Durabilidade de compósito biomassa vegetal-cimento modificado por polímero

The durability of the cellulose-cement composites is a decisive factor to introduce such material in the market. Polymers have been used in concrete and mortar production to increase its durability. The goal of this work was the physical and mechanical characterization of cellulose-cement composites modified by a polymer and the subsequent durability evaluation. The work also evaluated the dispersion of acrylic polymer in composites made of Pinus caribaea residues. The physical properties observed were water absorption by immersion and bulk density. Rupture modulus and toughness were determined by flexural test. The specimens were obtained from pads, produced by pressing and wet curing. Samples were subjected to accelerated aging tests by repeated wetting and drying cycles and hot-water bath and natural aging. The scanning electron microscopy (SEM) allowed verifying the fiber and composite characteristics along the time. For the composite range analyzed, it was observed the polymer improved the mechanical properties of composites besides a significant decreasing in water absorption. The use of polymer improved the performance of vegetable fiber-cement composites when compared to the conventional mortar, due to water absorption decreasing.

Eficiência do processo de recobrimento de sementes de brócolos recobertas com polímero em leito de jorro

Broccoli seeds were coated in a conical-cylindrical spouted bed with an aqueous suspension of hydroxy ethyl cellulose aiming to improve the seeds coating technique using a fluid-dynamic process. An experimental design was applied to investigate the effects of the operating variables: gas temperature, atomizing air pressure and suspension flow rate on the germination of the seeds and on the process efficiency. Results indicated that the operating variables affect both the coating process efficiency and the germination ability. However, the analysis didn t identify differences between the germination potential of coated and uncoated seeds. Coated seeds absorbed up to 10 percent less moisture than the uncoated ones, when the environment temperature and humidity were controlled over a period of time.

Estudo inicial da degradação in vivo de poli(L-co-D,L ácido lático), sintetizado em laboratório, aplicado como prótese tibial em coelhos

The copolymer poly (L-co-D,L lactic acid), PLDLA, has gained prominence in the field of temporary prostheses due to the fact that their time of degradation is quite compatible with the requirement in the case of osseous fracture. In this work the in vivo degradation of devices from copolymer, as a system of plates and screws, used in fixation of the tibia of rabbits was studied. The devices were implanted in 15 adult rabbits, albinos, New Zealand race, and they were used as control devices of alloys of titanium (Ti-6Al-4V/ V grade). The use of copolymers, synthesized in the laboratory, was tested in the repair of fracture in rabbits'tibias, being assessed in the following times: 2 weeks, 2 months and 3 months. Morphological analysis of tissue surrounding the plate and screw system, for 2 weeks of implantation, showed the presence of osteoblasts, indicating a pre bone formation. After 2 months there was new bone formation in the region in contact with the polymer. This bone growth occurred simultaneously with the process of PLDLA degradation, invading the region where there was polymer and after 3 months there was an intense degradation of the copolymer and hence greater tissue invasion compared to 2 months which characterized bone formation in a region where the polymer degraded. The in vivo degradation study of the devices for PLDLA by means of histological evaluations during the period of consolidation of the fracture showed the efficiency of plate and screw system, and it was possible to check formation of bone tissue at the implantation site, without the presence of inflammatory reaction

Desidratação osmótica de abacaxi aplicada à tecnologia de métodos combinados

The aim of this research was to optimize osmotic dehydration of pineapple, according to two criteria: maximize water loss and minimize solid gain. The process was made as an application to Combined Methods Technology, in which three preservation factors were combined: water activity, pH and chemical preservatives, all being applied at low levels, in order to get a product resembling non-processed fruit. The experiment was divided into three treatments, being: non-coated pineapple pieces (A), pieces coated with alginate (B) and coated with low-methoxyl pectin (C). Process involved the following main steps: enzymatic inactivation of fruit pieces; in treatments B and C, incorporation of their respective coatings; and osmotic dehydration, in sucrose syrup containing potassium sorbate and citric acid. Optimum conditions, determined from Response Surface Methodology, were the following: dehydration of fruit pieces coated by alginate, at 42-47° C, in sucrose syrup at 66-69° Brix, for 220 to 270 minutes. Results indicated that both coatings significantly affected the mass transfers of the process, reducing solid incorporation and increasing water loss; therefore, increasing weight loss and performance ratio (water loss: solid incorporation) took place. Water activity was not significantly affected by the coatings. The product obtained under optimum conditions was submitted to sensorial evaluation, and presented a good general acceptance. Moulds and yeasts countings indicated good microbiological stability of the product for at least 60 days at 30ºC.

A relevancia do treinamento complexo no desempenho de nadadores competitivos

Universidade Estadual de Campinas . Faculdade de Educação Física