Effect Of Simulated Microwave Disinfection On The Linear Dimensional Change, Hardness And Impact Strength Of Acrylic Resins Processed By Different Polymerizing Cycles.

This study investigated the effect of simulated microwave disinfection (SMD) on the linear dimensional changes, hardness and impact strength of acrylic resins under different polymerization cycles. Metal dies with referential points were embedded in flasks with dental stone. Samples of Classico and Vipi acrylic resins were made following the manufacturers' recommendations. The assessed polymerization cycles were: A-- water bath at 74ºC for 9 h; B-- water bath at 74ºC for 8 h and temperature increased to 100ºC for 1 h; C-- water bath at 74ºC for 2 h and temperature increased to 100ºC for 1 h;; and D-- water bath at 120ºC and pressure of 60 pounds. Linear dimensional distances in length and width were measured after SMD and water storage at 37ºC for 7 and 30 days using an optical microscope. SMD was carried out with the samples immersed in 150 mL of water in an oven (650 W for 3 min). A load of 25 gf for 10 sec was used in the hardness test. Charpy impact test was performed with 40 kpcm. Data were submitted to ANOVA and Tukey's test (5%). The Classico resin was dimensionally steady in length in the A and D cycles for all periods, while the Vipi resin was steady in the A, B and C cycles for all periods. The Classico resin was dimensionally steady in width in the C and D cycles for all periods, and the Vipi resin was steady in all cycles and periods. The hardness values for Classico resin were steady in all cycles and periods, while the Vipi resin was steady only in the C cycle for all periods. Impact strength values for Classico resin were steady in the A, C and D cycles for all periods, while Vipi resin was steady in all cycles and periods. SMD promoted different effects on the linear dimensional changes, hardness and impact strength of acrylic resins submitted to different polymerization cycles when after SMD and water storage were considered.

Effect Of Simulated Microwave Disinfection On The Linear Dimensional Change, Hardness And Impact Strength Of Acrylic Resins Processed By Different Polymerization Cycles.

This study investigated the effect of simulated microwave disinfection (SMD) on the linear dimensional changes, hardness and impact strength of acrylic resins under different polymerization cycles. Metal dies with referential points were embedded in flasks with dental stone. Samples of Classico and Vipi acrylic resins were made following the manufacturers' recommendations. The assessed polymerization cycles were: A) water bath at 74 ºC for 9 h; B) water bath at 74 ºC for 8 h and temperature increased to 100 ºC for 1 h; C) water bath at 74 ºC for 2 h and temperature increased to 100 ºC for 1 h; and D) water bath at 120 ºC and pressure of 60 pounds. Linear dimensional distances in length and width were measured after SMD and water storage at 37 ºC for 7 and 30 days using an optical microscope. SMD was carried out with the samples immersed in 150 mL of water in an oven (650 W for 3 min). A load of 25 gf for 10 s was used in the hardness test. Charpy impact test was performed with 40 kpcm. Data were submitted to ANOVA and Tukey's test (5%). The Classico resin was dimensionally steady in length in the A and D cycles for all periods, while the Vipi resin was steady in the A, B and C cycles for all periods. The Classico resin was dimensionally steady in width in the C and D cycles for all periods, and the Vipi resin was steady in all cycles and periods. The hardness values for Classico resin were steady in all cycles and periods, while the Vipi resin was steady only in the C cycle for all periods. Impact strength values for Classico resin were steady in the A, C and D cycles for all periods, while Vipi resin was steady in all cycles and periods. SMD promoted different effects on the linear dimensional changes, hardness and impact strength of acrylic resins submitted to different polymerization cycles when after SMD and water storage were considered.

Comparative In vitro Mechanical Evaluation Of Techniques Using A 2.0 mm Locking Fixation System For Simulated Fractures Of The Mandibular Body.

