Charge accumulation and transport in degenerately doped semiconducting polymers with mixed ionic and electronic conductivity

This thesis is part of the fields of Material Physics and Organic Electronics and aims to determine the charge carrier density and mobility in the hydrated conducting polymer–polyelectrolyte blend PEDOT:PSS. This kind of material combines electronic semiconductor functionality with selective ionic transport, biocompatibility and electrochemical stability in water. This advantageous material properties combination makes PEDOT:PSS a unique material to build organic electrochemical transistors (OECTs), which have relevant application as amplifying transducers for bioelectronic signals. In order to measure charge carrier density and mobility, an innovative 4-wire, contact independent characterization technique was introduced, the electrolyte-gated van der Pauw (EgVDP) method, which was combined with electrochemical impedance spectroscopy. The technique was applied to macroscopic thin film samples and micro-structured PEDOT:PSS thin film devices fabricated using photolithography. The EgVDP method revealed to be effective for the measurements of holes’ mobility in hydrated PEDOT:PSS thin films, which resulted to be <μ>=(0.67±0.02) cm^2/(V*s). By comparing this result with 2-point-probe measurements, we found that contact resistance effects led to a mobility overestimation in the latter. Ion accumulation at the drain contact creates a gate-dependent potential barrier and is discussed as a probable reason for the overestimation in 2-point-probe measurements. The measured charge transport properties of PEDOT:PSS were analyzed in the framework of an extended drift-diffusion model. The extended model fits well also to the non-linear response in the transport characterization and results suggest a Gaussian DOS for PEDOT:PSS. The PEDOT:PSS-electrolyte interface capacitance resulted to be voltage-independent, confirming the hypothesis of its morphological origin, related to the separation between the electronic (PEDOT) and ionic (PSS) phases in the blend.

Transporte de carga em compósitos de polianilina/V2O5

In this work, composites formed from a mixture of V2O5 and polyaniline (PANI) were investigated, for applications as cathode materials for secondary lithium batteries. Electrochemical quartz crystal microbalance (EQCM) data show that charge compensation in the [PANI]0.3V2O5 nanocomposite is achieved predominantly by Li+ migration. However, the charge compensation in the [PANI]V2O5 microcomposite occurs by Li+ and ClO4- transport. Electrochemical Impedance Spectroscopy (EIS) measurements reveal several benefits of nanohybrid formation, including the achievement of shorter ionic diffusion pathways, the higher diffusion rate of the lithium ion and also the higher electronic conductivity, which are responsible for a synergetic effect of the energy storage properties.

Haja-asutusalueiden pienjätevedenpuhdistamoiden online-monitoroinnin kehitysmahdollisuudet

The aim of this Bachelor's thesis was to investigate potentialities of online-monitoring the efficiency of small scale wastewater treatment systems. Evolving legislation currently sets minimum boundaries of relative decrease in levels of phosphorus, nitrogen and BOD in abovementioned applications, yet no monitoring requirements for such systems are determined. Inherently, no applicable monitoring system for these parameters exist. However, some measuring methods offer potentialities for estimating the reduction of these certain parameters in a wastewater stream treated in a small scale system. Such methods could be found for example among electronic noses, measuring of electronic conductivity or turbidity.

Lithium Containing Complex Metal Oxides and Metal phosphates:Investigations on their synthesis and various characterizations for rechargeable lithium battery applications

