Studies on structural and electrical properties of sprayed SnO2 : Sb films

Thin films of antimony-doped tin oxide (SnO2:Sb) were prepared by spray pyrolysis using stannous chloride (SnCl2) and antimony trichloride (SbCl3) as precursors. The antimony doping was varied from 0 to 4 wt%. Scanning electron microscopy (SEM) revealed the surface morphology to be very smooth, yet grainy in nature. X-ray diffraction (XRD) shows films to have preferred orientation, which varies with the extent of antimony doping: undoped films prefer the (2 1 1) orientation, while the (3 0 1) orientation is preferred for doping levels of 0.5 and 1.0 wt%. For higher doping levels, the (2 0 0) orientation is preferred. This difference in preferred orientations is reflected in the SEM of the films. Atomic force microscopy (AFM) reveals that film roughness is not affected by antimony doping. The minimum sheet resistance (2.17 ohm/square) achieved in the present study is lower than values reported to date in SnO2:Sb films prepared from SnCl2 precursor. The Hall mobility of undoped SnO2 films was found to be 109.52 cm(2)/V s, which reduces to 2.55 cm(2)/ Vs for the films doped with 4 wt% of Sb. On the other hand, the carrier concentration, which is 1.23 x 10(19) cm(-3) in undoped films, increases to 2.89 x 10(21) cm(-3) for the films doped with 4 wt% of Sb. (c) 2004 Elsevier B.V. All rights reserved.

Electrical characterization of SnO2 : Sb ultrathin films obtained by controlled thickness deposition

A representative study is reported on the electrical properties of SnO2: Sb. ultrathin films (thickness of 40-70 nm) produced by a deposition method based on aqueous colloidal suspensions of 3-5 nm crystalline oxides. The results revealed the films' electrical behavior in a range of 10-300 K, showing a strong dependence on dopant incorporation, with minimum resistivity values in 10 mol % of Sb content. All the samples displayed semiconductor behavior, but the transport mechanism showed a strong dependence on thickness, making it difficult to fit it to well-known models. In thicker films, the mechanism proved to be an intermediary system, with thermally activated and hopping features. Electron hopping was estimated in the range of 0.4-1.9 nm, i.e., in the same order as the particle size. (c) 2007 American Institute of Physics.

Influence of heat treatment on the optical properties of SnO2 : Sb thin films deposited by dip coating using aqueous solution

Antimony doped tin oxide thin films were deposited on glass by a chemical route derived from Pechini method. Particular emphasis was given to the microstructure of crystallized films. Crystalline phase formation was studied by grazing incident X-ray diffraction and by thermal analyses. Scanning electron microscopy was carried out for microstructure characterization, surface roughness was observed using scanning tunneling microscope and the optical transmittance measurements were performed in the wavelength range of 200-800 nm. (C) 2002 Kluwer Academic Publishers.

Deposition of controlled thickness ultrathin SnO2 : Sb films by spin-coating

The technological interest in transparent conductive oxide films (TCOs) has motivated several works in processing techniques, in order to obtain adequate routes to application. In this way, this work describes a new route to obtain antimony-doped tin oxide (ATO) films, based in colloidal dispersions of oxide nanocrystals. The nanoparticles were obtained by a hydrolisis method, using SnCl2 and SbCl3 in ethanolic solutions. The residual halides were removed by dyalisis, obtaining a limpid and transparent colloidal suspension. By this, the method offers the advantage of producing ultrathin films without organic contaminants. This route was employed to produce films with 5, 10, 14, and 18 mol% Sb doping, with thickness ranging from 40 to 70 nm. The physical characterization of the samples showed a uniform layer deposition, resulting in good packing density and high transmittance. A preliminar electrical study confirmed the low electrical resistivity even in the ultrathin films, in such level similar of reported data. The method described is similar in some aspects to layer-by-layer (LbL) techniques, allowing fine control of thickness and interesting properties for ultrathin films, however, with low cost when compared to similar routes.

