Microstructure of organometallic derived PLZT ceramics

The PLZT powders with the formula Pb0.905La0.095(Zr0.65Ti0.35)(0.976)O-3+3.5 wt.% PbO were prepared by the organometallic precursor method (Pechini and partial oxalate processes). The microstructure of sintered 9.5/65/35 PLZT ceramics obtained from a partial oxalate procedure shows that the outstanding feature of this microstructure is its fairly uniform grains of about 1.8 mum. The microstructure of sintered PLZT ceramics obtained by the Pechini process consists of uniform small randomly- oriented grains tightly bonded together in the central part of the sample with,a grain size of about 1.2 mum. Cubic and elongated grains are formed at the sample's border. The microstructures of hot pressed PLZT ceramics obtained from both processes are dense and rather uniform. After a double stage of hot pressing (2 plus 20 h) the microstructure of PLZT is fully dense, uniform and homogeneous with a grain size of approximately 2.5 mum. (C) 2001 Elsevier B.V. Ltd. All rights reserved.

How Cr2O3 influences the microstructure and nonohmic features of the SnO2(COx, Mn1-x)O-based varistor system

An investigation was made to discover how the addition of Cr2O3 affects the microstructural heterogeneity and nonohmic features of the SnO2(Co-x, Mn1-x)O-based varistor system, with x varying from 0 to 1. The presence of Cr2O3 was found to strongly increase the nonohmic features when x = 1. However, the nonohmic features of the system decrease when x drops from 1 to 0, a behavior explained by the increase of the junction heterogeneity within the system's microstructure. accompanied by ail excess of precipitates at the triple point in the grain boundary region due to modified MnO sintering. The presence of these precipitates causes the leakage current to increase in response to the creation of ail ineffective barrier. The effect produced by heat-treating these systems in oxygen- and nitrogen-rich atmospheres suggests that, according to mechanisms previously discussed in the literature, Cr2O3 is more susceptible to oxygen, so that increasing the amount of oxygen in the grain boundary region may improve the system's nonohmic properties. (c) 2005 Elsevier Ltd. All rights reserved.

Mechanical properties and cytotoxicity of 3Y-TZP bioceramics reinforced with Al(2)O(3) particles

The influence of Al(2)O(3) addition and sintering parameters on the mechanical properties and cytotoxicity of tetragonal ZrO(2)-3 mol% Y(2)O(3) ceramics was evaluated. Samples containing 0, 10, 20 and 30 wt.% of Al(2)O(3) particles were prepared by cold uniaxial pressing (80 MPa) and sintered in air at 1500, 1550 and 1600 degrees C for 120 min. The effects of the sintering conditions on the microstructure were analyzed by X-ray diffraction analysis and scanning electron microscopy. Hardness and fracture toughness were determined by the Vickers indentation method and the mechanical resistance by four-point bending tests. As a preliminary biological evaluation, ""in vitro"" cytotoxicity tests were realized to determine the cytotoxic level of the ZrO(2)-Al(2)O(3) composites, using the neutral red uptake method with NCTC clones L929 from the American Type Culture Collection (ATCC) bank. Fully dense ceramic materials were obtained with a hardness ranging between 1340 HV and 1585 HV, depending on the amount of Al(2)O(3) in the ZrO(2) matrix. On the other hand, no significant influence of the Al(2)O(3) addition on fracture toughness was observed, exhibiting values near 8 MPa m(1/2) for all compositions and sintering conditions studied. The non-cytotoxic behavior, the elevated fracture toughness, the good bending strength (sigma(f) = 690 MPa) and the elevated Weibull`s modulus (m = 11) exhibited by the material, show that these ceramic composites are highly suitable biomaterials for dental implant applications. (C) 2008 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Infiltration of Al2O3/Y2O3 mix into SiC ceramic preforms

Silicon carbide ceramics are very interesting materials to engineering applications because of their properties. These ceramics are produced by liquid phase sintering (LPS), where elevated temperature and time are necessary, and generally form volatile products that promote defects and damage their mechanical properties. In this work was studied the infiltration process to produce SiC ceramics, using shorter time and temperature than LPS, thereby reducing the undesirable chemical reactions. SiC powder was pressed at 300 MPa and pre-sintered at 1550 degrees C for 30 min. Unidirectional and spontaneous infiltration of this preform by Al2O3/Y2O3 liquid was done at 1850 degrees C for 5, 10, 30 and 60 min. The kinetics of infiltration was studied, and the infiltration equilibrium happened when the liquid infiltrated 12 mm into perform. The microstructures show grains of the SiC surrounded by infiltrated additives. The hardness and fracture toughness are similar to conventional SiC ceramics obtained by LPS. (c) 2007 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Phase and microstructural evolution during the heat treatment of Sm-Ca-alpha-sialon ceramics

