SEM analysis of internal adaptation of adhesive restorations after contamination with saliva

Purpose: This study tested the null hypothesis that different treatments of saliva-contaminated substrate would not affect microgap formation at the dentin walls of bonded restorations. Materials and Methods: Forty freshly extracted human molars received standardized Class V preparations on buccal and lingual surfaces. The specimens were assigned to four experimental groups (n = 20): [G1] no contamination (control group), [G2] saliva contamination (10 s) after etching followed by 5 s air stream; [G3] saliva contamination after etching and rinsed for 10 s; and [G4] re-etching for 10 s after saliva contamination. All specimens were restored with a one-bottle adhesive (Single Bond, 3M ESPE) and microhybrid composite resin (Filtek Z250, 3M ESPE) according to the manufacturer's instructions. The specimens were thermocycled, sectioned through the center of the restoration, and then processed for SEM. Microgaps were measured at the axial wall at 1500X magnification. The data were submitted to Kruskal-Wallis nonparametric statistical analysis at p < 0.05. Results: The data revealed that different groups resulted in a statistically significant difference (p < 0.01) in gap formation. Air drying [G2] and rinsing [G3] the saliva-contaminated dentin resulted in similar microgap values (p > 0.05). However, re-etching the dentin after saliva contamination [G4] increased microgap formation (p < 0.05) when compared with the groups G1 and G2. Although air drying and rinsing produced results comparable to noncontaminated dentin, the presence of microgaps was not completely eliminated. Conclusion: Contaminated saliva did not prevent hybrid layer formation; however, it did reduce the adaptation of the restorative material to bonded surfaces.

Direct Adhesive Pin-retained Restorations For Severely Worn Dentition Treatment: A 1.5-year Follow-up Report.

Excessive occlusal surface wear can result in occlusal disharmony, functional and esthetic impairment. As a therapeutic approach, conventional single crowns have been proposed, but this kind of treatment is complex, highly invasive and expensive. This case report describes the clinical outcomes of an alternative minimally invasive treatment based on direct adhesive-pin retained restorations. A 64-year-old woman with severely worn dentition, eating problems related to missing teeth and generalized tooth hypersensitivity was referred for treatment. Proper treatment planning based on the diagnostic wax-up simulation was used to guide the reconstruction of maxillary anterior teeth with direct composite resin over self-threading dentin pins. As the mandibular remaining teeth were extremely worn, a tooth-supported overdenture was installed. A stabilization splint was also used to protect the restorations. This treatment was a less expensive alternative to full-mouth rehabilitation with positive esthetic and functional outcomes after 1.5 years of follow-up.

Radiotherapy Does Not Impair Dentin Adhesive Properties In Head And Neck Cancer Patients.

This study evaluated the influence of radiotherapy on the dentin bond strength of teeth extracted from patients who had undergone head and neck radiotherapy. A total of 36 samples were divided into two experimental groups: group I (control group, n = 18) and group II (in vivo irradiated group, n = 18). Groups I and II were further separated into three subgroups (six specimens per subgroup), which were further assigned to the three adhesive system protocols employed: Single Bond 2 (SB) (3M ESPE), Easy Bond (EB) (3M ESPE) and Clearfil SE Bond (CSE) (Kuraray). The adhesive systems were applied to the prepared surface according to the manufacturers' instructions and restored using composite resin (Filtek Supreme, 3M ESPE). After 24 h in deionised water (37(o)C), teeth were horizontally and vertically cut to obtain beam specimens with a cross-section area of 0.8 ± 1.0 mm(2). Specimens were tested in tension using a universal testing machine at a cross-speed of 0.5 mm/min. Fracture patterns were observed under SEM. Data was analysed by two-way analysis of variance (p ≤ 0.05). No statistically significant difference was found between the irradiated (R/SB = 44.66 ± 10.12 MPa; R/EB = 41.48 ± 12.71 MPa; and R/CSE = 46.01 ± 6.98 MPa) and control group (C/SB = 39.12 ± 9.51 MPa; C/EB = 42.40 ± 6.66 MPa; and C/CSE = 36.58 ± 7.06 MPa) for any of the adhesive systems. All groups presented a predominance of mixed fracture modes. Head and neck radiotherapy did not affect dentin bond strength for the adhesive materials tested in this study.

Dentin Bond Strength Of A Fluoride-releasing Adhesive System Submitted To Ph-cycling.

