Effect Of Simulated Microwave Disinfection On The Linear Dimensional Change, Hardness And Impact Strength Of Acrylic Resins Processed By Different Polymerizing Cycles.

This study investigated the effect of simulated microwave disinfection (SMD) on the linear dimensional changes, hardness and impact strength of acrylic resins under different polymerization cycles. Metal dies with referential points were embedded in flasks with dental stone. Samples of Classico and Vipi acrylic resins were made following the manufacturers' recommendations. The assessed polymerization cycles were: A-- water bath at 74ºC for 9 h; B-- water bath at 74ºC for 8 h and temperature increased to 100ºC for 1 h; C-- water bath at 74ºC for 2 h and temperature increased to 100ºC for 1 h;; and D-- water bath at 120ºC and pressure of 60 pounds. Linear dimensional distances in length and width were measured after SMD and water storage at 37ºC for 7 and 30 days using an optical microscope. SMD was carried out with the samples immersed in 150 mL of water in an oven (650 W for 3 min). A load of 25 gf for 10 sec was used in the hardness test. Charpy impact test was performed with 40 kpcm. Data were submitted to ANOVA and Tukey's test (5%). The Classico resin was dimensionally steady in length in the A and D cycles for all periods, while the Vipi resin was steady in the A, B and C cycles for all periods. The Classico resin was dimensionally steady in width in the C and D cycles for all periods, and the Vipi resin was steady in all cycles and periods. The hardness values for Classico resin were steady in all cycles and periods, while the Vipi resin was steady only in the C cycle for all periods. Impact strength values for Classico resin were steady in the A, C and D cycles for all periods, while Vipi resin was steady in all cycles and periods. SMD promoted different effects on the linear dimensional changes, hardness and impact strength of acrylic resins submitted to different polymerization cycles when after SMD and water storage were considered.

Effect Of Simulated Microwave Disinfection On The Linear Dimensional Change, Hardness And Impact Strength Of Acrylic Resins Processed By Different Polymerization Cycles.

This study investigated the effect of simulated microwave disinfection (SMD) on the linear dimensional changes, hardness and impact strength of acrylic resins under different polymerization cycles. Metal dies with referential points were embedded in flasks with dental stone. Samples of Classico and Vipi acrylic resins were made following the manufacturers' recommendations. The assessed polymerization cycles were: A) water bath at 74 ºC for 9 h; B) water bath at 74 ºC for 8 h and temperature increased to 100 ºC for 1 h; C) water bath at 74 ºC for 2 h and temperature increased to 100 ºC for 1 h; and D) water bath at 120 ºC and pressure of 60 pounds. Linear dimensional distances in length and width were measured after SMD and water storage at 37 ºC for 7 and 30 days using an optical microscope. SMD was carried out with the samples immersed in 150 mL of water in an oven (650 W for 3 min). A load of 25 gf for 10 s was used in the hardness test. Charpy impact test was performed with 40 kpcm. Data were submitted to ANOVA and Tukey's test (5%). The Classico resin was dimensionally steady in length in the A and D cycles for all periods, while the Vipi resin was steady in the A, B and C cycles for all periods. The Classico resin was dimensionally steady in width in the C and D cycles for all periods, and the Vipi resin was steady in all cycles and periods. The hardness values for Classico resin were steady in all cycles and periods, while the Vipi resin was steady only in the C cycle for all periods. Impact strength values for Classico resin were steady in the A, C and D cycles for all periods, while Vipi resin was steady in all cycles and periods. SMD promoted different effects on the linear dimensional changes, hardness and impact strength of acrylic resins submitted to different polymerization cycles when after SMD and water storage were considered.

Association Of Lipophilic Opioids And Hyperbaric Bupivacaine In Spinal Anesthesia For Elective Cesarean Section. Randomized Controlled Study.

To evaluate the efficacy and side-effects of fentanyl and sufentanil combined with hyperbaric spinal bupivacaine in elective cesarean section. A prospective, randomized, double-blind study with 64 term parturients, distributed into 2 groups according to the opioid combined with hyperbaric bupivacaine 0.5% (10mg): GF - fentanyl (25 µg) and GS - sufentanil (5.0 µg). The latency and maximum sensory block level; degree and duration of motor block; duration and quality of analgesia; maternal-fetal repercussions were evaluated. This was an intention-to-treat analysis with a 5% significance level. The latency period, maximum sensory block level, motor block degree and perioperative analgesia were similar in both groups. Motor block and analgesia had a longer duration in the sufentanil group. Maternal adverse effects and neonatal repercussions were similar. The incidence of hypotension was higher in the fentanyl group. In both groups, there was a predominance of patients who were awake and either calm or sleepy. The addition of fentanyl and sufentanil to hyperbaric subarachnoid bupivacaine was shown to be effective for the performance of cesarean section, and safe for the mother and fetus. Analgesia was more prolonged with sufentanil.