Combined External Pressure And Cu-substitution Studies On Bafe2as2 Single Crystals.

We report a combined study of external pressure and Cu-substitution on BaFe2As2 single crystals grown by the in-flux technique. At ambient pressure, the Cu-substitution is known to suppress the spin density wave (SDW) phase in pure BaFe2As2(TSDW ≈ 140 K) and to induce a superconducting (SC) dome with a maximum transition temperature [Formula: see text]. This [Formula: see text] is much lower than the Tc ∼ 15-28 K achieved in the case of Ru, Ni and Co substitutions. Such a lower Tc is attributed to a Cu(2+) magnetic pair-breaking effect. The latter is strongly suppressed by applied pressure, as shown herein, Tc can be significantly enhanced by applying high pressures. In this work, we investigated the pressure effects on Cu(2+) magnetic pair-breaking in the BaFe2-xCuxAs2 series. Around the optimal concentration (xopd = 0.11), all samples showed a substantial increase of Tc as a function of pressure. Yet for those samples with a slightly higher doping level (over-doped regime), Tc presented a dome-like shape with maximum Tc ≃ 8 K. Remarkably interesting, the under-doped samples, e.g. x = 0.02 display a maximum pressure induced Tc ≃ 30 K which is comparable to the maximum Tc's found for the pure compound under external pressures. Furthermore, the magnetoresistance effect as a function of pressure in the normal state of the x = 0.02 sample also presented an evolution consistent with the screening of the Cu(2+) local moments. These findings demonstrate that the Cu(2+) magnetic pair-breaking effect is completely suppressed by applying pressure in the low concentration regime of Cu(2+) substituted BaFe2As2.

Estudo inicial da degradação in vivo de poli(L-co-D,L ácido lático), sintetizado em laboratório, aplicado como prótese tibial em coelhos

The copolymer poly (L-co-D,L lactic acid), PLDLA, has gained prominence in the field of temporary prostheses due to the fact that their time of degradation is quite compatible with the requirement in the case of osseous fracture. In this work the in vivo degradation of devices from copolymer, as a system of plates and screws, used in fixation of the tibia of rabbits was studied. The devices were implanted in 15 adult rabbits, albinos, New Zealand race, and they were used as control devices of alloys of titanium (Ti-6Al-4V/ V grade). The use of copolymers, synthesized in the laboratory, was tested in the repair of fracture in rabbits'tibias, being assessed in the following times: 2 weeks, 2 months and 3 months. Morphological analysis of tissue surrounding the plate and screw system, for 2 weeks of implantation, showed the presence of osteoblasts, indicating a pre bone formation. After 2 months there was new bone formation in the region in contact with the polymer. This bone growth occurred simultaneously with the process of PLDLA degradation, invading the region where there was polymer and after 3 months there was an intense degradation of the copolymer and hence greater tissue invasion compared to 2 months which characterized bone formation in a region where the polymer degraded. The in vivo degradation study of the devices for PLDLA by means of histological evaluations during the period of consolidation of the fracture showed the efficiency of plate and screw system, and it was possible to check formation of bone tissue at the implantation site, without the presence of inflammatory reaction