Measurement of the first neutron diffraction peak of D2O flowing in a 2 mm diameter aluminium tube as a function of temperature

A pilot experiment was performed using the WOMBAT powder diffraction instrument at ANSTO in which the first neutron diffraction peak (Q0) was measured for D2O flowing in a 2 mm internal diameter aluminium tube. Measurements of Q0 were made at -9, 4.3, 6.9, 12, 18.2 and 21.5 °C. The D2O was circulated using a siphon with water in the lower reservoir returned to the upper reservoir using a small pump. This enabled stable flow to be maintained for several hours. For example, if the pump flow increased slightly, the upper reservoir level rose, increasing the siphon flow until it matched the return flow. A neutron wavelength of 2.4 Å was used and data integrated over 60 minutes for each temperature. A jet of nitrogen from a liquid N2 Dewar was directed over the aluminium tube to vary water temperature. After collection of the data, the d spacing of the aluminium peaks was used to calculate the temperature of the aluminium within the neutron beam and therefore was considered to be an accurate measure of water temperature within the beam. Sigmaplot version 12.3 was used to fit a Weibull five parameter peak fit to the first neutron diffraction peak. The values of Q0 obtained in this experiment showed an increase with temperature consistent with data in the literature [1] but were consistently higher than published values for bulk D20. For example at 21.5 °C we obtained a value of 2.008 Å-1 for Q0 compared to a literature value of 1.988 Å-1 for bulk D2O at 20 °C, a difference of 1%. Further experiments are required to see if this difference is real or artifactual.

A neutron diffraction investigation of residual stresses in rail ends after severe deformation of rail surfaces

Insulated rail joints (IRJs) are a primary component of the rail track safety and signalling systems. Rails are supported by two fishplates which are fastened by bolts and nuts and, with the support of sleepers and track ballast, form an integrated assembly. IRJ failure can result from progressive defects, the propagation of which is influenced by residual stresses in the rail. Residual stresses change significantly during service due to the complex deformation and damage effects associated with wheel rolling, sliding and impact. IRJ failures can occur when metal flows over the insulated rail gap (typically 6-8 mm width), breaks the electrically isolated section of track and results in malfunction of the track signalling system. In this investigation, residual stress measurements were obtained from rail-ends which had undergone controlled amounts of surface plastic deformation using a full scale wheel-on-track simulation test rig. Results were compared with those obtained from similar investigations performed on rail ends associated with ex-service IRJs. Residual stresses were measured by neutron diffraction at the Australian Nuclear Science and Technology Organisation (ANSTO). Measurements with constant gauge volume 3x3x3 mm3 were carried in the central vertical plane on 5mm thick sliced rail samples cut by an electric discharge machine (EDM). Stress evolution at the rail ends was found to exhibit characteristics similar to those of the ex-service rails, with a compressive zone of 5mm deep that is counterbalanced by a tension zone beneath, extending to a depth of around 15mm. However, in contrast to the ex-service rails, the type of stress distribution in the test-rig deformed samples was apparently different due to the localization of load under the particular test conditions. In the latter, in contrast with clear stress evolution, there was no obvious evolution of d0. Since d0 reflects rather long-term accumulation of crystal lattice damage and microstructural changes due to service load, the loading history of the test rig samples has not reached the same level as the ex-service rails. It is concluded that the wheel-on-rail simulation rig provides the potential capability for testing the wheel-rail rolling contact conditions in rails, rail ends and insulated rail joints.