The work presented in the thesis is centered around two important types of cathode materials, the spinel structured LixMn204 (x =0.8to1.2) and the phospho -oIivine structured LiMP04 (M=Fe and Ni). The spinel system LixMn204, especially LiMn204 corresponding to x= 1 has been extensively investigated to understand its structural electrical and electrochemical properties and to analyse its suitability as a cathode material in rechargeable lithium batteries. However there is no reported work on the thermal and optical properties of this important cathode material. Thermal diffusivity is an important parameter as far as the operation of a rechargeable battery is concerned. In LixMn204, the electronic structure and phenomenon of Jahn-Teller distortion have already been established theoretically and experimentally. Part of the present work is an attempt to use the non-destructive technique (NDT) of photoacoustic spectroscopy to investigate the nature of the various electronic transitions and to unravel the mechanisms leading to the phenomenon of J.T distortion in LixMn204.The phospho-olivines LiMP04 (M=Fe, Ni, Mn, Co etc) are the newly identified, prospective cathode materials offering extremely high stability, quite high theoretical specific capacity, very good cycIability and long life. Inspite of all these advantages, most of the phospho - olivines especially LiFeP04 and LiNiP04 show poor electronic conductivity compared to LixMn204, leading to low rate capacity and energy density. In the present work attempts have been made to improve the electronic conductivity of LiFeP04 and LiNiP04 by adding different weight percentage MWNT .It is expected that the addition of MWNT will enhance the electronic conductivity of LiFeP04 and LiNiP04 with out causing any significant structural distortions, which is important in the working of the lithium ion battery.

New studies on the versatile roles of Polyaniline and its composites in polymer based optoelectronic and energy storage devices

