La_(0.5)R_(0.5)Ba_2Cu_3O_7,Pr_(0.5)R_(0.5)Ba_2Cu_3O_7以及RBa_2Cu_3O_7(R=稀土)的键共价性计算

使用复杂晶体化学键理论计算了La0 .5R0 .5Ba2 Cu3O7(R =Pr,Nd ,Sm ,Eu ,Gd ,Dy ,Y ,Ho,Er,Tm ,Yb ,Lu) (La-R12 3) ,Pr0 .5R0 .5Ba2 Cu3O7(R =La ,Nd ,Sm ,Eu ,Gd ,Dy ,Ho ,Y ,Er,Tm ,Yb ,Lu) (Pr -R12 3)以及RBa2 Cu3O7(R =La ,Pr,Nd ,Sm ,Eu ,Gd ,Dy ,Ho ,Y ,Er,Tm) (R12 3)中Cu—O键的键共价性 ,结果表明Pr-R12 3,La-R12 3,以及R12 3都应具有超导性 ,而实验结果是La0 .5Pr0 .5Ba2 Cu3O7,R0 .5Pr0 .5Ba2 Cu3O7(R =La,Nd ,Sm ,Eu ,Gd)无超导性 .产生这种矛盾的原因尚不明确 ,需要做进一步的研究.

Magnetization, magnetotransport and electron magnetic resonance studies of nanoparticles and nanowires of Pr0.5Sr0.5MnO3

In this paper, we present the preparation and characterization of nanoparticles and nanowires of Pr0.5Sr0.5MnO3 (PSMO). The main results of this investigation are as follows: (a) a comparison with the properties of the bulk material shows that the ferromagnetic (FM) transition at 270 K remains unaffected but the anti-ferromagnetic (AFM) transition at TN = 150 K disappears in the nanoparticles, (b) the size induced ground state magnetic phase (below 150 K) is predominantly FM, coexisting with a residual AFM phase, and (c) the temperature dependence of magnetic anisotropy shows complex behaviour, being higher in the nanoparticles at high temperatures and lower at moderately lower temperatures in comparison with the bulk. The results obtained from the extensive magnetization, magnetotransport and electron magnetic resonance studies made on various samples are presented and discussed in detail.

EPR Evidence for Premonitory Charge-Ordering Fluctuations in Hydrothermally Grown Pr0.57Ca0.41Ba0.02MnO3 Nanowires

Electron paramagnetic resonance (EPR) and magnetic properties of nanowires of Pr0.57Ca0.41Ba0.02MnO3 (PCBMO) are studied and compared with those of the bulk material. PCBMO nanowires with diameter of 80-90 nm and length of similar to 3.5 mu m were synthesized by a low reaction temperature hydrothermal method and the bulk sample was prepared following a solid-state reaction route. The samples were characterized by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The bulk PCBMO manganite exhibits charge order at 230 K along with a ferromagnetic transition at 110 K. However, superconducting quantum interference device measurements on the PCBMO nanowires show a complete `melting' of charge ordering and a ferromagnetic transition at 115 K. This result is confirmed by the EPR intensity behavior as well. However, the EPR line width, which is reflective of the spin dynamics, shows a shallow minimum for nanowires at the temperature corresponding to the charge-ordering transition, i.e., 230 K. We interpret this result as an indication of the presence of charge-ordering fluctuations in the nanowires even though the static charge order is absent, thus heralding the occurrence of charge order in the bulk sample.

Localized reversible nanoscale phase separation in Pr0.63Ca0.37MnO3 single crystal using a scanning tunneling microscope tip

We report the destabilization of the charge ordered insulating (COI) state in a localized region of Pr0.63Ca0.37MnO3 single crystal by current injection using a scanning tunneling microscope tip. This leads to controlled phase separation and formation of localized metallic nanoislands in the COI matrix which have been detected by local tunneling conductance mapping. The metallic regions thus created persist even after reducing the injected current to lower values. The original conductance state can be restored by injecting a current of similar magnitude but of opposite polarity. We thus achieve reversible nanoscale phase separation that gives rise to the possibility to "write, read, and erase" nanosized conducting regions in an insulating matrix with high spatial resolution. (c) 2007 American Institute of Physics.