The phase and microstructural evolution of multi-cation Sm-Ca-alpha-sialon ceramics was investigated. Six samples were prepared, ranging from a pure Sm-sialon to a pure Ca-sialon, with calcium replacing samarium in 20 eq% increments, thus maintaining an equivalent design composition in all samples. After pressureless sintering at 1820 degreesC for 2 It, all samples were subsequently heat treated up to 192 h at 1450 and 1300 degreesC. The amount of grain boundary glass in the samples after sintering was observed to decrease with increasing calcium levels. A M-ss' or M-ss',-gehlenite solid solution was observed to form during the 1450 degreesC heat treatment of all Sm-containing samples, and this phase forms in clusters in the high-Sm samples. The thermal stability of the alpha-sialon phase was improved in the multi-cation systems. Heat treatment at 1300 degreesC produces SmAlO3 in the high-Sm samples, a M-ss',-gehlenite solid solution in the high-Ca samples, and a Sm-Ca-apatite phase in some intermediate samples. (C) 2002 Elsevier Science Ltd. All rights reserved.

α′ phase stability in Nd-Li-sialon systems

The formability and stability of the alpha-sialon (alpha') phase was investigated in multi-cation Nd-Li-sialon systems. Four samples were prepared, ranging from a pure Nd-sialon to a pure Li-sialon, with two intermediate samples being prepared with either lithium or neodymium replacing the other alpha'-stabilising additive by 20 eq.%, as to maintain an equivalent design composition in all samples. After sintering, all samples were subsequently heat treated up to 192 h at 1450 and 1300 degreesC. While significant quantities of the beta'-sialon (beta' phase were found in most samples, the high-lithium Li-Nd-sialon sample was found to be almost pure a' phase after sintering. Furthermore, the long-term stability of the a' phase on heat treatment was also found to be superior in both multi-cation samples than in either of the single-alpha'-stabilising-cation samples. This is thought to be related to improved retention of the lithium in the multi-cation systems, as much of the lithium was found to volatilise during sintering in the neodymium-free sample. (C) 2002 Elsevier Science Ltd. All rights reserved.

Microstructural, structural and dielectric properties of Er(3+)-modified BaTi(0.85)Zr(0.15)O(3) ceramics

The (micro)structural and electrical properties of undoped and Er(3+)-doped BaTi(0.85)Zr(0.15)O(3) ceramics were studied in this work for both nominal Ba(2+) and Ti(4+) substitution formulations. The ceramics were produced from solid-state reaction and sintered at 1400 degrees C for 3 h. For those materials prepared following the donor-type nominal Ba(1-x)Er(x)(Ti(0.85)Zr(0.15))O(3) composition, especially, Er(3+) however showed a preferential substitution for the (Ti,Zr)(4+) lattice sites. This allowed synthesis of a finally acceptor-like, highly resistive Ba(Ti,Zr,Er)O(3-delta)-like system, with a solubility limit below but close to 3 cat.% Er(3+). The overall phase development is discussed in terms of the amphoteric nature of Er(3+), and appears to mainly or, at least, partially also involve a minimization of stress effects from the ion size mismatch between the dopant and host cations. Further results presented here include a comparative analysis of the behavior of the materials` grain size, electrical properties and nature of the ferroelectric-to-paraelectric phase transition upon variation of the formulation and Er(3+) content. (C) 2008 Elsevier Ltd. All rights reserved.

Microstructural, structural and electrical properties of La(3+)-modified Bi(4)Ti(3)O(12) ferroelectric ceramics

Bi(4-x)La(x)Ti(3)O(12) (BLT) ceramics were prepared and studied in this work in terms of La(3+)-modified microstructure and phase development as well as electrical response. According to the results processed from X-ray diffraction and electrical measurements, the solubility limit (XL) of La(3+) into the Bi(4)Ti(3)O(12) (BIT) matrix was here found to locate slightly above x = 1.5. Further, La(3+) had the effect of reducing the material grain size, while changing its morphology from the plate-like form, typical of BIT ceramics, to a spherical-like one. The electrical results presented and discussed here also include the behavior of the temperature of the ferroelectric-paraelectric phase transition as well as the normal or diffuse and/or relaxor nature of this transition depending on the La(3+) content. (c) 2008 Elsevier Ltd. All fights reserved.

Comparison of fracture surface and plane section analysis for ceramic grain size characterisation

A method has been developed to obtain quantitative information about grain size and shape from fractured surfaces of ceramic materials. One elaborated a routine to split intergranular and transgranular grains facets of ceramic fracture surfaces by digital image processing. A commercial ceramic (ALCOA A-16, Al2O3-1.5% of CrO) was used to test the proposed method. Microstructural measurements of grain shape and size taken from fracture surfaces have been compared through descriptive statistics of distributions, with the corresponding measurements from polished and etched surfaces. The agreement between results, with the expected bias on grain size values from fractures, obtained for both types of surfaces allowed to infer that this new technique can be used to extract the relevant microstructural information from fractured surfaces, thus minimising the time consuming steps of sample preparation. (C) 2003 Elsevier Ltd. All rights reserved.