Residual stresses in rail-ends from the in-service insulated rail joints using neutron diffraction

Insulated rail joints (IRJs) are an integral part of the rail track signaling system and pose significant maintenance and replacement costs due to their low and fluctuating service lives. Failure occurs mainly in rail head region, bolt- holes of fishplates and web-holes of the rails. Propagation of cracks is influenced by the evolution of internal residual stresses in rails during rail manufacturing (hot-rolling, roller-straightening, and head-hardening process), and during service, particularly in heavy rail haul freight systems where loads are high. In this investigation, rail head accumulated residual stresses were analysed using neutron diffraction at the Australian Nuclear Science and Technology Organisation (ANSTO). Two ex-service two head-hardened rail joints damaged under different loading were examined and results were compared with those obtained from an unused rail joint reference sample in order to differentiate the stresses developed during rail manufacturing and stresses accumulated during rail service. Neutron diffraction analyses were carried out on the samples in longitudinal, transverse and vertical directions, and on 5mm thick sliceed samples cut by Electric Discharge Machining (EDM). For the rail joints from the service line, irrespective of loading conditions and in-service times, results revealed similar depth profiles of stress distribution. Evolution of residual stress fields in rails due to service was also accompanied by evidence of larger material flow based on reflected light and scanning electron microscopy studies. Stress evolution in the vicinity of rail ends was characterised by a compressive layer, approximately 5 mm deep, and a tension zone located approximately 5- 15mm below the surfaces. A significant variation of d0 with depth near the top surface was detected and was attributed to decarburization in the top layer induced by cold work. Stress distributions observed in longitudinal slices of the two different deformed rail samples were found to be similar. For the undeformed rail, the stress distributions obtained could be attributed to variations associated with thermo-mechanical history of the rail.

Nanostructured metal hydrides for hydrogen storage studied by in situ synchrotron and neutron diffraction

This work was focused on studies of the metal hydride materials having a potential in building hydrogen storage systems with high gravimetric and volumetric efficiencies of H storage and formed / decomposed with high rates of hydrogen exchange. In situ diffraction studies of the metal-hydrogen systems were explored as a valuable tool in probing both the mechanism of the phase-structural transformations and their kinetics. Two complementary techniques, namely Neutron Powder Diffraction (NPD) and Synchrotron X-ray diffraction (SR XRD) were utilised. High pressure in situ NPD studies were performed at D2 pressures reaching 1000 bar at the D1B diffractometer accommodated at Institute Laue Langevin, Grenoble. The data of the time resolved in situ SR XRD were collected at the Swiss Norwegian Beam Lines, ESRF, Grenoble in the pressure range up to 50 bar H2 at temperatures 20-400°C. The systems studied by NPD at high pressures included deuterated Al-modified Laves-type C15 ZrFe2-xAlx intermetallics with x = 0.02; 0.04 and 0.20 and the CeNi5-D2 system. D content, hysteresis of H uptake and release, unit cell expansion and stability of the hydrides systematically change with Al content. Deuteration exhibited a very fast kinetics; it resulted in increase of the unit cells volumes reaching 23.5 % for ZrFe1.98Al0.02D2.9(1) and associated with exclusive occupancy of the Zr2(Fe,Al)2 tetrahedra. For CeNi5 deuteration yielded a hexahydride CeNi5D6.2 (20°C, 776 bar D2) and was accompanied by a nearly isotropic volume expansion reaching 30.1% (∆a/a=10.0%; ∆c/c=7.5%). Deuterium atoms fill three different interstitial sites including Ce2Ni2, Ce2Ni3 and Ni4. Significant hysteresis was observed on the first absorption-desorption cycle. This hysteresis decreased on the absorption-desorption cycling. A different approach to the development of H storage systems is based on the hydrides of light elements, first of all the Mg-based ones. These systems were studied by SR XRD. Reactive ball milling in hydrogen (HRBM) allowed synthesis of the nanostructured Mg-based hydrides. The experimental parameters (PH2, T, energy of milling, ball / sample ratio and balls size), significantly influence rate of hydrogenation. The studies confirmed (a) a completeness of hydrogenation of Mg into MgH2; (b) indicated a partial transformation of the originally formed -MgH2 into a metastable -MgH2 (a ratio / was 3/1); (c) yielded the crystallite size for the main hydrogenation product, -MgH2, as close to 10 nm. Influence of the additives to Mg on the structure and hydrogen absorption/desorption properties and cycle behaviour of the composites was established and will be discussed in the paper.

