Influence Of Successive Light-activation On Degree Of Conversion And Knoop Hardness Of The First Layered Composite Increment.

To evaluate the influence of light-activation of second, third and fourth increments on degree of conversion (DC) and microhardness (KHN) of the top (T) and bottom (B) surface of the first increment. Forty samples (n = 5) were prepared. In groups 1-4, after each increment light-activation (multiple irradiation), T and B of the first increment were measured in DC and KHN. In groups 5-8, only the first increment was made (single irradiation) and measurements of DC and KHN were taken at 15 min intervals. The light-activation modes were (XL) 500 mW/cm(2) × 38 s (G1/G5); (S) 1000 mW/cm(2) × 19 s (G2/G6), (HP) 1400 mW/cm(2) × 14 s (G3/G7); (PE) 3200 mW/cm(2) × 6 s (G4/G8). Data for DC and KHN were analyzed separately by using PROC MIXED for repeated measures and Tukey-Kramer test (α = 0.05). For KHN, B showed lower values than T. PE resulted in lower values of KHN in B surface. For single and multiple irradiations, T and B of first measurement showed the lowest KHN and the fourth measurement showed the highest, with significant difference between them. For single irradiation, first and second increments presented similar KHN, different from the third and fourth increment, which did not differ between them. For multiple irradiations, the second light-activation resulted in KHN similar to first, third and fourth increments. For DC, except QTH, T presented higher DC than B. The light-activation of successive increments was not able to influence the KHN and DC of the first increment.

Low-density Three-dimensional Foam Using Self-reinforced Hybrid Two-dimensional Atomic Layers.

Low-density nanostructured foams are often limited in applications due to their low mechanical and thermal stabilities. Here we report an approach of building the structural units of three-dimensional (3D) foams using hybrid two-dimensional (2D) atomic layers made of stacked graphene oxide layers reinforced with conformal hexagonal boron nitride (h-BN) platelets. The ultra-low density (1/400 times density of graphite) 3D porous structures are scalably synthesized using solution processing method. A layered 3D foam structure forms due to presence of h-BN and significant improvements in the mechanical properties are observed for the hybrid foam structures, over a range of temperatures, compared with pristine graphene oxide or reduced graphene oxide foams. It is found that domains of h-BN layers on the graphene oxide framework help to reinforce the 2D structural units, providing the observed improvement in mechanical integrity of the 3D foam structure.

Comparison Of Different Transfer Impression Techniques Accuracy For Osseointegrated Implants.

Abstract The aim of this study was to evaluate three transfer techniques used to obtain working casts of implant-supported prostheses through the marginal misfit and strain induced to metallic framework. Thirty working casts were obtained from a metallic master cast, each one containing two implant analogues simulating a clinical situation of three-unit implant-supported fixed prostheses, according to the following transfer impression techniques: Group A, squared transfers splinted with dental floss and acrylic resin, sectioned and re-splinted; Group B, squared transfers splinted with dental floss and bis-acrylic resin; and Group N, squared transfers not splinted. A metallic framework was made for marginal misfit and strain measurements from the metallic master cast. The misfit between metallic framework and the working casts was evaluated with an optical microscope following the single-screw test protocol. In the same conditions, the strain was evaluated using strain gauges placed on the metallic framework. The data was submitted to one-way ANOVA followed by the Tukey's test (α=5%). For both marginal misfit and strain, there were statistically significant differences between Groups A and N (p<0.01) and Groups B and N (p<0.01), with greater values for the Group N. According to the Pearson's test, there was a positive correlation between the variables misfit and strain (r=0.5642). The results of this study showed that the impression techniques with splinted transfers promoted better accuracy than non-splinted one, regardless of the splinting material utilized.

Strain Gauges's Analysis On Implant-retained Prosthesis' Cast Accuracy.

A proper cast is essential for a successful rehabilitation with implant prostheses, in order to produce better structures and induce less strain on the implants. The aim of this study was to evaluate the precision of four different mold filling techniques and verify an accurate methodology to evaluate these techniques. A total of 40 casts were obtained from a metallic matrix simulating three unit implant-retained prostheses. The molds were filled using four different techniques in four groups (n = 10): Group 1 - Single-portion filling technique; Group 2 - Two-step filling technique; Group 3 - Latex cylinder technique; Group 4 - Joining the implant analogs previously to the mold filling. A titanium framework was obtained and used as a reference to evaluate the marginal misfit and tension forces in each cast. Vertical misfit was measured with an optical microscope with an increase of 120 times following the single-screw test protocol. Strain was quantified using strain gauges. Data were analyzed using one-way ANOVA (Tukey's test) (α =0.05). The correlation between strain and vertical misfit was evaluated by Pearson test. The misfit values did not present statistical difference (P = 0.979), while the strain results showed statistical difference between Groups 3 and 4 (P = 0.027). The splinting technique was considered to be as efficient as the conventional technique. The strain gauge methodology was accurate for strain measurements and cast distortion evaluation. There was no correlation between strain and marginal misfit.

Ontogenia e estrutura do pericarpo de Prestonia riedelii (Müll. Arg.) Markgr. (Apocynaceae)

The aim of this work was to describe the morphology and ontogeny of P. riedelii fruits to aid in taxonomic, ecological and phylogenetic studies in Apocynaceae. Fruits were fixed in FAA, embedded in plastic resin, sectioned at 10 ìm and stained with toluidine blue, for structural analysis. The fruit of P. riedelii is a follicarium, with two follicular fruitlets. The epicarp is one-cell-layered, with trichomes and thick cuticle. The mesocarp, originating from fundamental ovary tissue, is parenchymatous with laticifers, non-lignified fibers and vascular bundles. The endocarp sensu lato is two-celllayered of crossed sclereids, originating from the inner ovary epidermis and from a single layer of parenchyma cells of fundamental ovary tissue. Follicle dehiscence is lateral and the dehiscence process involves anatomical characteristics such as a dehiscence zone with thin-walled cells, non-lignified fibers in the mesocarp and crossed sclereids in the endocarp.