Homogeneous precipitation from solution by urea hydrolysis: a novel chemical route to the a-hydroxides of nickel and cobalt

Homogeneous precipitation from solution by hydrolysis of urea at elevated temperatures (T=120 degrees C) yields novel ammonia-intercalated alpha-type hydroxide phases of the formula M(OH)(x)(NH3)(0.4)(H2O)(y)(NO3)(2-x) where x=2, y=0.68 for M=Ni and x=1.85, y=0 for M=Co. These triple-layered hexagonal phases (a=3.08+/-0.01 Angstrom, c=21.7+/-0.05 Angstrom) are more crystalline than similar phases obtained by chemical precipitation or electrosynthesis. This method can be adapted as a convenient chemical route to the bulk synthesis of alpha-hydroxides.

Stabilization of α-nickel hydoxide in the presence of organic additives: chemical route to bulk synthesis

Organic molecules such as glucose or lactose mediate the synthesis and stabilize alpha-nickel hydroxide in a simple precipitation reaction, while, in the absence of these additives, beta-nickel hydroxide is formed. The additives are not incorporated in the product phase.

A template-free, combustion-chemical route to macroporous nickel monoliths displaying a hierarchy of pore sizes

Recently, we demonstrated a very general route to monolithic macroporous materials prepared without the use of templates (Rajamathi et al. J. Mater. Chem. 2001, 11, 2489). The route involves finding a precursor containing two metals, A and B, whose oxides are largely immiscible. Firing of the precursor followed by suitable sintering results in a monolith from which one of the oxide phases can be chemically leached out to yield a macroporous mass of the other oxide phase. The metals A and B that we employed in the demonstration were Ni and Zn. From the NiO-ZnO monolith that was obtained by decomposing the precursor, ZnO could be leached out at high pH to yield macroporous NiO. In the present work, we show that combustion-chemical (also called self-propagating) decomposition of a mixture of Ni and Zn nitrates with urea as a fuel yields an intimate mixture of the oxides that can be sintered and leached with alkali to form a macroporous NiO monolith. The new process that we present here thereby avoids the need for a crystalline single-source precursor. A novel and unanticipated aspect of the present work is that the combination of high temperatures and rapid quenching associated with combustion synthesis results in an intimate mixture of wurtzite ZnO and the metastable rock-salt Ni1-xZnxO where x is about 0.3. Leaching this monolith with alkali gives a macroporous mass of rock-salt Ni1-xZnxO, which upon reduction in H-2/Ar forms macroporous Ni and ZnO. There are thus two stages in the process that lead to two modes of pore formation. The first is associated with leaching of ZnO by alkali. The second is associated with the reduction of porous Ni1-xZnxO to give porous Ni and ZnO.

Pristine, adherent ultrathin gold nanowires on substrates and between pre-defined contacts via a wet chemical route

We demonstrate a simple strategy of obtaining clean, ultrathin single crystal Au nanowires on substrates and interconnecting pre-defined contacts with an insight into the growth mechanism. The pristine nature enables electron transport measurement through such ultrathin wires and opens up possibilities of exploring its properties for a wide range of applications.

Size Control and Magnetic Property Trends in Cobalt Ferrite Nanoparticles Synthesized Using an Aqueous Chemical Route

Cobalt ferrite (CoFe2O4) is an engineering material which is used for applications such as magnetic cores, magnetic switches, hyperthermia based tumor treatment, and as contrast agents for magnetic resonance imaging. Utility of ferrites nanoparticles hinges on its size, dispersibility in solutions, and synthetic control over its coercivity. In this work, we establish correlations between room temperature co-precipitation conditions, and these crucial materials parameters. Furthermore, post-synthesis annealing conditions are correlated with morphology, changes in crystal structure and magnetic properties. We disclose the synthesis and process conditions helpful in obtaining easily sinterable CoFe2O4 nanoparticles with coercive magnetic flux density (H-c) in the range 5.5-31.9 kA/m and M-s in the range 47.9-84.9 A.m(2)Kg(-1). At a grain size of similar to 54 +/- 2 nm (corresponding to 1073 K sintering temperature), multi-domain behavior sets in, which is indicated by a decrease in H-c. In addition, we observe an increase in lattice constant with respect to grain size, which is the inverse of what is expected of in ferrites. Our results suggest that oxygen deficiency plays a crucial role in explaining this inverse trend. We expect the method disclosed here to be a viable and scalable alternative to thermal decomposition based CoFe2O4 synthesis. The magnetic trends reported will aid in the optimization of functional CoFe2O4 nanoparticles

Controlled synthesis of organic-inorganic hybrid nanofibers by a wet-chemical route

Organic-inorganic hybrid nanofibers are successfully synthesized by incorporating 3,3 ',5,5 '-tetramethylbenzidine (TMB) and H2PtCl6 at room temperature. The morphology and size can be simply controlled by tuning the molar ratio and initial concentration of reactants. A possible formation mechanism was suggested on the basis of the experimental results. The optical properties were investigated and the as-obtained product displays a strong fluorescence emission at room temperature that may be promising for applications in the fabrication of photoelectric materials. (C) 2008 Elsevier B.V. All rights reserved.

