Estudo inicial da degradação in vivo de poli(L-co-D,L ácido lático), sintetizado em laboratório, aplicado como prótese tibial em coelhos

The copolymer poly (L-co-D,L lactic acid), PLDLA, has gained prominence in the field of temporary prostheses due to the fact that their time of degradation is quite compatible with the requirement in the case of osseous fracture. In this work the in vivo degradation of devices from copolymer, as a system of plates and screws, used in fixation of the tibia of rabbits was studied. The devices were implanted in 15 adult rabbits, albinos, New Zealand race, and they were used as control devices of alloys of titanium (Ti-6Al-4V/ V grade). The use of copolymers, synthesized in the laboratory, was tested in the repair of fracture in rabbits'tibias, being assessed in the following times: 2 weeks, 2 months and 3 months. Morphological analysis of tissue surrounding the plate and screw system, for 2 weeks of implantation, showed the presence of osteoblasts, indicating a pre bone formation. After 2 months there was new bone formation in the region in contact with the polymer. This bone growth occurred simultaneously with the process of PLDLA degradation, invading the region where there was polymer and after 3 months there was an intense degradation of the copolymer and hence greater tissue invasion compared to 2 months which characterized bone formation in a region where the polymer degraded. The in vivo degradation study of the devices for PLDLA by means of histological evaluations during the period of consolidation of the fracture showed the efficiency of plate and screw system, and it was possible to check formation of bone tissue at the implantation site, without the presence of inflammatory reaction

Behaviour of oligodendrocytes and Schwann cells in an experimental model of toxic demyelination of the central nervous system

Oligodendrocytes and Schwann cells are engaged in myelin production, maintenance and repairing respectively in the central nervous system (CNS) and the peripheral nervous system (PNS). Whereas oligodendrocytes act only within the CNS, Schwann cells are able to invade the CNS in order to make new myelin sheaths around demyelinated axons. Both cells have some limitations in their activities, i.e. oligodendrocytes are post-mitotic cells and Schwann cells only get into the CNS in the absence of astrocytes. Ethidium bromide (EB) is a gliotoxic chemical that when injected locally within the CNS, induce demyelination. In the EB model of demyelination, glial cells are destroyed early after intoxication and Schwann cells are free to approach the naked central axons. In normal Wistar rats, regeneration of lost myelin sheaths can be achieved as early as thirteen days after intoxication; in Wistar rats immunosuppressed with cyclophosphamide the process is delayed and in rats administered cyclosporine it may be accelerated. Aiming the enlightening of those complex processes, all events concerning the myelinating cells in an experimental model are herein presented and discussed.

Análise de custo-efetividade de métodos preventivos para superfície oclusal de acordo com o risco de cárie: resultados de um ensaio clínico controlado

This study presents the results of a cost-effectiveness analysis in a controlled clinical trial on the effectiveness of a modified glass ionomer resin sealant ( Vitremer, 3M ESPE) and the application of fluoride varnish (Duraphat, Colgate) on occlusal surfaces of first permanent molars in children 6-8 years of age (N = 268), according to caries risk (high versus low). Children were examined semiannually by the same calibrated dentist for 24 months after allocation in six groups: high and low risk controls (oral health education every three months); high and low risk with varnish (oral health education every three months + varnish biannually); and high and low risk with sealant (oral health education every three months + a single application of sealant). Economic analysis showed that sealing permanent first molars of high-risk schoolchildren showed a C/E ratio of US$ 119.80 per saved occlusal surface and an incremental C/E ratio of US$ 108.36 per additional saved occlusal surface. The study concluded that sealing permanent first molars of high-risk schoolchildren was the most cost-effective intervention.

Avaliação in vitro do aparelho DIAGNOdent para diagnóstico oclusal

The aim of this study was to determine the effectiveness and reliability of laser fluorescence measurements in relation to occlusal caries diagnosis. DIAGNOdent 2095 (Kavo, Biberach, Germany), which has been developed especially for caries diagnosis, was utilized. Five (5) teeth were examined in the pilot test; after that, ten (10) teeth were examined in order to calibrate both examiners. Data were obtained from 66 teeth (36 molars and 30 premolars), totalizing 144 sites identified through photographs of the occlusal surfaces. Reproducibility was evaluated in 10 teeth. The interexaminer Spearman correlation (r) was 0.89 and the intra-examiner, 0.93 and 0.97 (examiner A and B, respectively). Validation was carried out by histological examination (stereomicroscope). For the two examiners the sensitivity of the device was relatively high, varying from 0.81 to 1.00, while specificity varied according to which validation criterion was used (0.77 - 0.86: enamel lesion / 0.52 - 0.59: dentin lesion). It was concluded that DIAGNodent presented good capacity of identifying any alteration of the dental surface, nevertheless it presents the disadvantage of accomplishing many false-positive diagnosis when the validation criterion is dentin lesion.

Efeito de baixas doses de radiação X em feridas suturadas e não suturadas - estudo experimental em ratos

The present work evaluated the effect of low doses of X-irradiation on the repairing process of sutured and nonsutured skin wounds in rats. For that, rats underwent a surgical proceedure, in which a 20 x 5-millimeter rectangular wound approximately 2-millimeter-deep was made in the dorsal region of each animal, and were divided in four groups: nonirradiated nonsutured; irradiated nonsutured ; nonirradiated sutured and irradiated sutured. The animals under irradiation were protected, during exposure, with a 2-millimeter-thick lead apron in such a way that only the incision was irradiated. Each animal was submitted to 18 seconds of exposure, undergoing a total of 7.4 rads. The evaluation of the effects of X-rays on the repairing process was carried out through microscopic observation by means of hematoxylin-eosin staining for morphological evaluation, and silver impregnation under polarized light for the observation of collagen synthesis. The results have shown that X-irradiation has caused delay in the repairing process, but it did not stop its development. The irradiated nonsutured group was considered to show the greater delay when compared with the other groups.

Desenvolvimento de uma metodologia para reconstrução da superficie do pe humano por videogrametria

Universidade Estadual de Campinas . Faculdade de Educação Física