The aim was to evaluate the relationship between orofacial function, dentofacial morphology, and bite force in young subjects. Three hundred and sixteen subjects were divided according to dentition stage (early, intermediate, and late mixed and permanent dentition). Orofacial function was screened using the Nordic Orofacial Test-Screening (NOT-S). Orthodontic treatment need, bite force, lateral and frontal craniofacial dimensions and presence of sleep bruxism were also assessed. The results were submitted to descriptive statistics, normality and correlation tests, analysis of variance, and multiple linear regression to test the relationship between NOT-S scores and the studied independent variables. The variance of NOT-S scores between groups was not significant. The evaluation of the variables that significantly contributed to NOT-S scores variation showed that age and presence of bruxism related to higher NOT-S total scores, while the increase in overbite measurement and presence of closed lip posture related to lower scores. Bite force did not show a significant relationship with scores of orofacial dysfunction. No significant correlations between craniofacial dimensions and NOT-S scores were observed. Age and sleep bruxism were related to higher NOT-S scores, while the increase in overbite measurement and closed lip posture contributed to lower scores of orofacial dysfunction.

Characterization Of Morphology And Composition Of Inorganic Fillers In Dental Alginates.

Energy dispersive X-ray spectroscopy microanalysis (EDX), scanning electron microscopy (SEM), and Archimedes' Principle were used to determine the characteristics of inorganic filler particles in five dental alginates, including Cavex ColorChange (C), Hydrogum 5 (H5), Hydrogum (H), Orthoprint (O), and Jeltrate Plus (JP). The different alginate powders (0.5 mg) were fixed on plastic stubs (n = 5) and sputter coated with carbon for EDX analysis, then coated with gold, and observed using SEM. Volume fractions were determined by weighing a sample of each material in water before and after calcining at 450(°)C for 3 h. The alginate materials were mainly composed of silicon (Si) by weight (C-81.59%, H-79.89%, O-78.87%, H5-77.95%, JP-66.88%, wt). The filler fractions in volume (vt) were as follows: H5-84.85%, JP-74.76%, H-70.03%, O-68.31%, and C-56.10%. The tested materials demonstrated important differences in the inorganic elemental composition, filler fraction, and particle morphology.