Crystallization Kinetics of Syndiotactic Polypropylene Studied by Time-Dependent Light Attenuation

Crystallization kinetics of syndiotactic polypropylene ( sPP) was observed by light attenuation measurements. The initial stages of temperature dependent sPP crystallization fall in the range of Rayleigh scattering and Rayleigh-Debye-Gans scattering. Initial time and growth time of crystallization were obtained, and the trend of crystallization temperature dependent linear attenuation coefficient on the radius and the index of the refraction of the spherulite were evaluated.

Synchrotron investigation on the sheared structure evolution of syndiotactic polypropylene crystallization process

The final structure of molten syndiotactic polypropylene (sPP) sheared under different conditions was investigated by synchrotron small-angle x-ray scattering (SAXS) and wide-angle x-ray diffraction (WAXD) techniques to elucidate the shear effects on sPP crystalline structure. The results obtained from the WAXD show that there is no variation on crystalline form but a little difference on the orientation of the 200 reflection. The SAXS data indicate that the lamellar thickness and long period have not been affected by shear but the lamellar orientation is dependent on shear. The experimental data of sPP crystallization from sheared melt may indicate a mesophase structure that is crucial to the shear effects on the final polymer multiscale crystalline structures.

Isochiral form II of syndiotactic polypropylene produced by epitaxial crystallization

Epitaxial crystallization of syndiotactic polypropylene (sPP) on 2-quinoxalinol (2-Quin) yields, in the lower part of the crystallization range, the less common and metastable form II based on the packing of isochiral helices, rather than the stable antichiral form I. The contact plane is (110)(II). Form II exits only as a thin layer (< 50 nm) near the substrate surface. During further growth away from the surface, a transition takes place to the disordered form I, observed in "conventional" thin film growth. The epitaxial relationship rests only partly on dimensional matching with the chain axis repeat distance (which would be valid for both forms I and II) and on interchain distances. Whereas a better dimensional match would be achieved with form I, selection of the isochiral form II results from better correspondence of the surface topographies of the deposit (110)(II) sPP and substrate 2-Quin (001) contact faces.

Mechanical and thermal induced chain conformational transformations in syndiotactic polypropylene (sPP)

Stretching a stacked sPP lamellar morphology at room temperature leads to a mechanical induced transformation from the (t(2)g(2))(2) (helical) into the (tttt) (zigzag) chain conformation of the polymer. The so prepared samples exhibit after annealing above 80 degreesC a thermal induced retransformation into the cell I and cell III crystal structure of the helical chain conformation. The mechanical induced chain conformational transformation as well as the thermal induced retransformation was studied by means of transmission electron microscopy and electron diffraction. (C) 2001 Kluwer Academic Publishers.

Conformation transformation of syndiotactic polypropylene induced by stretching and annealing

Conformation transformation of syndiotactic polypropylene(sPP) induced by stretching and annealing processes has been investigated by WAXD, IR and DSC, The results indicate that not only the quenched samples but also the isothermally crystallized samples can form the crystals with all-trans conformation by means of uniaxially stretching at room temperature. The all-trans conformation crystals are of metastability, which can transform to stable crystals with (TTGG)(2) helical conformation at higher annealing temperatures.

Crystallization of syndiotactic polypropylene (sPP) from oriented melts

The influence of the syndiotacticity on the crystallization behaviour of syndiotactic polypropylene (sPP) has been investigated. The syndiotacticity has been measured by C-13-NMR spectroscopy and the phase formation has been observed by electron diffraction of oriented samples. It is shown that the crystal phase formation depends strongly on the perfection of the tacticity of the macromolecules.

EPITAXIAL CRYSTALLIZATION OF SYNDIOTACTIC POLYPROPYLENE ON UNIAXIALLY ORIENTED POLYETHYLENE

The epitaxial crystallization of syndiotactic polypropylene (sPP) on uniaxially oriented polyethylene (PE) has been investigated by electron microscopy and electron diffraction. It is found that the sPP lamellae grow epitaxially on the PE substrate film with the preference in sPP for the b axis as the fast growth direction. Instead of 50-degrees as in the system of isotactic polypropylene with PE, the molecular chains of the sPP crystals are approximately +/- 37-degrees inclined to the chain direction of PE.

