Influence of microstructure variability on short crack growth behavior

Fatigue life in metals is predicted utilizing regression analysis of large sets of experimental data, thus representing the material’s macroscopic response. Furthermore, a high variability in the short crack growth (SCG) rate has been observed in polycrystalline materials, in which the evolution and distributionof local plasticity is strongly influenced by the microstructure features. The present work serves to (a) identify the relationship between the crack driving force based on the local microstructure in the proximity of the crack-tip and (b) defines the correlation between scatter observed in the SCG rates to variability in the microstructure. A crystal plasticity model based on the fast Fourier transform formulation of the elasto-viscoplastic problem (CP-EVP-FFT) is used, since the ability to account for the both elastic and plastic regime is critical in fatigue. Fatigue is governed by slip irreversibility, resulting in crack growth, which starts to occur during local elasto-plastic transition. To investigate the effects of microstructure variability on the SCG rate, sets of different microstructure realizations are constructed, in which cracks of different length are introduced to mimic quasi-static SCG in engineering alloys. From these results, the behavior of the characteristic variables of different length scale are analyzed: (i) Von Mises stress fields (ii) resolved shear stress/strain in the pertinent slip systems, and (iii) slip accumulation/irreversibilities. Through fatigue indicator parameters (FIP), scatter within the SCG rates is related to variability in the microstructural features; the results demonstrate that this relationship between microstructure variability and uncertainty in fatigue behavior is critical for accurate fatigue life prediction.

Modelling short crack growth behaviour in nickel-base superalloys

This paper provides a description of the features and mechanisms of facetted short crack growth in Ni-base superalloys, and briefly reviews existing short crack growth models in terms of their application to Ni-base alloys. The concept of “soft barriers” is introduced to produce a new two-phase model for local microstructural effects on short crack growth in Waspaloy. This is derived from detailed observations of crack growth through individual grains. The model differs from all previous approaches in highlighting the importance of crack path perturbations within grains. Potential applications of the model in alloy development are discussed.

Effects of microstructure on long and short crack growth in nickel base superalloys

The use of engineering materials in critical applications necessitates the accurate prediction of component lifetime for inspection and renewal purposes. In fatigue limited situations, it is necessary to be able to predict the growth rates of cracks from initiation at a defect through to final fracture. To this end, fatigue crack growth data are presented for different microstructures of typical nickel base superalloys used in gas turbine engines. Crack growth behaviour throughout the life history of the crack, i.e. from the short crack through to the long crack propagation regime, is described for each microstructural condition and discussed in terms of current theories of fatigue crack propagation.

Relevance of microstructural influences in the short crack regime to overall fatigue resistance

The behaviour of short fatigue cracks is shown to be relevant only to a limited number of engineering situations. Within these situations, further restrictions on the extent to which metallurgical control can be exerted to improve fatigue crack growth behaviour are identified. The degree of control remaining is discussed in terms of two separate regimes which are described as intrinsic and extrinsic crack growth resistance. These separate effects are highlighted by comparisons both within and between a wide range of alloy systems. The implications of such an analysis are discussed in terms of aerospace applications.

Fatigue crack growth behaviour in molten-metal processed SiC particle-reinforced aluminium alloys

Fatigue crack initiation and subsequent short crack growth behaviour of 2014-5wt%SiC aluminium alloy composites has been examined in 4-point bend loading using smooth bar specimens. The growth rates of long fatigue cracks have also been measured at different stress ratios using pre-cracked specimens. The distributions of SiC particles and of coarse constituent particles in the matrix (which arise as a result of the molten-metal processing and relatively slow cooling rate) have been investigated. Preferential crack initiation sites were found to be SiC-matrix interfaces, SiC particles associated with constituent particles and the coarse constituent particles themselves. For microstructurally short cracks the dispersed SiC particles also act as temporary crack arresters. In the long crack growth tests, higher fatigue crack growth rates were obtained than for monolithic alloys. This effect is attributed to the contribution of void formation, due to the decohesion of SiC particles, to the fatigue crack growth process in the composite. Above crack depths of about 200 μm 'short' crack growth rates were in good agreement with the long crack data, showing a Pris exponent, m = 4 in both cases. For the long crack and short crack growth tests little effect of specimen orientation and grain size was observed on fatigue crack growth rates, but, specimen orientation affected the toughness. No effect of stress ratio in the range R = 0.2-0.5 was seen for long crack data in the Paris region.

Growth of short fatigue cracks in titanium alloys

The initiation and early propagation of short fatigue cracks has been studied in detail in two alpha / beta titanium alloys as a function of microstructure. Detailed metallography is presented relating short crack growth rates to the microstructural features present. The work shows the significant differences in short crack propagation rates which can be achieved by microstructural changes within a single alloy.