To evaluate the microtensile bond strength (µTBS) of a fluoride-containing adhesive system submitted to a pH-cycling and storage time regimen for primary outcomes. As secondary outcomes the fluoride released amount was evaluated. Twelve dentin surfaces from sound third molar were divided into 2 groups according to adhesive systems: Clearfil SE Protect (PB) and Clearfil SE Bond (SE). Sticks obtained (1.0 mm2) from teeth were randomly divided into 3 subgroups according to storage regimen model: immediate (24h); 5-month deionized water (W); and pH-cycling model (C). All sticks were tested for µTBS in a universal testing machine. Fluoride concentration was obtained from 1-4 days and 30-day in W and 1-4 days in demineralization (DE)/remineralization (RE) solutions from C, using a fluoride-specific electrode. µTBS and fluoride released data were, respectively, submitted to ANOVA in a split plot design and Tukey, and Friedman' tests (a=0.05). There was no significant interaction between adhesive system and storage regimen for µTBS. W showed the lowest µTBS values. There was no significant difference between 24 h and C models for µTBS. There was no significant difference between adhesive systems. Failure mode was predominantly cohesive within composite for the 24 h and W, for the C group it was mixed for SE and cohesive within composite for PB adhesive system. Fluoride concentrations in the DE/RE solutions were less than 0.03125 ppm and not detected in W. In conclusion, the fluoride-containing adhesive system performed similarly to the regular one. Hydrolytic degradation is the main problem with both adhesive systems, regardless of fluoride contents.

Dentine Bond Strength And Antimicrobial Activity Evaluation Of Adhesive Systems.

This study evaluated the dentine bond strength (BS) and the antibacterial activity (AA) of six adhesives against strict anaerobic and facultative bacteria. Three adhesives containing antibacterial components (Gluma 2Bond (glutaraldehyde)/G2B, Clearfil SE Protect (MDPB)/CSP and Peak Universal Bond (PUB)/chlorhexidine) and the same adhesive versions without antibacterial agents (Gluma Comfort Bond/GCB, Clearfil SE Bond/CSB and Peak LC Bond/PLB) were tested. The AA of adhesives and control groups was evaluated by direct contact method against four strict anaerobic and four facultative bacteria. After incubation, according to the appropriate periods of time for each microorganism, the time to kill microorganisms was measured. For BS, the adhesives were applied according to manufacturers' recommendations and teeth restored with composite. Teeth (n=10) were sectioned to obtain bonded beams specimens, which were tested after artificial saliva storage for one week and one year. BS data were analyzed using two-way ANOVA and Tukey test. Saliva storage for one year reduces the BS only for GCB. In general G2B and GCB required at least 24h for killing microorganisms. PUB and PLB killed only strict anaerobic microorganisms after 24h. For CSP the average time to eliminate the Streptococcus mutans and strict anaerobic oral pathogens was 30min. CSB showed no AA against facultative bacteria, but had AA against some strict anaerobic microorganisms. Storage time had no effect on the BS for most of the adhesives. The time required to kill bacteria depended on the type of adhesive and never was less than 10min. Most of the adhesives showed stable bond strength after one year and the Clearfil SE Protect may be a good alternative in restorative procedures performed on dentine, considering its adequate bond strength and better antibacterial activity.

Self-etch Adhesive Systems: A Literature Review.

This paper presents the state of the art of self-etch adhesive systems. Four topics are shown in this review and included: the historic of this category of bonding agents, bonding mechanism, characteristics/properties and the formation of acid-base resistant zone at enamel/dentin-adhesive interfaces. Also, advantages regarding etch-and-rinse systems and classifications of self-etch adhesive systems according to the number of steps and acidity are addressed. Finally, issues like the potential durability and clinical importance are discussed. Self-etch adhesive systems are promising materials because they are easy to use, bond chemically to tooth structure and maintain the dentin hydroxyapatite, which is important for the durability of the bonding.

