, B2O3 and TeO2. Vitreous domains were established and a wide range of compositions including high heavy metal contents lead to stable glasses. Amorphous structures have been studied by short-range order spectroscopy techniques (Raman scattering and x-ray absorption) and molecular basic structures have been identified. Besides the usual oxides, the role of glass former could also be proposed for cadmium ions. Special attention has been paid for crystallization process. Cubic lead fluoride, cubic lead tellurite, tetragonal tellurium oxide and a solid solution of the type Pb1-xCdxF2 are obtained as crystallization products depending on the composition and temperature of heat treatments. Pb1-xCdxF2 solid solutions are well known superionic materials and obtaining this solid solution as a crystal phase could be very interesting for applications concerning ionic electrical conduction properties. The addition of rare earth ions led to the control of the crystallization process. In the presence of the nucleating ion only the cubic form beta-PbF2 was identified. Rare earth ions are present in the crystal phase and crystal-like spectroscopic properties were observed suggesting interesting applications for these perfectly transparent glass ceramics in photonics.

SiO2-PbF2-CdF2 glasses and glass ceramics

Lead-Cadmium fluorosilicate stable glasses were prepared and the vitreous domain region determined in the composition diagram. Characteristic temperatures were obtained from thermal analysis and the structural studies performed illustrate clearly the role played by lead atoms in the glasses crystallization behavior and the glass-forming ability of cadmium atoms. The occurrence of either a cubic lead fluoride or a lead-cadmium fluoride solid solution in crystallizing samples was found to be dependent on Er3+ doping. The optically active ions were found to concentrate in the crystalline phase and in fact play the role of nucleating agent as suggested from X-ray diffraction and EXAFS measurements. (C) 2002 Elsevier B.V. Ltd. All rights reserved.

Conductivity and F-19 NMR in PbGeO3-PbF2-CdF2 glasses and glass-ceramics

The temperature dependence of the electrical conductivity and the F-19 nuclear magnetic resonance (NMR) of PbGeO3-PbF2CdF, glasses and glass ceramics are investigated. The measured conductivity values of the glasses are above 10(-5) Skin at 500 K, and increase with increasing lead fluoride content. Activation energies extracted from the conductivity data are in the range 0.59-0.73 eV. Results are consistent with the hypothesis that in these oxyfluoride glasses lead fluoride rich clusters are dispersed in a metagermanate based matrix providing increasing mobility pathways for conducting ions. The conductivity of a sample of the glass ceramic of composition (mol%) 60PbGeO(3-)20PbF(2)-20CdF(2) was found to be smaller than that in the corresponding glass, suggesting that there are poor ionic conducting regions in the interface between the nanometer sized crystals. The temperature dependence of the F-19 relaxation times, measured in the range 100-800 K, exhibit the qualitative features associated with high fluorine mobility in both, glass and glass ceramics materials. We suggest that de-convolution of the spin-lattice relaxation rates observed in the glass ceramics shows that the observed high temperature rate maximum is associated with the diffusional motions of the fluorine ions in beta-PbF2 crystals. (c) 2005 Elsevier B.V. All rights reserved.

Structural and spectroscopic study of oxyfluoride glasses and glass-ceramics using europium ion as a structural probe

Transparent oxyfluoride glasses and beta-PbF(2) nanocrystals containing glass-ceramics were prepared with varying Eu(3+) content (0.3, 0.4, 0.5 and 0.6%). The effect of Eu(3+) content on the preparation of glass-ceramics was investigated. From differential scanning calorimetry, the T(x)-T(g)(T(x)-temperature of the onset of crystallization; T(g)-glass transition temperature) parameter for glasses has shown slight variation, and an exothermic peak near T(g) called the ceramization temperature (T(c)) has been observed. Heat treatments were performed at this temperature to obtain transparent glass-ceramics containing beta-PbF(2) nanocrystals, identified by x-ray diffraction. Heat treatments for different periods of time were performed and were observed to be very important in the control of the crystal size and of the crystallization rate. Based upon the absorption spectra, the scattering level due to the presence of beta-PbF(2) nanocrystals in the glass-ceramics was observed to be similar to that for the mother glasses. Detailed analysis of emission spectra and decay time measurements led to the identification of Eu(3+) ions as the beta-PbF(2) crystalline phase. Excitation spectra at 70 K show the interaction of Eu(3+) ions with the fluorogermanate network.