From the early stages of the twentieth century, polyaniline (PANI), a well-known and extensively studied conducting polymer has captured the attention of scientific community owing to its interesting electrical and optical properties. Starting from its structural properties, to the currently pursued optical, electrical and electrochemical properties, extensive investigations on pure PANI and its composites are still much relevant to explore its potentialities to the maximum extent. The synthesis of highly crystalline PANI films with ordered structure and high electrical conductivity has not been pursued in depth yet. Recently, nanostructured PANI and the nanocomposites of PANI have attracted a great deal of research attention owing to the possibilities of applications in optical switching devices, optoelectronics and energy storage devices. The work presented in the thesis is centered around the realization of highly conducting and structurally ordered PANI and its composites for applications mainly in the areas of nonlinear optics and electrochemical energy storage. Out of the vast variety of application fields of PANI, these two areas are specifically selected for the present studies, because of the following observations. The non-linear optical properties and the energy storing properties of PANI depend quite sensitively on the extent of conjugation of the polymer structure, the type and concentration of the dopants added and the type and size of the nano particles selected for making the nanocomposites. The first phase of the work is devoted to the synthesis of highly ordered and conducting films of PANI doped with various dopants and the structural, morphological and electrical characterization followed by the synthesis of metal nanoparticles incorporated PANI samples and the detailed optical characterization in the linear and nonlinear regimes. The second phase of the work comprises the investigations on the prospects of PANI in realizing polymer based rechargeable lithium ion cells with the inherent structural flexibility of polymer systems and environmental safety and stability. Secondary battery systems have become an inevitable part of daily life. They can be found in most of the portable electronic gadgets and recently they have started powering automobiles, although the power generated is low. The efficient storage of electrical energy generated from solar cells is achieved by using suitable secondary battery systems. The development of rechargeable battery systems having excellent charge storage capacity, cyclability, environmental friendliness and flexibility has yet to be realized in practice. Rechargeable Li-ion cells employing cathode active materials like LiCoO2, LiMn2O4, LiFePO4 have got remarkable charge storage capacity with least charge leakage when not in use. However, material toxicity, chance of cell explosion and lack of effective cell recycling mechanism pose significant risk factors which are to be addressed seriously. These cells also lack flexibility in their design due to the structural characteristics of the electrode materials. Global research is directed towards identifying new class of electrode materials with less risk factors and better structural stability and flexibility. Polymer based electrode materials with inherent flexibility, stability and eco-friendliness can be a suitable choice. One of the prime drawbacks of polymer based cathode materials is the low electronic conductivity. Hence the real task with this class of materials is to get better electronic conductivity with good electrical storage capability. Electronic conductivity can be enhanced by using proper dopants. In the designing of rechargeable Li-ion cells with polymer based cathode active materials, the key issue is to identify the optimum lithiation of the polymer cathode which can ensure the highest electronic conductivity and specific charge capacity possible The development of conducting polymer based rechargeable Li-ion cells with high specific capacity and excellent cycling characteristics is a highly competitive area among research and development groups, worldwide. Polymer based rechargeable batteries are specifically attractive due to the environmentally benign nature and the possible constructional flexibility they offer. Among polymers having electrical transport properties suitable for rechargeable battery applications, polyaniline is the most favoured one due to its tunable electrical conducting properties and the availability of cost effective precursor materials for its synthesis. The performance of a battery depends significantly on the characteristics of its integral parts, the cathode, anode and the electrolyte, which in turn depend on the materials used. Many research groups are involved in developing new electrode and electrolyte materials to enhance the overall performance efficiency of the battery. Currently explored electrolytes for Li ion battery applications are in liquid or gel form, which makes well-defined sealing essential. The use of solid electrolytes eliminates the need for containment of liquid electrolytes, which will certainly simplify the cell design and improve the safety and durability. The other advantages of polymer electrolytes include dimensional stability, safety and the ability to prevent lithium dendrite formation. One of the ultimate aims of the present work is to realize all solid state, flexible and environment friendly Li-ion cells with high specific capacity and excellent cycling stability. Part of the present work is hence focused on identifying good polymer based solid electrolytes essential for realizing all solid state polymer based Li ion cells.The present work is an attempt to study the versatile roles of polyaniline in two different fields of technological applications like nonlinear optics and energy storage. Conducting form of doped PANI films with good extent of crystallinity have been realized using a level surface assisted casting method in addition to the generally employed technique of spin coating. Metal nanoparticles embedded PANI offers a rich source for nonlinear optical studies and hence gold and silver nanoparticles have been used for making the nanocomposites in bulk and thin film forms. These PANI nanocomposites are found to exhibit quite dominant third order optical non-linearity. The highlight of these studies is the observation of the interesting phenomenon of the switching between saturable absorption (SA) and reverse saturable absorption (RSA) in the films of Ag/PANI and Au/PANI nanocomposites, which offers prospects of applications in optical switching. The investigations on the energy storage prospects of PANI were carried out on Li enriched PANI which was used as the cathode active material for assembling rechargeable Li-ion cells. For Li enrichment or Li doping of PANI, n-Butyllithium (n-BuLi) in hexanes was used. The Li doping as well as the Li-ion cell assembling were carried out in an argon filled glove box. Coin cells were assembled with Li doped PANI with different doping concentrations, as the cathode, LiPF6 as the electrolyte and Li metal as the anode. These coin cells are found to show reasonably good specific capacity around 22mAh/g and excellent cycling stability and coulombic efficiency around 99%. To improve the specific capacity, composites of Li doped PANI with inorganic cathode active materials like LiFePO4 and LiMn2O4 were synthesized and coin cells were assembled as mentioned earlier to assess the electrochemical capability. The cells assembled using the composite cathodes are found to show significant enhancement in specific capacity to around 40mAh/g. One of the other interesting observations is the complete blocking of the adverse effects of Jahn-Teller distortion, when the composite cathode, PANI-LiMn2O4 is used for assembling the Li-ion cells. This distortion is generally observed, near room temperature, when LiMn2O4 is used as the cathode, which significantly reduces the cycling stability of the cells.

Síntese citrato-hidrotermal e caracterização eletroquímica de LSCF para aplicação como catodo em célula a combustível de temperatura intermediária