Influence of different adhesive systems on the pull-out bond strength of glass fiber posts

This in vitro study evaluated the tensile bond strength of glass fiber posts (Reforpost - Angelus-Brazil) cemented to root dentin with a resin cement (RelyX ARC - 3M/ESPE) associated with two different adhesive systems (Adper Single Bond - 3M/ESPE and Adper Scotchbond Multi Purpose (MP) Plus - 3M/ESPE), using the pull-out test. Twenty single-rooted human teeth with standardized root canals were randomly assigned to 2 groups (n=10): G1- etching with 37% phosphoric acid gel (3M/ESPE) + Adper Single Bond + #1 post (Reforpost - Angelus) + four #1 accessory posts (Reforpin - Angelus) + resin cement; G2- etching with 37% phosphoric acid gel + Adper Scotchbond MP Plus + #1 post + four #1 accessory posts + resin cement. The specimens were stored in distilled water at 37°C for 7 days and submitted to the pull-out test in a universal testing machine (EMIC) at a crosshead speed of 0.5 mm/min. The mean values of bond strength (kgf) and standard deviation were: G1- 29.163 ± 7.123; G2- 37.752 ±13.054. Statistical analysis (Student's t-test; a=0.05 showed no statistically significant difference (p<0.05) between the groups. Adhesive bonding failures between resin cement and root canal dentin surface were observed in both groups, with non-polymerized resin cement in the apical portion of the post space when Single Bond was used (G1). The type of adhesive system employed on the fiber post cementation did not influence the pull-out bond strength.

Bond strength of a pit-and-fissure sealant associated to etch-and-rinse and self-etching adhesive systems to saliva-contaminated enamel: individual vs. simultaneous light curing

This study evaluated in vitro the shear bond strength (SBS) of a resin-based pit-and-fissure sealant [Fluroshield (F), Dentsply/Caulk] associated with either an etch-and-rinse [Adper Single Bond 2 (SB), 3M/ESPE] or a self-etching adhesive system [Clearfil S3 Bond (S3), Kuraray Co., Ltd.] to saliva-contaminated enamel, comparing two curing protocols: individual light curing of the adhesive system and the sealant or simultaneous curing of both materials. Mesial and distal enamel surfaces from 45 sound third molars were randomly assigned to 6 groups (n=15), according to the bonding technique: I - F was applied to 37% phosphoric acid etched enamel. The other groups were contaminated with fresh human saliva (0.01 mL; 10 s) after acid etching: II - SB and F were light cured separately; III - SB and F were light cured together; IV - S3 and F were light cured separately; V - S3 and F were light cured simultaneously; VI - F was applied to saliva-contaminated, acid-etched enamel without an intermediate bonding agent layer. SBS was tested to failure in a universal testing machine at 0.5 mm/min. Data were analyzed by one-way ANOVA and Fisher's test (α=0.05).The debonded specimens were examined with a stereomicroscope to assess the failure modes. Three representative specimens from each group were observed under scanning electron microscopy for a qualitative analysis. Mean SBS in MPa were: I-12.28 (±4.29); II-8.57 (±3.19); III-7.97 (±2.16); IV-12.56 (±3.11); V-11.45 (±3.77); and VI-7.47 (±1.99). In conclusion, individual or simultaneous curing of the intermediate bonding agent layer and the resin sealant did not seem to affect bond strength to saliva-contaminated enamel. S3/F presented significantly higher SBS than the that of the groups treated with SB etch-and-rinse adhesive system and similar SBS to that of the control group, in which the sealant was applied under ideal dry, noncontaminated conditions.

Influence of sodium hypochlorite and edta on the microtensile bond strength of a self-etching adhesive system

Chemical substances used during biomechanical preparation of root canals can alter the composition of dentin surface and affect the interaction with restorative materials. OBJECTIVE: The purpose of this study was to evaluate the microtensile bond strength (µTBS) of a self-etching adhesive system to dentin irrigated with sodium hypochlorite (NaOCl) and ethylenediaminetetraacetic acid (EDTA). MATERIAL AND METHODS: Thirty human third molars were sectioned 3 mm below the occlusal surface, polished with 600- to 1200-grit silicon carbide papers, and randomly divided into 3 groups: G1 (control): no irrigating solution; G2: 1% NaOCl; and G3: 1% NaOCl followed by the application of 17% EDTA. The specimens received the self-etching adhesive system (XENO III - Dentsply), restored with microhybrid composite resin (Z250 - 3M ESPE), sectioned and trimmed to create 4 hourglass-shaped slabs of each tooth. The slabs were tested in microtensile strength in a universal testing machine (Emic DL 2000) at a crosshead speed of 0.5 mm/min until fracture. The results were analyzed statistically by ANOVA and Newman-Keuls test. RESULTS: Mean µTBS values and standard deviations in MPa were: G1 = 11.89 ± 4.22; G2 = 19.41 ± 5.32; G3 = 11.34 ± 4.73. 1% NaOCl increased the adhesive resistance significantly (p<0.001/F=22.5763). The application of 1% NaOCl/17% EDTA resulted in statistically similar µTBS to the control group. CONCLUSIONS: None of the irrigants affected negatively the µTBS of XENO III to dentin. The use of 1% NaOCl alone resulted in higher bond strength than the other treatments. The combination of 1% NaOCl and 17% EDTA produced similar bond strength to that of untreated dentin.