Probing the existing magnetic phases in Pr0.5Ca0.5MnO3 (PCMO) nanowires and nanoparticles: magnetization and magneto-transport investigations

We show from conventional magnetization measurements that the charge order (CO) is completely suppressed in 10 nm Pr0.5Ca0.5MnO3 (PCMO 10) nanoparticles. Novel magnetization measurements, designed by a special high field measurement protocol, show that the dominant ground state magnetic phase is ferromagnetic-metallic (FM-M), which is an equilibrium phase, which coexists with the residual charge ordered anti-ferromagnetic phase (CO AFM) (an arrested phase) and exhibits the characteristic features of a `magnetic glassy state' at low temperatures. It is observed that there is a drastic reduction in the field required to induce the AFM to FM transition (similar to 5-6 T) compared to their bulk counterpart(similar to 27 T); this phase transition is of first order in nature, broad, irreversible and the coexisting phases are tunable with the cooling field. Temperature-dependent magneto-transport data indicate the occurrence of a size-induced insulator-metal transition (TM-I) and anomalous resistive hysteresis (R-H) loops, pointing out the presence of a mixture of the FM-M phase and AFM-I phase.

Scanning Tunneling Spectroscopy on Pr0.68Pb0.32MnO3 single crystals

Scanning tunneling microscopy/spectroscopy studies were carried out on single crystals of colossal magnetoresistive manganite Pr0.68Pb0.32MnO3 at different temperatures in order to probe their spatial homogeneity across the metal-insulator transition temperature TM-I(similar to 255 K). A metallic behavior of the local conductance was observed for temperatures T < TM-I. Zero bias conductance (dI/dV)v=(0), which is directly proportional to the local surface density of states at the Fermi level, shows a single distribution at temperatures T < 200 K suggesting a homogeneous electronic phase at low temperatures. In a narrow temperature window of 200 K < T < TM-I, however, an inhomogeneous distribution of (dI/dV)v=(0) has been observed. This result gives evidence for phase separation in the transition region in this compound.

Scanning Tunneling Spectroscopy on Pr0.68Pb0.32MnO3 single crystals

Scanning tunneling microscopy/spectroscopy studies were carried out on single crystals of colossal magnetoresistive manganite Pr0.68Pb0.32MnO3 at different temperatures in order to probe their spatial homogeneity across the metal-insulator transition temperature TM-I(similar to 255 K). A metallic behavior of the local conductance was observed for temperatures T < TM-I. Zero bias conductance (dI/dV)v=(0), which is directly proportional to the local surface density of states at the Fermi level, shows a single distribution at temperatures T < 200 K suggesting a homogeneous electronic phase at low temperatures. In a narrow temperature window of 200 K < T < TM-I, however, an inhomogeneous distribution of (dI/dV)v=(0) has been observed. This result gives evidence for phase separation in the transition region in this compound.

Scanning Tunneling Spectroscopy on Pr0.68Pb0.32MnO3 single crystals

Scanning tunneling microscopy/spectroscopy studies were carried out on single crystals of colossal magnetoresistive manganite Pr0. 68Pb0.32MnO3 at different temperatures in order to probe their spatial homogeneity across the metal-insulator transition temperature TM-I(similar to 255 K). A metallic behavior of the local conductance was observed for temperatures T < TM-I. Zero bias conductance (dI/dV)v=(0), which is directly proportional to the local surface density of states at the Fermi level, shows a single distribution at temperatures T < 200 K suggesting a homogeneous electronic phase at low temperatures. In a narrow temperature window of 200 K < T < TM-I, however, an inhomogeneous distribution of (dI/dV)v=(0) has been observed. This result gives evidence for phase separation in the transition region in this compound.

An electron paramagnetic resonance study of Pr0.6Ca0.4MnO3 across the charge-ordering transition

We report the first electron paramagnetic resonance studies of single crystals and powders of Pr0.6Ca0.4MnO3 in the 300-4.2 K range, covering the charge-ordering transition (Tco) at ~240 K and antiferromagnetic transition (TN) at ~170 K. The asymmetry parameter for the Dysonian single-crystal spectra shows an anomalous increase at Tco. Below Tco the g-value increases continuously, suggesting a gradual strengthening of the orbital ordering. The linewidth undergoes a sudden increase at Tco and continues to increase down to TN. The intensity increases as the temperature is decreased until Tco is reached, due to the renormalization of the magnetic susceptibility arising from the build-up of ferromagnetic correlations.