The lanthanum strontium cobalt iron oxide (La1-xSrxCo1-yFeyO3 LSCF) is the most commonly used material for application as cathode in Solid Oxide Fuel Cells (SOFCs), mainly due to their high mixed ionic electronic conductivity between 600 and 800ºC. In this study, LSCF powders with different compositions were synthesized via a combination between citrate and hydrothermal methods. As-prepared powders were calcined from 700 to 900°C and then characterized by X-ray fluorescence, X-ray diffraction, thermal analyses, particle size analyses, nitrogen adsorption (BET) and scanning electronic microscopy. Films of composition La0,6Sr0,4Co0,2Fe0,8O3 (LSCF6428), powders calcined at 900°C, were screen-printed on gadolinium doped ceria (CGO) substrates and sintered between 1150 and 1200°C. The effects of level of sintering on the microstructure and electrochemical performance of electrodes were evaluated by scanning electronic microscopy and impedance spectroscopy. Area specific resistance (ASR) exhibited strong relation with the microstructure of the electrodes. The best electrochemical performance (0.18 ohm.cm2 at 800°C) was obtained for the cathode sintered at 1200°C for 2 h. The electrochemical activity can be further improved through surface activation by impregnation with PrOx, in this case the electrode area specific resistance decreases to values as low as 0.12 ohm.cm2 (800°C), 0.17 ohm.cm2 (750°C) and 0.31 ohm.cm2 (700°C). The results indicate that the citrate-hydrothermal method is suitable for the attainment of LSCF particulates with potential application as cathode component in intermediate temperature solid oxide fuel cells (IT-SOFCs)

Síntese e caracterização de pós Ba(x)Sr(1-x)Co0,8Fe0,2O3- através do método de coprecipitação via oxalato

Ceramic powders based on oxides of perovskite-type structure is of fundamental interest nowadays, since they have important ionic-electronic conductivity in the use of materials with technological applications such as gas sensors, oxygen permeation membranes, catalysts and electrolytes for solid oxide fuel cells (SOFC). The main objective of the project is to develop nanostructured ceramic compounds quaternary-based oxide Barium (Br), Strontium (Sr), Cobalt (Co) and Iron (Fe). In this project were synthesized compounds BaxSr(1-x)Co0, 8Fe0,2O3- (x = 0.2, 0.5 and 0.8) through the oxalate co-precipitation method. The synthesized powders were characterized by thermogravimetric analysis and differential thermal analysis (TGADTA), X-ray diffraction (XRD) with the Rietveld refinement using the software MAUD and scanning electron microscopy (SEM). The results showed that the synthesis technique used was suitable for production of nanostructured ceramic solid solutions. The powders obtained had a crystalline phase with perovskite-type structure. The TGA-DTA results showed that the homogeneous phase of interest was obtained temperature above 1034°C. It was also observed that the heating rate of the calcination process did not affect the elimination of impurities present in the ceramic powder. The variation in the addition of barium dopant promoted changes in the average crystallite size in the nanometer range, the composition being BSCF(5582) obtained the lowest value (179.0nm). The results obtained by oxalate co-precipitation method were compared with those synthesis methods in solid state and EDTA-citrate method

Effect of structural anisotropy on electrical and magnetic properties of polyaniline conducting films

It is shown that highly conducting films of polyaniline protonated with di-esters of sulfosuccinic and sulfophthalic acids which contain alkyl- or alkoxy-type substituents exhibit highly anisotropic structural, electrical and magnetic properties. The layered-like structure of these films can be described as consisting of polyaniline chains which are mainly oriented parallel to the plane of the film and form regular out-of-plane stacks. These stacks are separated by bilayers of the dopant anions. Accordingly, the main anisotropy observed for solution cast films implies in-plane and out-of-plane measurements. An electrical anisotropy of about 80 is found for the in-plane and out-of-plane electronic conductivities at 5 K. The temperature dependences of the in-plane and out-of-plane conductivities are qualitatively similar and have been fitted as a series combination of variable-range-hopping-type and power law contributions. A maximum is observed in the temperature dependence of the electrical anisotropy at low temperature. The films also show a clear anisotropy of magnetization whose temperature and field characteristics depend on the chemical structure of the dopant anion. © 2013 Elsevier B.V.