Can previous acid etching increase the bond strength of a self-etching primer adhesive to enamel?

Because a greater research effort has been directed to analyzing the adhesive effectiveness of self etch primers to dentin, the aim of this study was to evaluate, by microtensile testing, the bond strength to enamel of a composite resin combined with a conventional adhesive system or with a self-etching primer adhesive, used according to its original prescription or used with previous acid etching. Thirty bovine teeth were divided into 3 groups with 10 teeth each (n= 10). In one of the groups, a self-etching primer (Clearfil SE Bond - Kuraray) was applied in accordance with the manufacturer's instructions and, in the other, it was applied after previous acid etching. In the third group, a conventional adhesive system (Scotchbond Multipurpose Plus - 3M-ESPE) was applied in accordance with the manufacturer's instructions. The results obtained by analysis of variance revealed significant differences between the adhesive systems (F = 22.31). The self-etching primer (Clearfil SE Bond) presented lower enamel bond strength values than the conventional adhesive system (Scotchbond Multipurpose Plus) (m = 39.70 ± 7.07 MPa) both when used according to the original prescription (m = 27.81 ± 2.64 MPa) and with previous acid etching (m = 25.08 ± 4.92 MPa).

Influence of intrapulpal pressure simulation on the bond strength of adhesive systems to dentin

The purpose of this study was to evaluate the influence of intrapulpal pressure simulation on the bonding effectiveness of etch & rinse and self-etch adhesives to dentin. Eighty sound human molars were distributed into eight groups, according to the permeability level of each sample, measured by an apparatus to assess hydraulic conductance (Lp). Thus, a similar mean permeability was achieved in each group. Three etch & rinse adhesives (Prime & Bond NT - PB, Single Bond -SB, and Excite - EX) and one self-etch system (Clearfil SE Bond - SE) were employed, varying the presence or absence of an intrapulpal pressure (IPP) simulation of 15 cmH2O. After adhesive and restorative procedures were carried out, the samples were stored in distilled water for 24 hours at 37°C, and taken for tensile bond strength (TBS) testing. Fracture analysis was performed using a light microscope at 40 X magnification. The data, obtained in MPa, were then submitted to the Kruskal-Wallis test ( a = 0.05). The results revealed that the TBS of SB and EX was significantly reduced under IPP simulation, differing from the TBS of PB and SE. Moreover, SE obtained the highest bond strength values in the presence of IPP. It could be concluded that IPP simulation can influence the bond strength of certain adhesive systems to dentin and should be considered when in vitro studies are conducted.

Do the origins of primary teeth affect the bond strength of a self-etching adhesive system to dentin?

The aim of this in vitro study was to evaluate the tensile bond strength of a self-etching adhesive system to three different dentinal substrates. Primary molar teeth that had been recently exfoliated (RE), with unknown time of exfoliation (UT), and extracted due to prolonged retention (PR) were used for this investigation. Ten primary molar teeth of each group were cut in the middle following the mesio-distal direction, creating a total of twenty specimens per group. The specimens were included in acrylic resin and had a flat dentin surface exposed. The self-etching adhesive system was applied to this surface and a 3-millimeter high cone with diameter of 2 mm in the adhesion area was constructed using composite resin. The specimens were stored in distilled water at 37ºC for 24 hours. Fifteen specimens of each substrate were used for the tensile bond test (n = 15) and 5 had the interface analyzed by scanning electron microscopy (SEM). The data was examined by one-way ANOVA and presented no significant differences between groups (p = 0.5787). The mean values obtained for RE, UT and PR were 18.39 ± 9.70, 19.41 ± 7.80, and 23.30 ± 9.37 MPa, respectively. Any dentinal substrates of primary teeth studied are safe for tensile bond strength tests with adhesive systems.