Leakage current, ferroelectric and structural properties in Pb(1-x)Ba(x)TiO(3) thin films prepared by chemical route

Single-phase perovskite structure Pb(1-x)Ba(x)TiO(3) thin films (x = 0.30, 0.50 and 0.70) were deposited on Pt/Ti/SiO(2)/Si substrates by the spin-coating technique. The dielectric study reveals that the thin films undergo a diffuse type ferroelectric phase transition, which shows a broad peak. An increase of the diffusivity degree with the increasing Barium contents was observed, and it was associated to a grain decrease in the studied composition range. The temperature dependence of the phonon frequencies was used to characterize the phase transition temperatures. Raman modes persist above tetragonal to cubic phase transition temperature, although all optical modes should be Raman inactive. The origin of these modes was interpreted in terms of breakdown of the local cubic symmetry by chemical disorder. The absence of a well-defined transition temperature and the presence of broad bands in some interval temperature above FE-PE phase transition temperature Suggested a diffuse type phase transition. This result corroborates the dielectric constant versus temperature data, which showed a broad ferroelectric phase transition in these thin films. The leakage Current density of the PBT thin films was studied at different temperatures and the data follow the Schottky emission model. Through this analysis the Schottky barrier height values 0.75, 0.53 and 0.34 eV were obtained to the PBT70, PBT50 and PBT30 thin films, respectively. (C) 2008 Elsevier Ltd. All rights reserved.

Effect of strontium addition on ferroelectric phase transition of PZT thin films prepared by chemical route

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Indium tin oxide films prepared via wet chemical route

In this work, indium tin oxide (ITO) films were prepared using a wet chemical route, the Pechini method. This consists of a polyesterification reaction between an alpha-hydroxicarboxylate complex (indium citrate and tin citrate) with a polyalcohol (ethylene glycol) followed by a post annealing at 500 degrees C. A 10 at.% of doping of Sn4+ ions into an In2O3 matrix was successfully achieved through this method. In order to characterize the structure, the morphology as well as the optical and electrical properties of the produced ITO films, they were analyzed using different experimental techniques. The obtained films are highly transparent, exhibiting transmittance of about 85% at 550 nm. They are crystalline with a preferred orientation of [222]. Microscopy discloses that the films are composed of grains of 30 nm average size and 0.63 nm RMS roughness. The films' measured resistivity, mobility and charge carrier concentration were 5.8 x 10(-3) Omega cm, 2.9 cm(2)/V s and -3.5 x 10(20)/cm(3), respectively. While the low mobility value can be related to the small grain size, the charge carrier concentration value can be explained in terms of the high oxygen concentration level resulting from the thermal treatment process performed in air. The experimental conditions are being refined to improve the electrical characteristics of the films while good optical, chemical, structural and morphological qualities already achieved are maintained. (C) 2007 Elsevier B.V. All rights reserved.

Correlation between the surface morphology and structure and the photoluminescence of amorphous PbTiO3 thin films obtained by the chemical route

A polymeric precursor method was used to synthesis PbTiO3 amorphous thin film processed at low temperature. The luminescence spectra of PbTiO3 amorphous thin films at room temperature revealed an intense single-emission band in the visible region, the visible emission band was found to be dependent on the thermal treatment history, Photoluminescence properties Versus different annealing temperatures were investigated. The experimental results (XRD, AFM, FL) indicate that the nature of photoluminescence (PL) must be related to the disordered structure of PbTiO3 amorphous thin films, Copyright (C) 2000 John Wiley & Sons, Ltd.

Preparation, structural and optical characterization of BaWO4 and PbWO4 thin films prepared by a chemical route

Polycrystalline BaWO4 and PbWO4 thin films having a tetragonal scheelite structure were prepared at different temperatures. Soluble precursors such as barium carbonate, lead acetate trihydrate and tungstic acid, as starting materials, were mixed in aqueous solution. The thin films were deposited on silicon, platinum-coated silicon and quartz substrates by means of the spinning technique. The surface morphology and crystal structure of the thin films were investigated using scanning electron microscopy (SEM), atomic force microscopy (AFM), X-ray diffraction, and specular reflectance infrared Fourier transform spectroscopy, respectively. Nucleation stages and surface morphology evolution of thin films on silicon substrates have been studied by atomic force microscopy. XRD characterization of these films showed that BaWO4 and PbWO4 phase crystallize at 500 degreesC from an inorganic amorphous phase. FTIR spectra revealed the complete decomposition of the organic ligands at 500 degreesC and the appearance of two sharp and intense bands between 1000 and 600 cm(-1) assigned to vibrations of the antisymmetric stretches resulting from the high crystallinity of both thin films. The optical properties were also studied. It was found that BaWO4 and PbWO4 thin films have Eg = 5.78 eV and 4.20 eV, respectively, of a direct transition nature. The excellent microstructural quality and chemical homogeneity results confirmed that soft solution processing provides an inexpensive and environmentally friendly route for the preparation of BaWO4 and PbWO4 thin films. (C) 2003 Elsevier Ltd. All rights reserved.