Síntese e caracterização da cerâmica 'Ti IND. x''('Sm IND. 0,2''Ce IND. 0,8') IND. (1-x)''O IND. (2-Б) para aplicação como anodo em células a combustível de óxido sólido

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Transport properties of polycrystalline boron doped diamond

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Propriedades físicas de vidros Sb2O3-P2O5

This work presents experimental results of some physical properties of antimony phosphate glasses with compositions (x) Sb2O3 - (1-x) P2O5 (x = 0.75, 0.85, 0.90). Mechanical, thermal, optical and electrical properties were investigated: density, elastic moduli (Young's moduli and Poisson's ratio), Vickers microhardness, coefficient of thermal expansion, glass transition temperature, refractive index and electrical conductivity (for x = 0.75). There was no evidence of electronic conductivity by bipolaron hopping. Measurements of energy dispersive spectroscopy (EDS) showed that volatilization of Sb2O3 takes place during the glass melting

Analysis of transport properties of mechanically alloyed [Pb1-xSnxTe]

The work described in this thesis had two objectives. The first objective was to develop a physically based computational model that could be used to predict the electronic conductivity, Seebeck coefficient, and thermal conductivity of Pb1-xSnxTe alloys over the 400 K to 700 K temperature as a function of Sn content and doping level. The second objective was to determine how the secondary phase inclusions observed in Pb1-xSnxTe alloys made by consolidating mechanically alloyed elemental powders impact the ability of the material to harvest waste heat and generate electricity in the 400 K to 700 K temperature range. The motivation for this work was that though the promise of this alloy as an unusually efficient thermoelectric power generator material in the 400 K to 700 K range had been demonstrated in the literature, methods to reproducibly control and subsequently optimize the materials thermoelectric figure of merit remain elusive. Mechanical alloying, though not typically used to fabricate these alloys, is a potential method for cost-effectively engineering these properties. Given that there are deviations from crystalline perfection in mechanically alloyed material such as secondary phase inclusions, the question arises as to whether these defects are detrimental to thermoelectric function or alternatively, whether they enhance thermoelectric function of the alloy. The hypothesis formed at the onset of this work was that the small secondary phase SnO2 inclusions observed to be present in the mechanically alloyed Pb1-xSnxTe would increase the thermoelectric figure of merit of the material over the temperature range of interest. It was proposed that the increase in the figure of merit would arise because the inclusions in the material would not reduce the electrical conductivity to as great an extent as the thermal conductivity. If this were to be true, then the experimentally measured electronic conductivity in mechanically alloyed Pb1-xSnxTe alloys that have these inclusions would not be less than that expected in alloys without these inclusions while the portion of the thermal conductivity that is not due to charge carriers (the lattice thermal conductivity) would be less than what would be expected from alloys that do not have these inclusions. Furthermore, it would be possible to approximate the observed changes in the electrical and thermal transport properties using existing physical models for the scattering of electrons and phonons by small inclusions. The approach taken to investigate this hypothesis was to first experimentally characterize the mobile carrier concentration at room temperature along with the extent and type of secondary phase inclusions present in a series of three mechanically alloyed Pb1-xSnxTe alloys with different Sn content. Second, the physically based computational model was developed. This model was used to determine what the electronic conductivity, Seebeck coefficient, total thermal conductivity, and the portion of the thermal conductivity not due to mobile charge carriers would be in these particular Pb1-xSnxTe alloys if there were to be no secondary phase inclusions. Third, the electronic conductivity, Seebeck coefficient and total thermal conductivity was experimentally measured for these three alloys with inclusions present at elevated temperatures. The model predictions for electrical conductivity and Seebeck coefficient were directly compared to the experimental elevated temperature electrical transport measurements. The computational model was then used to extract the lattice thermal conductivity from the experimentally measured total thermal conductivity. This lattice thermal conductivity was then compared to what would be expected from the alloys in the absence of secondary phase inclusions. Secondary phase inclusions were determined by X-ray diffraction analysis to be present in all three alloys to a varying extent. The inclusions were found not to significantly degrade electrical conductivity at temperatures above ~ 400 K in these alloys, though they do dramatically impact electronic mobility at room temperature. It is shown that, at temperatures above ~ 400 K, electrons are scattered predominantly by optical and acoustical phonons rather than by an alloy scattering mechanism or the inclusions. The experimental electrical conductivity and Seebeck coefficient data at elevated temperatures were found to be within ~ 10 % of what would be expected for material without inclusions. The inclusions were not found to reduce the lattice thermal conductivity at elevated temperatures. The experimentally measured thermal conductivity data was found to be consistent with the lattice thermal conductivity that would arise due to two scattering processes: Phonon phonon scattering (Umklapp scattering) and the scattering of phonons by the disorder induced by the formation of a PbTe-SnTe solid solution (alloy scattering). As opposed to the case in electrical transport, the alloy scattering mechanism in thermal transport is shown to be a significant contributor to the total thermal resistance. An estimation of the extent to which the mean free time between phonon scattering events would be reduced due to the presence of the inclusions is consistent with the above analysis of the experimental data. The first important result of this work was the development of an experimentally validated, physically based computational model that can be used to predict the electronic conductivity, Seebeck coefficient, and thermal conductivity of Pb1-xSnxTe alloys over the 400 K to 700 K temperature as a function of Sn content and doping level. This model will be critical in future work as a tool to first determine what the highest thermoelectric figure of merit one can expect from this alloy system at a given temperature and, second, as a tool to determine the optimum Sn content and doping level to achieve this figure of merit. The second important result of this work is the determination that the secondary phase inclusions that were observed to be present in the Pb1-xSnxTe made by mechanical alloying do not keep the material from having the same electrical and thermal transport that would be expected from “perfect" single crystal material at elevated temperatures. The analytical approach described in this work will be critical in future investigations to predict how changing the size, type, and volume fraction of secondary phase inclusions can be used to impact thermal and electrical transport in this materials system.