Grain-boundary segregation and precipitates in La2O3 and Pr2O3 doped SnO2 center dot CoO-based varistors

Structural heterogeneities in SnO2.CoO-based varistors were analyzed by transmission electron microscopy. In SnO2.CoO-based system doped with La2O3 and Pr2O3 two kinds of precipitate phases at grain boundary region were found. Using energy dispersive spectrometry they were found to be Co2SnO4 and Pr2Sn2O7, presenting a defined crystalline structure. It was also identified that such precipitate phases are mainly located in triple-junctions of the microstructure. HRTEM analysis revealed the existence of other two types of junctions, one as being homo-junctions of SnO2 grains and other due to twin grain boundaries inside the SnO2.CoO grain. The role of these types of junction in the overall nonlinear electrical features is also discussed. (C) 2003 Elsevier B.V. Ltd. All rights reserved.

Electrical and micro structural properties of (Zn, Nb, Fe)-doped SnO2 varistor systems

The electrical and microstructural properties of SnO2-based varistors with the addition of 0.025 and 0.050 mol% of Fe2O3 have been characterised. Electric field (E) versus current density (J) curves showed that the effect of Fe2O3 addition is to increase both the non-linear coefficient and the breakdown voltage. Variations in the potential barrier height were inferred from impedance spectroscopy (IS) analysis. Through transmission electron microscopy (TEM), the presence of precipitates of secondary phases was confirmed. Samples with precipitates displayed poor electrical properties. (c) 2004 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Microstructural investigation of the PZT films prepared from the suspension of nanocrystalline powders

PZT thin films of composition Pb(Zr0.52Ti0.48)O-3 were prepared by a novel method from the suspension of nanocrystalline PZT powders. The powders were obtained by mechanochemical synthesis. Films were deposited on silicon (100) and platinum covered silicon substrates (Pt (111) /Ti/SiO2/Si) Using spin-on technique. Substrate type has influence on films crystallinity, orientation and can react with the films changing its phase composition. Films microstructure strongly depends on thermal treatment conditions due to phase and compositional changes of the films. (C) 2003 Elsevier Ltd. All rights reserved.

Effect of ceria content on the sintering of ZrO2 based ceramics synthesized from a polymeric precursor

Zirconia-ceria powders with ceria concentration varying from 0 to 12 mol% were synthesized using a polymeric precursor route based on the Pechini process. Powder characteristics were evaluated with regard to the crystallite size, BET surface area, phase distribution, nitrogen adsorption/desorption behavior, and agglomeration state. Sintering was studied considering the shrinkage rate, densification, grain size, and phase evolution. It was demonstrated that the synthesis method is effective to prepare nanosized powders of tetragonal zirconia single-phase. Sinterability mainly depended on the agglomeration state of powders and the monoclinic phase content, fully tetragonal zirconia ceramic, with grain size of 2.4 mu m, was obtained after addition of at least 9 mol% ceria and sintering at 1500 degrees C for 4 h. (C) 2000 Elsevier B.V. Ltd. All rights reserved.

Multi-layered LiNbO3 films prepared by a polymeric precursor method

The polymeric precursor method was used to prepare multi-layered LiNbO3 films. The overall process consists of preparing a coating solution from the Pechini process and the deposited film is subsequently heat-treated. Two-layered films were prepared by this process, onto (0001) sapphire substrates. Two different routes were investigated for the heat-treatment. The amorphous route consisted of performing, after each deposition, a pre-treatment at low temperature to eliminate the organic material. In this case, the crystallization heat-treatment was performed only after the two layers had been deposited. on the other hand, a process layer-after-layer crystallization was used. Both routes led to (0001) LiNbO3 oriented films. However, only the film prepared by the layer-after-layer crystallization presented an epitaxial growth and a crack-free morphology. Moreover, the layer-after-layer crystallization process led to a film exhibiting the best optical properties. (C) 2001 Elsevier B.V. Ltd. All rights reserved.

Analysis of secondary phases segregated and precipitated in SnO2-based varistors

Transmission and scanning electron microscopy techniques were used to study the heterogeneities found in the microstructure of (SnO2Co3O4Nb2O5Fe2O3)-Co-.-Nb-.-Fe-. and (SnO2ZnONb2O5FC2O3)-Zn-.-Nb-.-F-. varistors. Second phases encountered both inside the grains and ingrain boundary regions were identified using energy dispersive spectrometry and electron diffraction patterns. Through the electrical characterisation, the presence of iron oxide among the additives was determined to highlight the non-linear properties of the specimens. A discussion on the influence of second phases on the non-linear features of these systems is also addressed. (C) 2004 Elsevier Ltd. All rights reserved.