Preparation of Pb(Zr,Ti)O-3 thin films by soft chemical route

Lead zirconate titanate, Pb(Zr0.3Ti0.7)O-3 (PZT) thin films were prepared with success by the polymeric precursor method. Differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), Fourier-transform infrared spectroscopy (FT-IR), Micro-Raman spectroscopy and X-ray diffraction (XRD) were used to investigate the formation of the PZT perovskite phase. X-ray diffraction revealed that the film showed good crystallinity and no presence of secondary phases was identified. This indicates that the PZT thin films were crystallized in a single phase. PZT thin films showed a well-developed dense grain structure with uniform distribution, without the presence of rosette structure. The Raman spectra undoubtedly revealed these thin films in the tetragonal phase. For the thin films annealed at the 500-700 degreesC range, the vibration modes of the oxygen sublattice of the PZT perovskite phase were confirmed by FT-IR. The room temperature dielectric constant and dielectric loss of the PZT films, measured at 1 kHz were 646 and 0.090, respectively, for thin film with 365 nm thickness annealed at 700 degreesC for 2 h. A typical P-E hysteresis loop was observed and the measured values of P-s, P-r and E-c were 68 muC/cm(2), 44 muC/cm(2) and 123 kV/cm, respectively. The leakage current density was about 4.8 x 10(-7) A/cm(2) at 1.5 V. (C) 2003 Elsevier Ltd. All rights reserved.

Preparation, microstructural and electrical characterization of SrTiO3 thin films prepared by chemical route

Polycrystalline SrTiO3 thin films having a cubic perovskite structure were prepared at different temperatures by the polymeric precursor method on platinum-coated silicon substrate. Crystalline films with uniform composition and thickness were prepared by spin-coating and the post-deposition heat treatment was carried out at different temperatures. The film showed good structural, dielectric, and insulating properties, Scanning electron microscopy (SEM) micrographs showed no occurrence of interdiffusion between the bottom electrode (platinum) and the film during post-annealing, indicating a stable interface between the SrTiO3 and the bottom electrode. The dielectric constant and dissipation factor at a frequency of 100 kHz were 250 and 0.01, respectively, for a 360 nm thick film annealed at 600 degreesC. The capacitance versus applied voltage characteristics showed that the capacitance was almost independent of the applied voltage. The I-V characteristics were ohmic in low fields and a Schottky emission and/or Poole-Frenkel emission were postulated in high fields. Room temperature leakage current density was found to be in the order of 10(-7) A/cm(2) for a 360 nm thick film in an applied electric field of about 100 kV/cm. The charge storage density of 36 fC/mum(2) was obtained in an applied electric field of about 100 kV/cm. (C) 2001 Published by Elsevier B.V. Ltd. All rights reserved.

Dielectric properties and microstructure of SrTiO3/BaTiO3 multilayer thin films prepared by a chemical route

Multilayer thin films with perovskite structures were produced by the polymeric precursor method. SrTiO3/BaTiO3 (STO/BTO) multilayers were deposited on Pt(111)/Ti/SiO2/Si(100) substrates by the spin-coating technique and heated in air at 700 degreesC. The microstructure and crystalline phase of the multilayered thin films were examined by field-emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), resolution-high transmission electron microscopy (HRTEM), atomic force microscopy (AFM) and X-ray diffraction. The SrTiO3/BaTiO3 multilayer thin films consisted of grainy structures with an approximate grain size of 60 nm. The multilayered thin films showed a very clear interface between the components. The SrTiO3/BaTiO3 multilayer thin films revealed dielectric constants of approximately 527 and loss tangents of 0.03 at 100 kHz. The dielectric constant calculated for this multilayer film system is the value of the sum of each individual component of the film, i.e. The total value of the sum of each SrTiO3 (STO) and BaTiO3 (BTO) layer. The multilayer SrTiO3/BaTiO3 obtained by the polymeric precursor method, also showed a ferroelectric behavior with a remanent polarization of 2.5 muC/cm(2) and a coercive field of 30 kV/cm. The multilayer films displayed good fatigue characteristics under bipolar stressing after application of 10(10) switching cycles. (C) 2001 Published by Elsevier B.V. B.V. All rights reserved.