Structural correlations in GexSe1-x glasses - a neutron diffraction study

Neutron diffraction measurement is carried out on GexSe1-x glasses, where 0.1 less than or equal to x less than or equal to 0.4, in a Q interval of 0.55-13.8 Angstrom(-1). The first sharp diffraction peak (FSDP) in the structure factor, S(Q), shows a systematic increase in the intensity and shifts to a lower Q with increasing Ge concentration. The coherence length of FSDP increases with x and becomes maximum for 0.33 less than or equal to x less than or equal to 0.4. The Monte-Carlo method, due to Soper, is used to generate S(Q) and also the pair correlation function, g(r). The generated S(Q) is in agreement with the experimental data for all x. Analysis of the first four peaks in the total correlation function, T(r), shows that the short range order in GeSe2 glass is due to Ge(Se-1/2)(4) tetrahedra, in agreement with earlier reports. Se-rich glasses contain Se-chains which are cross-linked with Ge(Se-1/2)(4) tetrahedra. Ge-2(Se-1/2)(6) molecular units are the basic structural units in Ge-rich, x = 0.4, glass. For x = 0.2, 0.33 and 0.4 there is evidence for some of the tetrahedra being in an edge-shared configuration. The number of edge-shared tetrahedra in these glasses increase with increasing Ge content.

A neutron diffraction investigation of the structure of PBO-PBCL2 glasses

Neutron diffraction techniques have been employed to investigate the structure of PbO-PbCl2 glasses as a function of composition in the nominal range PbO.PbCl2 to 9PbO.PbCl2. It is concluded that, whereas the first Pb-O distance is well defined, the distribution of Pb-Cl distances is much broader, in agreement with a previous EXAFS study.

Neutron-diffraction study of structure and conformation of nucleotide uridine-5 phosphate (disodium salt)

Acta Crystallographica Section A: Foundations of Crystallography covers theoretical and fundamental aspects of the structure of matter. The journal is the prime forum for research in diffraction physics and the theory of crystallographic structure determination by diffraction methods using X-rays, neutrons and electrons. The structures include periodic and aperiodic crystals, and non-periodic disordered materials, and the corresponding Bragg, satellite and diffuse scattering, thermal motion and symmetry aspects. Spatial resolutions range from the subatomic domain in charge-density studies to nanodimensional imperfections such as dislocations and twin walls. The chemistry encompasses metals, alloys, and inorganic, organic and biological materials. Structure prediction and properties such as the theory of phase transformations are also covered.

Neutron diffraction evidence for oxygen dimers in Bi-Ca-Sr-Cu-O superconductors

A comparative neutron diffraction study of Bi2CaSr2Cu2O8+δ, Bi2Ca2SrCu2O8+δ and Bi2Ca1.5Y0.5SrCu2O8+δ has not only shown the presence of considerable oxygen excess in the Bi layers, but also evidence for oxygen pairing giving rise to O1−2 or O2−2 type species, probably the latter. The proportion of the paired species increases when Y partly replaces Ca. Furthermore, the Tc decreases with an increase in paired species.

A neutron diffraction study of LaBa2Cu3O7−δ

The correlation between structure and oxygen content in the LaBa2Cu3O7+δ was investigated by neutron powder diffraction. It is shown that the structure is orthorhombic (Pmmm) when δ = −0.04 and tetragonal (P4/mmm) when δ = −0.06. Such a change in structure accompanying a very small variation in oxygen stoichiometry is remarkable. In the orthorhombic structure of the δ = −0.04 sample, there is 70% oxygen occupancy for the linear chain site Image and 34% for the Image site. The La sites have 13.6% Ba when δ = −0.04 and 11.2% Ba when δ = −0.06; the Ba sites have 10% La in both cases.

