Effect of Abutment Screw Surface Treatment on Reliability of Implant-Supported Crowns

Purpose: To evaluate and compare the reliability of implant-supported single crowns cemented onto abutments retained with coated (C) or noncoated (NC) screws and onto platform-switched abutments with coated screws. Materials and Methods: Fifty-four implants (DT Implant 4-mm Standard Platform, Intra-Lock International) were divided into three groups (n = 18 each) as follows: matching-platform abutments secured with noncoated abutment screws (MNC); matching-platform abutments tightened with coated abutment screws (MC); and switched-platform abutments secured with coated abutment screws (SC). Screws were characterized by scanning electron microscopy and x-ray photoelectron spectroscopy (XPS). The specimens were subjected to step-stress accelerated life testing. Use-level probability Weibull curves and reliability for 100,000 cycles at 200 N and 300 N (90% two-sided confidence intervals) were calculated. Polarized light and scanning electron microscopes were used for fractographic analysis. Results: Scanning electron microscopy revealed differences in surface texture; noncoated screws presented the typical machining grooves texture, whereas coated screws presented a plastically deformed surface layer. XPS revealed the same base components for both screws, with the exception of higher degrees of silicon in the SiO2 form for the coated samples. For 100,000 cycles at 300 N, reliability values were 0.06 (0.01 to 0.16), 0.25 (0.09 to 0.45), and 0.25 (0.08 to 0.45), for MNC, MC, and SC, respectively. The most common failure mechanism for MNC was fracture of the abutment screw, followed by bending, or its fracture, along with fracture of the abutment or implant. Coated abutment screws most commonly fractured along with the abutment, irrespective of abutment type. Conclusion: Reliability was higher for both groups with the coated screw than with the uncoated screw. Failure modes differed between coated and uncoated groups.

Effect of microthread presence and restoration design (screw versus cemented) in dental implant reliability and failure modes

Objectives: This study evaluated the reliability and failure modes of implants with a microthreaded or smooth design at the crestal region, restored with screwed or cemented crowns. The postulated null hypothesis was that the presence of microthreads in the implant cervical region would not result in different reliability and strength to failure than smooth design, regardless of fixation method, when subjected to step-stress accelerated life-testing (SSALT) in water. Materials and methods: Eighty four dental implants (3.3 × 10 mm) were divided into four groups (n = 21) according to implant macrogeometric design at the crestal region and crown fixation method: Microthreads Screwed (MS); Smooth Screwed (SS); Microthreads Cemented (MC), and Smooth Cemented (SC). The abutments were torqued to the implants and standardized maxillary central incisor metallic crowns were cemented (MC, SC) or screwed (MS, SS) and subjected to SSALT in water. The probability of failure versus cycles (90% two-sided confidence intervals) was calculated and plotted using a power law relationship for damage accumulation. Reliability for a mission of 50,000 cycles at 150 N (90% 2-sided confidence intervals) was calculated. Differences between final failure loads during fatigue for each group were assessed by Kruskal-Wallis along with Benferroni's post hoc tests. Polarized-light and scanning electron microscopes were used for failure analyses. Results: The Beta (β) value (confidence interval range) derived from use level probability Weibull calculation of 1.30 (0.76-2.22), 1.17 (0.70-1.96), 1.12 (0.71-1.76), and 0.52 (0.30-0.89) for groups MC, SC, MS, and SS respectively, indicated that fatigue was an accelerating factor for all groups, except for SS. The calculated reliability was higher for SC (99%) compared to MC (87%). No difference was observed between screwed restorations (MS - 29%, SS - 43%). Failure involved abutment screw fracture for all groups. The cemented groups (MC, SC) presented more abutment and implant fractures. Significantly higher load to fracture values were observed for SC and MC relative to MS and SS (P < 0.001). Conclusion: Since reliability and strength to failure was higher for SC than for MC, our postulated null hypothesis was rejected. © 2012 John Wiley & Sons A/S.

