Corrosion Kinetics And Topography Analysis Of Ti-6al-4v Alloy Subjected To Different Mouthwash Solutions.

This study evaluated the corrosion kinetics and surface topography of Ti-6Al-4V alloy exposed to mouthwash solutions (0.12% chlorhexidine digluconate, 0.053% cetylpyridinium chloride and 3% hydrogen peroxide) compared to artificial saliva (pH6.5) (control). Twenty Ti-6Al-4V alloy disks were used and divided into 4 groups (n=5). For the electrochemical assay, standard tests as open circuit potential and electrochemical impedance spectroscopy (EIS) were applied at baseline, 7 and 14days after immersion in the solutions. Scanning electron microscopy, atomic force microscopy and profilometry (average roughness - Ra) were used for surface characterization. Total weight loss of disks was calculated. Data were analyzed by ANOVA and Bonferroni's test (α=0.05). Hydrogen peroxide generated the lowest polarization resistance (Rp) values for all periods (P<0.05). For the capacitance (Cdl), similar results were observed among groups at baseline (P=0.098). For the 7 and 14-day periods, hydrogen peroxide promoted the highest Cdl values (P<0.0001). Hydrogen peroxide promoted expressive superficial changes and greater Ra values than the others (P<0.0001). It could be concluded that solutions containing cetylpyridinium chloride and chlorhexidine digluconate might be the mouthwashes of choice during the post-operatory period of dental implants. However, hydrogen peroxide is counter-indicated in these situations. Further studies evaluating the dynamics of these solutions (tribocorrosion) and immersing the disks in daily cycles (two or three times a day) to mimic a clinical situation closest to the application of mouthwashes in the oral cavity are warranted to prove our results.

The Effect Of Poly(methyl Methacrylate) Surface Treatments On The Adhesion Of Silicone-based Resilient Denture Liners.

Different surface treatment protocols of poly(methyl methacrylate) have been proposed to improve the adhesion of silicone-based resilient denture liners to poly(methyl methacrylate) surfaces. The purpose of this study was to evaluate the effect of different poly(methyl methacrylate) surface treatments on the adhesion of silicone-based resilient denture liners. Poly(methyl methacrylate) specimens were prepared and divided into 4 treatment groups: no treatment (control), methyl methacrylate for 180 seconds, acetone for 30 seconds, and ethyl acetate for 60 seconds. Poly(methyl methacrylate) disks (30.0 × 5.0 mm; n = 10) were evaluated regarding surface roughness and surface free energy. To evaluate tensile bond strength, the resilient material was applied between 2 treated poly(methyl methacrylate) bars (60.0 × 5.0 × 5.0 mm; n = 20 for each group) to form a 2-mm-thick layer. Data were analyzed by 1-way ANOVA and the Tukey honestly significant difference tests (α = .05). A Pearson correlation test verified the influence of surface properties on tensile bond strength. Failure type was assessed, and the poly(methyl methacrylate) surface treatment modifications were visualized with scanning electron microscopy. The surface roughness was increased (P < .05) by methyl methacrylate treatment. For the acetone and ethyl acetate groups, the surface free energy decreased (P < .05). The tensile bond strength was higher for the methyl methacrylate and ethyl acetate groups (P < .05). No correlation was found regarding surface properties and tensile bond strength. Specimens treated with acetone and methyl methacrylate presented a cleaner surface, whereas the ethyl acetate treatment produced a porous topography. The methyl methacrylate and ethyl acetate surface treatment protocols improved the adhesion of a silicone-based resilient denture liner to poly(methyl methacrylate).

Indicações para ceratoplastia penetrante no Hospital das Clínicas-UNICAMP

PURPOSE: To determine the main causes of penetrating keratoplasty indications at Hospital das Clínicas-UNICAMP (January, 1999 to December, 2003). METHODS: A non-comparative, retrospective series of case studies. The authors reviewed the files of 857 patients who underwent penetrating keratoplasty at Hospital das Clínicas-UNICAMP between 1999-2003 and classified them into different categories according to diagnostic indication for surgery. RESULTS: The age range was between 0-88 years (average 44 years ±1.2). The main causes of penetrating keratoplasty were: keratoconus in 427 cases (49.82%); 152 cases (17.74%) of corneal ulceration (perforated or not); corneal graft failure in 87 cases (10.15%); bullous keratopathy, 72 cases (8.40%); Fuchs dystrophy in 59 cases (6.88%); trachoma complications in 28 cases (3.27%); other causes, 32 (3.74%). In children under 10 years of age, the main cause of penetrating keratoplasty indications was infectious ulcer (77.78%) and between 11-50 years of age, keratoconus was the main cause (71.65%). CONCLUSION: This study was composed of a young population, and the main causes of penetrating keratoplasty were keratoconus and therapeutic keratoplasty.