To perform a comparative evaluation of the mechanical resistance of simulated fractures of the mandibular body which were repaired using different fixation techniques with two different brands of 2.0 mm locking fixation systems. Four aluminum hemimandibles with linear sectioning simulating a mandibular body fracture were used as the substrates and were fixed using the two techniques and two different brands of fixation plate. These were divided into four groups: groups I and II were fixed with one four-hole plate, with four 6 mm screws in the tension zone and one four-hole plate, with four 10 mm screws in the compression zone; and groups III and IV were fixed with one four-hole plate with four 6 mm screws in the neutral zone. Fixation plates manufactured by Tóride were used for groups I and III, and by Traumec for groups II and IV. The hemimandibles were submitted to vertical, linear load testing in an Instron 4411 servohydraulic mechanical testing unit, and the load/displacement (3 mm, 5 mm and 7 mm) and the peak loads were measured. Means and standard deviations were evaluated applying variance analysis with a significance level of 5%. The only significant difference between the brands was seen at displacements of 7 mm. Comparing the techniques, groups I and II showed higher mechanical strength than groups III and IV, as expected. For the treatment of mandibular linear body fracture, two locking plates, one in the tension zone and another in the compression zone, have a greater mechanical strength than a single locking plate in the neutral zone.

Development Plates For Stable Internal Fixation: Study Of Mechanical Resistance In Simulated Fractures Of The Mandibular Condyle.

To develop Y-shaped plates with different thicknesses to be used in simulated fractures of the mandibular condyle. Ten plates were developed in Y shape, containing eight holes, and 30 synthetic polyurethane mandible replicas were developed for the study. The load test was performed on an Instron Model 4411 universal testing machine, applying load in the mediolateral and anterior-posterior positions on the head of the condyle. Two-way ANOVA with Tukey testing with a 5% significance level was used. It was observed that when the load was applied in the medial-lateral plate of greater thickness (1.5 mm), it gave the highest strength, while in the anteroposterior direction, the plate with the highest resistance was of the lesser thickness (0.6 mm). A plate with a thickness of 1.5 mm was the one with the highest average value for all displacements. In the anteroposterior direction, the highest values of resistance were seen in the displacement of 15 mm. After comparing the values of the biomechanical testing found in the scientific literature, it is suggested that the use of Y plates are suitable for use in subcondylar fractures within the limitations of the study.

Comparação da eficiência do processo de ozonização e ozonização catalítica (Mn II e Cu II) na degradação de fenol

This paper discusses the results obtained with homogeneous catalytic ozonation [Mn (II) and Cu (II)] in phenol degradation. The reduction of total phenols and total organic carbon (TOC) and the ozone consumption were evaluated. The efficiency in phenol degradation (total phenol removal) at pH 3, with the catalytic process (Mn (II)), increased from 37% to 55% while the TOC removal increased from 4 to 63% in a seven-minute treatment. The ozonation process efficiency at pH 10 was 43% and 39% for phenol and TOC removal, respectively. The presence of both metallic ions (Mn2+ and Cu+2) in the ozonation process resulted in a positive effect.

Teores de corantes artificiais em alimentos determinados por cromatografia líquida de alta eficiência

Synthetic dyes are much used in processed foods. HPLC was applied to different types of snacks, such as colored cereals, chocolate confetti, chewing gums and candies for the determination of those additives. In the case of artificially colored breakfast cereals, 71% of the samples exceeded the allowed limits. Regarding the portions recommended for consumption by the makers of two of the samples, the amounts exceeded those allowed by the Brazilian legislation. In the case of chocolate confetti and candies none of the samples showed higher amounts than those allowed. However 37% of the chewing gum samples presented larger contents than the authorized ones, and one sample contained five times more synthetic dyes than allowed.

Validação e estimativa da incerteza de método para análise de licopeno e β-caroteno em polpa de tomate por cromatografia líquida de alta eficiência

A method to quantify lycopene and β-carotene in freeze dried tomato pulp by high performance liquid chromatography (HLPC) was validated according to the criteria of selectivity, sensitivity, precision and accuracy, and uncertainty estimation of measurement was determined with data obtained in the validation. The validated method presented is selective in terms of analysis, and it had a good precision and accuracy. Detection limit for lycopene and β-carotene was 4.2 and 0.23 mg 100 g-1, respectively. The estimation of expanded uncertainty (K = 2) for lycopene was 104 ± 21 mg 100 g-1 and for β-carotene was 6.4 ± 1.5 mg 100 g-1.