Nonlinear conduction in charge-ordered Pr0.63Ca0.37MnO3: Effect of magnetic fields

Nonlinear conduction in a single crystal of charge-ordered Pr0.63Ca0.37MnO3 has bren investigated in an applied magnetic field. In zero field, the nonlinear conduction, which starts at T< T-CO, can give rise to a region of negative differential resistance (NDR) which shows up below the Neel temperature. Application of a magnetic field Inhibits the appearance of NDR and makes the nonlinear conduction strongly hysteritic on cycling of the bias current. This is most severe in the temperature range where the charge-ordered state melts in an applied magnetic field. Our experiment strongly suggests that application of a magnetic field in the charge-ordering regime causes a coexistence of two phases.

Complete 'melting' of charge order in hydrothermally grown Pr0.57Ca0.41Ba0.02MnO3 nanowires

Nanowires of Pr0.57Ca0.41Ba0.02MnO3 (PCBM) (diameter similar to 80-90 nm and length similar to 3.5 mu m) were synthesized by a low reaction temperature hydrothermal method. Single-phase nature of the sample was confirmed by XRD experiments. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to characterize the morphology and microstructures of the nanowires. While the bulk PCBM is known to exhibit charge order (CO) below 230 K along with a ferromagnetic transition at 110 K, SQUID measurements on the nanowires of PCBM show that the charge order is completely absent and a ferromagnetic transition occurs at 115 K. However, the magnetization in the nanowires is observed to be less compared to that in the bulk. This observation of the complete 'melting' of the charge order in the PCBM nanowires is particularly significant in view of the observation of only a weakening of the CO in the nanowires of Pr0.5Ca0.5MnO3. Electron paramagnetic resonance experiments were also carried out on the PCBM nanowires using an X-band EPR spectrometer. Characteristic differences were observed in the line width of nanowires when compared with that of the bulk.

Weakening of charge order and antiferromagnetic to ferromagnetic switch over in Pr0.5Ca0.5MnO3 nanowires

We have prepared crystalline nanowires (diameter ∼ 50 nm, length ∼ a few microns) of the charge-ordering manganite Pr0.5Ca0.5MnO3 using a low reaction temperature hydrothermal method and characterized them using x-ray diffraction, transmission electron microscopy, superconducting quantum interference device (SQUID) magnetometry and electron magnetic resonance measurements. While the bulk sample shows a charge ordering transition at 245 K and an antiferromagnetic transition at 175 K, SQUID magnetometry and electron magnetic resonance experiments reveal that in the nanowires phase, a ferromagnetic transition occurs at ∼ 105 K. Further, the antiferromagnetic transition disappears and the charge ordering transition is suppressed. This result is particularly significant since the charge order in Pr0.5Ca0.5MnO3 is known to be very robust, magnetic fields as high as 27 T being needed to melt it.

Oscillatory exchange bias and training effects in nanocrystalline Pr0.5Ca0.5MnO3

We report on exchange bias effects in 10 nm particles of Pr0.5Ca0.5MnO3 which appear as a result of competing interactions between the ferromagnetic (FM)/anti-ferromagnetic (AFM) phases. The fascinating new observation is the demonstration of the temperature dependence of oscillatory exchange bias (OEB) and is tunable as a function of cooling field strength below the SG phase, may be attributable to the presence of charge/spin density wave (CDW/SDW) in the AFM core of PCMO10. The pronounced training effect is noticed at 5 K from the variation of the EB field as a function of number of field cycles (n) upon the field cooling (FC) process. For n > 1, power-law behavior describes the experimental data well; however, the breakdown of spin configuration model is noticed at n >= 1. Copyright 2012 Author(s). This article is distributed under a Creative Commons Attribution 3.0 Unported License. http://dx.doi.org/10.1063/1.3696033]