Polímeros de coordenação à base de cobalto(II) e N,N'-bis(4-piridil)-1,4,5,8-naftaleno diimida como ligante e suas propriedade estruturais, espectroscópicas e fotoelétricas

Polímeros de coordenação têm atraído a atenção de pesquisadores na última década por conta de sua incrível versatilidade e virtualmente infinito número de possibilidades de combinação de ligantes orgânicos e centros metálicos. Estes compostos normalmente herdam as características magnéticas, eletrônicas e espectroscópicas de seus componentes base. Entretanto, apesar do crescente número de trabalhos na área, ainda são raros os polímeros de coordenação que apresentem condutividade elétrica. Para este fim, utilizou-se a N,N\'-bis(4-piridil)-1,4,5,8-naftaleno diimida, ou NDI-py, que pertence a uma classe de compostos rígidos, planares, quimicamente e termicamente estáveis e que já foram extensamente estudados por suas propriedades fotoeletroquímicas e semicondução do tipo n. O primeiro polímero de coordenação sintetizado, MOF-CoNDI-py-1, indicou ser um polímero linear, de estrutura 1D. O segundo, MOF-CoNDI-py-2, que conta com ácido tereftálico como ligante suporte, é um sólido cristalino com cela unitária monoclínica pertencente ao grupo espacial C2/c, determinado por difração de raios-X de monocristal. A rede apresenta um arranjo trinuclear de íons Co(II) alto spin com coordenados em uma geometria de octaedro distorcido, enquanto os ligantes NDI-py se encontram em um arranjo paralelo na estrutura, em distâncias apropriadas para transferência eletrônica. Com o auxílio de cálculo teóricos a nível de DFT, foi realizado um estudo aprofundado dos espectros eletrônicos e vibracionais, com atribuição das transições observadas, tanto para o MOF-CoNDI-py-2 quanto para o ligante NDI-py livre. A rede de coordenação absorve em toda a região do espectro eletrônico analisada, de 200 nm a 2500 nm, além de apresentar luminescência com característica do ligante. Dispositivos eletrônicos fabricados com um cristal do MOF-CoNDI-py-2 revelaram condutividades da ordem de 7,9 10-3 S cm -1, a maior já observada para um MOF. Além de elevada, a condutividade elétrica dos cristais demonstrou-se altamente anisotrópica, sendo significativamente menos condutor em algumas direções. Os perfis de corrente versus voltagem foram analisados em termos de mecanismos de condutividade, sendo melhores descritos por um mecanismo limitado pelo eletrodo to tipo Space-Charge Limited Current, concordando com a proposta de condutividade através dos planos de NDI-py na rede. A condutividade dos cristais também é fortemente dependente de luz, apresentando fotocondução quando irradiado por um laser vermelho, de 632 nm, enquanto apresenta um comportamento fotorresistivo frente a uma fonte de luz branca. Estes resultados, combinados, trazem um MOF em uma estrutura incomum e com elevada condutividade elétrica, modulada por luz, em medidas diretas de corrente. Não existem exemplos conhecidos de MOFs na literatura com estas características.