Raman and infrared investigations of glass and glass-ceramics with composition 2Na2O·1CaO·3SiO2

Precursor glass and glass-ceramics with molar composition 2Na2O·1CaO·3SiO2 are studied by infrared, conventional, and microprobe Raman techniques. The Gaussian deconvoluted Raman spectrum of the glass presents bands at 625 and 660 cm-1, attributed to bending vibrations of Si-O-Si bonds, and at 860, 920, 975, and 1030 cm-1, attributed to symmetric stretching vibrations of SiO4 tetrahedra with 4, 3, 2, and 1 nonbridging oxygens, respectively. The Raman microprobe spectrum of a highly crystallized sample presents two narrow and intense bands at about 590 and 980 cm-1, associated with vibrations of SiO4 tetrahedra with two nonbridging oxygens, in agreement with the predicted chain-like structure of crystalline metasilicates. Scanning electron microscopy shows that the crystals distributed in partially crystallized samples have a spherical shape, built up by radially oriented needle-like single crystals. The Raman microprobe spectra of these spherulites show that they still contain residual amorphous material. A comparison of Raman and infrared spectra of amorphous and highly crystallized samples is presented.

Local order around rare earth ions during the devitrification of oxyfluoride glasses

Erbium L-3-edge extended x-ray absorption fine structure (EXAFS) measurements were performed on rare earth doped fluorosilicate and fluoroborate glasses and glass ceramics. The well known nucleating effects of erbium ions for the crystallization of cubic lead fluoride (based on x-ray diffraction measurements) and the fact that the rare earth ions are present in the crystalline phase (as indicated by Er3+ emission spectra) seem in contradiction with the present EXAFS analysis, which indicates a lack of medium range structural ordering around the Er3+ ions and suggests that the lead fluoride crystallization does not occur in the nearest neighbor distance of the rare earth ion. Molecular dynamics simulations of the devitrification process of a lead fluoride glass doped with Er3+ ions were performed, and results indicate that Er3+ ions lower the devitrification temperature of PbF2, in good agreement with the experimental results. The genuine role of Er3+ ions in the devitrification process of PbF2 has been investigated. Although Er3+ ions could indeed act as seeds for crystallization, as experiments suggest, molecular dynamics simulation results corroborate the experimental EXAFS observation that the devitrification does not occur at its nearest neighbor distance. (c) 2008 American Institute of Physics.

Transparent Er3+-activated lead fluorogermanate glass ceramics

Transparent glass ceramics containing β-PbF2:Er 3+ nanocrystals were obtained through appropriate thermal treatments of a glass of molar composition 60PbGeO3-10PbF2-30CdF 2 doped with 0.5 mol% Er3+. Their optical properties, as well as upconversion processes among erbium ions in the glass and glass ceramic matrix were studied. From absorption spectra, Judd-Ofelt parameters and radiative transition rates for several excited levels were calculated. Emission spectra in the visible and NIR regions were collected, and stimulated emission cross sections were obtained by McCumber theory for the 4F 13/2→4I15/2 transition at 1.5 μm. Red and green upconversion emissions were measured in glass and glass ceramics upon excitation at 980 nm; lifetimes were measured in order to assess the upconversion mechanisms.

Evaluation of the micro-hardness and fracture toughness of amorphous and partially crystallized 3CaO center dot P2O5-SiO2-MgO bioglasses

In this work, the effect of the indentation load on the results of hardness and fracture toughness, determined by Vickers micro-hardness measurements, of some glasses and glass-ceramics has been investigated. Furthermore, in order to verify the effect of crystallinity on the results, glasses of composition 52.75 wt.% 3CaO center dot P2O5, 30 wt.% SiO2 and 17.25 wt.% MgO were fused at 1600 degrees C for 4 h and annealed at 700 degrees C for 2h, and further heat-treated at 700, 775, 800 and 900 degrees C for 4h. The obtained materials were analyzed by high resolution X-ray diffraction, HRXRD, to determine the crystallization degree in function of the heat-treatment temperature. The hardness of the different specimens was determined by Vickers' micro-hardness measurements under various loads. It has been observed that with increasing crystallization of the materials their hardness increased. Furthermore, it has been possible to verify the so-called indentation size effect (ISE), i.e. hardness decreases as the indentation depth, under higher loads, increases. This effect has been more pronounced in the glass-ceramic samples. Fracture toughness has been determined by the crack length induced by the Vickers indentations and relating them to the applied loads. Glass materials presented a fracture pattern with characteristics of cleavage, forming cracks of the half-penny shaped type, while the glass-ceramic materials exhibited crack bridging effects and Palmqvist type cracks. (C) 2011 Elsevier B.V. All rights reserved.