Influence of Abutment Type and Esthetic Veneering on Preload Maintenance of Abutment Screw of Implant-Supported Crowns

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Carbon Film Coating of Abutment Surfaces: Effect on the Abutment Screw Removal Torque

Purpose: To evaluate the effect of diamond-like carbon (DLC) coating of prefabricated implant abutment on screw removal torque (RT) before and after mechanical cycling (MC).Materials and Methods: Fifty-four abutments for external-hex implants were divided among 6 groups (n = 9): S, straight abutment (control); SC, straight coated abutment; SCy, straight abutment and MC; SCCy, straight coated abutment and MC; ACy, angled abutment and MC; and ACCy, angled coated abutment and MC. The abutments were attached to the implants by a titanium screw. RT values were measured and registered. Data (in Newton centimeter) were analyzed with analysis of variance and Dunnet test (alpha = 0.05).Results: RT values were significantly affected by MC (P = 0.001) and the interaction between DLC coating and MC (P = 0.038). SCy and ACy showed the lowest RT values, statistically different from the control. The abutment coated groups had no statistical difference compared with the control. Scanning electron microscopy analysis showed DLC film with a thickness of 3 mm uniformly coating the hexagonal abutment.Conclusion: DLC film deposited on the abutment can be used as an alternative procedure to reduce abutment screw loosening.

Histomorphometric evaluation of a threaded, sandblasted, acid-etched implant retrieved from a human lower jaw: A case report

The purpose of this study was to histomorphometrically evaluate the bone-to-implant contact and bone area around a titanium implant retrieved from a human lower jaw. A screw-shaped titanium implant (sandblasted and acid-etched surface) was removed from a 68-year-old male after having been in function for 40 months because of a fracture of the abutment screw. Following the implant removal, an undecalcified section was obtained. The histomorphometric analysis showed a rate of 75.40% of bone-to-implant contact and 89.30% of bone area filling within the limits of the implant threads. The surrounding bone healed in a well-organized pattern and could not be differentiated from the anginal alveolus. The histologic evidence showed a high degree of osseointegration in a threaded, sandblasted, and acid-etched implant retrieved from a human lower jaw after functional loading for 40 months. Copyright © 2005 by Lippincott Williams & Wilkins.

Mechanical Evaluation of Four Narrow-Diameter Implant Systems

Purpose: This study aimed to evaluate the survival probability of four narrow-diameter implant systems when subjected to fatigue loading. Materials and Methods: Seventy-two narrow-diameter implants to be restored with single-unit crowns were divided into four groups (n = 18): Astra Tech (3.5-mm diameter), with a standard connection (ASC); BioHorizon (3.4-mm diameter), with a standard connection (BSC); Intra-Lock (3.4-mm diameter), with a standard multilobular connection (ISC); and Intra-Lock (3.4-diameter), with a modified square connection (IMC). The corresponding abutments were screwed onto the implants, and standardized metal crowns (maxillary central incisors) were cemented and subjected to step-stress accelerated life testing in water. Use-level probability Weibull curves and reliability for 100,000 cycles at 150 and 200 N (90% two-sided confidence intervals) were calculated. Polarized light and scanning electron microscopes were used to access the failure modes. Results: The calculated survival probability for 100,000 cycles at 150 N was approximately 93% in group ASC, 98% in group BSC, 94% in group ISC, and 99% in group IMC. At 200 N, the survival rate was estimated to be approximately < 0.1% for ASC, 77% for BSC, 34% for ISC, and 93% for IMC. Abutment screw fracture was the main failure mode for all groups. Conclusions: Although the probability of survival was not significantly different among systems at a load of 150 N, a significant decrease was observed at 200 N for all groups except IMC.

A systematic review of the survival and complication rates of implant supported fixed dental prostheses with cantilever extensions after an observation period of at least 5 years

