Effect Of Simulated Microwave Disinfection On The Linear Dimensional Change, Hardness And Impact Strength Of Acrylic Resins Processed By Different Polymerizing Cycles.

This study investigated the effect of simulated microwave disinfection (SMD) on the linear dimensional changes, hardness and impact strength of acrylic resins under different polymerization cycles. Metal dies with referential points were embedded in flasks with dental stone. Samples of Classico and Vipi acrylic resins were made following the manufacturers' recommendations. The assessed polymerization cycles were: A-- water bath at 74ºC for 9 h; B-- water bath at 74ºC for 8 h and temperature increased to 100ºC for 1 h; C-- water bath at 74ºC for 2 h and temperature increased to 100ºC for 1 h;; and D-- water bath at 120ºC and pressure of 60 pounds. Linear dimensional distances in length and width were measured after SMD and water storage at 37ºC for 7 and 30 days using an optical microscope. SMD was carried out with the samples immersed in 150 mL of water in an oven (650 W for 3 min). A load of 25 gf for 10 sec was used in the hardness test. Charpy impact test was performed with 40 kpcm. Data were submitted to ANOVA and Tukey's test (5%). The Classico resin was dimensionally steady in length in the A and D cycles for all periods, while the Vipi resin was steady in the A, B and C cycles for all periods. The Classico resin was dimensionally steady in width in the C and D cycles for all periods, and the Vipi resin was steady in all cycles and periods. The hardness values for Classico resin were steady in all cycles and periods, while the Vipi resin was steady only in the C cycle for all periods. Impact strength values for Classico resin were steady in the A, C and D cycles for all periods, while Vipi resin was steady in all cycles and periods. SMD promoted different effects on the linear dimensional changes, hardness and impact strength of acrylic resins submitted to different polymerization cycles when after SMD and water storage were considered.

Effect Of Simulated Microwave Disinfection On The Linear Dimensional Change, Hardness And Impact Strength Of Acrylic Resins Processed By Different Polymerization Cycles.

This study investigated the effect of simulated microwave disinfection (SMD) on the linear dimensional changes, hardness and impact strength of acrylic resins under different polymerization cycles. Metal dies with referential points were embedded in flasks with dental stone. Samples of Classico and Vipi acrylic resins were made following the manufacturers' recommendations. The assessed polymerization cycles were: A) water bath at 74 ºC for 9 h; B) water bath at 74 ºC for 8 h and temperature increased to 100 ºC for 1 h; C) water bath at 74 ºC for 2 h and temperature increased to 100 ºC for 1 h; and D) water bath at 120 ºC and pressure of 60 pounds. Linear dimensional distances in length and width were measured after SMD and water storage at 37 ºC for 7 and 30 days using an optical microscope. SMD was carried out with the samples immersed in 150 mL of water in an oven (650 W for 3 min). A load of 25 gf for 10 s was used in the hardness test. Charpy impact test was performed with 40 kpcm. Data were submitted to ANOVA and Tukey's test (5%). The Classico resin was dimensionally steady in length in the A and D cycles for all periods, while the Vipi resin was steady in the A, B and C cycles for all periods. The Classico resin was dimensionally steady in width in the C and D cycles for all periods, and the Vipi resin was steady in all cycles and periods. The hardness values for Classico resin were steady in all cycles and periods, while the Vipi resin was steady only in the C cycle for all periods. Impact strength values for Classico resin were steady in the A, C and D cycles for all periods, while Vipi resin was steady in all cycles and periods. SMD promoted different effects on the linear dimensional changes, hardness and impact strength of acrylic resins submitted to different polymerization cycles when after SMD and water storage were considered.

Determinação direta de molibdênio em comprimidos polivitamínicos por voltametria em meio não aquoso

Adsorptive stripping voltammetry carried out in a homogeneous ternary solvent composed of N,N-dimethylformamide, water and ethanol, with alpha-benzoinoxime (alphaBO) as the complexing agent for Mo(VI) and a 0.5 mol L-1 acetic acid - sodium acetate buffer as supporting electrolyte was successfully used for the determination of molybdenum in polyvitamin-polymineral tablets. Tablet samples were analyzed and the results were compared with those obtained both by graphite furnace atomic absorption and by recovery tests, with good correlations, indicating that this may be considered as an alternative procedure for routine determination of Mo(VI) in pharmaceutical samples.

Determinação espectrofotométrica de hexametilenotetramina (HMT) em medicamentos, utilizando ácido cromotrópico e forno de micro-ondas

This paper proposes a methodology for spectrophotometric determination of hexamethylenetetramine (HMT) by using chromotropic acid in a phosphoric acid media employing a domestic microwave oven as a source of heating. The reddish-purple soluble product is quantitatively formed after 30 s of irradiation and obeys the Beer´s law in the range between 0.1-1.2 mg L-1 HMT (r = 0.99925). The method was applied successfully in commercial pharmaceutical preparations containing dyes in their composition. The results showed that the method proposed is feasible for simplicity, speed, low cost, precision and accuracy when compared with United States Pharmacopeia official method.

Alteração dimensional linear de resinas para bases de próteses polimerizadas com microondas

This study examined the influence of three polymerization cycles (1: heat cure - long cycle; 2: heat cure - short cycle; and 3: microwave activation) on the linear dimensions of three denture base resins, immediately after deflasking, and 30 days after storage in distilled water at 37± 2ºC. The acrylic resins used were: Clássico, Lucitone 550 and Acron MC. The first two resins were submitted to all three polymerization cycles, and the Acron MC resin was cured by microwave activation only. The samples had three marks, and dimensions of 65 mm in length, 10 mm in width and 3 mm in thickness. Twenty-one test specimens were fabricated for each combination of resin and cure cycle, and they were submitted to three linear dimensional evaluations for two positions (A and B). The changes were evaluated using a microscope. The results indicated that all acrylic resins, regardless of the cure cycle, showed increased linear dimension after 30 days of storage in water. The composition of the acrylic resin affected the results more than the cure cycles, and the conventional acrylic resin (Lucitone 550 and Clássico) cured by microwave activation presented similar results when compared with the resin specific for microwave activation.

COMPARAÇÃO DAS PROPRIEDADES REOLÓGICAS DA MASSA DE CACAU TORRADA CONVENCIONALMENTE E POR MICROONDAS

Two kinds of roasting cocoa system: conventional batch method in electrical oven, and by microwaves, in a continuous microwave rotary applicator (2450MHz), were compared with respect to viscosity. Cocoa was roasted in whole beans and in nibs. The variable used in the microwave treatment was the power density applied to the whole beans (254,45 to 290,80 Wh/kg) and to the nibs (227,27 to 262,23 Wh/kg), with a constant holding time of 10 minutes. The variable used in the conventional roasting process was the roasting time of the beans (40 to 44 min) and the nibs (34 to 38 min), with constant temperature in the jacket of electric oven (150°C). Viscosity was measured in a Brookfield rheometer (mod RV-DVIII) at 40°C. In general, the plastic viscosity of the microwaved samples was lower than that of the conventional roasted samples. Also the nibs showed lower viscosities than the whole beans when roasted in the electric oven. The viscosity of the samples roasted in the microwave oven was lower in the whole beans than in the nibs. The product was sensorially evaluated by three experts in cocoa flavour, and it was shown that the flavour of the microwave roasted products was similar to that of the conventionally roasted products, with the advantage of a reduction in process time.