Initiation and early crack growth in VHCF of stainless steels : Experimental and theoretical analysis

Mechanical fatigue is a failure phenomenon that occurs due to repeated application of mechanical loads. Very High Cycle Fatigue (VHCF) is considered as the domain of fatigue life greater than 10 million load cycles. Increasing numbers of structural components have service life in the VHCF regime, for instance in automotive and high speed train transportation, gas turbine disks, and components of paper production machinery. Safe and reliable operation of these components depends on the knowledge of their VHCF properties. In this thesis both experimental tools and theoretical modelling were utilized to develop better understanding of the VHCF phenomena. In the experimental part, ultrasonic fatigue testing at 20 kHz of cold rolled and hot rolled stainless steel grades was conducted and fatigue strengths in the VHCF regime were obtained. The mechanisms for fatigue crack initiation and short crack growth were investigated using electron microscopes. For the cold rolled stainless steels crack initiation and early growth occurred through the formation of the Fine Granular Area (FGA) observed on the fracture surface and in TEM observations of cross-sections. The crack growth in the FGA seems to control more than 90% of the total fatigue life. For the hot rolled duplex stainless steels fatigue crack initiation occurred due to accumulation of plastic fatigue damage at the external surface, and early crack growth proceeded through a crystallographic growth mechanism. Theoretical modelling of complex cracks involving kinks and branches in an elastic half-plane under static loading was carried out by using the Distributed Dislocation Dipole Technique (DDDT). The technique was implemented for 2D crack problems. Both fully open and partially closed crack cases were analyzed. The main aim of the development of the DDDT was to compute the stress intensity factors. Accuracy of 2% in the computations was attainable compared to the solutions obtained by the Finite Element Method.

Fatigue in SiC-particulate-reinforced aluminium alloy composites

The fatigue behaviour in SiC-particulate-reinforced aluminium alloy composites has been briefly reviewed. The improved fatigue life reported in stress-controlled test results from the higher stiffness of the composites; therefore it is generally inferior to monolithic alloys at a constant strain level. The role of SiC particulate reinforcement has been examined for fatigue crack initiation, short-crack growth and long-crack growth. Crack initiation is observed to occur at matrix-SiC interface in cast composites and either at or near the matrix-SiC interface or at cracked SiC particles in powder metallurgy processed composites depending on particle size and morphology. The da/dN vs ΔK relationship in the composites is characterized by crack growth rates existing within a narrow range of ΔK and this is because of the lower fracture toughness and relatively high threshold values in composites compared with those in monolithic alloys. An enhanced Paris region slope attributed to the monotonic fracture contribution are reported and the extent of this contribution is found to depend on particle size. The effects of the aging condition on crack growth rates and particle size dependence of threshold values are also treated in this paper. © 1991.

Short fatigue crack path determinants in polycrystalline Ni-base superalloys

Fifty seven short fatigue cracks in the Ni-base superalloy AP1 have been examined, to ascertain how the paths taken by growing fatigue cracks are determined. The observations were made on the surface of a smooth specimen, and on the exposed fracture surfaces. Three dimensional reconstructions of the vulnerable microstructures in the vicinity of the cracks were produced. Initiation occurred in mode II, with the lines of intersection of the initiation sites with the specimen top surface orientated at approximately 45° to the tensile axis. These initiation sites developed in slip bands which crossed a large grain and at least one other grain via a grain boundary with a low angle of misorientation. 'River markings' on one of the initiation facets, indicated that the crack first opened from the top centre of the initiation grain. Subsequent to initiation, the growth paths of these cracks are related to the misorientations of the grains and the progress of the crack front.

Short fatigue crack growth behaviour:data analysis effects

Consideration of the influence of test technique and data analysis method is important for data comparison and design purposes. The paper highlights the effects of replication interval, crack growth rate averaging and curve-fitting procedures on crack growth rate results for a Ni-base alloy. It is shown that an upper bound crack growth rate line is not appropriate for use in fatigue design, and that the derivative of a quadratic fit to the a vs N data looks promising. However, this type of averaging, or curve fitting, is not useful in developing an understanding of microstructure/crack tip interactions. For this purpose, simple replica-to-replica growth rate calculations are preferable. © 1988.