Single crystal structure of form I syndiotactic poly(butene-1)

The structures of single crystals of syndiotactic poly(butene-1) in form I, produced by thin-film growth, are studied by transmission electron microscopy and electron diffraction. Bright-field electron microscopy observation shows that the single crystal exhibits a regular rectangular shape with the long axis along its crystallographic b-axis. Electron diffraction results indicate an isochiral C-centered packing of a-fold helical chains in an orthorhombic unit cell corresponding to the C222(1) space group, according to the model proposed in the literature. The differences with the polymorphic behavior of syndiotactic polypropylene concerning the formation and the stability of the isochiral mode of packing are outlined.

Isothermal and non-isothermal crystallization kinetics of syndiotactic polypropelene

Isothermal and non-isothermal crystallization kinetics of a syndiotactic polypropylene(sPP) sample synthesized by new metallocene catalyst at different annealing temperatures and different cooling rates have been investigated by using differential scanning calorimetry(DSC) and density analysis. The equilibrium melting temperature( T-m(0)) is 158 degrees C by Hoffman-Weeks method. The equilibrium heat of fusion(Delta H-m(0)) is 88J/g in terms of the density analysis and DSC methods. The lateral and end surface free energies derived from the Lauritzen-Hoffman spherulitic growth rate equation are sigma = 5.2erg/cm(2) and sigma(e) = 69erg/cm(2), respectively. The work of chain folding is determined to be q = 33.75kJ/mol. Modified Avrami equation and Ozawa equation can be used to describe the non-isothermal crystallization behavior. And a new and convenient approach by combining the Avrami equation and Ozawa equation in a same crystallinity is used to describe the non-isothermal behavior as well. The crystallization activation energies are evaluated to be 73.7kJ/mol and 73.1kJ/mol for isothermal crystallization and non-isothermal crystallization, respectively. The Avrami exponent n is 1.5 similar to 1.6 for isothermal crystallization procedure, while the Avrami exponent n,is 2.5 similar to 3.5 for non-isothermal crystallization procedure. This indicated the difference of nucleation and growth between the two procedures.

Critical crystallization temperature for the occurrence of epitaxy between high-density polyethylene and isotactic polypropylene

The crystallization behavior of high-density polyethylene (HDPE) on highly oriented isotactic polypropylene (iPP) at elevated temperatures (e.g., from 125 to 128 degrees C), was studied using transmission electron microscopy and electron diffraction. The results show that epitaxial crystallization of HDPE on the highly oriented iPP substrates occurs only in a thin layer which is in direct contact with the iPP substrate, when the HDPE is crystallized from the melt on the oriented iPP substrates at 125 degrees C. The critical layer thickness of the epitaxially crystallized HDPE is not more than 30 nm when the HDPE is isothermally crystallized on the oriented iPP substrates at 125 degrees C. When the crystallization temperature is above 125 degrees C, the HDPE crystallizes in the form of crystalline aggregates and a few individual crystalline lamellae. But both the crystalline aggregates and the individual crystalline lamellae have no epitaxial orientation relationship with the iPP substrate. This means that there exists a critical crystallization temperature for the occurrence of epitaxial crystallization of HDPE on the melt-drawn oriented iPP substrates (i.e., 125 degrees C). (C) 1997 John Wiley & Sons, Inc.

Simulated morphological landscape of polymer single crystals by phase-field model

The novel phase field model with the "polymer characteristic" was established based on a nonconserved spatiotemporal Ginzburg-Landau equation (TDGL model A). Especially, we relate the diffusion equation with the crystal growth faces of polymer single crystals. Namely, the diffusion equations are discretized according to the diffusion coefficient of every lattice site in various crystal growth faces and the shape of lattice is selected based on the real proportion of the unit cell dimensions.

