Method for determining reaction rate of mild steel containers during melting of magnesium-aluminium alloys and effect of aluminium content on directionally solidified microstructures

A magnesium alloy of eutectic composition (33 wt-'%Al) was directionally solidified in mild steel tubes at two growth rates, 32 and 580 mum s(-1,) in a temperature gradient between 10 and 20 K mm(-1). After directional solidification, the composition of each specimen varied dramatically, from 32'%Al in the region that had remained solid to 18%Al (32 mum s(-1) specimen) and 13%Al (580 mum s(-1) specimen) at the plane that had been quenched from the eutectic temperature. As the aluminium content decreased, the microstructure contained an increasing volume fraction of primary magnesium dendrites and the eutectic morphology gradually changed from lamellar to partially divorced. The reduction in aluminium content was caused by the growth of an Al-Fe phase ahead of the Mg-Al growth front. Most of the growth of the Al-Fe phase occurred during the remelting period before directional solidification. The thickness of the Al-Fe phase increased with increased temperature and time of contact with the molten Mg-Al alloy. (C) 2003 Maney Publishing.

Semi-empirical procedures for estimation of residual velocity and ballistic limit for impact on mild steel plates by projectiles

This paper deals with the development of simplified semi-empirical relations for the prediction of residual velocities of small calibre projectiles impacting on mild steel target plates, normally or at an angle, and the ballistic limits for such plates. It has been shown, for several impact cases for which test results on perforation of mild steel plates are available, that most of the existing semi-empirical relations which are applicable only to normal projectile impact do not yield satisfactory estimations of residual velocity. Furthermore, it is difficult to quantify some of the empirical parameters present in these relations for a given problem. With an eye towards simplicity and ease of use, two new regression-based relations employing standard material parameters have been discussed here for predicting residual velocity and ballistic limit for both normal and oblique impact. The latter expressions differ in terms of usage of quasi-static or strain rate-dependent average plate material strength. Residual velocities yielded by the present semi-empirical models compare well with the experimental results. Additionally, ballistic limits from these relations show close correlation with the corresponding finite element-based predictions.

Effect of prestrain on fatigue crack propagation in mild steel containing non-metallic inclusions

The effect of tensile prestrain on fatigue crack propagation behaviour of commercial mild steel with significant amount of stringer inclusions has been studied. In prestrained materials the usual stable stage II crack growth region is preceded by a phase wherein a retardation in crack growth rate occurs. No such behaviour is observed in annealed material. The amount of retardation is found to increase with increase in prestrain. A mechanism for the observed retardation in crack growth rate is also presented.

Effect of Prestrain on Fracture Toughness of Rolled Mild Steel with Significant Inclusion Content

The basic method of JIc calculation using a single specimen is discussed. Dokouipil's approach for evaluating the JIc value is extended further and the effect of prestrain on rolled mild steel with significant inclusions is studied using this modified approach. Although this method does not give an accurate value of JIc, it is quite effective for a comparative study. While the fracture toughness of annealed and 7% prestrained materials are about the same, the fracture toughness of 3% prestrained material is significantly lower.

A numerical study of projectile impact on mild steel armour plates

The present article deals with the development of a finite element modelling approach for the prediction of residual velocities of hard core ogival-nose projectiles following normal impact on mild steel target plates causing perforation. The impact velocities for the cases analysed are in the range 818–866.3 m/s. Assessment of finite element modelling and analysis includes a comprehensive mesh convergence study using shell elements for representing target plates and solid elements for jacketed projectiles with a copper sheath and a rigid core. Dynamic analyses were carried out with the explicit contact-impact LS-DYNA 970 solver. It has been shown that proper choice of element size and strain rate-based material modelling of target plate are crucial for obtaining test-based residual velocity.The present modelling procedure also leads to realistic representation of target plate failure and projectile sheath erosion during perforation, and confirms earlier observations that thermal effects are not significant for impact problems within the ordnance range. To the best of our knowledge, any aspect of projectile failure or degradation obtained in simulation has not been reported earlier in the literature. The validated simulation approach was applied to compute the ballistic limits and to study the effects of plate thickness and projectile diameter on residual velocity, and trends consistent with experimental data for similar situations were obtained.