Estudo dos espectros vibracionais de poliacetilenos substituídos

Neste trabalho foram sintetizados a poli-2-etinilpiridina (P2EP), poli-4etinilpiridina (P4EP), o iodeto de poli(2-N-t-butilpiridiniumilacetileno) (P2EPtBu) e a poli-β-etinilnaftaleno (Pβ:EN), os quais são poliacetilenos substituídos. Estes polímeros, juntamente com o cloreto de poli(2-piridínio-2-piridilacetileno) (P2EPH), foram caracterizados por espectroscopia vibracional no infravermelho e Raman. Estes polímeros apresentaram variação na posição das bandas Raman com a energia da radiação excitante - chamada dispersão Raman ou fotosseletividade - da ordem de 10 cm-1, bem inferior ao apresentado pelo poliacetileno (cerca de 60 cm-1). Este deslocamento foi interpretado utilizando-se dois dos modelos existentes para descrever este fenômeno: o Modelo de Modo de Amplitude (AMM) e o Modelo de Coordenada de Conjugação Efetiva (ECCM), os quais fornecem informações sobre a estrutura polimérica e sobre seus níveis eletrônicos. Utilizando-se o AMM foi possível obter informações sobre os níveis eletrônicos excitados de mesma simetria que o estado eletrônico fundamental. Por outro lado, o ECCM, com a ajuda de cálculos DFT, mostrou diferenças na extensão da conjugação e no grau de dimerização entre o P2EP na forma cis e trans e indicou que este polímero apresentava, predominantemente, a estrutura cis, fato este confirmado pelos espectros no infravermelho. A dopagem com I2 provocou efeitos diferentes na estrutura dos polímeros. Os espectros no infravermelho dos polímeros dopados indicaram que o P2EP e o P2EPH apresentaram aumento na quantidade de segmentos cis enquanto o P2EPtBu apresentou diminuição na quantidade desses segmentos. Os espectros Raman dos polímeros dopados confirmaram os dados dos espectros no infravermelho. Esta diferença foi interpretada como sendo devida à diferença no volume do substituinte, pois grupos volumosos favorecem o isômero trans-cisóide onde a distância entre os substituintes é maior. A dopagem também levou a um aumento na condutividade dos polímeros, porém os valores de condutividade obtidos foram bem inferiores que os apresentados pelo poliacetileno dopado (10-5 a 10-7 contra 102 S cm-1, tipicamente).

Electrocatalytic oxidation of ascorbic acid on mesostructured SiO2-conducting polymer composites

The conducting self-doping copolymer poly(aniline-co-ABA) preserves its redox activity at pH values as high as 7. This observation was the starting point to synthesize an organic–inorganic hybrid composite able to electrochemically oxidize ascorbic acid molecules at that pH. The inorganic part of the catalytic element was an ordered mesoporous electrodeposit of SiO2, which has been used as the template for the electrochemical insertion of the self-doping copolymer. The oxidation of ascorbate ions at a fixed potential on this composite was studied by means of the kinetic model proposed by Bartlett and Wallace (2001). It was observed that the effective kinetic constant KME increased significantly but, simultaneously, k′ME remained almost constant when the composite was employed as the electrocatalytic substrate. These results were interpreted in the light of two combinations of kinetic constants, which strongly suggested that the increase in KME should be ascribed to the improvement in electronic conductivity of the copolymer induced by the highly ordered silica template.