Electrical properties of highly conducting Sno2:Sb nanocrystals synthesized using a nonaqueous sol gel method

This work describes the synthesis of highly conducting antimony-doped tin oxide (ATO) nanocrystals prepared via a nonaqueous sol–gel route in the size range of 4–6 nm and provides insights into its electrical properties. The antimony composition was varied from 1 to 18 mol% and the lowest resistivity (4.0 × 10−4Ω·cm) was observed at room temperature in the SnO2:8.8 mol% Sb composition. The samples were evaluated by X-ray diffraction, high-resolution transmission electron microscopy, energy-dispersive X-ray spectroscopy, and scanning electron microscope, and resistivity measurements were taken in the four-probe mode in the temperature range of 13–300 K. The results show highly crystalline nanoparticles in a monodisperse colloidal system, dependence on the shape of ATO nanoparticles as a function of Sb distribution, low resistivity, and semiconductor–metal transition.

Enhanced electrical property of nanostructured Sb-doped SnO2 thin film processed by soft chemical method

The effect of the Sb addition on the microstructural and electrical conductivity of the SnO2 thin film was studied in this work. Experimental results show that the Sb addition allowed to control the grain size and electrical conductivity of the SnO2 thin film, resulting in a nanostructured material. The nanostructured Sb-doped SnO2 thin films present high electrical conductivity, even in the presence of high porosity, supporting the hypothesis that nanostructured material must possess strong electrical conductivity. This work involves important aspects that can be applied to the development of high performance transparent conducting thin film. (C) 2003 Elsevier B.V. All rights reserved.

Estrutura eletrônica e propriedades elétricas fotoinduzidas em filmes finos de SnO2 com dopagem de Sb, e formação de heteroestruturas com TiO2

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Influence of the concentration of Sb2O3 and the viscosity of the precursor solution on the electrical and optical properties of SnO2 thin films produced by the Pechini method

SnO2:Sb multi-layer coatings were prepared by the Pechini method. An investigation was made of the influence of the concentration of Sb2O3 and the viscosity of the precursor solution on the electrical and optical properties of SnO2 thin films. The use of a multi-layer system as an alternative form of increasing the packing and. thus. decreasing porosity proved to be efficient, decreasing the system's resistivity without altering its optical properties. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Célula solar de SnO2/TiO2 preparada por spray - pirólise ativada com corante orgânico

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Growth and Characterization of ZnO based Heterojunction diodes and ZnO Nanostructuresby Pulsed Laser Ablation

Transparent conducting oxides (TCO’s) have been known and used for technologically important applications for more than 50 years. The oxide materials such as In2O3, SnO2 and impurity doped SnO2: Sb, SnO2: F and In2O3: Sn (indium tin oxide) were primarily used as TCO’s. Indium based oxides had been widely used as TCO’s for the past few decades. But the current increase in the cost of indium and scarcity of this material created the difficulty in obtaining low cost TCO’s. Hence the search for alternative TCO material has been a topic of active research for the last few decades. This resulted in the development of various binary and ternary compounds. But the advantages of using binary oxides are the easiness to control the composition and deposition parameters. ZnO has been identified as the one of the promising candidate for transparent electronic applications owing to its exciting optoelectronic properties. Some optoelectronics applications of ZnO overlap with that of GaN, another wide band gap semiconductor which is widely used for the production of green, blue-violet and white light emitting devices. However ZnO has some advantages over GaN among which are the availability of fairly high quality ZnO bulk single crystals and large excitonic binding energy. ZnO also has much simpler crystal-growth technology, resulting in a potentially lower cost for ZnO based devices. Most of the TCO’s are n-type semiconductors and are utilized as transparent electrodes in variety of commercial applications such as photovoltaics, electrochromic windows, flat panel displays. TCO’s provide a great potential for realizing diverse range of active functions, novel functions can be integrated into the materials according to the requirement. However the application of TCO’s has been restricted to transparent electrodes, ii notwithstanding the fact that TCO’s are n-type semiconductors. The basic reason is the lack of p-type TCO, many of the active functions in semiconductor originate from the nature of pn-junction. In 1997, H. Kawazoe et al reported the CuAlO2 as the first p-type TCO along with the chemical design concept for the exploration of other p-type TCO’s. This has led to the fabrication of all transparent diode and transistors. Fabrication of nanostructures of TCO has been a focus of an ever-increasing number of researchers world wide, mainly due to their unique optical and electronic properties which makes them ideal for a wide spectrum of applications ranging from flexible displays, quantum well lasers to in vivo biological imaging and therapeutic agents. ZnO is a highly multifunctional material system with highly promising application potential for UV light emitting diodes, diode lasers, sensors, etc. ZnO nanocrystals and nanorods doped with transition metal impurities have also attracted great interest, recently, for their spin-electronic applications This thesis summarizes the results on the growth and characterization of ZnO based diodes and nanostructures by pulsed laser ablation. Various ZnO based heterojunction diodes have been fabricated using pulsed laser deposition (PLD) and their electrical characteristics were interpreted using existing models. Pulsed laser ablation has been employed to fabricate ZnO quantum dots, ZnO nanorods and ZnMgO/ZnO multiple quantum well structures with the aim of studying the luminescent properties.

