Effect Of Simulated Microwave Disinfection On The Linear Dimensional Change, Hardness And Impact Strength Of Acrylic Resins Processed By Different Polymerizing Cycles.

This study investigated the effect of simulated microwave disinfection (SMD) on the linear dimensional changes, hardness and impact strength of acrylic resins under different polymerization cycles. Metal dies with referential points were embedded in flasks with dental stone. Samples of Classico and Vipi acrylic resins were made following the manufacturers' recommendations. The assessed polymerization cycles were: A-- water bath at 74ºC for 9 h; B-- water bath at 74ºC for 8 h and temperature increased to 100ºC for 1 h; C-- water bath at 74ºC for 2 h and temperature increased to 100ºC for 1 h;; and D-- water bath at 120ºC and pressure of 60 pounds. Linear dimensional distances in length and width were measured after SMD and water storage at 37ºC for 7 and 30 days using an optical microscope. SMD was carried out with the samples immersed in 150 mL of water in an oven (650 W for 3 min). A load of 25 gf for 10 sec was used in the hardness test. Charpy impact test was performed with 40 kpcm. Data were submitted to ANOVA and Tukey's test (5%). The Classico resin was dimensionally steady in length in the A and D cycles for all periods, while the Vipi resin was steady in the A, B and C cycles for all periods. The Classico resin was dimensionally steady in width in the C and D cycles for all periods, and the Vipi resin was steady in all cycles and periods. The hardness values for Classico resin were steady in all cycles and periods, while the Vipi resin was steady only in the C cycle for all periods. Impact strength values for Classico resin were steady in the A, C and D cycles for all periods, while Vipi resin was steady in all cycles and periods. SMD promoted different effects on the linear dimensional changes, hardness and impact strength of acrylic resins submitted to different polymerization cycles when after SMD and water storage were considered.

Effect Of Simulated Microwave Disinfection On The Linear Dimensional Change, Hardness And Impact Strength Of Acrylic Resins Processed By Different Polymerization Cycles.

This study investigated the effect of simulated microwave disinfection (SMD) on the linear dimensional changes, hardness and impact strength of acrylic resins under different polymerization cycles. Metal dies with referential points were embedded in flasks with dental stone. Samples of Classico and Vipi acrylic resins were made following the manufacturers' recommendations. The assessed polymerization cycles were: A) water bath at 74 ºC for 9 h; B) water bath at 74 ºC for 8 h and temperature increased to 100 ºC for 1 h; C) water bath at 74 ºC for 2 h and temperature increased to 100 ºC for 1 h; and D) water bath at 120 ºC and pressure of 60 pounds. Linear dimensional distances in length and width were measured after SMD and water storage at 37 ºC for 7 and 30 days using an optical microscope. SMD was carried out with the samples immersed in 150 mL of water in an oven (650 W for 3 min). A load of 25 gf for 10 s was used in the hardness test. Charpy impact test was performed with 40 kpcm. Data were submitted to ANOVA and Tukey's test (5%). The Classico resin was dimensionally steady in length in the A and D cycles for all periods, while the Vipi resin was steady in the A, B and C cycles for all periods. The Classico resin was dimensionally steady in width in the C and D cycles for all periods, and the Vipi resin was steady in all cycles and periods. The hardness values for Classico resin were steady in all cycles and periods, while the Vipi resin was steady only in the C cycle for all periods. Impact strength values for Classico resin were steady in the A, C and D cycles for all periods, while Vipi resin was steady in all cycles and periods. SMD promoted different effects on the linear dimensional changes, hardness and impact strength of acrylic resins submitted to different polymerization cycles when after SMD and water storage were considered.

Rugosidade e pigmentação superficial de materiais ionoméricos

The aim of this study was to compare two methods of surface roughness analysis, perfilometry and spectrophotometry, applied to the surface of ionomeric materials (Chelon Fil, Vitremer and Dyract), submitted to different surface finishing treatments. For the perfilometric analysis, sixty specimens of each material were made and randomly separated into three experimental groups. The average surface roughness (Ra, mm) was measured on each specimen by a surface perfilometer (Mitutoyo Surftest 211). The spectrophotometric analysis consisted in quantifying the dye impregnated in the samples. The dyes used were 0.5% fuchsin and 0.5% erythrosin. Data were submitted to variance analysis (ANOVA) and t-Student test at a 0.05 significance level. There was no linear correlation between average roughness and superficial deposition of dye. Perfilometric analysis revealed that 12- and 30-bladed carbide burs caused the roughest surface of Chelon Fil, followed by Sof-Lex discs and mylar band. There were no significant differences between the specimens submitted to finishing and polishing with Sof-Lex discs and the control group (mylar band) for Vitremer, nevertheless, the highest Ra values were obtained when 12- and 30-bladed burs were used. For Dyract, there was no significant difference between the three treatments. The mean values of superficial deposition of dye for Chelon Fil, Vitremer and Dyract were: 1.7261, 1.4759, 1.3318, respectively. There were no significant differences between the restorative materials when different finishing and polishing systems were used.

Recreação e lazer como integrantes de curriculos dos cursos de graduação em educação fisica

Universidade Estadual de Campinas . Faculdade de Educação Física

Recreação e lazer como integrantes dos curriculos dos cursos de graduação em educação fisica

Universidade Estadual de Campinas. Faculdade de Educação Física