OBJECTIVE: The aim of this systematic review was to assess the survival rates of short-span implant-supported cantilever fixed dental prostheses (ICFDPs) and the incidence of technical and biological complications after an observation period of at least 5 years. MATERIAL AND METHODS: An electronic MEDLINE search supplemented by manual searching was conducted to identify prospective or retrospective cohort studies reporting data of at least 5 years on ICFDPs. Five- and 10-year estimates for failure and complication rates were calculated using standard or random-effect Poisson regression analysis. RESULTS: The five studies eligible for the meta-analysis yielded an estimated 5- and 10-year ICFDP cumulative survival rate of 94.3% [95 percent confidence interval (95% CI): 84.1-98%] and 88.9% (95% CI: 70.8-96.1%), respectively. Five-year estimates for peri-implantitis were 5.4% (95% CI: 2-14.2%) and 9.4% (95% CI: 3.3-25.4%) at implant and prosthesis levels, respectively. Veneer fracture (5-year estimate: 10.3%; 95% CI: 3.9-26.6%) and screw loosening (5-year estimate: 8.2%; 95% CI: 3.9-17%) represented the most common complications, followed by loss of retention (5-year estimate: 5.7%; 95% CI: 1.9-16.5%) and abutment/screw fracture (5-year estimate: 2.1%; 95% CI: 0.9-5.1%). Implant fracture was rare (5-year estimate: 1.3%; 95% CI: 0.2-8.3%); no framework fracture was reported. Radiographic bone level changes did not yield statistically significant differences either at the prosthesis or at the implant levels when comparing ICFDPs with short-span implant-supported end-abutment fixed dental prostheses. CONCLUSIONS: ICFDPs represent a valid treatment modality; no detrimental effects can be expected on bone levels due to the presence of a cantilever extension per se.

Implant Abutment Deformation During Prosthetic Cylinder Screw Tightening: An In Vitro Study

Purpose: Nonpassive fit frameworks are believed to lead to implant overload and consequently loss of osseointegration. This is one of the most commonly reported failures of implant prostheses. In an ideal situation of passive fit, when torque is applied to bring the abutment-cylinder interface together some amount of deformation can be expected, and it should be homogeneous along the periphery of the abutment. The aim of this study was to verify the amount of abutment deformation that can be expected when a free-standing cylinder is screwed into place. This could give insight into what should be accepted as passive fit. Materials and Methods: Strain gauges were bonded to the sides of five standard abutments that had machined palladium-silver cylinders or cobalt-chromium cast cylinders screwed into place. Measurements were taken to verify the deformation at each site. Results: Values of abutment deformation after abutment screw tightening ranged from -127.70 to -590.27 mu epsilon. The deformation recorded for palladium-silver prosthetic cylinder tightening ranged from 56.905 to -381.50 mu epsilon (mean: 173.298 mu epsilon) and from -5.62638 to -383.86 mu epsilon ( mean: 200.474 mu epsilon) for cobalt-chromium cylinders. There was no statistically significant difference among the two groups. Conclusion: Both abutment screw tightening and prosthetic cylinder screw tightening result in abutment deformation, which is compressive most of the time. Int J Prosthodont 2009; 22: 391-395.

Influence of repeated screw tightening on bacterial leakage along the implant-abutment interface

Objectives Bacterial penetration along the implant-abutment interface as a consequence of abutment screw loosening has been reported in a number of recent studies. The aim of this in vitro study was to investigate the influence of repeated tightening of the abutment screw on leakage of Streptococcus mutans along the interface between implants and pre-machined abutments. Materials and methods Twenty pre-machined abutments with a plastic sleeve were used. The abutment screws were tightened to 32 N cm in group 1 (n=10 - control) and to 32 N cm, loosened and re-tightened with the same torque twice in group 2 (n=10). The assemblies were completely immersed in 5 ml of Tryptic Soy Broth medium inoculated with S. mutans and incubated for 14 days. After this period, contamination of the implant internal threaded chamber was evaluated using the DNA Checkerboard method. Results Microorganisms were found on the internal surfaces of both groups evaluated. However, bacterial counts in group 2 were significantly higher than that in the control group (P < 0.05). Conclusion These results suggest that bacterial leakage between implants and abutments occurs even under unloaded conditions and at a higher intensity when the abutment screw is tightened and loosened repeatedly. To cite this article:do Nascimento C, Pedrazzi V, Kirsten Miani P, Daher Moreira L, de Albuquerque Junior RF. Influence of repeated screw tightening on bacterial leakage along the implant-abutment interface.Clin. Oral Impl. Res. 20, 2009; 1394-1397.doi: 10.1111/j.1600-0501.2009.01769.x.

