Control Of The Properties Of Porous Chitosan-alginate Membranes Through The Addition Of Different Proportions Of Pluronic F68.

This work addresses the development and characterization of porous chitosan-alginate based polyelectrolyte complexes, obtained by using two different proportions of the biocompatible surfactant Pluronic F68. These biomaterials are proposed for applications as biodegradable and biocompatible wound dressing and/or scaffolds. The results indicate that thickness, roughness, porosity and liquid uptake of the membranes increase with the amount of surfactant used, while their mechanical properties and stability in aqueous media decrease. Other important properties such as color and surface hydrophilicity (water contact angle) are not significantly altered or did not present a clear tendency of variation with the increase of the amount of surfactant added to the polyelectrolyte complexes, such as real density, average pore diameter, total pore volume and surface area. The prepared biomaterials were not cytotoxic to L929 cells. In conclusion, it is possible to tune the physicochemical properties of chitosan-alginate polyelectrolyte complexes, through the variation of the proportion of surfactant (Pluronic F68) added to the mixture, so as to enable the desired application of these biomaterials.

O emprego de quitosana quimicamente modificada com anidrido succínico na adsorção de azul de metileno

The adsorption capacity of alpha-chitosan and its modified form with succinic anhydride was compared with the traditional adsorbent active carbon by using the dye methylene blue, employed in the textile industry. The isotherms for both biopolymers were classified as SSA systems in the Giles model, more specifically in L class and subgroup 3. The dye concentration in the supernatant in the adsorption assay was determined through electronic spectroscopy. By calorimetric titration thermodynamic data of the interaction between methyene blue and the chemically modified chitosan at the solid/liquid interface were obtained. The enthalpy of the dye/chitosan interaction gave 2.47 ± 0.02 kJ mol-1 with an equilibrium constant of 7350 ± 10 and for the carbon/dye interaction this constant gave 5951 ± 8. The spontaneity of these adsorptions are reflected by the free Gibbs energies of -22.1 ± 0.4 and -21.5 ± 0.2 kJ mol-1, respectively, found for these systems. This new adsorbent derived from a natural polysaccharide is as efficient as activated carbon. However 97% of the bonded dye can be eluted by sodium chloride solution, while this same operation elutes only 42% from carbon. Chitosan is efficient in dye removal with the additional advantage of being cheap, non-toxic, biocompatible and biodegradable.

Blendas de PHB e seus copolímeros: miscibilidade e compatibilidade

Poly(hydroxybutyrate) and its copolymers are linear polyesters behaving as conventional thermoplastic materials. However, they are totally biodegradable and produced by a wide variety of bacteria from renewable sources. Some properties and high production cost are still preventing future applications. In an attempt to improve the properties and to reduce cost blending PHB with others polymeric materials is one of the most efficient method. In this paper, miscibility, compatibility, morphological and mechanical aspects of PHB blends will be reviewed. An extensive revision over twenty last years was realized about works of blends based on PHB and its copolymers.

Microencapsulação de óleo essencial de laranja

It was done microencapsulation of natural essencial orange oil through spray-drying. The purpose was to use the best proportion of wall materials among maltodextrin, acacia gum, and modified starch (capsul) in order to retain greater amount of orange oil. The orange oil (10%) and maltodextrin (36%) remained constant. Three spray drying temperatures were employed: 180°C, 200°C and 220°C, therefore, nine final products were obtained. The superficial and inner oil concentrations were measured. The microcapsules were also examined through optical and scanning electron microscopy. The three temperatures employed did not affect the microencapsulation. The microstructure of the capsules were almost similar regardless the proportion employed among the carbohydrates to wall composition. At light microscopy it was observed a great heterogeneity of capsules diameters, and probably not smooth surfaces; at scanning electron microscopy it was clear that the walls displayed porosity over round surfaces. The best retention was given by the formula containing 10% of capsul, 10% of orange oil and 36% of maltodextrin, when total oil retention was 94%, regardless the drying temperature here employed.