Novel co-evaporation approach for the growth of Sb doped SnO2 nanowires

Antimony doped tin oxide (Sb:SnO2) nanowires were grown by thermal and e-beam assisted co-evaporation of Sb and Sn in the presence of oxygen at a low substrate temperature of 450 degrees C. The field emission scanning electron microscopy study revealed that the nanowires had a length and diameter of 2-4 mu m and 20-60 nm respectively. Transmission electron microscopy study revealed the single crystalline nature of the nanowires; energy dispersive X-ray spectroscopy (EDS) and EDS mapping on the nanowires confirmed the presence of Sb doping in the nanowires. UV light detection study on the doped SnO2 nanowire films exhibited fast response and recovery time compared to undoped SnO2 nanowire films. This is an innovative and simple method to grow doped SnO2 nanowires.

Structural Characterization of Nanocrystalline Sb-Doped SnO2 Xerogels by Multiedge X-ray Absorption Spectroscopy

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

The effect of preparation method and Sb content on SnO2-CuO sintering

The sintering behavior of SnO2-CuO system has been investigated for two preparation methods and as a function of antimony concentration. A chemical preparation (Pechini's method) resulted in powders with smaller particle sizes than for a conventional oxide mixture. This led to smaller grain sizes in Pechini's method ceramics. The microstructures were heterogeneous in both systems, showing grain coarsening. The densification was aided by liquid phase formation, due to copper, in both systems, but the temperature of maximum shrinkage rate was larger for the Pechini's method ceramic because copper had to diffuse to the grain surface. Independently of the preparation method, antimony did not aid densification, and increasing its concentration led to a higher densification temperature and lower shrinkage rate. (C) 2003 Kluwer Academic Publishers.

Dynamical scaling properties of nanoporous undoped and Sb-doped SnO2 supported thin films during tri- and bidimensional structure coarsening

The coarsening of the nanoporous structure developed in undoped and 3% Sb-doped SnO2 sol-gel dip-coated films deposited on a mica substrate was studied by time-resolved small-angle x-ray scattering (SAXS) during in situ isothermal treatments at 450 and 650 degrees C. The time dependence of the structure function derived from the experimental SAXS data is in reasonable agreement with the predictions of the statistical theory of dynamical scaling, thus suggesting that the coarsening process in the studied nanoporous structures exhibits dynamical self-similar properties. The kinetic exponents of the power time dependence of the characteristic scaling length of undoped SnO2 and 3% Sb-doped SnO2 films are similar (alpha approximate to 0.09), this value being invariant with respect to the firing temperature. In the case of undoped SnO2 films, another kinetic exponent, alpha('), corresponding to the maximum of the structure function was determined to be approximately equal to three times the value of the exponent alpha, as expected for the random tridimensional coarsening process in the dynamical scaling regime. Instead, for 3% Sb-doped SnO2 films fired at 650 degrees C, we have determined that alpha(')approximate to 2 alpha, thus suggesting a bidimensional coarsening of the porous structure. The analyses of the dynamical scaling functions and their asymptotic behavior at high q (q being the modulus of the scattering vector) provided additional evidence for the two-dimensional features of the pore structure of 3% Sb-doped SnO2 films. The presented experimental results support the hypotheses of the validity of the dynamic scaling concept to describe the coarsening process in anisotropic nanoporous systems.