Alteração dimensional linear de resinas para bases de próteses polimerizadas com microondas

This study examined the influence of three polymerization cycles (1: heat cure - long cycle; 2: heat cure - short cycle; and 3: microwave activation) on the linear dimensions of three denture base resins, immediately after deflasking, and 30 days after storage in distilled water at 37± 2ºC. The acrylic resins used were: Clássico, Lucitone 550 and Acron MC. The first two resins were submitted to all three polymerization cycles, and the Acron MC resin was cured by microwave activation only. The samples had three marks, and dimensions of 65 mm in length, 10 mm in width and 3 mm in thickness. Twenty-one test specimens were fabricated for each combination of resin and cure cycle, and they were submitted to three linear dimensional evaluations for two positions (A and B). The changes were evaluated using a microscope. The results indicated that all acrylic resins, regardless of the cure cycle, showed increased linear dimension after 30 days of storage in water. The composition of the acrylic resin affected the results more than the cure cycles, and the conventional acrylic resin (Lucitone 550 and Clássico) cured by microwave activation presented similar results when compared with the resin specific for microwave activation.

COMPARAÇÃO DAS PROPRIEDADES REOLÓGICAS DA MASSA DE CACAU TORRADA CONVENCIONALMENTE E POR MICROONDAS

Two kinds of roasting cocoa system: conventional batch method in electrical oven, and by microwaves, in a continuous microwave rotary applicator (2450MHz), were compared with respect to viscosity. Cocoa was roasted in whole beans and in nibs. The variable used in the microwave treatment was the power density applied to the whole beans (254,45 to 290,80 Wh/kg) and to the nibs (227,27 to 262,23 Wh/kg), with a constant holding time of 10 minutes. The variable used in the conventional roasting process was the roasting time of the beans (40 to 44 min) and the nibs (34 to 38 min), with constant temperature in the jacket of electric oven (150°C). Viscosity was measured in a Brookfield rheometer (mod RV-DVIII) at 40°C. In general, the plastic viscosity of the microwaved samples was lower than that of the conventional roasted samples. Also the nibs showed lower viscosities than the whole beans when roasted in the electric oven. The viscosity of the samples roasted in the microwave oven was lower in the whole beans than in the nibs. The product was sensorially evaluated by three experts in cocoa flavour, and it was shown that the flavour of the microwave roasted products was similar to that of the conventionally roasted products, with the advantage of a reduction in process time.