An X-ray and neutron diffraction study of cation substituted TlSr2CuO5

The structures of TlSr(2−x)LaxCuO(5+δ), with x=0.5, 0.75 and 1, and Tl.5Pb0.5Sr2CuO(5+δ) have been examined with X-ray and neutron powder Rietveld refinement. They are isostructural (P4/mmm) with the corresponding thallium-barium cuprate having one Cu-O layer with Cu3+ ions in octahedral coordination with oxygen (structure type 1201). The influence of cation substitution and disorder on the structure and superconducting properties of these phases have been investigated. La3+ substitution for Sr2+ stabilises the structure and reduces Cu3+, permitting superconductivity, while Pb2+ substitution for Tl3+ only stabilises the structure, without reducing Cu3+.

A structural study of Li2S---B2S3 glasses by neutron diffraction

The radial distribution functions (RDFs) of five xLi2S.(1 - x)B2S3 glasses (x = 0.55, 0.60, 0.67, 0.71 and 0.75) have been determined from neutron diffraction experiments performed at the Institut Laue-Langevin, Grenoble. These glasses are prepared by casting a molten mixture of boron, sulphur and Li2S inside a controlled atmosphere glovebox. Addition of the Li2S Modifier is found gradually to suppress all peaks corresponding to interatomic distances > 3.5 angstrom, which implies that the structural entities present in these glasses become segmented, and therefore more ionic, as x increases. The assumption of the existence of four main structural entities based on four- and three-coordinated borons (the latter carrying bridging and/or non-bridging sulphurs) accounts for all the peaks present in the RDFs as a function of composition. Furthermore, in the most modified glass (x = 0.75), that which contains only 'isolated' BS33- triangles, there seems to be evidence for either octahedral or tetrahedral coordination of Li+ by S- ions

Neutron diffraction study of the coupling between spin, lattice, and structural degrees of freedom in 0.8BiFeO(3)-0.2PbTiO(3)

A powder neutron diffraction study was carried out on 0.8BiFeO(3)-0.2PbTiO(3) in the temperature range 27-1000 degrees C. The system exhibits magnetic transition at similar to 300 degrees C and a rhombohedral (R3c)-cubic (Pm3m) ferroelectric phase transition at similar to 650 degrees C. Anomalous variation in the lattice parameters and the octahedral tilt angle is observed across the magnetic transition temperature. In the magnetic phase, the c parameter is contracted and the octahedral tilt angle is slightly increased. The results suggest coupling between the spin, lattice and structural degrees of freedom. (C) 2011 American Institute of Physics. doi:10.1063/1.3555093]

Neutron diffraction, Mossbauer effect and Electron Paramagnetic Resonance studies on multiferroic Pb(Fe2/3W1/3)O-3

Multiferroic Pb(Fe2/3W1/3)O-3 ceramics were synthesized via a modified two-stage Columbite method. Single phase formation was confirmed from the analysis of x-ray and neutron diffraction patterns recorded at room temperature. Structural analysis of the diffraction data reveals cubic phase (space group Pm-3m) for the title compound. Magnetic structure of the title compound at room temperature exhibits G-type antiferromagnetic structure. The Mossbauer spectroscopy and Electron Paramagnetic Resonance (EPR) studies were carried out at 300 K. The isomer shift and quadrupole splitting of the Mossbauer spectra confirms the trivalent state of iron (Fe3+). The Mossbauer spectra also suggest that the iron and tungsten are randomly distributed at the octahedral, B site. EPR spectra show a single broad line associated with Fe3+ ions. Both spectra clearly exhibit weak ferromagnetic behaviour of Pb(Fe2/3W1/3)O-3 ceramic at 300 K. Considering neutron diffraction, Mossbauer and EPR results together, it may be stated here that Pb(Fe2/3W1/3)O-3 exhibits antiferromagnetic behavior along with weak ferromagnetism at room temperature.

Liquid alumina: detailed atomic coordination determined from neutron diffraction data using empirical potential structure refinement

Greaves, George; Jenkins, T.E.; Landron, C.; Hennet, L., (2001) 'Liquid alumina: detailed atomic coordination determined from neutron diffraction data using empirical potential structure refinement', Physical Review Letters 86 pp.4839-4842 RAE2008