Studies of instrumental spreading in gel permeation chromatography by coupling with a two-angle laser light scattering detector

The instrumental spreading of a high temperature gel permeation chromatograph (GPC) was evaluated by coupling with a two-angle laser light scattering (TALLS) detector, using narrow polystyrene, polyethylene, and syndiotactic polypropylene samples. The determined spreading factor increased with increasing molecular weight of polymers, and no maximum for spreading 174 tor was observed in the studied retention volume, while the spreading factors for single low molecular weight alkanes are independent of their molecular weight. Neglecting of the spreading effect for GPC would not introduce much error in molecular weight calculation when high quality high performance columns were used, especially when equipped with a laser light scattering detector. The scaling relationship between radius of gyration and molecular weight of polymer, determined by GPC with a TALLS detector, was independent of the instrumental spreading.

Liquid crystalline phases, microtwinning in crystals and helical chirality transformations in a main-chain chiral liquid crystalline polyester

A main-chain nonracemic chiral liquid crystalline polymer was synthesized from (R)-(-)4'-{w-[2-(p-hydroxy-o-nitrophenyloxy)-1-propyloxy]-1-decyloxyl-4-biphenylcarboxylic acid. This polymer contained 10 methylene units in each chemical repeating unit and was abbreviated PET(R*-10). On the basis of differential scanning calorimetry, wide-angle X-ray diffraction, and polarized light microscopy experiments, chiral smectic C (S-C*) and chiral smectic A (S-A*) phases were identified. Both flat-elongated and helical lamellar crystal morphologies were observed in transmission electron microscopy. Of particular interest was the flat-elongated lamellar crystals were constructed via microtwinning of an orthorhombic cell with dimensions of a = 1.42 nm, b = 1.28 nm, and c = 3.04 nm. On the other hand, the helical lamellar crystals were exclusively left-handed, which was opposite to the right-handed helical crystals grown in PET(R*-9) and PET(R*-11) (having 9 and 11 methylene units, respectively). Note that these three polymers had identical right-handed chiral centers (R*-). Therefore, a single methylene unit difference on the polymer backbones on an atomic length scale substantially changed the chirality of the crystals in the micrometer length scale. Furthermore, aggregates of these helical crystals in PET(R*-10) did not generate banded spherulites in polarized light microscopy. Possible reasons for this change and loss of helical senses (handedness) on different length scales in chirality transferring processes were discussed.

Epitaxial crystallization of sPP on the (100) lattice plane of HDPE crystals

Crystallization behavior of syndiotactic polypropylene(sPP) on the (100) lattice plane of high-density polyethylene(HDPE) crystals was studied by means of transmission electron microscopy and electron diffraction. The results indicate that sPP crystals can grow epitaxially on the (100) PE lattice plane with their chain directions +/-37 degrees apart from the chain direction of the HDPE substrate. The contact planes are (100) lattice planes for both polymers. This kind of epitaxy is explained in terms of parallel alignment of HDPE chains along the rows formed by the {CH3, CH2,CH3} groups in the (100) lattice plane of the sPP crystals. This implies that in the epitaxial crystallization of sPP with fiber oriented HDPE substrate, not only the (110) but also the (100) HDPE lattice planes can act as the oriented nucleation sites. Furthermore, according to the poor matching between HDPE chains in the (100) lattice plane and the {CH3, CH2, CH3} group rows in the (100) lattice plane of the sPP crystals, it is concluded that the geometric matching is not the only controlling factor for the occurrence of polymer epitaxy.

Epitaxial recrystallization of HDPE-quenched ultrathin films on oriented iPP substrates

The recrystallization behavior of high-density polyethylene (HDPE) on the highly oriented isotactic polypropylene (iPP) substrates at temperatures below the melting temperature of HDPE has been investigated by means of transmission electron microscopy. The results obtained by the bright-field observation and the electron diffraction show that upon annealing the HDPE-quenched films on the oriented iPP substrates at temperatures below 125 degrees C, only a small amount of HDPE recrystallizes on the iPP substrate with [001](HDPE)//[001](iPP), while annealing the HDPE-quenched films at temperatures above 125 degrees C, all of the HDPE crystallites recrystallize epitaxially on the iPP substrate with [001](HDPE)//[101](iPP). (C) 1997 John Wiley & Sons, Inc.