Effectiveness of sealing active proximal caries lesions with an adhesive system: 1-year clinical evaluation

The objective of this study was to evaluate the effectiveness of a therapeutic sealant to arrest non-cavitated proximal carious lesion progression. The study population comprised 44 adolescents who had bitewing radiographs taken for caries diagnosis. Non-cavitated lesions extending up to half of dentin thickness were included in the sample. In the experimental group (n = 33), the proximal caries-lesion surfaces were sealed with an adhesive (OptiBond Solo, Kerr) after tooth separation. The control group (n = 11) received no treatment, except for oral hygiene instructions including use of dental floss. Follow-up radiographs were taken after one year and were analyzed in comparison with baseline radiographs. In a blind study setting, visual readings were performed by two examiners, blinded to whether the examined radiograph was baseline or follow-up, and whether it concerned a test or control lesion. The efficacy of sealing treatment was evaluated by the McNemar test (0.05). About 22% of the sealed lesions showed reduction, 61% showed no change and 16% showed progression. For the control lesions, the corresponding values were 27%, 36% and 36% respectively. The number of lesions that showed reduction and no changes were merged and therefore 83.3% of the sealed lesions and 63.6% of the control lesions were considered clinically successful. No statistical significance was detected (p > 0.05). In the course of 1 year, sealing proximal caries lesions was not shown to be superior to lesion monitoring.

Lsa21, a novel leptospiral protein binding adhesive matrix molecules and present during human infection

Background: It has been well documented over past decades that interaction of pathogens with the extracellular matrix (ECM) plays a primary role in host cell attachment and invasion. Adherence to host tissues is mediated by surface-exposed proteins expressed by the microorganisms during infection. The mechanisms by which pathogenic leptospires invade and colonize the host remain poorly understood since few virulence factors contributing to the pathogenesis of the disease have been identified. Whole-genome sequencing analysis of L. interrogans allowed identification of a repertoire of putative leptospiral surface proteins. Results: Here, we report the identification and characterization of a new leptospiral protein that exhibits extracellular matrix-binding properties, called as Lsa21 (leptospiral surface adhesin, 21 kDa). Compatible with its role in adhesion, the protein was shown to be surface-exposed by indirect immunofluorescence. Attachment of Lsa21 to laminin, collagen IV, and plasma fibronectin was specific and dose dependent. Laminin oxidation by sodium metaperiodate reduced the protein-laminin interaction in a concentration-dependent manner, indicating that laminin sugar moieties are crucial for this interaction. The gene coding for Lsa21 is present in pathogenic strains belonging to the L. interrogans species but was not found in the saprophytic L. biflexa serovar Patoc strain Patoc 1. Loss of gene expression occurs upon culture attenuation of pathogenic strains. Environmental factors such as osmolarity and temperature affect Lsa21 expression at the transcriptional level. Moreover, anti-Lsa21 serum labeled liver and kidney tissues of human fatal cases of leptospirosis. Conclusion: Our data suggest a role of Lsa21 in the pathogenesis of leptospirosis.

Influence of laser surface texturing on surface microstructure and mechanical properties of adhesive joined steel sheets

This work discusses the resultant microstructure of laser surface treated galvanised steel and the mechanical properties of adhesively bonded surfaces therein. The surface microstructure obtained at laser intensities between 170 and 1700 MW cm 22 exhibit zinc melting and cavity formation. The wavy surface morphology of the treated surface exhibits an average roughness Ra between 1.0 and 1.5 mu m, and a mean roughness depth R(z) of 8.6 mu m. Atomic force microscopic analyses revealed that the R(z) inside the laser shot cavities increased from 68 to 243 nm when the incident laser intensity was increased from 170 to 1700 MW cm(-2). X-ray fluorescence analyses were used to measure Zn coating thicknesses as a function of process parameters. Both X-ray fluorescence and X-ray diffraction analyses demonstrated that the protective coating remains at the material surface, and the steel structure beneath was not affected by the laser treatment. Tensile tests under peel strength conditions demonstrated that the laser treated adhesively joined samples had resistance strength up to 88 MPa, compared to a maximum of only 23 MPa for the untreated surfaces. The maximum deformation for rupture was also greatly increased from 0.07%, for the original surface, to 0.90% for the laser treated surfaces.