Efeito do Carbeto de Boro na Densificação da Alumina e na Formação de Novas Fase

O carbeto de boro tem efeito inibidor sobre a densificação da matriz de alumina. A maior densidade obtida foi de 80% da densidade teórica. A sinterização foi conduzida nas temperaturas de 1700, 1750 e 1800°C/1 hora em atmosfera de argônio. A caracterização microestrutural foi realizada por difração de raios X, MEV e MET. Foi observada a formação de uma fase identificada por MET como sendo A13B06.

Thermal analysis and vibrational spectroscopic characterization of the boro silicate mineral datolite – CaBSiO4(OH)

The objective of this work is to determine the thermal stability and vibrational spectra of datolite CaBSiO4(OH) and relate these properties to the structure of the mineral. The thermal analysis of datolite shows a mass loss of 5.83% over a 700–775 °C temperature range. This mass loss corresponds to 1 water (H2O) molecules pfu. A quantitative chemical analysis using electron probe was undertaken. The Raman spectrum of datolite is characterized by bands at 917 and 1077 cm−1 assigned to the symmetric stretching modes of BO and SiO tetrahedra. A very intense Raman band is observed at 3498 cm−1 assigned to the stretching vibration of the OH units in the structure of datolite. BOH out-of-plane vibrations are characterized by the infrared band at 782 cm−1. The vibrational spectra are based upon the structure of datolite based on sheets of four- and eight-membered rings of alternating SiO4 and BO3(OH) tetrahedra with the sheets bonded together by calcium atoms.

Optical absorption and photoluminescence studies of Nd3 doped alkali boro germanate glasses

Optical absorption and photoluminescence studies have been carried out at room temperature in 25 R2O-25 GeO2-49.5 B2O3-0.5 Nd2O3 glass systems, (Composition in mol%, R= Li, Na, K and Rb). Judd Ofelt Intensity parameters and other parameters like Racah (E-1, E-2 and E-3), Slater-Condon-Shortley (F-2, F-4 and F-6) Spin-Orbit Coupling (xi(4f)) and Configuration Interaction (alpha,beta and gamma) for Nd3+ ion in the glass system are calculated. The variation of the 02 parameters are interpreted in terms of the covalency of the RE ion in the glass matrix. Further the hypersensitive transition I-4(9/2) -> (4)G(5/2), (2)G(7/2) is analyzed with respect to the intensity ratio I-L/I-S and is found to be dependent on the type of alkali in the glass matrix. The Photoluminescence studies do not show any appreciable shift in the peak emission wavelength of the F-4(3/2) to I-4(11/2) transition with the change in alkali type. (C) 2010 Elsevier B.V. All rights reserved.

Propiedades radiativas y ópticas de una herramienta de corte compuesta por nitruro de boro cúbico

Se ha medido la emisividad espectral (2,5-25 micras) normal de una herramienta de corte industrial, compuesta en un 55% por nitruro de boro cúbico (cBN), en el rango de temperaturas 200-1000 ºC. La emisividad medida muestra un comportamiento suavemente descendente al aumentar la longitud de onda, propio de metales, con un descenso pronunciado alrededor de 9 micras. Este valle se corresponde con la emisividad calculada para el cBN cúbico puro en la literatura, que sin embargo no exhibe el comportamiento metálico medido. Así mismo, se observa que la emisividad espectral es esencialmente independiente de la temperatura, aunque no así la emisividad total. Los resultados experimentales para el cBN puro indican que la reflectividad de dicho compuesto se puede explicar satisfactoriamente mediante un modelo de Lorentz para dieléctricos, mientras que el ajuste teórico de la reflectividad medida para la herramienta de corte necesita incluir una contribución del modelo de Drude para explicar el comportamiento metálico observado. Este modelo combinado se ajusta razonablemente bien a las medidas, y revela que la herramienta de corte se comporta como un semiconductor degenerado, con una alta densidad de portadores libres. Además, permite realizar una estimación teórica de sus constantes ópticas. Por último, se ha realizado un estudio sobre la medida y el control de la temperatura de la muestra, empleando distintos métodos de unión termopar.

