Effect Of Platform Connection And Abutment Material On Stress Distribution In Single Anterior Implant-supported Restorations: A Nonlinear 3-dimensional Finite Element Analysis.

Although various abutment connections and materials have recently been introduced, insufficient data exist regarding the effect of stress distribution on their mechanical performance. The purpose of this study was to investigate the effect of different abutment materials and platform connections on stress distribution in single anterior implant-supported restorations with the finite element method. Nine experimental groups were modeled from the combination of 3 platform connections (external hexagon, internal hexagon, and Morse tapered) and 3 abutment materials (titanium, zirconia, and hybrid) as follows: external hexagon-titanium, external hexagon-zirconia, external hexagon-hybrid, internal hexagon-titanium, internal hexagon-zirconia, internal hexagon-hybrid, Morse tapered-titanium, Morse tapered-zirconia, and Morse tapered-hybrid. Finite element models consisted of a 4×13-mm implant, anatomic abutment, and lithium disilicate central incisor crown cemented over the abutment. The 49 N occlusal loading was applied in 6 steps to simulate the incisal guidance. Equivalent von Mises stress (σvM) was used for both the qualitative and quantitative evaluation of the implant and abutment in all the groups and the maximum (σmax) and minimum (σmin) principal stresses for the numerical comparison of the zirconia parts. The highest abutment σvM occurred in the Morse-tapered groups and the lowest in the external hexagon-hybrid, internal hexagon-titanium, and internal hexagon-hybrid groups. The σmax and σmin values were lower in the hybrid groups than in the zirconia groups. The stress distribution concentrated in the abutment-implant interface in all the groups, regardless of the platform connection or abutment material. The platform connection influenced the stress on abutments more than the abutment material. The stress values for implants were similar among different platform connections, but greater stress concentrations were observed in internal connections.

Direct Adhesive Pin-retained Restorations For Severely Worn Dentition Treatment: A 1.5-year Follow-up Report.

Excessive occlusal surface wear can result in occlusal disharmony, functional and esthetic impairment. As a therapeutic approach, conventional single crowns have been proposed, but this kind of treatment is complex, highly invasive and expensive. This case report describes the clinical outcomes of an alternative minimally invasive treatment based on direct adhesive-pin retained restorations. A 64-year-old woman with severely worn dentition, eating problems related to missing teeth and generalized tooth hypersensitivity was referred for treatment. Proper treatment planning based on the diagnostic wax-up simulation was used to guide the reconstruction of maxillary anterior teeth with direct composite resin over self-threading dentin pins. As the mandibular remaining teeth were extremely worn, a tooth-supported overdenture was installed. A stabilization splint was also used to protect the restorations. This treatment was a less expensive alternative to full-mouth rehabilitation with positive esthetic and functional outcomes after 1.5 years of follow-up.

Spectrophotometric Evaluation Of Dental Bleaching Under Orthodontic Bracket In Enamel And Dentin.

Aware of the diffusion capacity of bleaching in the dental tissues, many orthodontists are subjecting their patients to dental bleaching during orthodontic treatment for esthetic purposes or to anticipate the exchange of esthetic restorations after the orthodontic treatment. For this purpose specific products have been developed in pre-loaded whitening trays designed to fit over and around brackets and wires, with clinical efficacy proven. The objective of this study was to evaluate, through spectrophotometric reflectance, the effectiveness of dental bleaching under orthodontic bracket. Thirty-two bovine incisors crown blocks of 8 mm x 8 mm height lengths were used. Staining of tooth blocks with black tea was performed for six days. They were distributed randomly into 4 groups (1-home bleaching with bracket, 2- home bleaching without bracket, 3- office bleaching with bracket, 4 office bleaching without bracket). The color evaluation was performed (CIE L * a * b *) using color reflectance spectrophotometer. Metal brackets were bonded in groups 1 and 3. The groups 1 and 2 samples were subjected to the carbamide peroxide at 15%, 4 hours daily for 21 days. Groups 3 and 4 were subjected to 3 in-office bleaching treatment sessions, hydrogen peroxide 38%. After removal of the brackets, the second color evaluation was performed in tooth block, difference between the area under the bracket and around it, and after 7 days to verified color stability. Data analysis was performed using the paired t-test and two-way variance analysis and Tukey's. The home bleaching technique proved to be more effective compared to the office bleaching. There was a significant difference between the margin and center color values of the specimens that were subjected to bracket bonding. The bracket bond presence affected the effectiveness of both the home and office bleaching treatments. Key words:Tooth bleaching, spectrophotometry, orthodontics.

Influence Of Successive Light-activation On Degree Of Conversion And Knoop Hardness Of The First Layered Composite Increment.

To evaluate the influence of light-activation of second, third and fourth increments on degree of conversion (DC) and microhardness (KHN) of the top (T) and bottom (B) surface of the first increment. Forty samples (n = 5) were prepared. In groups 1-4, after each increment light-activation (multiple irradiation), T and B of the first increment were measured in DC and KHN. In groups 5-8, only the first increment was made (single irradiation) and measurements of DC and KHN were taken at 15 min intervals. The light-activation modes were (XL) 500 mW/cm(2) × 38 s (G1/G5); (S) 1000 mW/cm(2) × 19 s (G2/G6), (HP) 1400 mW/cm(2) × 14 s (G3/G7); (PE) 3200 mW/cm(2) × 6 s (G4/G8). Data for DC and KHN were analyzed separately by using PROC MIXED for repeated measures and Tukey-Kramer test (α = 0.05). For KHN, B showed lower values than T. PE resulted in lower values of KHN in B surface. For single and multiple irradiations, T and B of first measurement showed the lowest KHN and the fourth measurement showed the highest, with significant difference between them. For single irradiation, first and second increments presented similar KHN, different from the third and fourth increment, which did not differ between them. For multiple irradiations, the second light-activation resulted in KHN similar to first, third and fourth increments. For DC, except QTH, T presented higher DC than B. The light-activation of successive increments was not able to influence the KHN and DC of the first increment.

Efeito cariostático de restaurações adesivas em superfícies radiculares: estudo in vitro

Dental materials that release fluoride have been shown to be effective in caries inhibition around restorations. Adhesive materials would also be effective in caries inhibition by sealing and protecting cavity margins from acidic demineralization. This in vitro study tested the hypothesis that composite restorations with a dentin adhesive system have a caries preventive effect similar to that of an adhesive material with fluoride - glass-ionomer cement - on root surfaces. Twenty roots from extracted sound third molars were embedded in polystyrene resin and ground flat. Standardized cavities were prepared in leveled root surfaces and randomly restored with (a) Chelon-Fil (Espe) or (b) Z100/SingleBond (3M). Baseline indentations were measured at 100, 200 and 300 mum from the occlusal margins of each restoration and the surface microhardness values were obtained using a Knoop diamond indenter. A 2.0 mm wide margin around the restorations was submitted to a pH-cycling model, at 37ºC. After that, surface microhardness was measured again, as it was before. The differences between baseline and final surface microhardness were considered for statistical analysis. The median values of differences were (a): -3.8; -0.3; -1.0; and (b): 3.3; 2.5; 1.7, for the distances of 100, 200 and 300 mum, respectively. The Kruskal-Wallis test did not show statistically significant difference between 100, 200 and 300 mum distances in each tested group. There was no difference between the studied materials at the distances of 200 and 300 mum. Chelon-Fil was statistically different from Z100/SingleBond, at 100 mum (p<0.05). Under the studied conditions, the glass-ionomer cement had a higher caries preventive effect than the composite/dentin adhesive restorations.