Short and long fatigue crack growth in a SiC reinforced aluminium alloy

Fatigue crack growth behaviour in a 15 wt% SiC particulate reinforced 6061 aluminium alloy has been examined using pre-cracked specimens. Crack initiation and early growth of fatigue cracks in smooth specimens has also been investigated using the technique of periodic replication. The composite contained a bimodal distribution of SiC particle sizes, and detailed attention was paid to interactions between the SiC particles and the growing fatigue-crack tip. At low stress intensity levels, the proportion of coarse SiC particles on the fatigue surfaces was much smaller than that on the metallographic sections, indicating that the fatigue crack tends to run through the matrix avoiding SiC particles. As the stress intensity level increases, the SiC particles ahead of the growing fatigue crack tip are fractured and the fatigue crack then links the fractured particles. The contribution of this monotonic fracture mode resulted in a higher growth rate for the composite than for the unreinforced alloy. An increase in the proportion of cracked, coarse SiC particles on the fatigue surface was observed for specimens tested at a higher stress ratio.

La crisi sub-prime i el crack de 1929: Comparació d'episodis d'eufòria financera

Treball de recerca realitzat per un alumne d'ensenyament secundari i guardonat amb un Premi CIRIT per fomentar l'esperit científic del Jovent l'any 2009. La present investigació té per objecte d’estudi la relació, atès el període de turbulències econòmiques que travessa el món globalitzat, entre els episodis d’eufòria financera i les crisi financeres i econòmiques, i la periodicitat amb les que aquestes es produeixen. Aquesta pretén confrontar-se des d’una aproximació històric-econòmica, mitjançant l’anàlisi i la comparació de dos successos -el crack borsari de 1929 i la crisi sub-prime- per tal de demostrar la existència de comuns denominadors, i, a la llum dels resultats, apreciar les conclusions que aporta la Història. Serà, doncs, aquesta periodicitat i les seves implicacions la qual s'ambicionarà contrastar amb la realitat mitjançant l'aplicació i l'anàlisi pràctica de dos episodis rellevants i paradigmàtics, amb el recolzament i l'autoritat del model comparatiu establerts per l'economista John Kenneth Galbraith al seu llibre ''Breve historia de la euforia financiera''.

Observation of crack initiation during hot tearing

While the general mechanisms of hot tearing are understood, i.e. the inability of liquid to feed imposed strain on the mushy material, work continues on improving the understanding of the mechanisms at play. A hot tear test rig that measures the temperature and load imposed on the mushy zone during solidification has been successfully used to study hot tearing. The mould has now been modified to incorporate a window above the hot spot region to allow observation of hot tear formation and growth. Combining information from visual observation with load and temperature data has led to a better understanding of the mechanism of hot tearing. Tests were carried out on an Al-0.5 wt-% Cu alloy. It was found that load development began at about 90% solid and a hot tear formed a short time later, at between 93% and 96% solid. Hot tearing started at a very low load.

"Crack down on the celebrity junkies": does media coverage of celebrity drug use pose a risk to young people?

This study analysed news media content to examine the role played by celebrity drug use in young people's perceptions of drug use. We know that young people have access to discourses of drug use through music and other media which may emphasise short term gains (of pleasure or sexual success) over longer term health and social problems. This study goes beyond a simple modelling approach by using Media Framing Analysis (MFA) to take an in-depth look at the messages themselves and how they are 'framed'. New stories about Amy Winehouse's drug use were used and we conducted focus groups with young people asking them questions about drugs, celebrity and the media. Frames identified include: 'troubled genius', 'losing patience' and 'glamorization or gritty realism'. Initially, the press championed Winehouse's musical talent but soon began to tire of her recklessness; the participants tended to be unimpressed with Winehouse's drug use, characterising her as a promising artist who had 'gone off the rails'. Young people were far more critical of Winehouse than might be expected, demonstrating that concerns about the influence of celebrity drug use and its impact on future health risk behaviour among young people may have been over-simplified and exaggerated. This study illustrates the need to understand young people and their frames of reference within popular culture when designing drug awareness information relevant to them. Furthermore, it indicates that critical media skills analysis may contribute to health risk education programmes related to drug use.

[temporomandibular Disorders In Fibromyalgia Syndrome: A Short-communication.]

Fibromyalgia syndrome (FMS) is a chronic painful syndrome and the coexistence of a painful condition caused by Temporomandibular Disorders (TMD) and FMS has been frequently raised for several studies, however, more likely hypothesis is that a set of FMS characteristics may lead to the onset of TMD symptoms and they are not merely coexisting conditions. Therefore, our aim is presenting a review of literature about the relation between fibromyalgia and the signs and symptoms of temporomandibular disorders. For this purpose, a bibliographic search was performed of the period of 1990-2013, in the Medline, Pubmed, Lilacs and Scielo databases, using the keywords fibromyalgia, temporomandibular disorders and facial pain. Here we present a set of findings in the literature showing that fibromyalgia can lead to TMD symptoms. These studies demonstrated greater involvement of the stomatognathic system in FMS and myogenic disorders of masticatory system are the most commonly found in those patients. FMS appears to have a series of characteristics that constitute predisposing and triggering factors for TMD.