Suitability of rich-fish culture under mono and polyculture systems in the boro rice ecosystem

An experiment was conducted in farmers’ fields under Paikgacha thana, Khulna to study the suitability of integrated rice-cum-fish culture. Three treatments namely T1 (Puntius gonionotus), T2 (Puntius gonionotus and Cyprinus carpio) and T3 ( Cyprinus carpio) were included for the study each having three replicates. The fish were stocked at a density of 3750/ha in all the rice plots. The physicochemical parameters of water viz., water depth, temperature, dissolved oxygen, pH, salinity, nitrate and phosphate etc. recorded during the study period were found within optimum range. Of the two cultured species C. carpio attained the highest average individual weight (160g) and survival (81.06%). With respect to biomass and income, highest average fish production and net profit per hectare (306.74kg and Tk. 8177.91) were obtained in T2 and the lowest (184.17kg and Tk. 2049.41) obtained in T1 and a significant variation (p<0.05) in fish production was observed among the treatments while for rice production, it was insignificant. The cost benefit ratio of fish production found were 1:1.29, 1:2.14 and 1:1.90 for T1, T2 and T3, respectively.

Growth and production of Nile tilapia (Oreochromis niloticus Lin.) in irrigated Boro rice under floodplain environment

The experiment was conducted at BRRI Regional Station, Habiganj during 1994-95 to evaluate the growth and economic performance of Nile tilapia, Oreochromis niloticus, fish reared in the field of irrigated boro rice with different fertilizer levels. Grain yield of rice was not affected by fish culture. It was observed that 50% of recommended fertilizer was enough to produce increased rice yield (8-10 t/ha) at floodplain environment and additional yield was obtained with the increasing fertilizer rates. Results further indicated that O. niloticus could successfully be reared in the field of irrigated boro rice with recommended fertilizer level. Larger size of fingerlings at release had improved recovery percent, body weight gain and higher fish yield. Results also revealed that rice + fish production system produced higher net return than the system with rice alone.

A importância do boro para a videira.

1996

Correção de deficiência de boro em videira.

2003

Deficiência de boro em mamoeiro.

Informacoes tecnicas sobre a deficiencia de boro em mamoeiro, envolvendo desde a ocorrencia ate as medidas preventivas e controle para o Estado do Amazonas.

Deficiência de boro em coqueiro - sintomas e correção.

Informações técnicas sobre sintomas e correção de deficiência de boro em coqueiro (Cocos nucifera), em Manaus-AM, Brasil.

Extratores ácidos e sais na determinação da disponibilidade de boro no solo.

O objetivo deste trabalho foi verificar a eficiência de seis extratores comparando-os com o extrator H2O quente, método atualmente utilizado na determinação da disponibilidade do B do solo.

Efeito da aplicação de boro via foliar na qualidade e na colheita de frutos de macieira.

2014

Evaluación del efecto de la fertilización con boro para híbridos de girasol en suelos haplustoles énticos de Gral. Pico, Departamento de Maracó, Prov. de La Pampa

p.45-49

Low frequency Raman scattering in amorphous materials: fused quartz, "pyrex" boro-silicate glass and soda-lime silicate glass

Raman scattering in the region 20 to 100 cm -1 for fused quartz, "pyrex" boro-silicate glass, and soft soda-lime silicate glass was investigated. The Raman spectra for the fused quartz and the pyrex glass were obtained at room temperature using the 488 nm exciting line of a Coherent Radiation argon-ion laser at powers up to 550 mW. For the soft soda-lime glass the 514.5 nm exciting line at powers up to 660 mW was used because of a weak fluorescence which masked the Stokes Raman spectrum. In addition it is demonstrated that the low-frequency Raman coupling constant can be described by a model proposed by Martin and Brenig (MB). By fitting the predicted spectra based on the model with a Gaussian, Poisson, and Lorentzian forms of the correlation function, the structural correlation radius (SCR) was determined for each glass. It was found that to achieve the best possible fit· from each of the three correlation functions a value of the SCR between 0.80 and 0.90 nm was required for both quartz and pyrex glass but for the soft soda-lime silicate glass the required value of the SCR. was between 0.50 and 0.60 nm .. Our results support the claim of Malinovsky and Sokolov (1986) that the MB model based on a Poisson correlation function provides a universal fit to the experimental VH (vertical and horizontal polarizations) spectrum for any glass regardless of its chemical composition. The only deficiency of the MB model is its failure to fit the experimental depolarization spectra.

Estudio de las propiedades mecánicas, tribológicas y electroquímicas de aleaciones CoCrMoC con adiciones de boro.

Tesis (Doctor en Ingeniería de Materiales) UANL, 2014.