Cristalização de Biomateriais Vitrocerâmicos e Mineralização em Meio Fisiológico Simulado

We propose new theoretical models, which generalize the classical Avrami-Nakamura models. These models are suitable to describe the kinetics of nucleation and growth in transient regime, and/or with overlapping of nucleation and growth. Simulations and predictions were performed for lithium disilicate based on data reported in the literature. One re-examined the limitations of the models currently used to interpret DTA or DSC results, and to extract the relevant kinetic parameters. Glasses and glass-ceramics with molar formulation 0.45SiO2? (0.45-x)MgO?xK2O?0.1(3CaO.P2O5) (0?x?0.090) were prepared, crystallized and studied as potential materials for biomedical applications. Substitution of K+ for Mg2+ were used to prevent devritification on cooling, to adjust the kinetics of crystallization and to modify the in vitro behaviour of resulting biomaterials. The crystallization of the glass frits was studied by DTA, XRD and SEM. Exothermic peaks were detected corresponding to bulk crystallization of whitlockite-type phosphate, Ca9MgK(PO4)7, at approximately 900ºC, and surface crystallization of a predominant forsterite phase (Mg2SiO4) at higher temperatures. XRD also revealed the presence of diopside (CaMgSi2O6 in some samples. The predominant microstructure of the phosphate phase is of the plate-type, seemingly crystallizing by a 2-dimensional growth mechanism. Impedance spectroscopy revealed significant changes in electrical behaviour, associated to crystallization of the phosphate phase. This showed that electrical measurements can be used to study the kinetics of crystallization for cases when DTA or DSC experiments reveal limitations, and to extract estimates of relevant parameters from the dependence of crystallization peak temperature, and its width at half height. In vitro studies of glasses and glass-ceramics in acelular SBF media showed bioactivity and the development of apatite layers The morphology, composition and adhesion of the apatite layer could be changed by substitution of Mg2+ by K+. Apatite layers were deposited on the surface of glass-ceramics of the nominal compositions with x=0 and 0.09, in contact with SBF at 37ºC. The adhesion of the apatite layer was quantified by the scratch test technique, having been related with SBF?s immersion time, with composition and structure of the glass phase, and with the morphology of the crystalline phase of the glass-ceramics. The structure of three glasses (x=0, 0.045 and 0.090) were investigated by MAS-NMR ( 29Si and 31P), showing that the fraction of Q3 structural units increases with the contents of Mg, and that the structure of these glasses includes orthophosphate groups (PO43-) preferentially connected to Ca2+ ions. Mg2+ ions show preference towards the silicate network. Substitution of Mg2+ by K+ allowed one to change the bioactivity. FTIR data revealed octacalcium phosphate precipitation (Ca8H2(PO4)6.5H2O) in the glass without K, while the morphology of the layer acquires the shape of partially superimposed hemispheres, spread over the surface. The glasses with K present a layer of acicular hidroxyapatite, whose crystallinity and needles thickness tend to increase along with K content.

Nano vitrocerâmica de escória de aciaria

The manufacture of glass-ceramics is an alternative route for the commercial use of metallurgical slags. Such types of glass-ceramics may find commercial applications owing to their low cost, good mechanical properties and superior visual aspect. Besides, due to the elimination of that industrial residue from the environment and also due to the possibility of replacement of natural stones such as marbles and granites, the use of slags is an activity with strong ecological appeal. While the use of blast-furnace slags for the production of glass-ceramics is well known, the utilization of steel making slags constitutes a challenge, because these materials possess low concentration of SiO2. In this work a novel composition for producing glasses and glass-ceramics from a steelmaking slag is presented. The crystal nucleation kinetics, the characterization of the resulting microstructures for two different thermal treatments and mechanical properties of the glass-ceramics are discussed. A glass-ceramic having a marble aspect, fine volumetric crystallization, high degree of crystallization and improved mechanical strength was obtained.

Biosilicato®: histórico de uma vitrocerâmica brasileira de elevada bioatividade

This paper presents a historical of the Biosilicate®, a bioactive glass-ceramic developed at the Vitreous Materials Laboratory of the Federal University of São Carlos, Brazil. After decades of study accomplished with bioactive glasses and glass-ceramics, Biosilicate® results from a natural evolution and has similar bioactivity index, but far superior mechanical properties than of all bioactive glasses. Biosilicate® is almost fully crystalline and also exhibits much higher bioactivity than all the currently commercially available bioactive glass-ceramics. Due to its special characteristics, Biosilicate® has been successfully tested for several medical and dental applications as we thoroughly discuss in this review paper.

Preparação de vidros e vitrocerâmicas de óxidos de metais pesados contendo prata: propriedades ópticas, estruturais e eletroquímicas

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)