Aplicações de cromatografia líquida de alta eficiência para o estudo de poluentes orgânicos emergentes

Emerging organic pollutants (EOP) include many environmental contaminants based on commercial products such as pharmaceuticals, personal care products, detergents, gasoline, polymers, etc. EOP may be candidates for future regulation as they offer potential risk to environmental and human health due to their continual entrance into the environment and to the fact that even the most modern wastewater treatment plants are not able to totally transform / remove these compounds. High performance liquid chromatography is recommended to separate emerging organic pollutants with characteristics of high polarity and low volatility, especially pharmaceuticals, from environmental matrices.

Efeito da adição de cinza da casca de arroz em misturas cimento-casca de arroz

The rice husk and its ash are abundant and renewable and can be used to obtain alternative building materials. An increase in the consumption of such waste could help minimize the environmental problems from their improper disposal. This study aimed to evaluate the use of ashes as a cargo mineral (filler). However, the rice husk chemically interferes in the conduct of the based cement mixtures. Thus, different mixes cement-rice husk with and without the addition of ash were evaluated in order to highlight the influence of its components (husk; ash), which could otherwise be excluded or be underestimated. Cylindrical samples (test of simple compression and traction by diametrical compression) and samples extracted from manufactured pressed board (test of bending and parallel compression to the surface), were used to evaluate the behavior of different mixtures of components (rice hush; RHA - rice husk ahs). The results of the mechanical tests showed, in general, there is not a statistical difference between the mixtures, which are associated with the chemical suppressive effect of the rice husk ash. The mixture of rice husk of 10 mm, with an addition of 35% of the rice husk ash, is notable for allowing the highest consumption of rice husk and rice husk ash, to reduce 25% the consumption of cement and to allow the storage (without emissions to the atmosphere), around 1.9 ton of CO2 per ton of cement consumed, thus contributing to the reduction of CO2 emissions, which can stimulate rural constructions under an ecological point of view.

Eficiência do processo de recobrimento de sementes de brócolos recobertas com polímero em leito de jorro

Broccoli seeds were coated in a conical-cylindrical spouted bed with an aqueous suspension of hydroxy ethyl cellulose aiming to improve the seeds coating technique using a fluid-dynamic process. An experimental design was applied to investigate the effects of the operating variables: gas temperature, atomizing air pressure and suspension flow rate on the germination of the seeds and on the process efficiency. Results indicated that the operating variables affect both the coating process efficiency and the germination ability. However, the analysis didn t identify differences between the germination potential of coated and uncoated seeds. Coated seeds absorbed up to 10 percent less moisture than the uncoated ones, when the environment temperature and humidity were controlled over a period of time.

Otimização da eficiência de limpeza em equipamento de beneficiamento de tomate de mesa

The post-harvesting cleaning process in fresh market tomatoes production is essential to the consumer acceptance, since the degree of dirtiness of the fruits is directly related to its quality. However, the washing stage of the cleaning process of commercial packinghouse demands an excessive water volume, bringing serious environmental concerns. The objective of this work was to compare the cleaning efficiency in two cleaning systems through the evaluation of different operational conditions of the cleaning process, related with the brush rotation, water flow and fruit standing time under the system. It was compared the conventional system utilized in commercial equipment with a system using commercial sprays. The results showed that the cleaning efficiency was not directly related to the water volume used, but to the water pressure, standing time and brushes rotation. Therefore, the use of commercial sprays can bring benefits to the cleaning efficiency, increasing it up to 13%, and to the environmental, decreasing water consumption.

Caminhada de pessoas com deficiencia visual em areas naturais : um estudo com auxilio do GPS (Sistema de Posicionamento Global)

Universidade Estadual de Campinas . Faculdade de Educação Física

Analise das capacidades de resistencia, força e velocidade na periodização de modalidades intermitentes

Universidade Estadual de Campinas . Faculdade de Educação Física