Removal torque of zirconia abutment screws under dry and wet conditions

The aim of this study was to verify whether screw abutment lubrication can generate higher preload values compared to non-lubricated screws, a titanium abutment was screwed onto an implant analog and scanned with the Procera System to generate 20 zirconia abutments. MKIII Brånemark implants were clamped to a precision torque device, and the abutments were distributed in dry and wet groups with 10 specimens each. In the wet groups, the inner threads of the implants were filled with artificial saliva. All abutments were fastened with a Torqtite screw under 32 Ncm. Ten detorque measurements were performed per group pushing the reverse button of the Torque controller soon after screw tightening with values registered. The mean detorque values were calculated and compared by a Student's t test (?=0.05). The wet condition presented significantly higher mean detorque than the dry condition (31.5 ± 1.2 versus 27.5 ± 1.5 Ncm, respectively; p=0.0000024). In conclusion, there was always a loss in the initial torque values when the removal torque was measured under both conditions. The wet condition presented higher mean torque than the dry condition. Better preload values were established in the wet group, suggesting that the abutment screw must be lubricated in saliva to avoid further loosening.

Evaluation of Torque Maintenance of Abutment and Cylinder Screws With Morse Taper Implants

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of implant connection and restoration design (screwed vs. cemented) in reliability and failure modes of anterior crowns

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effectiveness of Screw Surface Coating on the Stability of Zirconia Abutments After Cyclic Loading

Purpose: Different surface treatments have been developed in attempts to prevent the loosening of abutment screws. The aim of the current study was to compare the effectiveness of titanium alloy screws with tungsten-doped diamond-like carbon (W-DLC) coating and uncoated screws in providing stability to zirconia (ZrO2) ceramic abutments after cyclic loading. Materials and Methods: Twenty prefabricated ZrO2 ceramic abutments on their respective external-hex implants were divided into two groups of equal size according to the type of screw used: uncoated titanium alloy screw (Ti) or titanium alloy screw with W-DLC coating (W-DLC/Ti). The removal torque value (preload) of the abutment screw was measured before and after loading. Cyclic loading between 11 and 211 N was applied at an angle of 30 degrees to the long axis of the implants at a frequency of 15 Hz. A target of 0.5 x 10(6) cycles was defined. Group means were calculated and compared using analysis of variance and the F test (alpha=.05). Results: Before cyclic loading, the preload for Ti screws was significantly higher than that for W-DLC/Ti screws (P=.021). After cyclic loading, there was no significant difference between them (P=.499). Conclusions: Under the studied conditions, it can be concluded that, after cyclic loading, both abutment screws presented a significant reduction in the mean retained preload and similar effectiveness in maintaining preload. INT J ORAL MAXILLOFAC IMPLANTS 2012;27:1061-1067

Reliability and failure modes of internal conical dental implant connections

Objective: Biological and mechanical implant-abutment connection complications and failures are still present in clinical practice, frequently compromising oral function. The purpose of this study was to evaluate the reliability and failure modes of anterior single-unit restorations in internal conical interface (ICI) implants using step-stress accelerated life testing (SSALT). Materials and methods: Forty-two ICI implants were distributed in two groups (n = 21 each): group AT-OsseoSpeed™ TX (Astra Tech, Waltham, MA, USA); group SV-Duocon System Line, Morse Taper (Signo Vinces Ltda., Campo Largo, PR, Brazil). The corresponding abutments were screwed to the implants and standardized maxillary central incisor metal crowns were cemented and subjected to SSALT in water. Use-level probability Weibull curves and reliability for a mission of 50,000 cycles at 200 N were calculated. Differences between groups were assessed by Kruskal-Wallis along with Bonferroni's post-hoc tests. Polarized-light and scanning electron microscopes were used for failure analyses. Results: The Beta (β) value derived from use level probability Weibull calculation was 1.62 (1.01-2.58) for group AT and 2.56 (1.76-3.74) for group SV, indicating that fatigue was an accelerating factor for failure of both groups. The reliability for group AT was 0.95 and for group SV was 0.88. Kruskal-Wallis along with Bonferroni's post-hoc tests showed no significant difference between the groups tested (P > 0.27). In all specimens of both groups, the chief failure mode was abutment fracture at the conical joint region and screw fracture at neck's region. Conclusions: Reliability was not different between investigated ICI connections supporting maxillary incisor crowns. Failure modes were similar. © 2012 John Wiley & Sons A/S.