Preparation of Self Assembled Sodium Oleate Monolayer on Mild Steel and Its Corrosion Inhibition Behavior in Saline water

A self assembled monolayer (SAM) of sodium oleate was generated on mild steel by the dip coating method. Formation of the SAM on mild steel was examined using Infrared Reflection Absorption Spectroscopy (IRRAS) and contact angle measurements. The chemical and anticorrosive properties of the SAM were analyzed using different techniques. IRRAS and water contact angle data revealed the crystallinity and chemical stability of the SAM modified mild steel. The electrochemical measurements showed that the mild steel with the sodium oleate derived SAM exhibited better corrosion resistance in saline water. The effect of temperature and pH on the SAM formation and its anti corrosion ability was explored.

Synergistic effect of colchicine and iodide ions on the corrosion of mild steel in 0.5 M H2SO4

The inhibition behavior of colchicine (CC) on the corrosion of mild steel in 0.5 M H2SO4 was evaluated by electrochemical methods such as potentiodynamic polarization and electrochemical impedance spectroscopic measurements. The inhibition efficiency increases with increasing concentration of CC. The potentiodynamic polarization results reveal that CC act as a mixed-type inhibitor by retarding both cathodic and anodic corrosion reactions. Additionally, the synergism was carried out between CC and KI to improve the corrosion inhibition behavior of CC on mild steel. The adsorption of both CC alone and the combined inhibitor (CC + KI) on mild steel surface follows Langmuir adsorption isotherm. The synergism parameter (S (theta) ) was calculated to recognize the existence of synergism between CC and iodide ions. Lastly, an adsorption mechanism of CC molecules with iodide ions is discussed.

Investigation of the inhibition effect of ibuprofen triazole against mild steel corrosion in an acidic environment

The inhibition performance of ibuprofen triazole (IT) on mild steel (MS) corrosion in 1.0 M HCl and 0.5 M H2SO4 has been investigated by using electrochemical (potentiodynamic polarization and electrochemical impedance spectroscopy), gravimetric, and quantum chemical studies. Electrochemical investigation indicates that IT hampers MS corrosion via adsorption through a mixed inhibition mechanism. The protection ability of IT increases with an increasing concentration of inhibitor and decreases with increasing temperature. The adsorption of IT molecules on MS surface follows the Langmuir adsorption isotherm. Certain quantum chemical parameters were calculated to ascertain the correlation between inhibitive effect and molecular structure of IT.

Surface modification of mild steel by a self-assembled cetyl-trimethyl ammonium bromide (CTAB) monolayer: Evaluation of its corrosion protection property

The surface of mild steel was modified by generating cetyl-trimethyl ammonium bromide (CTAB) self-assembled monolayer (SAM) to enhance the corrosion resistance property. The experimental parameters (pH and time) for SAM generation were optimized. The modified surface was characterized by infrared reflection absorption spectroscopy (IRRAS) and contact angle measurements. The SAM generated in 1 mM solution of CTAB at pH 2.5 for 2 h showed a regimented monolayer. Polarization and electrochemical impedance spectroscopic (EIS) studies demonstrated a significant enhancement in the corrosion resistance property of the SAM protected steel in both 1 M HCl and 3.5% NaCl solution. The CTAB SAM surface substantially reduced the corrosion rate by approximately 4 times in 1 M HCl and 1.5 times in 3.5% NaCl media as compared to bare steel. Scanning electron microscopy images confirmed the formation of lesser amounts of corrosion products on the SAM protected surface. (C) 2015 Elsevier B.V. All rights reserved.

Electrochemical, gravimetric and quantum chemical analysis of mild steel corrosion inhibition by colchicine in 1 M HCl medium

The inhibition effect of colchicine (CC) on mild steel (MS) corrosion in 1 M HCl solution has been investigated by electrochemical techniques such as electrochemical impedance spectroscopy, potentiodynamic polarization, chronoamperometry and also by the gravimetric method. Polarization studies showed that CC acts as mixed type corrosion inhibitor. The inhibitor adsorption process in the MS/CC/HCl system was studied at different temperatures (303-333 K). The adsorption of CC on MS surface is an exothermic process and obeys the Langmuir adsorption isotherm. Based on potential of zero charge values and quantum chemical parameters, the mechanism of adsorption has been proposed.