Eficácia na utilização de córneas no transplante penetrante

PURPOSES: 1) To verify the impact of the creation of the Single Technical Record (STR) at the University of Campinas (Unicamp) Hospital das Clínicas, on the preservation period of corneas which were used in elective penetrating keratoplasties, and 2) to compare the primary failure incidence in cornea penetrating keratoplasties regarding the periods before and after the creation of STR. METHODS: A retrospective study was conducted at the Unicamp Hospital, which evaluated 15 consecutive cornea penetrating keratoplasties between January 1st and April 30th, 2000 and 24 consecutive penetrating keratoplasties between May 1st and September 20th of the same year (corneas under the control of the STR), totaling 39 keratoplasties. RESULTS: The mean time between cornea preparation and transplantation was 3.8 days (±1.78) in the period before STR creation, and 6.0 days (±2.97) after STR creation, representing a 36.7% increase in the preservation time. There was a statistically significant difference (p=0.02) between the two groups. No corneal primary failure was observed among the 39 transplanted patients in both groups. CONCLUSION: Based on the results of this study, it can be concluded that this new concept of the State Transplantation System has caused a statistically significant increase in the conservation period of corneas, which may reduce the period of a clear transplant due to an increased loss of endothelial cells, as well as increase the primary failure incidence or result in a high number of corneas that cannot be used due to having exceeded the preservation time recommended by the literature.

Assessment of ocular surface toxicity after topical instillation of nitric oxide donors

PURPOSE: To evaluate the ocular surface toxicity of two nitric oxide donors in ex vivo and in vivo animal models: S-nitrosoglutathione (GSNO) and S-nitroso-N-acetylcysteine (SNAC) in a hydroxypropyl methylcellulose (HPMC) matrix at final concentrations 1.0 and 10.0 mM. METHODS: Ex vivo GSNO and SNAC toxicities were clinically and histologically analyzed using freshly excised pig eyeballs. In vivo experiments were performed with 20 albino rabbits which were randomized into 4 groups (5 animals each): Groups 1 and 2 received instillations of 150 µL of aqueous HPMC solution containing GSNO 1.0 and 10.0 mM, respectively, in one of the eyes; Groups 3 and 4 received instillations of 150 µL of aqueous HPMC solution-containing SNAC 1.0 and 10.0 mM, respectively, in one of the eyes. The contralateral eyes in each group received aqueous HPMC as a control. All animals underwent clinical evaluation on a slit lamp and the eyes were scored according to a modified Draize eye test and were histologically analyzed. RESULTS: Pig eyeballs showed no signs of perforation, erosion, corneal opacity or other gross damage. These findings were confirmed by histological analysis. There was no difference between control and treated rabbit eyes according to the Draize eye test score in all groups (p>0.05). All formulations showed a mean score under 1 and were classified as non-irritating. There was no evidence of tissue toxicity in the histological analysis in all animals. CONCLUSION: Aqueous HPMC solutions containing GSNO and SNAC at concentrations up to 10.0 mM do not induce ocular irritation.

Topiramate-associated acute, bilateral, angle-closure glaucoma: case report

This paper describes a topiramate induced acute bilateral angle-closure glaucoma. This rare adverse effect is an idiosyncratic reaction characterized by uveal effusion and lens forward displacement, leading to increased intraocular pressure and vision loss. We describe a 55 year-old white woman with migraine, spasmodic torticollis and essential tremor, who developed bilateral acute angle-closure glaucoma, one week after starting topiramate 25 mg/day. She was seen at the Ophthalmology Emergency Department of the Fundação João Penido Burnier (Campinas, SP, Brazil) with a 4 hours history of blurry vision, ocular pain and bright flashes vision. Slit lamp examination revealed moderate conjunctival injection and corneal edema, and shallow anterior chambers. Intraocular pressure was 48 mmHg in both eyes. Fundoscopic examination findings were normal. She was treated with timolol, brimonidine, dorzolamide, pilocarpine, prednisone acetate eye drops and acetazolamide. One hour after those measures, as the intraocular pressure was 30 mmHg, she received a manitol intravenous injection and the intraocular pressure normalized. After 24 hours an iridotomy with Yag laser was performed. Topiramate was discontinued and she was totally recovered after one week.